KR102658723B1 - 리튬 이차전지용 음극의 제조방법 - Google Patents
리튬 이차전지용 음극의 제조방법 Download PDFInfo
- Publication number
- KR102658723B1 KR102658723B1 KR1020190110716A KR20190110716A KR102658723B1 KR 102658723 B1 KR102658723 B1 KR 102658723B1 KR 1020190110716 A KR1020190110716 A KR 1020190110716A KR 20190110716 A KR20190110716 A KR 20190110716A KR 102658723 B1 KR102658723 B1 KR 102658723B1
- Authority
- KR
- South Korea
- Prior art keywords
- lithium
- negative electrode
- layer
- manufacturing
- protective layer
- Prior art date
Abstract
본 발명의 리튬 이차전지용 음극의 제조방법은, 기재와 보호층을 포함하는 전사용 필름의 보호층 상에 리튬 층을 형성하여 리튬 전사용 필름을 제조하는 단계; 집전체 상에 음극활물질 층이 형성된 음극을 준비하여, 음극활물질 층 상에 리튬 층이 대면하도록 상기 리튬 전사용 필름을 접합 및 압연하는 전사 단계를 포함하고, 상기 보호층은 아크릴계 수지를 포함하고, 상기 전사 단계에서 음극활물질 층 상에 리튬층 및 보호층이 전사되는 것을 특징으로 한다.
Description
본 발명은 리튬 이차전지용 음극 및 이의 제조방법에 관한 것이다.
최근, 모바일 기기, 퍼스널 컴퓨터, 전기 모터, 일시 축전 장치의 개발 및 보급에 따라 고용량의 에너지원이 요구되고 있으며, 그 대표적인 예로서 리튬 이차 전지를 들 수 있다. 차세대형 비수 전해질 이차 전지의 음극 재료로서 종래의 흑연계 재료(이론 용량이 372mAh/g)의 10배 이상의 용량(4200mAh/g)을 가지는 규소(Si)가 주목받고 있다.
이로부터, 탄소계 재료를 대신할 신규 재료로서 높은 이론 용량을 나타내는 규소 산화물이나 주석 산화물과 같은 금속 산화물을 음극활물질로 이용하는 것이 제안되고 있다. 그러나, 이러한 금속 산화물은 충방전시 부피 변화가 발생하여 활물질에 균열 및 퇴화가 진행되어 이에 의해 사이클 수명이 저하되는 단점이 있다.
한편, 금속 산화물에 리튬을 선 삽입하는 전리튬화 기술이 시도되고 있다. 이러한 전리튬화 기술의 일예로 종래에는 음극활물질 층 표면에 리튬 금속 박막을 전사(라미네이션)하여 전극조립체를 제조한 후 전해액을 주액하여 리튬이 음극활물질층 내로 확산됨으로써 전리튬화되는 방식이 이용되고 있다.
위와 같은 전리튬화 방법은, 지지체 상에 리튬 금속을 형성한 후에 전사에 의해 리튬을 음극활물질 층 상에 부여할 때, 지지체로부터 리튬을 박리하는 것이 어렵다는 문제가 있다.
일본공개특허 제2013-020974호에는, 이차전지용 음극의 음극활물질 층 상에 리튬 금속 박막을 용이하게 전사할 수 있는 기술이 개시되어 있다. 이에 따르면 이형층 상에 리튬 보다 이형층에 대한 반응성이 낮은 보조층을 형성하고, 상기 보조층 상에 리튬을 증착하여 제조한 전사용 필름을 음극에 전사하여 보조층과 리튬층을 전사하는 공정을 포함하고 있다. 그러나 상기 기술은 보조층으로써 구리, 알루미늄, 니켈과 같은 금속 또는 금속 산화물을 적용하기 때문에, 전지의 조립 후 음극에 잔류하는 상기 보조층이 저항으로 작용하는 문제가 있었다.
이에 음극활물질 층 상에 리튬 금속을 전사함에 있어서, 지지체로부터 리튬을 용이하게 박리하면서도, 전지의 저항을 상승시키지 않는 기술 개발이 필요한 실정이다.
본 발명은, 음극활물질 층 상에 리튬 금속을 전사함에 있어서, 지지체로부터 리튬을 용이하게 박리하면서도, 전지의 저항을 상승시키지 않는 방법을 제공하는 것을 목적으로 한다.
상기 기술적 과제를 해결하기 위한 본 발명의 이차전지용 음극의 제조방법은, 기재와 보호층을 포함하는 전사용 필름의 보호층 상에 리튬 층을 형성하여 리튬 전사용 필름을 제조하는 단계; 집전체 상에 음극활물질 층이 형성된 음극을 준비하여, 음극활물질 층 상에 리튬 층이 대면하도록 상기 리튬 전사용 필름을 접합 및 압연하는 전사 단계를 포함하고, 상기 보호층은 아크릴계 수지를 포함하고, 상기 전사 단계에서 음극활물질 층 상에 리튬층 및 보호층이 전사되는 것을 특징으로 한다.
본 발명의 일 실시예에서, 상기 아크릴계 수지는, 메틸아크릴레이트, 에틸아크릴레이트, 이소프로필아크릴레이트, n-부틸아크릴레이트, 2-에틸헥실아크릴레이트, 메틸메타크릴레이트, 에틸메타크릴레이트, 이소프로필메타크릴레이트, n-부틸메타크릴레이트, 이소부틸메타크릴레이트, n-헥실메타크릴레이트 및 라우릴메타크릴레이트로 이루어진 군에서 선택한 1종 이상의 단량체로 이루어진 중합체이거나, 또는 상기 군에서 선택한 2종 이상의 단량체로 이루어진 공중합체이다.
본 발명의 일 실시예에서, 상기 전사용 필름의 보호층의 두께는 0.01 내지 5 ㎛일 수 있다.
본 발명의 일 실시예에서, 상기 전사용 필름의 기재와 보호층 사이에 이형층이 개재되어 있을 수 있다.
이때, 상기 이형층은 폴리에스터 주사슬에 실리콘 사슬이 그라프트 결합된 실리콘 변성 폴리에스터, 실리콘, 멜라민 및 불소로 이루어진 군에서 선택된 1종 또는 2종 이상일 수 있다.
본 발명의 일 실시예에서, 상기 리튬 전사용 필름을 제조하는 단계에서, 리튬층은 열 증착법(Thermal evaporation deposition), 진공 증착법(evaporation deposition), 화학 증착법(chemical deposition), 화학기상 증착법(CVD, chemical vapor deposition) 및 물리 증착법(physical vapor deposition) 중에서 선택된 하나의 방법으로 증착되어 형성되는 것일 수 있다.
본 발명의 일 실시예에서, 상기 리튬 전사용 필름을 제조하는 단계에서, 리튬층의 두께는 0.01 내지 20㎛의 범위가 바람직하다.
본 발명의 일 실시예에서, 상기 전사 단계 이후에 기재를 제거하는 단계를 더 포함한다.
본 발명의 일 실시예에서, 상기 리튬층의 증착 시 패턴 마스크를 이용하여 증착함으로써, 리튬층이 패턴을 가질 수 있다.
상기 방법으로 제조된 본 발명의 이차전지용 음극은 아크릴계 수지층이 저항으로 작용하지 않는 특징이 있다.
본 발명의 리튬 이차전지용 음극의 제조방법은, 리튬층이 기재층으로부터 용이하게 박리되는 효과가 있다.
또한, 리튬층과 함께 리튬층을 대기나 수증기로부터 보호하는 보호층도 함께 음극에 전사됨으로써, 리튬의 손실을 최소화하는 효과가 있다.
또한, 상기 보호층이 이차전지의 조립 후, 저항체로 작용하지 않아 전기적 성능 및 용량이 우수한 이차전지를 제공하는 효과가 있다.
도 1은 전사용 필름 상에 리튬층을 형성하는 리튬 전사용 필름을 제조하는 단계를 나타내는 모식도이다.
도 2는 음극활물질 층 상에 리튬층 및 보호층을 전사하는 단계를 나타내는 모식도이다.
도 3은 본 발명의 제조방법에 따라 제조된 리튬 이차전지용 음극의 단면도이다.
도 4 내지 7은 본 발명의 보호층에 포함되는 아크릴계 수지가 포함된 전해액에 의한 저항을 확인하기 위한 순환전압주사법에 의한 실험 결과를 나타내는 그래프이다.
도 2는 음극활물질 층 상에 리튬층 및 보호층을 전사하는 단계를 나타내는 모식도이다.
도 3은 본 발명의 제조방법에 따라 제조된 리튬 이차전지용 음극의 단면도이다.
도 4 내지 7은 본 발명의 보호층에 포함되는 아크릴계 수지가 포함된 전해액에 의한 저항을 확인하기 위한 순환전압주사법에 의한 실험 결과를 나타내는 그래프이다.
본 명세서 및 특허청구범위에 사용된 용어는 통상적이거나 사전적인 의미로 한정해서 해석되어서는 아니 되며, 발명자는 그 자신의 발명을 가장 최선의 방법으로 설명하기 위해 용어의 개념을 적절하게 정의할 수 있다는 원칙에 입각하여 본 발명의 기술적 사상에 부합하는 의미와 개념으로 해석되어야만 한다. 따라서, 본 명세서에 기재된 실시예에 도시된 구성은, 본 발명의 가장 바람직한 하나의 실시양태에 불과하고 본 발명의 기술적 사상을 모두 대변하는 것은 아니므로, 본 출원 시점에 있어서 이들을 대체할 수 있는 다양한 균등물 및 변형예가 있을 수 있음을 이해하여야 한다.
이하 본 발명을 자세히 설명한다.
본 발명의 리튬 이차전지용 음극의 제조방법은, 기재와 보호층을 포함하는 전사용 필름의 보호층 상에 리튬 층을 형성하여 리튬 전사용 필름을 제조하는 단계; 집전체 상에 음극활물질 층이 형성된 음극을 준비하여, 음극활물질 층 상에 리튬 층이 대면하도록 상기 리튬 전사용 필름을 접합 및 압연하는 전사 단계를 포함하고, 상기 보호층은 아크릴계 수지를 포함하고, 상기 전사 단계에서 음극활물질 층 상에 리튬층 및 보호층이 함께 전사되는 것을 특징으로 한다.
본 발명의 발명자들은, 리튬 전사용 필름의 보호층이 아크릴계 수지를 포함하는 경우, 리튬층과 보호층의 전사 후 기재가 용이하게 박리되어 리튬의 손실을 최소화 하면서도, 놀랍게도 보호층으로서 잔류하는 아크릴계 수지가 전지의 저항으로 작용하지 않는다는 사실을 발견하고 본 발명에 이르게 되었다.
도 1 은 리튬 전사용 필름을 제조하는 단계를 나타낸다. 도 1을 참조하면, 본 발명의 리튬 전사용 필름을 제조하는 단계는, 기재(12)와 보호층(11)을 포함하는 전사용 필름을 준비하고, 상기 보호층(11) 상에 리튬을 증착함으로써 리튬층(13)을 형성하는 것을 내용으로 한다.
상기 기재는, 리튬 금속을 증착시키는 단계에서의 높은 온도와 같은 공정 조건을 견뎌낼 수 있고, 증착된 리튬층을 전사하기 위한 권취 공정 중 리튬층이 기재 상으로 전사되는 역박리 문제를 방지할 수 있는 특징을 가지는 것일 수 있다.
예를 들면, 상기 기재는 폴리에틸렌테레프탈레이트(polyethylene terephthalate, PET), 폴리이미드(polyimide, PI), 폴리메틸메타크릴산(poly(methylmethacrylate), PMMA), 폴리프로필렌(Polypropylene), 폴리에틸렌(Polyethylene) 및 폴리카보네이트(Polycarbonate)로 이루어진 군에서 선택된 1종 이상일 수 있다.
또한, 상기 기재는 적어도 일면에 이형층이 형성된 것일 수 있으며, 양면에 이형층이 형성된 것일 수 있다. 상기 이형층으로 인하여 증착된 리튬층을 음극으로 전사하기 위한 권취 공정 중 리튬층이 기재 상으로 전사되는 역박리 문제를 방지할 수 있고, 또한, 리튬층 및 보호층을 음극활물질 층 상에 전사시킨 후 기재를 용이하게 분리시킬 수 있다. 상기 기재의 일면에 이형층이 형성된 경우, 상기 이형층은, 기재와 후술하는 보호층 사이에 개재된다.
상기 이형층은, 폴리에스터 주사슬에 실리콘 사슬이 그라프트 결합된 실리콘 변성 폴리에스터, Si, 멜라민 및 불소로 이루어진 군에서 선택된 1종 이상을 포함할 수 있다.
상기 이형층은 코팅법에 의해 형성될 수 있으며, 예컨대, 상기 코팅법은 딥코팅(dip coating), 분사코팅(spray coating), 스핀코팅(spin coating), 다이코팅(die coating), 그라비어 코팅(Gravure coating), 마이크로-그라비어 코팅(Micro-Gravure coating), 콤마 코팅(Comma coating) 및 롤코팅(roll coating)으로 이루어진 군에서 선택되는 방법일 수 있으나, 이에 제한되는 것은 아니며, 당업계에서 코팅층을 형성하기 위해 사용할 수 있는 코팅법을 다양하게 사용할 수 있다.
본 발명의 전사용 필름을 구성하는 보호층은 아크릴계 고분자 수지를 포함하는 것을 특징으로 한다. 보호층은, 전사 이후에 리튬 층을 공기나 수증기로부터 차단하는 역할을 하여 반응성이 큰 리튬의 손실을 감소시킬 수 있다는 이점이 있다.
상기 아크릴계 수지는, 아크릴레이트계 반복단위 및 메타크릴레이트계 반복단위로 이루어진 군에서 선택된 1종 이상의 반복단위를 포함하는 고분자일 수 있고, 구체적으로는 메틸아크릴레이트, 에틸아크릴레이트, 이소프로필아크릴레이트, n-부틸아크릴레이트, 2-에틸헥실아크릴레이트, 메틸메타크릴레이트, 에틸메타크릴레이트, 이소프로필메타크릴레이트, n-부틸메타크릴레이트, 이소부틸메타크릴레이트, n-헥실메타크릴레이트 및 라우릴메타크릴레이트로 이루어진 군에서 선택한 1종 이상의 단량체로 이루어진 중합체이거나, 또는 상기 군에서 선택한 2종 이상의 단량체로 이루어진 공중합체이다.
또한 상기 메타크릴레이트계 반복단위는, 방향족 고리를 갖는 메타크릴레이트 반복단위일 수 있으며, 상기 방향족 고리를 갖는 메타크릴레이트 반복단위는, 예를 들면, 탄소수 6 내지 12의 방향족 고리를 포함하는 메타크릴레이트로부터 유도된 반복단위들을 들 수 있고, 구체적으로는 페닐 메탈크릴레이트, 벤질 메타크릴레이트 등을 들 수 있다.
또한, 상기 아크릴계 수지는, 내열성 향상을 위해 방향족 비닐께 반복단위; 이미드계 반복단위; 비닐 시아나이드계 반복단위; 및 적어도 하나의 카르보닐기로 치환된 3원 내지 6월 헤테로 고리 반복단위로 이루어진 군에서 선택된 1종 이상의 반복단위를 추가로 포함할 수 있다.
상기 보호층은 상기 아크릴계 수지 외에 이형제를 더 포함할 수 있다. 이때, 아크릴계 수지는 보호층의 총 중량을 기준으로, 99.9 내지 99.99 중량%, 바람직하게는 99.92 내지 99.98 중량%, 보다 바람직하게는 99.94 내지 99.96 중량%를 포함할 수 있다. 아크릴계 수지가, 99.9 중량% 미만이면, 리튬 금속에 대한 보호 기능이 저하될 수 있고, 99.99 중량%를 초과하는 경우에는 산성 이형제의 함량이 상대적으로 감소하여 제조과정에서 이형성이 저하될 수 있으므로 바람직하지 않다. 보호층 자체에 이형제가 포함된 경우에는 리튬 금속에 대한 보호층 기능과 동시에 전사용 필름에 포함된 기재를 제거할 때 이형층의 역할을 할 수 있으므로, 전사용 필름에 전술한 바와 같은 별도의 이형층은 불필요할 것이다.
또한, 상기 이형제는 산성(acid) 이형제인 것이 바람직하고, 산성 이형제로는 지방산(fatty acid), 스테아릭산(stearic acid), 팔미트산(palmitic acid) 및 올레산으로 이루어진 군에서 선택되는 1종 또는 2종 이상일 수 있으며, 바람직하기로는 지방산일 수 있다.
상기 보호층에 포함되는 산성 이형제의 함량은 0.01 내지 0.1 중량%, 바람직하게는 0.03 내지 0.9 중량%, 보다 바람직하게는 0.05 내지 0.8 중량%를 포함할 수 있다.
상기 보호층의 두께는 0.01 내지 5 ㎛가 바람직하다. 보호층의 두께가 5 ㎛를 초과할 경우에는 전지 내에서 저항으로 작용할 가능성이 있고, 리튬의 열증착 공정에 있어서, 열전달이 용이하지 않을 수 있으므로, 바람직하지 않고, 보호층의 두께를 0.01 ㎛ 미만으로 형성하는 것은, 코팅 기술 상 한계가 있다.
상기 보호층은, 코팅법에 의해 형성될 수 있으며, 예컨대, 상기 코팅법은 딥코팅(dip coating), 분사코팅(spray coating), 스핀코팅(spin coating), 다이코팅(die coating), 그라비어 코팅(Gravure coating), 마이크로-그라비어 코팅(Micro-Gravure coating), 콤마 코팅(Comma coating) 및 롤코팅(roll coating)으로 이루어진 군에서 선택되는 방법일 수 있으나, 이에 제한되는 것은 아니며, 당업계에서 코팅층을 형성하기 위해 사용할 수 있는 코팅법을 다양하게 사용할 수 있다.
상기 기재와 보호층을 포함하는 전사용 필름의 두께는, 2 내지 100 ㎛ 일 수 있다.
상기 전사용 필름 상에 리튬층을 형성하기 위해 보호층(11) 상에 리튬을 증착할 수 있다. 상기 리튬을 증착하기 위한 증착 방법으로는 진공 증착법(evaporation deposition), 화학 증착법(chemical vapor deposition) 화학기상증착 (CVD, chemical vapor deposition), 및 물리 증착법(physical vapor depositio) 중에서 선택될 수 있으나, 이에 제한되는 것은 아니며, 당업계에서 사용되는 증착법을 다양하게 사용할 수 있다.
본 발명에 있어서, 증착에 의해 상기 보호층 상에 형성된 리튬층은, 두께가 0.01 ㎛ 내지 20 ㎛일 수 있다. 상기 리튬층의 두께는 보상하고자 하는 비가역 용량, 음극활물질의 종류 등에 따라 달라질 수 있다.
본 발명의 일 실시예에서는, 음극의 전해액 함침성을 향상시키기 위하여 리튬을 증착하는 과정에서 패턴을 형성할 수 있다. 리튬을 증착하는 과정에서 패턴을 형성하는 방법은, 보호층 상에 패턴 마스크를 올리고, 증착 공정을 수행하는 방법 등에 의할 수 있다. 이때 상기 패턴 마스크는 패턴에 따른 관통 홀을 구비하고 있으며, 보호층 상에 패턴 마스크를 올린 후에 증착을 하게 되면 보호층 상에 관통 홀을 통해서만 리튬이 증착될 수 있어, 용이하게 패턴을 가지는 리튬층을 형성할 수 있게 된다.
도 2는 전사 단계를 나타내는 모식도로써, 이들 도면을 참조하면, 우선, 집전체(110) 상에 음극활물질 층(120)이 형성된 음극(100)을 준비하고, 상기 음극(100)의 음극활물질 층(120) 상에 리튬 층(13)이 대면하도록 상기 리튬 전사용 필름을 접합한다. 이후, 상기 음극(100)과 리튬 전사용 필름의 적층체를 압연 롤러(200)와 같은 압연 수단으로 가열 및 가압하여 압연을 수행함으로써, 리튬 전사용 필름의 리튬층(13) 및 보호층(11)이 상기 음극(100) 상에 전사되도록 한다.
상기 압연 공정은, 공지의 방법에 따라 수행될 수 있다. 이러한 압연 공정은, 리튬층과 보호층 및 음극을 가열/가압하는 것으로, 이를 위한 가열 방법으로는 복사 및 대류에 의한 간접 가열 방식을 사용할 수 있다.
상기 가열 온도는 20 내지 150℃, 바람직하게는 40 내지 130℃, 더욱 바람직하게는 60 내지 110℃이다. 상기 온도가 20℃ 미만이면, 전사 온도에 도달하는 시간이 길어질 수 있고, 반대로 150℃를 초과하면, 기재 필름의 수축으로 인해 셀 성능 저하를 일으킬 수 있다.
상기 전사 단계 이후에는 기재를 박리하는 단계를 수행한다. 이때 기재가 제거되어, 음극활물질 층 상에는, 리튬층 및 보호층이 남게된다. 도 3은 기재를 박리함으로써 리튬층 및 보호층이 형성된 음극이 도시되어 있으며, 전술한 바와 같이, 본 발명의 이차전지용 음극은 보호층의 아크릴계 수지가 잔류함에도 불구하고, 상기 아크릴계 수지가 저항으로 작용하지 않는 이점이 있다.
본 발명의 아크릴계 보호층이 저항으로 작용하지 않는다는 점을 확인하기 위해, 아래의 실험을 수행하였다.
제조예 1
EC(ethylene carbonate)와 EMC(ethyl methyl carbonate)가 3:7로 혼합된 혼합 용매에 1M의 LiPF6 를 첨가한 전해액을 준비하고, 상기 전해액에 메틸아크릴레이트와 n-부틸아크릴레이트 단위를 가지는 공중합체를 0.1wt% 첨가하여 완전히 용해시켰다.
대극과 참조극으로 두께 20㎛의 리튬 메탈을(Honzo 社), 작업 전극으로 스테인레스 스틸 판재를 적용한 코인형 삼전극 셀을 제조하였다. 이때 분리막은 다공성 폴리에틸렌을 적용하였으며, 코인형 삼전극 셀의 조립 후, 상기 전해액을 주입하였다.
제조예 2
전해액에 메틸아크릴레이트와 n-부틸아크릴레이트 단위를 가지는 공중합체를 0.5wt% 첨가한 것을 제외하고는, 상기 제조예 1과 동일한 방법으로 삼전극 셀을 제조하였다.
제조예 3
전해액에 메틸아크릴레이트와 n-부틸아크릴레이트 단위를 가지는 공중합체를 1.0wt% 첨가한 것을 제외하고는, 상기 제조예 1과 동일한 방법으로 삼전극 셀을 제조하였다.
제조예 4
전해액에 메틸아크릴레이트와 n-부틸아크릴레이트 단위를 가지는 공중합체를 첨가하지 않을 것을 제외하고는, 상기 제조예 1과 동일한 방법으로 삼전극 셀을 제조하였다.
실험예 1
상기 제조예 1 내지 4의 삼전극 셀에 대하여, Potentiostat 장비에서 초당 10mV 의 속도로 충방전하며, 순환전압주사법(cyclic voltammetry)에 따라 전압에 대한 전류의 변화를 관찰하였다. 첫번째 사이클에서의 산화/환원 반응의 전류-전압도를 도 4 및 도 5에, 다섯 번째 사이클에서의 산화/환원 반응의 각 전류-전압도를 도 6,7에 각각 나타내었다.
도 4 내지 7을 참조하면, 아크릴계 고분자 수지가 첨가되지 않은 제조예 4의 전해액과 비교했을 때, 특별한 피크가 관찰되지 않았는바, 이 같은 결과로부터 본 발명의 보호층 소재인 아크릴계 수지가 전지의 저항으로 작용하지 않는 효과가 있음을 확인할 수 있었다.
실시예 1
폴리에틸렌테레프탈레이트 기재 상에 아크릴계 수지가 1㎛ 코팅된 전사용 필름(제조사:아이원필름)을 준비하였다. 상기 전사용 필름의 아크릴계 수지 코팅층 상에 열 증착(Thermal evaporation) 방식으로 리튬을 증착시켜 5㎛ 두께의 리튬층을 형성하여 리튬 전사용 필름을 제조하였다. 이때 증착기기는 ULVAC 사의 EWK-060 이며, 속도는 2.5m/min, 리튬 공급부의 온도는 500℃, 메인 롤의 온도는 -25℃로 설정하여 증착 공정을 실시하였다.
구리 집전체 상에 순수 규소로 이루어진 음극활물질 층을 도포하여 제조된 음극을 준비하였다. 상기 음극의 음극활물질 층 상에, 상기 리튬 전사용 필름의 리튬층이 대면하도록 접합한 후, 압연하고, 폴리에틸렌테레프탈레이트 기재를 제거하였다. 이로써 리튬층과 아크릴 수지층이 전사된 음극을 제조하였다.
상기 리튬층 등이 전사된 음극을 가로 34mm, 세로 51mm 크기로 타발한 뒤, 양극활물질로서 Li(Ni0.8Co0.1Mn0.1)O2를 포함하는 양극 사이에 다공성의 폴리에틸렌 분리막을 개재시켜 모노셀을 제조하였다.
실시예 2
폴리에틸렌테레프탈레이트 기재 상에 아크릴계 수지가 0.5㎛ 코팅된 전사용 필름을 사용하여 리튬층을 전사한 점을 제외하고는 상기 실시예 1과 동일한 방법으로 모노셀을 제조하였다.
비교예
상기 실시예 1과 동일한 음극활물질 층을 포함하는 음극에, 리튬층을 전사하는 과정 없이 그대로 음극으로 적용한 점을 제외하고는 실시예 1과 동일한 방법으로 모노셀을 제조하였다.
실험예 2
상기 실시예 1,2 및 비교예에서 각각 제조된 모노셀을 충방전기(제조사:PNESOLUTION)에서 HPPC(Hybrid Pulse Power Characterization) 실험을 진행하여 이들 모노셀들의 저항을 비교하였다. 그 결과 실시예 1,2의 모노셀이 비교예에서 사용된 규소 전극의 저항과 차이가 거의 없는 것을 확인하였다.
실험예 3
상기 실시예 1,2 및 비교예에서 각각 제조된 모노셀을 충방전기(제조사:PNESOLUTION)에서 충방전 실험(4.2~2.5V)을 진행하며, 용량을 측정하였다. 그 결과 실시예 1,2의 모노셀 용량이 비교예보다 크게 증가된 것을 확인할 수 있었다. 이로부터 실시예 1,2와 같이 전사된 리튬층이 규소 음극의 초기 비가역을 보상하고, 용량 증대에 기여한 것을 알 수 있다.
10: 전사용 필름
11: 기재 12: 보호층
13: 리튬층
100: 음극
110: 집전체 120: 음극활물질 층
130: 리튬층 140: 보호층
200: 압연 롤러
11: 기재 12: 보호층
13: 리튬층
100: 음극
110: 집전체 120: 음극활물질 층
130: 리튬층 140: 보호층
200: 압연 롤러
Claims (10)
- 기재와 보호층을 포함하는 전사용 필름의 보호층 상에 리튬 층을 형성하여, 음극의 전리튬화를 위한 리튬 전사용 필름을 제조하는 단계;
집전체 상에 음극활물질 층이 형성된 음극을 준비하여, 음극활물질 층 상에 리튬 층이 대면하도록 상기 리튬 전사용 필름을 접합 및 압연하는 전사 단계를 포함하고,
상기 보호층은 아크릴계 수지를 포함하고, 상기 전사 단계에서 음극활물질 층 상에 리튬층 및 보호층이 전사되는 것을 특징으로 하는 리튬 이차전지용 음극의 제조방법.
- 제 1 항에 있어서, 상기 아크릴계 수지는, 메틸아크릴레이트, 에틸아크릴레이트, 이소프로필아크릴레이트, n-부틸아크릴레이트, 2-에틸헥실아크릴레이트, 메틸메타크릴레이트, 에틸메타크릴레이트, 이소프로필메타크릴레이트, n-부틸메타크릴레이트, 이소부틸메타크릴레이트, n-헥실메타크릴레이트 및 라우릴메타크릴레이트로 이루어진 군에서 선택한 1종 이상의 단량체로 이루어진 중합체이거나, 또는 상기 군에서 선택한 2종 이상의 단량체로 이루어진 공중합체인 것을 특징으로 하는 리튬 이차전지용 음극의 제조방법.
- 제 1 항에 있어서, 상기 전사용 필름의 보호층의 두께는 0.01 내지 5 ㎛인 것을 특징으로 하는 리튬 이차전지용 음극의 제조방법.
- 제 1 항에 있어서, 상기 전사용 필름의 기재와 보호층 사이에 이형층이 개재되어 있는 것을 특징으로 하는 리튬 이차전지용 음극의 제조방법.
- 제 4 항에 있어서, 상기 이형층은 폴리에스터 주사슬에 실리콘 사슬이 그라프트 결합된 실리콘 변성 폴리에스터, 실리콘, 멜라민 및 불소로 이루어진 군에서 선택된 1종 또는 2종 이상을 포함하는 리튬 이차전지용 음극의 제조방법.
- 제 1 항에 있어서, 리튬 전사용 필름을 제조하는 단계에서, 리튬 층은 열 증착법(Thermal evaporation deposition), 진공 증착법(evaporation deposition), 화학 증착법(chemical deposition), 화학기상 증착법(CVD, chemical vapor deposition) 및 물리 증착법(physical vapor deposition) 중에서 선택된 하나의 방법으로 증착되어 형성되는 것을 특징으로 하는 리튬 이차전지용 음극의 제조방법.
- 제 1 항에 있어서, 리튬 전사용 필름을 제조하는 단계에서, 리튬 층의 두께는 0.01 내지 20㎛인 것을 특징으로 하는 리튬 이차전지용 음극의 제조방법.
- 제 1 항에 있어서, 전사 단계 이후에 기재를 제거하는 단계를 더 포함하는 리튬 이차전지용 음극의 제조방법.
- 제 6 항에 있어서, 패턴 마스크를 이용하여 증착함으로써, 리튬 층이 패턴을 가지는 것을 특징으로 하는 리튬 이차전지용 음극의 제조방법.
- 제 1 항의 방법으로 제조된 리튬 이차전지용 음극.