KR900003301A - 내충격성 폴리아미드 수지 조성물의 제조방법 - Google Patents
내충격성 폴리아미드 수지 조성물의 제조방법 Download PDFInfo
- Publication number
- KR900003301A KR900003301A KR1019890012007A KR890012007A KR900003301A KR 900003301 A KR900003301 A KR 900003301A KR 1019890012007 A KR1019890012007 A KR 1019890012007A KR 890012007 A KR890012007 A KR 890012007A KR 900003301 A KR900003301 A KR 900003301A
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- ethylene
- parts
- group
- copolymer
- Prior art date
Abstract
내용 없음
Description
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
Claims (10)
- (1)(A) 폴리아미드 수지 60 내지 20중량부를, (B)불포화 디카르복실산 무수물 0.01 내지 9중량%가 첨가된 올레핀고무, 불포화 디카르복실산 무수물 0.01 내지 9중량%가 첨가된 α-올레핀 중합체, 불포화 디카르복실산 무수물 0.01 내지 9중량%가 첨가된 결정성 에틸렌-α-올레핀 공중합체, 및 불포화 디카르복실산 무수물 0.01 내지 9중량%가 첨가된 에틸렌-에틸렌게 불포화 에스테르 공중합체로 이루어진 군으로부터 선택된 적어도 1종의 변성 올레핀 중합체 40 내지 80중량부와 응용-혼련하여 혼합물(Ⅰ)를 제조하고, (2)상기 혼합물 (Ⅰ)100중량부를, (C)카르복실기, 카르복실산 무수물기 또는 아미노기와 반응성인 2개 이상의 작응기를 분자내에 갖는 다작용성 화합물 0.01 내지 20중량부와 응용-혼련하여 혼합물(Ⅱ)를 제조하며, (3)상기 혼합물(Ⅱ) 100중량부를 (D)폴리아미드 수지 50 내지 1,000중량부와 응용-혼련함을 특징으로 하는, 내충격성 폴라아미드 수지 조성물의 제조방법.
- (1)(A)폴리아미드 수지 60 내지 20중량부를, (B)올레핀 고무, α-올래핀 중합체, 결정성 에틸렌-α-올레핀 공중합체 및 에틸렌-에틸렌계 불포화 에스테르 공중합체로 이루어진 군으로부터 선택되고 유리전이 온도가 -10℃이하인 적어도 1종의 올레핀 중합체 100중량부를 불포화 디카르복실산 무수물 0.1 내지 10중량부와 응용-혼련하여 수득된 변성 올래핀 중합체 40 내지 80중량부와 응용-혼련하여 혼합물 (Ⅰ)를 제조하고, (2)상기 혼합물(Ⅰ) 100중량부를, (C)카르복실기, 카르복실산 무수물기 또는 아미노기와 반응성인 2개 이상의 작용기를 분자내에 갖는 다작용성 화합물 0.01 내지 20중량부와 응용-혼련하여 혼합물(Ⅱ)를 제조하며, (3)상기 혼합물(Ⅱ) 100중량부를 (D)폴라아미드 수지 50 내지 1,000중량부와 응용-혼련함을 특징으로 하는, 내충격성 폴리아미드 수지 조성물의 제조방법.
- 제2항에 있어서, 변성 올레핀 중합체(B)를, 올레핀 고무 α-올레핀 중합체, 결정성 에틸렌-α-올레핀 공중합체 및 에틸렌-에틸렌게 불포화 에스테르 공중합체로 이루어진 군으로부터 선택되고 유리 전이온도가-10℃ 이하인 적어도 1종의 올레핀 중합체 100중량부를 불포화 디카르복실산 무수물 0.1 내지 10중량부 및 방향족 비닐 단량체 0.01 내지 50중량부와 응용-혼련하여 수둑하는 방법.
- 제2항에 있어서, 변성 올레핀 중합체(B)에 첨가된 불포화 디카르복실산 무수물이 말레산 무수물인 방법.
- 제1 또는 2항에 있어서, 변성 올레핀 중합체(B)의 기본 중합체가 올레핀 고무인 방법.
- 제5항에 있어서, 올레핀 고무가 에틸렌-프로필렌 공중합체인 방법.
- 제1 또는 2항에 있어서, 다작용성 화합물의 작용기가 아미노기, 애폭시기 및 히드록시기로 이루어진 군으로부터 선택되는 방법.
- 제1 또는 2항에 있어서, 다작용성 화합물이 지방족 디아민 카르바메이트인 방법.
- 제1 또는 2항에 있어서, 다작용성 화합물이 에틸렌유니트 및 N,N-디알킬아미노알킬 α,β-불포화 카르복실산 에스테르 유니트로 이루어진 에틸렌 공중합체, 또는 에틸렌유니트 및 N,N-디알킬아미노알킬 α,β-불포화카르복실산 아미드 유니트로 이루어진 에틸렌 공중합체인 방법.
- 제1 또는 2항에 있어서, 다작용성 화합물이 에틸렌 유니트 및 α,β-불포화 카르복실산 글리시딜 에스테르 유니트로 이루어진 에틸렌 공중합체 ; 에틸렌 유니트, α,β-불포화 카르복실산 글리시딜에스테르 유니트 및 α,β-불포화 카르복실산 알킬 에스테르 유니트로 이루어진 공중합체 ; 또는 에틸렌 유니트, α,β-불포화 카르복실산 글리시딜에스테르 유니트 및 카르복실산 비닐 에트테르 유니트로 이루어진 에틸렌 공중합체인 방법.※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.