KR870007294A - 엔드밀용 입방정질화붕소 소결체 - Google Patents

엔드밀용 입방정질화붕소 소결체 Download PDF

Info

Publication number
KR870007294A
KR870007294A KR870000029A KR870000029A KR870007294A KR 870007294 A KR870007294 A KR 870007294A KR 870000029 A KR870000029 A KR 870000029A KR 870000029 A KR870000029 A KR 870000029A KR 870007294 A KR870007294 A KR 870007294A
Authority
KR
South Korea
Prior art keywords
binder
titanium
tungsten
aluminum
sintered body
Prior art date
Application number
KR870000029A
Other languages
English (en)
Other versions
KR930000466B1 (ko
Inventor
데쯔오 나까이
미쯔히로 고또오
Original Assignee
나까하라 쓰네오
스미도모덴기고오교오 가부시기가이샤
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 나까하라 쓰네오, 스미도모덴기고오교오 가부시기가이샤 filed Critical 나까하라 쓰네오
Publication of KR870007294A publication Critical patent/KR870007294A/ko
Application granted granted Critical
Publication of KR930000466B1 publication Critical patent/KR930000466B1/ko

Abstract

내용 없음

Description

엔드밀용 입방정질화붕소 소결체
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음

Claims (9)

  1. 평균입경이 2㎛이하인 입방정질화붕소분말을 35내지 50체적% 함유하고 잔부로서 결합제를 함유하는 혼합분말을 CBN 안정조건하에서 소결하여서 얻고, 상기 결합재는 대략 20내지 30중량%의 알루미늄과 TiNz, Ti(C,N)z, TICz, (Ti,M)Cz, (Ti,M)(C,N)z 및 (Ti,M)Nz(M은 티탄을 제외한 주기율표의 Ⅳa, Va 또는 Ⅵa족의 전이금속원소를 표시하고 z는 0.7z0.85의 범위내에 있다)의 군에서 선택된 1종 이상의 티탄화합물을 함유하고, 티탄을 제외한 주기율표의 Ⅳa, Va 또는 Ⅵa족의 상기 전이금속원소의 함유량에 대한 상기 결합재의 티탄함유량의 원자비는 대략 2/3 내지 97/100이고, 상기 티탄화합물 및 WC 중 적어도 한가지 형태의 텅스텐을 함유하고, 결합재중의 텅스텐 총농도는 대략 5내지 20중량%인 것을 특징으로하는 엔드밀용 CBN 소결체.
  2. 제1항에 있어서, 상기 소결체는 CBN 이외에, TiN, Ti(C,N), TIC, (Ti,M)C, (Ti,M)(C,N) 및 (Ti,M)N의 군에서 선택된 1종 이상과, 붕화티탄, 붕화알루미늄, 질화알루미늄, 텅스텐화합물 및 텅스텐의 군에서 선택된 1종 이상을 함유하는 것을 특징으로하는 엔드밀용 CBM 소결체.
  3. 제1항에 있어서, 상기 결합재는 대략 20내지 30중량%의 알루미늄을 함유하고 상기 티탄화합물은 TiNz 또는 (Ti,W)Nz(z는 대략 0.7z대략 0.85)이고 상기 텅스텐은 탄화텅스텐의 형태로 상기 결합재중에 대략 5내지 15중량%가 함유되는 것을 특징으로 하는 엔드밀용 CBN 소결체.
  4. 제1항에 있어서, 상기 알루미늄은 알루미늄화합물의 형태로 혼합되는 것을 특징으로하는 엔드밀용 CBN 소결체.
  5. 제1항에 있어서, 상기 CBN 분말은 평균입경이 대략 1㎛이하인 것을 특징으로하는 엔드밀용 CBN소결체.
  6. 평균입경이 대략 2㎛이하인 입방정질화붕소분말 대략 35내지 50체적%를 결합재 50내지 65체적%와 혼합하여 혼합분말을 얻는 공정과, 상기 결합재는 대략 20내지 30중량%의 알루미늄과 TiNz, Ti(C,N)z, TiCz, (Ti,M)Cz, (Ti,M)(C,N)z 및 (Ti,M)Nz(M은 티탄을 제외한 주기율표의 Ⅳa, Va 또는 Ⅵa족의 전이금속원소를 표시하고 z는 0.7z0.85의 범위내에 있다)의 군에서 선택된 1종 이상의 티탄화합물을 함유하고, 티탄을 제외한 주기율표의 Ⅳa, Va 또는 Ⅵa족의 상기 전이금속원소의 함유량에 대한 상기 결합재의 티탄함유량의 원자비는 대략 2/3 내지 97/100이고, 상기 티탄화합물 및 WC 중 적어도 한가지 형태의 텅스텐을 함유하고, 결합재중의 텅스텐 총농도는 대략 5내지 20중량%이고, 상기 혼합분말은 CBN이 안정한 초고압조건하에서 소결하는 공정으로 이루어지는 것을 특징으로 하는 엔드밀용 CBN 소결체의 제조방법.
  7. 제6항에 있어서, 상기 소결은 대략 20kb이상의 압력 및 1000℃ 내지 1500℃의 온도에서 행하는 것을 특징으로 하는 엔드밀용 CBN 소결체의 제조방법.
  8. 제6항에 있어서, 상기 텅스텐은 탄화텅스텐의 형태로 혼합되는 것을 특징으로 하는 엔드밀용 CBN소결체의 제조방법.
  9. 제6항에 있어서, 상기 알루미늄은 알루미늄화합물의 형태로 혼합되는 것을 특징으로하는 엔드밀용 CBN 소결체의 제조방법.
    ※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.
KR1019870000029A 1986-01-06 1987-01-06 엔드 밀용 입방정질화붕소 소결체 및 그 제조방법 KR930000466B1 (ko)