KR20150135235A - 물-용해성 주조 몰드를 이용하여 몰딩을 생성하기 위한 프로세스 및 그의 생성을 위한 물질 시스템 - Google Patents

물-용해성 주조 몰드를 이용하여 몰딩을 생성하기 위한 프로세스 및 그의 생성을 위한 물질 시스템 Download PDF

Info

Publication number
KR20150135235A
KR20150135235A KR1020157022638A KR20157022638A KR20150135235A KR 20150135235 A KR20150135235 A KR 20150135235A KR 1020157022638 A KR1020157022638 A KR 1020157022638A KR 20157022638 A KR20157022638 A KR 20157022638A KR 20150135235 A KR20150135235 A KR 20150135235A
Authority
KR
South Korea
Prior art keywords
casting mold
water
soluble
casting
producing
Prior art date
Application number
KR1020157022638A
Other languages
English (en)
Other versions
KR102048732B1 (ko
Inventor
다니엘 귄터
잉고 뉘흐텔
비트 바레르
Original Assignee
복셀젯 아게
플루이드 솔리즈 아게
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 복셀젯 아게, 플루이드 솔리즈 아게 filed Critical 복셀젯 아게
Publication of KR20150135235A publication Critical patent/KR20150135235A/ko
Application granted granted Critical
Publication of KR102048732B1 publication Critical patent/KR102048732B1/ko

Abstract

몰딩(16)을 생성하기 위한 프로세스로서, 제 1 단계에서, 물-용해성 주조 몰드(6)는 층 구조 프로세스에 의해, 특히 분말 베드-기반의 층 구조 프로세스에 의해 생성된다. 제 2 단계에서, 주조 몰드(6)의 표면은 물질(9; 10)로 밀봉된다. 그런 후에, 몰딩(16)의 주조는 흐를 수 있는 경화가능 물질(13), 특히 수압 설정 물질로 주조 몰드(6)를 채움으로써 형성된다. 주조가 고체화된 후에, 주조 몰드(6)는 수용성 용액(18), 특히 제어된 온도에서의 수용성 용액(18)으로 용해된다. 본 출원은 또한 물-용해성 주조 몰드(6)를 생성하기 위한 물질 시스템에 관한 것으로, 층 구조 프로세스에서 주조 몰드(6)를 구축하기 위한 적어도 하나의 물-수용성 물질을 포함하고, 또한 주조 몰드(6)의 표면을 밀봉하기 위한 적어도 하나의 물질(9; 10)을 포함한다.

Description

물-용해성 주조 몰드를 이용하여 몰딩을 생성하기 위한 프로세스 및 그의 생성을 위한 물질 시스템{PROCESS FOR PRODUCING A MOULDING USING A WATER-SOLUBLE CASTING MOULD AND MATERIAL SYSTEM FOR THE PRODUCTION THEREOF}
본 발명은 물-용해성 주조 몰드를 이용하여 몰딩된 부분을 생성하기 위한 방법뿐 아니라 그 생성을 위한 물질 시스템에 관한 것이다.
알려진 사출-몰딩 방법을 이용하여 생성되는 플라스틱 부분은 높은 강도와 양호한 표면 품질 및 저렴한 생산 비용을 특징으로 한다. 이것은 주조 콘크리트, 석고 또는 다른 경화 물질로 만들어진 성분에 적용된다. 하지만, 대응하는 주조 몰드의 생성은 높은 정밀도를 요구하기 때문에 비교적 비용이 많이 든다.
신속 조형술(rapid prototyping)과 같이, 층에서 객체를 구축하는 방법, 예를 들어 3D 프린팅 방법은 양호한 정밀도 레벨로 객체를 빠르고 비용에 효율적으로 생성하는 것을 가능하게 한다. 그러므로, 경화 물질을 위한 주조 몰드를 생성하기 위해 이러한 유형의 방법을 이용하는 것이 바람직하다. 하지만, 층화(layering) 방법을 이용하여 생성된 주조 몰드의 다공성은 경화 물질의 설정 및 몰드 충진 행동 및 표면 품질에 악영향을 끼친다.
몰드로부터 주조를 파손하는 문제는 또한 최근까지 만족스럽게 해결되지 않았다.
DE 691 25 064 T2는 언더컷(undercuts) 또는 공동(cavity) 구성과 같은 복잡한 형태를 이용하여 몰드에서 제품을 주조하는 방법을 기재한다. 이 방법에서, 미립자 물질로 만들어진 물-용해성 주조 몰드 코어와, 주조 이후에 물로 용해될 수 있는 물-용해성 카본히드레이트가 생성된다. 하지만, 주조가능한 물질은 몰드를 침투하지 않는데, 이는 몰드가 경계 표면 상에서 다공성이 아니기 때문이다.
DE 195 25 307 A1은 결합제(binder)의 도움으로 고체화되는 건조 요소로부터 생성되는 주조 코어를 개시한다. 주조 코어는, 주조가 생성된 후에 물의 도움으로 용해되고 세척된다. 주조 코어는 건조사(dry sand) 또는 펄라이트로 생성될 뿐 아니라, 물-용해성 결합제로서 디소듐 포스페이트로 생성된다.
DE 10 2005 019 699 B3는 주조 몰드 또는 주조 코어로서 금속 염 입자로부터 3차원 객체를 생성하는 방법을 기재한다. 이러한 이유로 인해, 3차원 객체는 일가 또는 다가, 물-용해성 및/또는 알코올-용해성 금속 염을 포함하는 입자로 만들어진 층화 방법에 사용된다.
인용된 종래 기술의 문헌 어느 것도 본 발명을 개시하거나 제안하지 않는다.
분말 베드-기반의 층화 방법을 이용하여 생성된 주조 몰드를 이용하는 것에서의 중요한 단점은 그 다공성에 있고, 이것은 분말 물질의 이용으로부터 초래된다. 이러한 다공성은 유압 설정 물질로부터 정확하고 치수적으로 정밀한 주조의 생성에 대한 장애물이다.
알려진 방법의 다른 단점은 생성될 몰딩된 부분으로부터 주조 프로세스에 필요한 몰드를 쉽고 완전히 분리할 수 있는 능력(이에 따라, 무능력)이다.
본 발명의 목적은 도입부에 언급된 기술 분야에 속하는 방법을 제공하는 것이고, 이것은 층화 방법, 용이하게 되는 몰드로부터 몰딩된 부분의 정확하고 치수적으로 정밀한 주조뿐 아니라 간단한 이탈(breakout)을 이용하여 생성된 주조 몰드의 도움으로, 또는 적어도 종래 기술의 단점을 감소시키거나 완전히 피하기 위해, 몰딩된 부분을 생성하는 것을 가능하게 한다.
목적의 달성은 제1항의 특징에 의해 한정된다. 본 발명에 따라, 물-용해성 주조 몰드는 층화 방법을 이용하여 제 1 단계에서 생성된다. 특히, 주조 몰드는 바람직하게 분말 베드-기반의 층화 방법을 이용하여 생성된다. 주조 몰드의 표면은 제 2 단계에서 물-용해성 물질로 밀봉된다. 몰딩된 부분의 주조는 후속하여 자유롭게 흐르는 경화 물질로 주조 몰드를 채움으로써 생성된다. 주조가 고체화된 후에, 주조 몰드는 특히 가열될 수 있는 수용성 용액의 도움으로 용해된다.
물-불용해성 물질로 밀봉하는 것으로 인해, 주조 몰드에 존재하는 기공은 차단될 수 있고, 주조 몰드의 가능한 표면 거칠기(roughness)는 매끄럽게 될 수 있다. 그 결과, 치수적으로 정확하고 정밀한 주조를 용이하게 하는 매끄러운 표면은 분말 베드-기반의 층화 방법으로 생성된 주조 몰드에서도 생성될 수 있다. 주조 몰드가 물-용해성 물질로 만들어지기 때문에, 수용성 용액의 도움으로 고체화된 몰딩된 부분으로부터 쉽고 빠르게 제거될 수 있고, 몰딩된 부분으로부터의 밀봉에 사용된 물-불용해성 물질을 동시에 세척하는 것이 가능하다. 또한, 밀봉 프로세스로 인해, 자유롭게 흐르는 경화 물질에 의해 주조 몰드의 표면의 상당한 침투가 발생하지 않는다는 것이 놀랍게도 결정되었다.
본 발명은 이에 따라 유리하게 복잡한 주조 몰드를 제공하고, 이것은 3D 프린팅으로 인해 쉽고 빠르게 그리고 비용에 효율적으로 생성될 수 있다. 더욱이, 본 발명에 따라 생성된 주조 몰드의 도움으로 복잡한 주조 몰드를 생성하는 것이 가능할 뿐 아니라, 주조 몰드가 주조 이후에 제거될 수 있는 방식으로 인해 주조에서 언더컷을 구현하는 것이 가능하다.
놀랍게도, 세척 단계는 이러한 방식으로 쉽게 수행되고, 주조 몰드가 완전히 제거될 수 있다. 본 발명에 따른 방법으로 인해, 이에 따라 구성요소는 소량의 물질, 에너지 및 시간을 이용하여 비용에 효율적인 작업 단계에서 빠르고 완전히 제거될 수 있다.
더욱이, 놀랍게도, 밀봉을 생성하는 것이 쉽고, 매우 양호한 주조 결과가 달성될 수 있다. 그 대신, 주조 물질에 의해 주조 몰드 및 밀봉의 상당한 침투와, 이에 의해 예상될 주조 부정밀도를 알도록 예측되었다. 하지만, 이것은 본 발명에 따른 방법에 사용된 방법 단계와, 선택된 밀봉 프로세스에 그러하지 않았고, 매우 양호한 주조 품질이 달성될 수 있다. 그러므로, 놀랍게도 양호한 표면은 와이드 프로세스 윈도우 내에서 달성될 수 있다.
본 발명에 따른 방법 및 물질의 특수한 조합을 이용하여, 이제 3D 프린팅 동안 초래되는 다공성 뿐 아니라 주조를 위한 부정적인 및 바람직하지 않은 부정밀도를 피하는 것이 가능하다. 예기치 않게, 매우 높은 표면 품질은 본 발명에 따른 방법의 도움으로 달성될 수 있고, 이것은 주조 단계에서 높은 정확도를 용이하게 한다.
본 출원의 의미 내에서 "물-용해성 물질"은 초과 물 또는 수용성 용액의 존재에서 완전히 용해되는 물질인 것으로 이해된다. 초과라는 것은, 물 또는 수용성 용액의 부피가 용해될 물질의 부피보다 적어도 동일하거나 크다는 것을 의미하는 것으로 이해된다. 특히, 물-용해성 물질의 용해도는 리터당 1g보다 크다.
주조는 생성될 몰딩된 부분의 외부 형태의 적어도 하나의 음의 압인(impression)을 갖는다. 층화 방법을 이용하여 생성된 주조 몰드는 바람직하게 또한 생성될 몰딩된 부분 내에서 내부 형태 또는 공동을 형성하는 코어를 포함한다. 특히, 본 발명에 따른 주조 몰드는 언더컷과 같이 복잡한 기하학적 형태를 갖는다.
종래 기술로부터 알려진 모든 층화 방법은 예를 들어 융합된 증착 모델링과 같은 층화 방법으로서 사용될 수 있다. 이러한 방법에서, 물-용해성 물질은 공간에서 이동가능한 압출기 노즐에 의해 층에 도포된다. 하지만, 분말 베드-기반의 층화 방법이 특히 바람직하게 사용되며, 여기서 미립자 물질은 플랫폼 상으로 얇은 층에서 도포되고, 컴퓨터-제어된 프린트 헤드는 이들 영역의 본딩을 위해 디지털 데이터 리코드에 기초하여 결합제를 가지고 영역을 프린팅한다. 방법의 마지막에서 본딩되지 않은 초과 미립자 물질은 후속하여 본딩된 물질로부터 제거될 수 있는데, 예를 들어 재사용될 수 있다.
사실상, 3D 프린팅을 위한 종래 기술로부터 알려진 모든 물질은 미립자 물질, 예를 들어, 모래, 석고, 열가소성 물질뿐 아니라 금속, 광물, 실리케이트 또는 세라믹 분말로서 사용될 수 있다. 본 출원의 범주 내에 사용된 "미립자 물질"이라는 용어는 셀룰로오스 섬유, 목질 섬유, 그래스 섬유(grass fiber) 등과 같은 섬유 물질 및 입상 물질 모두를 포함한다. 물-용해성 결합제는 적어도 다당류, 단백질, 염, 실리케이트, 탄닌, 폴리비닐 아세테이트, 폴리비닐 알코올, 폴리비닐피롤리돈 또는 이들의 혼합물과 같은 결합제로서 사용된다.
주조 몰드는 물-불용해성 물질의 도움으로 표면을 밀봉하기 전에 바람직하게 세척된다. 더욱이, 주조 몰드의 표면은 또한 밀봉 이전에, 예를 들어, 그라인딩(grinding)에 의해 기계적으로 처리될 수 있다.
본 출원의 의미 내에서 "물-불용해성 물질"은 물에서 용해도가 없거나 매우 작은 용해도, 예를 들어 리터당 1g 미만을 갖는 물질인 것으로 이해된다. 온수로 주조 몰드를 용해할 때 낮은 유리 전이 온도를 갖는 경화 물질로부터 생성된 몰딩된 부분의 가능한 변형을 피하기 위해, 특히 매우 낮은-용해 왁스 또는 지방이 사용될 수 있다.
본 출원의 관점에서 "경화 물질"은 화학 반응에 의해 자유롭게 흐르는 상태로부터 경화된 상태로 전이하는 물질인 것으로 이해된다. 바람직하게, 특히 이것은 중축합, 중첨가 또는 이온 중합화에 의해 중합화 반응이 발생하는 물질이다. 특히, 경화 물질은 바람직하게 수압 설정 물질, 즉 흡습(hydroscopic) 특징을 갖고 결정 구조에서 결정의 물로서 물을 저장하는 물질을 포함하고, 물질은 결정 구조의 형성으로 인해 경화된다.
물질은 바람직하게 시멘트-결속 물질, 아연 포스페이트 시멘트, 석고, 칼슘 설페이트(경석고)뿐 아니라 폴리우레탄, 에폭시 수지, 폴리스티렌, 폴리아크릴레이트, 폴리아미드, 폴리에스테르 및/또는 폴리이미드뿐 아니라 생물 분해성 플라스틱을 포함한다. 주조 몰드가 충진되는 경화가능 물질이 경화된 물질의 기본 물질 또는 대응하는 폴리머의 단량체를 포함하는 것이 이해된다. 그러므로, 예를 들어, 이소시아네이트뿐 아니라 폴리우레탄을 형성하기 위한 폴리올을 [이에 따라, 포함한다]. 몰딩된 부분의 주조를 생성하기 위해, 물질은 자유롭게 흐르는데, 즉 주조 몰드가 물질로 채워지게 할 정도로 충분히 낮은 점도를 갖는다.
사실상, 고체화를 위해 용매의 제거를 요구하지 않는 모든 시스템이 적합하다. 이것은 모든 2-구성요소 플라스틱 시스템을 포함한다. 하나의 특히 바람직한 특정 실시예에서, 섬유 유리 강화재는 주조 몰드에 주입되고, 주조 몰드는 후속하여 2-구성요소 주조 폴리우레탄으로 채워진다. 경화 동안 강력한 발열 반응을 나타내는 물질에 대해, 주조 몰드는 주조 몰드의 표면을 밀봉하는데 사용된 물-불용해성 물질의 용해를 피하기 위해 외부로부터 추가로 냉각될 수 있다.
본 발명의 의미 내에서 "수용성 용액"은 50% 이상, 바람직하게 75% 이상의 부피 비인 물을 함유하는 용액인 것으로 이해된다. 순수한 물은 특히 바람직하게 수용성 용액으로서, 특히 증류수에서 사용된다.
수용성 용액은 특히 바람직하게 주조 몰드를 용해하기 위해 가열되는데, 즉 20℃의 일반적인 실온보다 높은 온도, 예를 들어, 80℃를 갖는다. 특히, 사용된 물-불용해성 물질의 용해 온도보다 높은 온도가 선택된다. 그 결과, 물-불용해성 물질은, 주조 몰드가 용해됨과 동시에 몰딩된 부분의 주조로부터 빠르고 신뢰성있게 제거될 수 있다.
물-용해성 주조 몰드의 생성에 사용된 물질의 선택뿐 아니라 물-불용해성 물질의 선택은 바람직하게, 주조 몰드가 용해되고 개별적으로 재사용된 후에 이들 물질이 수용성 용액으로부터 쉽게 분리될 수 있는 방식으로 발생한다. 예를 들어, 물-불용해성 물질은 수용성 용액이 냉각된 후에 결정화될 수 있고, 주조 몰드의 물-용해성 물질은 수용성 용액으로부터 필터링될 수 있다.
주조 몰드는 바람직하게 3D 프린팅 프로세스로 생성된다. 이것은 특히 바람직하게 분말 베드-기반의 3D 프린팅 프로세스로 생성된다.
주조 몰드의 표면은 바람직하게 배스(bath)에서의 침지에 의해, 이를 분무함으로써 및/또는 이를 브러싱(brushing)함으로써 물-불용해성 물질로 밀봉된다. 물-불용해성 물질은 바람직하게 용해 온도보다 높게 가열함으로써 밀봉하기 전에 액화된다. 대안적으로, 물-불용해성 물질은 또한 휘발성의 유기 용매의 도움으로서 용해될 수 있고, 유기 용액으로서 주조 몰드의 표면에 도포될 수 있고, 물-불용해성 물질의 층은 용매가 완전히 증발된 후에 주조 몰드의 표면 상에 남아있다.
주조 물질이 물질로 채워지는 동안, 및/또는 요동(shaking) 운동 또는 온도 증가를 받는 동안 저압(underpressure) 또는 과압(overpressure)은 바람직하게 주조 몰드에 가해진다. 이것은, 주조 몰드에 존재하는 몰딩된 부분의 음의 압입이 자유롭게 흐르는 경화 물질로 완전히 채워지는 것을 보장하는 것을 가능하게 한다.
시멘트-결속 물질이 사용되면, 특히 주조에서의 강화재를 포함하는 것이 가능하다. 이들 강화재는 와이어 메쉬, 섬유 유리 직물 또는 비교가능한 구조로서 설계될 수 있다. 하지만, 시멘트 물질은 주조 몰드를 채우기 위한 낮은 점도로 설정되어야 한다. 종래 기술로부터 알려진 흐름 개선 첨가물 및 구체 응집물 또는 특수 모래는 이러한 목적에 적합하다. 중공의 유리 볼을 추가로 도입함으로써, 몰딩된 부분은 본 발명에 따른 방법을 이용하여 극도로 경량의 시멘트 물질로 생성될 수 있다.
강화재는 발생할 수 있지만, 반드시 그럴 필요는 없다. 마찬가지로, 몰딩된 부분을 강화하기 위해 다른 충진재, 특히 단섬유(short fibers) 또는 나노 입자가 물질에 첨가될 수 있다.
특히, 탄성 몰딩된 부분은 본 발명에 따른 방법을 이용하여 바람직하게 생성될 수 있다. 2-구성요소 실리콘은 그 상당히 낮은 점도로 인해 이를 위해 특히 적합하다.
주조 몰드는 바람직하게 수용성 용액을 함유하는 배스에 주조 몰드를 침지함으로써 용해된다. 용해는 바람직하게 배스 내의 주조 몰드의 이동에 의해 또는 온도 증가에 의해 및/또는 초음파를 적용함으로써 가속화된다.
주조 몰드는 예를 들어, 주조 몰드를 손으로 앞뒤로 시프팅(shifting)함으로써, 배스에서 활성적으로 이동될 수 있다. 대안적으로, 배스는 락커(rocker) 상에 위치될 수 있거나, 수용성 용액은 혼합 디바이스의 도움으로 운동 상태로 설정될 수 있다. 온도 증가는 바람직하게, 배스가 그 위에 위치되는 외부 열원에 의해, 또는 침지 가열 시스템의 도움으로 발생한다. 초음파의 적용은 바람직하게 상업적으로 이용가능한 초음파 배스에서 발생한다.
주조 몰드의 용해는 특히 바람직하게 압력솥에서 발생한다. 압력솥에서 생성된 과압 및 스팀의 높은 열로 인해, 본 발명에 따른 주조 몰드, 및 밀봉에 사용된 물-불용해성 물질은 몰딩된 부분의 주조로부터 잔여물 없이 빠르게 제거될 수 있다.
특히, 주조 폴리아미드는 물-불용해성 물질로서 사용된다. "주조 폴리아미드"는 이온 중합화에 의해 카프롤락탐으로부터 얻어지는 열가소성 물질인 것으로 이해된다.
본 발명의 다른 양상은, 특히 본 발명에 따른 방법에 사용되는 물-용해성 주조 몰드를 생성하기 위한 물질 시스템을 제공하는 것이다. 물질 시스템은 층화 방법으로 주조 몰드를 구축하기 위한 적어도 하나의 물-용해성 물질뿐 아니라 주조 몰드의 표면을 밀봉하기 위한 적어도 하나의 물-불용해성 물질을 포함한다. 물-용해성 물질은 적어도 하나의 미립자 물질뿐 아니라 적어도 하나의 물-용해성 결합제를 포함한다.
이러한 물질 시스템은 층화 방법으로 주조 몰드를 생성하는데 사용될 수 있고, 이것은 생성될 몰딩된 부분의 주조를 생성한 후에 수용성 용액에서 쉽게 용해될 수 있고, 몰드로부터의 이탈 및 언더컷 또는 코어와 같은 복잡한 형태의 형성은 이를 통해 간략화된다.
적어도 하나의 결합제는 바람직하게 무기 화합물을 포함한다. 특히, 적어도 하나의 결합제는 바람직하게 나트륨 및/또는 칼륨 실리케이트를 포함한다. 또한 "물유리(water glass)"라는 명칭으로 알려진 이들 실리케이트는 높은 물-용해성이고, 독성을 갖지 않는다. 적어도 하나의 결합제는 또한 바람직하게 시트 실리케이트를 포함할 수 있다.
적어도 하나의 결합제는 바람직하게 적어도 하나의 다당류, 특히 수크로오스 또는 전분, 적어도 하나의 단백질, 적어도 하나의 실리케이트, 적어도 하나의 염 및/또는 적어도 하나의 물-용해성 폴리머, 특히 폴리비닐 알코올, 폴리비닐 아세테이트 또는 폴리비닐피롤리돈 또는 이들의 혼합물을 포함한다.
다당류는 특히, 재결정화에 의해, 예를 들어, 이전에 가열된 과도 포화된 용액을 냉각시킴으로써 환경적으로 호환가능하고 무독성 결합제로서 사용될 수 있다.
물-불용해성 물질은 바람직하게 왁스, 적어도 하나의 지방산, 적어도 하나의 물-불용해성 폴리머, 스테아릴 알코올 및/또는 세틸 알코올 또는 이들의 혼합물을 포함한다.
적합한 왁스는 예를 들어, 밀납과 같은 동물성 왁스 또는 카르나우바 왁스와 같은 식물성 왁스이다. 하지만, 가격으로 인해 파라핀과 같은 합성 왁스가 바람직하게 사용된다.
본 발명의 다른 양상은 본 발명에 따른 물질 시스템으로부터 생성되는 주조 몰드에 관한 것이다. 이러한 유형의 주조 몰드는 층화 방법에 의해 쉽고 빠르게 생성될 수 있고, 물-불용해성 물질로 주조 몰드의 표면을 밀봉함으로써 몰딩된 부분의 정밀하고 치수적으로 정확한 주조를 생성하는 것이 가능하다. 주조 몰드는 후속하여 수용성 용액을 도포함으로써 쉽고 빠르게 제거될 수 있다.
본 발명의 다른 양상은 본 발명에 따른 방법에 의해 생성되는 몰딩된 부분에 관한 것이다.
본 발명의 다른 유리한 특정 실시예 및 특징 조합은 다음의 상세한 설명 및 특허 청구항 전체로부터 도출된다.
도면은 예시적인 실시예를 설명하는데 사용된다.
본 발명은 층화 방법, 용이하게 되는 몰드로부터 몰딩된 부분의 정확하고 치수적으로 정밀한 주조뿐 아니라 간단한 이탈(breakout)을 이용하여 생성된 주조 몰드의 도움으로, 또는 적어도 종래 기술의 단점을 감소시키거나 완전히 피하기 위해, 몰딩된 부분을 생성하는 것을 가능하게 하는 효과를 갖는다.
도 1은 몰딩된 부분의 음의 압입과, 코어를 포함하는 주조 몰드를 도시한 도면.
도 2는 몰딩된 부분의 층 등급 및 다공성을 도시한 도면.
도 3a 및 도 3b는 2가지 유형의 밀봉을 도시한 도면.
도 4는 주조 몰드를 포함하는 침지 배스를 도시한 도면.
도 5는 경화 물질을 이용한 주조 몰드의 충진을 도시한 도면.
도 6은 주조 몰드를 용해하기 위한 배스의 제 1 특정 실시예를 도시한 도면.
도 7은 주조 몰드를 용해하기 위한 배스의 제 2 특정 실시예를 도시한 도면.
도 8은 주조 몰드를 용해하기 위한 배스의 제 3 특정 실시예를 도시한 도면.
도 9는 주조 몰드를 용해하기 위한 분무 챔버를 도시한 도면.
사실상, 동일한 부분은 도면에서 동일한 도면 부호를 구비한다.
도 1은 본 발명에 따른 방법의 특정 실시예에 사용되는 물-용해성 주조 몰드(1)를 도시한다. 주조 몰드(1)는 생성될 몰딩된 부분의 외부 형태의 음의 압인(3)을 갖는다. 음의 압인(3) 내에 배치되는 코어(4)는 또한 예시된 예시적인 실시예에 도시된다. 주조 몰드(1)는 경화 물질로 주조 몰드(1)를 채우기 위한 충진 개구부(2)를 갖는다. 추가적인 층화 방법은 몰드(1) 및 코어(4)를 생성하는데 사용될 수 있다. 미립자 물질을 선택하는데 있어서 특별한 자유도로 인해, 3D 프린팅 방법이 특히 바람직하게 사용된다.
단면도에 기초하여, 도 2는 분말 베드-기반의 층화 방법의 도움으로 생성된 주조 몰드(1)의 결과적인 다공성(6) 및 층 구조(5)의 예를 도시한다. 사용된 3D 프린팅 방벙에서, 코팅기는 미립자 물질 또는 미립자 물질의 혼합물 및 결합제를 빌딩 플랫폼(building platform) 상에 층에 도포하고, 각 층(5)은 정밀하게 레벨화(leveled)된다. 결합제를 활성화하는 결합제 또는 액체는 후속하여 잉크젯 프린트 헤드의 도움으로 도포된다. 이러한 도포는 생성될 몰드의 단면에 대응한다. 현재 층(5)은 낮아지고, 사이클은 새로운 코팅으로 다시 전면적으로 시작한다. 사이클은, 전체 단면이 원하는 주조 몰드(1)에서 초래될 때까지 반복한다. 특정 휴지(rest) 시간에 뒤이어, 주조 몰드(1)는 제거될 수 있고, 결속되지 않은 미립자 물질은 그로부터 세척될 수 있다. 건조 단계 또는 열 처리는 후속하여 고체화 목적을 위해 수행될 수 있다. 이러한 단계는, 주조 몰드(1)의 물 용해도가 손실되지 않는 방식으로 설정되어야 한다.
물-불용해성 물질을 이용하여 주조 몰드(1)의 표면을 밀봉하는 2가지 방식은 도 3a 및 도 3b에 도시된다. 도 3a는 표피적인 밀봉을 도시하고, 물-불용해성 물질은 주조 몰드(1)의 표면 상에 밀봉 층(9)을 형성하였다. 개방-기공 네트워크를 형성하는 개별적인 입자(7) 사이의 기공(8)은 밀봉 표면(9) 아래에 나타난다. 밀봉 표면(9)은, 주조 몰드(1)가 경화 물질로 채워질 때 경화 물질이 기공(8)에 들어가는 것을 방지하고, 이것은 경화 물질의 도움으로 생성된 주조의 표면 특성이 저하되도록 한다. 도 3b는, 물-불용해성 물질(10)이 침투되어, 기공(8)의 네트워크를 밀봉하는 밀봉 방법을 도시한다. 후자의 밀봉 방법은 특히, 낮은 점도를 갖는 물-불용해성 물질을 이용할 때 발생한다. 물-불용해성 물질의 점도에 따라, 도 3a 및 도 3b에서의 2가지 밀봉 방법의 혼합된 형태가 또한 초래된다.
도 4는, 주조 몰드(1)가 액화된 물-불용해성 물질(12)에 주입되도록 하는 침지 배스(11)의 개략도를 도시한다. 주조 몰드(1)의 전체 표면에 걸친 밀봉은 주조 몰드(1)를 이러한 유형의 침지 배스(11)에 도입함으로써 비교적 바르게 달성될 수 있다.
밀봉 단계는, 주조 몰드가 경화 물질과 상호 작용하는 것을 방지하고, 높은 표면 품질을 보장하는데 필요하다. 예를 들어, 콘크리트로 채워지는 동안 어떠한 물도 주조 몰드를 침투하지 않을 수 있는데, 이는 물의 손실로 인해 콘크리트의 유동성이 손실되도록 하고, 몰드의 불충분한 충진이 이를 통해 달성되기 때문이다. 더욱이, 밀봉은 더 양호한 표면 품질을 달성하는데 도움을 줄 수 있다. 경화 물질과 결합제 또는 주조 몰드의 미립자 물질 사이의 화학 반응이 또한 방지될 수 있다.
도 5는 경화 물질(13)로 주조 몰드(1)를 채우는 단계를 도시한다. 경화 물질(13)은 주조 몰드(1)의 충진 개구부(3)를 통해 자유롭게 흐르는 형태로 음의 압인(4)에 채워진다. 진동(15)은 요동 테이블(shaking table)과 같은 적합한 디바이스의 도움으로 주조 몰드(1)에 가해질 수 있다.
주조 몰드의 충진은 순수한 중력 주조 프로세스로서 수행될 수 있다. 이를 위해 어떠한 특정 예방책도 취할 필요도 없다. 경화 물질은 낮은 점도를 가져야 하고, 주조 몰드의 설계는, 변위된 공기가 물질의 상승 레벨을 통해 빠져나가도록 해야 한다.
도 6은, 물질이 수용성 용액(18)으로 이루어진 배스(17)에서 경화된 후에 몰딩된 부분(16)을 도시한다. 예시된 배스(17)에서, 수용성 용액(18)은 주조 몰드(1)의 용해를 가속화하도록 가열된다. 예시된 특정 실시예에서, 용해된 주조 몰드의 미립자 물질(20)은 배스(17)의 하부 상에서 수집되는 한편, 용해된 물-불용해성 물질은 수용성 용액(18)의 표면 상에 층(19)을 형성한다. 이러한 층(19)은 후속하여 수용성 용액(18)의 표면으로부터 간단히 걷어질 수 있고, 재사용되는 한편, 미립자 물질(20)은 수용성 용액(18)으로부터 필터링될 수 있다.
도 7 및 도 8은 수용성 용액(18)을 함유하는 배스(17)의 2가지 다른 바람직한 특정 실시예를 도시한다. 도 7에 도시된 특정 실시예에서, 몰딩된 부분(16)은 격자(grating)(21)의 도움으로 수용성 용액(18)에서 운동으로 추가로 설정된다. 도 8에서의 특정 실시예에서, 몰딩된 부분(16)은 몰딩된 부분(16)을 잡는 그리퍼(22)의 도움으로 수용성 용액에서 시프팅되고, 그 안에서 주조된다.
주조 몰드(1)를 용해하기 위한 다른 특정 실시예는 도 9에 도시된다. 특정 실시예에서, 몰딩된 부분(16)은 분무 챔버(24) 내에 유지되고, 온수는 다중 스프레이 헤드(25)를 통해 주조 몰드(1) 또는 몰딩된 부분(16) 상으로 스프레이된다. 분무 챔버(24)의 하부 상에서 수집된 물은 후속하여 주조 몰드의 용해된 물질로부터, 그리고 적합한 필터를 통해 물-불용해성 물질로부터 분리될 수 있고, 이것은 가열된 요소(23)의 도움으로 가열되고, 펌프(26)(26.1, 26.2)의 도움으로 스프레이 헤드(25)를 통해 주조 몰드 또는 몰딩된 부분(16) 상으로 다시 스프레이된다.

Claims (10)

  1. 몰딩된 부분(16)을 생성하기 위한 방법으로서,
    a) 층화(layering) 방법을 이용하여, 특히 분말-베드 기반의 층화 방법을 이용하여 물-용해성 주조 몰드(6)를 생성하는 단계와;
    b) 주조 몰드(6)의 표면을 물질(9;10)로 밀봉하는 단계와;
    c) 자유롭게 흐르는 경화가능 물질(13), 특히 수압 설정 물질로 주조 몰드(6)를 채움으로써 몰딩된 부분(16)의 주조를 생성하는 단계와;
    d) 수용성 용액(18), 특히 주조가 고체화된 후에 온도-제어된 수용성 용액(18)의 도움으로 주조 몰드(6)를 용해하는 단계를
    포함하는, 몰딩된 부분(16)을 생성하기 위한 방법에 있어서,
    바람직하게 주조 몰드(6)는 3D 프린팅 방법으로 생성되고,
    바람직하게 주조 몰드(6)의 표면을 밀봉하기 위한 물질(9;10)은 물-용해성인 것을 특징으로 하는, 몰딩된 부분을 생성하기 위한 방법.
  2. 제 1항에 있어서, 주조 몰드(6)의 표면은 배스(bath)(11)에서의 침지에 의해, 물질(9;10)로 스프레이됨으로써 및/또는 브러슁(brushed)됨으로써 밀봉되는 것을 특징으로 하는, 몰딩된 부분을 생성하기 위한 방법.
  3. 제 1항 또는 제 2항에 있어서, 저압 또는 과압은 자유롭게 흐르는 경화가능 물질(13)로 채워질 때 주조 몰드(6)에 가해지고, 및/또는 요동 운동 또는 온도 증가를 받는 것을 특징으로 하는, 몰딩된 부분을 생성하기 위한 방법.
  4. 제 1항 내지 제 3항 중 어느 한 항에 있어서, 주조 몰드(6)는 수용성 용액(18)을 함유하는 배스(17)에서의 침지에 의해 용해되고, 용해는 바람직하게 배스(17) 내의 주조 몰드(6)의 이동에 의해 또는 온도 증가에 의해 및/또는 초음파의 적용에 의해 가속화되는 것을 특징으로 하는, 몰딩된 부분을 생성하기 위한 방법.
  5. 제 1항 내지 제 4항 중 어느 한 항에 있어서, 주조 몰드(6)의 용해는 압력솥에서 발생하는 것을 특징으로 하는, 몰딩된 부분을 생성하기 위한 방법.
  6. 제 1항 내지 제 5항 중 어느 한 항에 있어서, 주조 몰드(6)는 경화가능 물질로서 주조 폴리아미드를 이용하기 위한 비열 저항을 갖는 물질(9; 10)의 도움으로 밀봉되는 것을 특징으로 하는, 몰딩된 부분을 생성하기 위한 방법.
  7. 특히 제 1항 내지 제 6항 중 어느 한 항에 따른 방법에 사용하기 위해 물-용해성 주조 몰드(6)를 생성하기 위한 물질 시스템으로서,
    a) 층화 방법으로 주조 몰드(6)를 구축하기 위한 적어도 하나의 물-용해성 물질로서, 적어도 하나의 미립자 물질(7) 및 적어도 하나의 물-용해성 결합제를 포함하는, 적어도 하나의 물-용해성 물질과;
    b) 주조 몰드(6)의 표면을 밀봉하기 위한 적어도 하나의 물질(9; 10)을
    포함하는, 물-용해성 주조 몰드(6)를 생성하기 위한 물질 시스템에 있어서,
    바람직하게 적어도 하나의 물-용해성 결합제는 적어도 하나의 무기 화합물, 바람직하게 칼슘, 칼륨 및/또는 시트 실리케이트를 포함하고,
    바람직하게 적어도 하나의 결합제는 적어도 하나의 다당류, 특히 수크로오스 또는 전분, 적어도 하나의 염 및/또는 적어도 하나의 물-용해성 폴리머, 특히 단백질, 폴리비닐 알코올, 폴리비닐 아세테이트 또는 폴리비닐피롤리돈 또는 이들의 혼합물을 포함하는 것을 특징으로 하는, 물-용해성 주조 몰드를 생성하기 위한 물질 시스템.
  8. 제 7항에 있어서, 주조 몰드(6)를 밀봉하기 위한 물질(9, 10)은 왁스, 적어도 하나의 지방산, 적어도 하나의 물-불용해성 폴리머, 스테아릴 알코올 및/또는 세틸 알코올 또는 이들의 혼합물을 포함하는 것을 특징으로 하는, 물-용해성 주조 몰드를 생성하기 위한 물질 시스템.
  9. 제 7항 또는 제 8항에 따른 물질 시스템의 도움으로 생성된 주조 몰드(6).
  10. 제 1항 내지 제 5항 중 어느 한 항에 따른 방법에 따라 생성된 몰딩된 부분.
KR1020157022638A 2013-02-28 2014-02-18 물-용해성 주조 몰드를 이용하여 몰딩을 생성하기 위한 프로세스 및 그의 생성을 위한 물질 시스템 KR102048732B1 (ko)