KR880005032A - 결합된 지얼라이트 및 이의 제조방법 - Google Patents
결합된 지얼라이트 및 이의 제조방법 Download PDFInfo
- Publication number
- KR880005032A KR880005032A KR870011855A KR870011855A KR880005032A KR 880005032 A KR880005032 A KR 880005032A KR 870011855 A KR870011855 A KR 870011855A KR 870011855 A KR870011855 A KR 870011855A KR 880005032 A KR880005032 A KR 880005032A
- Authority
- KR
- South Korea
- Prior art keywords
- zeolite
- ammonium
- range
- alkyl
- weight
- Prior art date
Abstract
내용 없음
Description
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
Claims (12)
- 올리고머 실리카로 결합된 지얼라이트의 제조방법에 있어서, 물에 전술한 지얼라이트를 녹인 현탁액을 올리고머 실리카와 수산화 알킬-암모늄의 수용액으로 혼합시키며, 이렇게 수득한 현탁액을 급속 건조처리하는 것을 포함하며, 물속에 지얼라이트만이든 현탁액에서의 지얼라이트의 %가 20 내지 50중량%, 바람직하게는 25내지 35중량%의 범위에 포함되고, 용액에서의 올리고머 실리카와 수산화 알킬-암모늄간의 몰비가 0.05 내지 0.2, 바람직하게는 0.08 내지 0.15의 범위에 포함되고, 올리고머 실리카와 물간의 비가 0.025 내지 0.00125 범위내에 포함되고, 올리고머 실리카와 지얼라이트간의 비가 5:95내지 20:80의 범위내에 포함되고, 이 지얼라이트는 5 내지 13Å의 범위에 포함되는 다공의 직경을 가지며, 이 지얼라이트는 아래에서 선택되는 것을 특징으로 하는 제조방법:1) 소성되고 무수물의 지얼라이트,2) 소성되고 무수물로서 바람직하게는 암모늄이온으로 교환된 지얼라이트,3) 최종 소성의 실시없이, 수열처리의 수단에 의해서 수득되는것 같이, 임의로 과잉의 관련된 수산화물의 존제하에, 카운터-양이온으로서 암모늄 또는 알킬-암모늄 양이온을 포함하는 습윤의 지얼라이트.
- 제1항에 있어서, 지얼라이트가: A) Si, AL 및 B; B) Si, AL 및 Ti; C) Si, Ti 및 Fe; D) Ti 및 Si; E) Si 및 B;F) 지얼라이트 ZSM-5;G)지얼라이트 ZSM-11;H)지얼라이트 T. 을 기제로하는 방법.
- 제2항에 있어서, Si, AL 및 B를 기제로한 지얼라이트가 소성되고 무수물일때 아래의 몰비로 표시된 일반식을 만족하는 것을 특징으로 하는 방법:pHALO2ㆍqB2O3ㆍSiO2(1)이때 조건은 암모늄염기를 포함하는 지얼라이트 수화물에 대해서 만일 소성되고 무수물의 지얼라이트의 무게를 “Z”, 암모늄이온 또는 알킬-암모늄염기의 무게를 “A”,그리고 물의 무게를 “H”라하면, 아래의 관계식이 성립되고:여기서, 일반식(1)에서p는 0.034 내지 0.0050의 범위에 포함되는 값을 가지고q는 0.1내지 0.005의 범위에 포함되는 값을 가지고, 그리고 HALO2의 H+는 양이온에 의해서 최소한 부분적으로 대체될 수 있으며, 일반식(1)의 지얼라이트는 중요라인이 표A에 보고된 분말 X-선 회절 스펙트럼과 최소한 아래의 밴드를 나타내는 I.R. 스펙트럼을 가지며:여기서 wn는 cm-1로된 파장수이고, Irel은 상대강도이고, 여기서 s는 강함; ms는 중간-강함;m는 중간;mw는 중간-약함;w는 약함을 의미한다.
- 제2항에 있어서, Si,AL 및 Ti를 기제로한 지얼라이트가 소성되고 무수물일때 몰비로 표시된 아래의 일반식을 만족하는 것을 특징으로 하는 방법:pHALO2ㆍqTiO2ㆍSiO2(2)이때의 조건은, 암모늄 염기를 포함하는 지얼라이트 수화물에 대해서, 만일 소성되고 무수물의 지얼라이트의 무게를 “Z”, 암모늄이온 또는 알킬-암모늄 염기의 무게를 “A+”, 그리고 물의 무게를 “H”라하면, 아래의 관계식이 성립되고:여기서, 일반식(2)에서,p는 0이상, 0.050이하 또는 이와 같은 값을 가지고,q는 0이상 및 0.025이하 또는 이와 같은 값을; HALO2의 H+는 양이온에 의해서 최소한 부분적으로 대체가능하며, 여기서 지얼라이트는 그중에 라인이 표B에 보고된 분말의 X선회질 스펙트럼과 최소한 아래의 밴드를 나타내는 I.R.스펙트럼을 가지며:여기서 wn는 cm-1로된 파장수이고, Irel은 상대강도이고, 여기서 s는 강함; ms는 중간-강함;m는 중간;mw는 중간-약함;w는 약함을 의미한다.
- 제2항에 있어서, Si와 Ti를 기제로한 지얼라이트가 소성되고 무수물일때 몰비로 표시된 아래의 일반식을 만족시키는 것을 특징으로 하는 방법:xTiO2ㆍ(1-x)SiO2(3)이때의 조건은, 암모늄 염기를 포함하는 지얼라이트 수화물에 대해서, 만일 소성된 무수물의 지얼라이트의 무게를 “Z”, 암모늄이온이나 알킬-암모늄 염기의 무게를 “A+”, 그리고 물의 무게를 “H”라하면, 아래의 관계식이 성립되며:여기서 일반식(3)에서, x는 미국특허 제 4,410,501호에 따라 0.0005 내지 0.04, 바람직하게는 0.01 내지 0.025의 범위에 포함된다.
- 제2항에 있어서, Si,Ti 및 Fe를 기제로한 지얼라이트가 소성되어 무수일때, 몰비로서 아래의 일반식을 만족하는 것을 특징으로 하는 방법:pHFeO2ㆍqTiO2ㆍSiO2(4)이때 조건은, 암모늄 염기를 포함하는 지얼라이트 수화물에 대해서, 만일 소성된 무수물인 지얼라이트의 무게를 “Z”, 암모늄이온 또는 알킬-암모늄 염기의 무게를 “A+”, 그리고 물의 무게를 “H”라고하면, 아래의 관계식이 성립되며:여기서, 일반식(4)에서,p는 0이상의 그리고 0.050이하 또는 이와 같은 값을 가지고,q는 0이상 및 0.025이하 또는 이와 같은 값을 가지고; 그리고 HFeO2의 H+는 양이온에 의해서 최소한 부분적으로 대체가능하며, 여기서, 일반식(4)을 가지는 지얼라이트는 최소한 아래의 밴드를 나타내는 I.R.스펙트럼을 나타내며:여기서 wn는 cm-1로된 파장수이고, Irel은 상대강도이고, 여기서 s는 강함; ms는 중간-강함;m는 중간;mw는 중간-약함;w는 약함을 의미한다.
- 제1항에 있어서, 실리카 및 수산화 알킬-알모늄의 용액을 2℃내지 120℃의 범위, 바람직하게는 50℃내지 60℃ 범위에 포함되는 온도에서, 0.2 내지 24시간의 범위에 포함되는 시간동안, 수산화 알킬-암모늄의 수용액에든 테트라알킬-오르토실리케이트가 테트라에틸-오르토실리케이트인 방법.
- 제7항에 있어서, 테트라알킬-오르토실리케이트가 테트라에틸-오르토실리케이트인 방법.
- 제1항에 있어서, 수산화 알킬-암모늄이 1내지 5의 범위에 포함되는 탄소원자수를 가진 알킬을 가지는 방법.
- 제9항에 있어서, 알킬-암모늄이 테트라프로필-암모늄인 방법.
- 지얼라이트 A, 또는 지얼라이트 B, 또는 지얼라이트 C, 또는 지얼라이트 D, 또는 지얼라이트 E, 또는 지얼라이트 F, 또는 지얼라이트 G, 또는 지얼라이트 H의 결정체가 5:95 내지 20:80의 범위에 포함되는 올리고머 실리카 대 지얼라이트 A, 또는 대 지얼라이트 B,또는 대 지얼라이트 C, 또는 대 지얼라이트 D, 또는 대 지얼라이트 E, 또는 대 지얼라이트 F, 또는 대 지얼라이트 G, 또는 대 지얼라이트 H의 몰비를 가지는 미세구 형태이고, 지얼라이트 A, 또는 지얼라이트 B, 또는 지얼라이트 C, 또는 지얼라이트 D, 또는 지얼라이트 E, 또는 지얼라이트 F, 또는 지얼라이트 G, 또는 지얼라이트 H의 결정체가 Si-O-Si 가교의 수단에의해서 서로서로 가두어지는 것을 특징으로 하는 올리고머 실리카로 결합된 지얼라이트.
- 제11항에 있어서, 미세구가 5내지 1,000μm의 범위에 포함되는 직경을 가지는 결합된 실리카.※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.