KR101705999B1 - 열간 성형용 아연계 도금 강판 - Google Patents

열간 성형용 아연계 도금 강판 Download PDF

Info

Publication number
KR101705999B1
KR101705999B1 KR1020157003038A KR20157003038A KR101705999B1 KR 101705999 B1 KR101705999 B1 KR 101705999B1 KR 1020157003038 A KR1020157003038 A KR 1020157003038A KR 20157003038 A KR20157003038 A KR 20157003038A KR 101705999 B1 KR101705999 B1 KR 101705999B1
Authority
KR
South Korea
Prior art keywords
steel sheet
zinc
hot
plating
plated
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
KR1020157003038A
Other languages
English (en)
Korean (ko)
Other versions
KR20150029734A (ko
Inventor
히로유키 다카하시
가즈히토 이마이
히토미 니시바타
Original Assignee
신닛테츠스미킨 카부시키카이샤
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 신닛테츠스미킨 카부시키카이샤 filed Critical 신닛테츠스미킨 카부시키카이샤
Publication of KR20150029734A publication Critical patent/KR20150029734A/ko
Application granted granted Critical
Publication of KR101705999B1 publication Critical patent/KR101705999B1/ko
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Links

Classifications

    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B15/00—Layered products comprising a layer of metal
    • B32B15/01—Layered products comprising a layer of metal all layers being exclusively metallic
    • B32B15/013—Layered products comprising a layer of metal all layers being exclusively metallic one layer being formed of an iron alloy or steel, another layer being formed of a metal other than iron or aluminium
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
    • C21D1/18—Hardening; Quenching with or without subsequent tempering
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
    • C21D1/62—Quenching devices
    • C21D1/673—Quenching devices for die quenching
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0247—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
    • C21D9/46—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for sheet metals
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C18/00—Alloys based on zinc
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C18/00—Alloys based on zinc
    • C22C18/04—Alloys based on zinc with aluminium as the next major constituent
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/001—Ferrous alloys, e.g. steel alloys containing N
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/002—Ferrous alloys, e.g. steel alloys containing In, Mg, or other elements not provided for in one single group C22C38/001 - C22C38/60
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/005—Ferrous alloys, e.g. steel alloys containing rare earths, i.e. Sc, Y, Lanthanides
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/02—Ferrous alloys, e.g. steel alloys containing silicon
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/04—Ferrous alloys, e.g. steel alloys containing manganese
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/06—Ferrous alloys, e.g. steel alloys containing aluminium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/22—Ferrous alloys, e.g. steel alloys containing chromium with molybdenum or tungsten
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/24—Ferrous alloys, e.g. steel alloys containing chromium with vanadium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/26—Ferrous alloys, e.g. steel alloys containing chromium with niobium or tantalum
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/28—Ferrous alloys, e.g. steel alloys containing chromium with titanium or zirconium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/32—Ferrous alloys, e.g. steel alloys containing chromium with boron
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/38—Ferrous alloys, e.g. steel alloys containing chromium with more than 1.5% by weight of manganese
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
    • C22C38/42—Ferrous alloys, e.g. steel alloys containing chromium with nickel with copper
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
    • C22C38/44—Ferrous alloys, e.g. steel alloys containing chromium with nickel with molybdenum or tungsten
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
    • C22C38/50—Ferrous alloys, e.g. steel alloys containing chromium with nickel with titanium or zirconium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
    • C22C38/54—Ferrous alloys, e.g. steel alloys containing chromium with nickel with boron
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
    • C22C38/58—Ferrous alloys, e.g. steel alloys containing chromium with nickel with more than 1.5% by weight of manganese
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/04—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the coating material
    • C23C2/06—Zinc or cadmium or alloys based thereon
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/26—After-treatment
    • C23C2/28—Thermal after-treatment, e.g. treatment in oil bath
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/26—After-treatment
    • C23C2/28—Thermal after-treatment, e.g. treatment in oil bath
    • C23C2/29—Cooling or quenching
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/34—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the shape of the material to be treated
    • C23C2/36—Elongated material
    • C23C2/40—Plates; Strips
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/005—Ferrite
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/12—All metal or with adjacent metals
    • Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
    • Y10T428/12771—Transition metal-base component
    • Y10T428/12785—Group IIB metal-base component
    • Y10T428/12792—Zn-base component
    • Y10T428/12799—Next to Fe-base component [e.g., galvanized]

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Materials Engineering (AREA)
  • Mechanical Engineering (AREA)
  • Metallurgy (AREA)
  • Organic Chemistry (AREA)
  • Thermal Sciences (AREA)
  • Physics & Mathematics (AREA)
  • Crystallography & Structural Chemistry (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Oil, Petroleum & Natural Gas (AREA)
  • Heat Treatment Of Sheet Steel (AREA)
  • Coating With Molten Metal (AREA)
  • Shaping Metal By Deep-Drawing, Or The Like (AREA)
KR1020157003038A 2012-08-07 2013-08-05 열간 성형용 아연계 도금 강판 Active KR101705999B1 (ko)

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
JP2012175280 2012-08-07
JPJP-P-2012-175280 2012-08-07
PCT/JP2013/071118 WO2014024825A1 (ja) 2012-08-07 2013-08-05 熱間成形用亜鉛系めっき鋼板

Publications (2)

Publication Number Publication Date
KR20150029734A KR20150029734A (ko) 2015-03-18
KR101705999B1 true KR101705999B1 (ko) 2017-02-10

Family

ID=50068051

Family Applications (1)

Application Number Title Priority Date Filing Date
KR1020157003038A Active KR101705999B1 (ko) 2012-08-07 2013-08-05 열간 성형용 아연계 도금 강판

Country Status (15)

Country Link
US (1) US9902135B2 (cg-RX-API-DMAC10.html)
EP (1) EP2883976B1 (cg-RX-API-DMAC10.html)
JP (1) JP5720856B2 (cg-RX-API-DMAC10.html)
KR (1) KR101705999B1 (cg-RX-API-DMAC10.html)
CN (1) CN104520464B (cg-RX-API-DMAC10.html)
BR (1) BR112015001774B1 (cg-RX-API-DMAC10.html)
CA (1) CA2879069C (cg-RX-API-DMAC10.html)
ES (1) ES2725831T3 (cg-RX-API-DMAC10.html)
IN (1) IN2015DN00788A (cg-RX-API-DMAC10.html)
MX (1) MX373551B (cg-RX-API-DMAC10.html)
PL (1) PL2883976T3 (cg-RX-API-DMAC10.html)
RU (1) RU2603762C2 (cg-RX-API-DMAC10.html)
TW (1) TWI484047B (cg-RX-API-DMAC10.html)
WO (1) WO2014024825A1 (cg-RX-API-DMAC10.html)
ZA (1) ZA201500490B (cg-RX-API-DMAC10.html)

Families Citing this family (25)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
MX2015001772A (es) 2012-08-15 2015-05-08 Nippon Steel & Sumitomo Metal Corp Plancha de acero para uso en prensado en caliente, metodo para producirla, y miembro de plancha de acero de prensado en caliente.
JP6414387B2 (ja) * 2014-04-09 2018-10-31 新日鐵住金株式会社 自動車部材の製造方法
MX379121B (es) * 2014-05-29 2025-03-10 Nippon Steel Corp Material de acero tratado térmicamente y método para producirlo.
WO2016005780A1 (fr) * 2014-07-11 2016-01-14 Arcelormittal Investigación Y Desarrollo Sl Tôle d'acier laminée à chaud et procédé de fabrication associé
CN104152811A (zh) * 2014-07-25 2014-11-19 安徽霍山科皖特种铸造有限责任公司 一种高韧性钢
KR101569508B1 (ko) * 2014-12-24 2015-11-17 주식회사 포스코 굽힘 특성이 우수한 hpf 성형부재 및 그 제조방법
JP2016199777A (ja) 2015-04-07 2016-12-01 株式会社神戸製鋼所 耐食性に優れる塗装用鋼材
KR102100746B1 (ko) * 2015-11-26 2020-04-14 제이에프이 스틸 가부시키가이샤 고강도 용융 아연 도금 강판의 제조 방법, 고강도 용융 아연 도금 강판용 열연 강판의 제조 방법, 고강도 용융 아연 도금 강판용 냉연 강판의 제조 방법 및, 고강도 용융 아연 도금 강판
JP2017115205A (ja) * 2015-12-24 2017-06-29 日新製鋼株式会社 めっき密着性に優れた溶融Ｚｎ−Ａｌ−Ｍｇ合金めっき鋼板の製造方法
KR101726094B1 (ko) * 2015-12-24 2017-04-12 주식회사 포스코 미세크랙이 억제된 열간 프레스 성형품 및 그 제조방법
EP3521469A4 (en) * 2016-09-28 2020-03-11 Nippon Steel Corporation STEEL
WO2018115914A1 (en) 2016-12-19 2018-06-28 Arcelormittal A manufacturing process of hot press formed aluminized steel parts
CN107099748B (zh) * 2017-04-28 2019-03-26 武汉钢铁有限公司 高温成型用超高强锌铝镁镀层钢板及其制造方法
WO2018203097A1 (en) * 2017-05-05 2018-11-08 Arcelormittal A method for the manufacturing of liquid metal embrittlement resistant galvannealed steel sheet
JP6992499B2 (ja) * 2017-12-26 2022-01-13 日本製鉄株式会社 鋼材
JP7006257B2 (ja) * 2017-12-27 2022-01-24 日本製鉄株式会社 ホットスタンプ成形体及びホットスタンプ成形体の製造方法
JP7006256B2 (ja) * 2017-12-27 2022-02-10 日本製鉄株式会社 ホットスタンプ用溶融亜鉛めっき鋼板及びホットスタンプ用溶融亜鉛めっき鋼板の製造方法
WO2019169198A1 (en) 2018-03-01 2019-09-06 Nucor Corporation Zinc alloy coated press-hardenable steels and method of manufacturing the same
WO2021002422A1 (ja) 2019-07-02 2021-01-07 日本製鉄株式会社 ホットスタンプ成形体
US20220186351A1 (en) * 2019-07-02 2022-06-16 Nippon Steel Corporation Zinc-plated steel sheet for hot stamping, method of manufacturing zinc-plated steel sheet for hot stamping, and hot-stamping formed body
US12031215B2 (en) 2020-01-29 2024-07-09 Nucor Corporation Zinc alloy coating layer of press-hardenable steel
MX2022011220A (es) * 2020-03-27 2022-10-07 Nippon Steel Corp Cuerpo formado por estampado en caliente.
WO2021193632A1 (ja) * 2020-03-27 2021-09-30 日本製鉄株式会社 溶融亜鉛めっき鋼板
EP4227430B1 (en) * 2020-10-12 2025-07-02 Nippon Steel Corporation Hot-dip galvanized steel sheet
JP7670954B2 (ja) * 2021-02-26 2025-05-01 日本製鉄株式会社 ホットスタンプ用合金化溶融亜鉛めっき鋼板およびその製造方法

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2011026674A (ja) * 2009-07-28 2011-02-10 Jfe Steel Corp 耐めっき剥離性に優れる高強度溶融亜鉛めっき鋼板
JP2011256404A (ja) * 2010-05-10 2011-12-22 Sumitomo Metal Ind Ltd 溶融めっき鋼板およびその製造方法
JP2012102359A (ja) * 2010-11-09 2012-05-31 Sumitomo Metal Ind Ltd 熱処理用溶融亜鉛めっき鋼板およびその製造方法

Family Cites Families (19)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
AU7081398A (en) * 1997-04-24 1998-11-13 Nippon Steel Corporation Surface-treated metal plate and metal surface treating fluid
EP1160346B1 (en) * 1999-02-22 2006-03-08 Nippon Steel Corporation High strength galvanized steel plate excellent in adhesion of plated metal and formability in press working and high strength alloy galvanized steel plate and method for production thereof
JP3840864B2 (ja) * 1999-11-02 2006-11-01 Ｊｆｅスチール株式会社 高張力溶融亜鉛めっき鋼板およびその製造方法
FR2807447B1 (fr) 2000-04-07 2002-10-11 Usinor Procede de realisation d'une piece a tres hautes caracteristiques mecaniques, mise en forme par emboutissage, a partir d'une bande de tole d'acier laminee et notamment laminee a chaud et revetue
JP3569487B2 (ja) * 2000-09-21 2004-09-22 新日本製鐵株式会社 スポット溶接性に優れた合金化溶融亜鉛めっき鋼板及びその製造方法
WO2002101112A2 (en) * 2001-06-06 2002-12-19 Nippon Steel Corporation High-strength hot-dip galvanized steel sheet and hot-dip galvannealed steel sheet having fatigue resistance, corrosion resistance, ductility and plating adhesion, after severe deformation, and a method of producing the same
JP3582504B2 (ja) 2001-08-31 2004-10-27 住友金属工業株式会社 熱間プレス用めっき鋼板
JP4214006B2 (ja) * 2003-06-19 2009-01-28 新日本製鐵株式会社 成形性に優れた高強度鋼板およびその製造方法
JP3931859B2 (ja) 2003-07-30 2007-06-20 住友金属工業株式会社 熱間成形用亜鉛系めっき鋼材と熱間成形方法
JP4449795B2 (ja) * 2005-03-22 2010-04-14 住友金属工業株式会社 熱間プレス用熱延鋼板およびその製造方法ならびに熱間プレス成形部材の製造方法
RU2418094C2 (ru) * 2006-01-30 2011-05-10 Ниппон Стил Корпорейшн Высокопрочный горячеоцинкованный погружением стальной лист и высокопрочный отожженный после цинкования стальной лист с превосходными формуемостью и способностью к нанесению гальванопокрытия и способы изготовления и устройства для изготовления таких листов
JP4967360B2 (ja) * 2006-02-08 2012-07-04 住友金属工業株式会社 熱間プレス用めっき鋼板およびその製造方法ならびに熱間プレス成形部材の製造方法
JP5228447B2 (ja) * 2006-11-07 2013-07-03 新日鐵住金株式会社 高ヤング率鋼板及びその製造方法
JP5417797B2 (ja) 2008-08-12 2014-02-19 Ｊｆｅスチール株式会社 高強度溶融亜鉛系めっき鋼板およびその製造方法
JP4924730B2 (ja) 2009-04-28 2012-04-25 Ｊｆｅスチール株式会社 加工性、溶接性および疲労特性に優れる高強度溶融亜鉛めっき鋼板およびその製造方法
EP2474639B1 (en) * 2009-08-31 2019-04-17 Nippon Steel & Sumitomo Metal Corporation High-strength galvannealed steel sheet
ES2711891T3 (es) 2010-09-16 2019-05-08 Nippon Steel & Sumitomo Metal Corp Lámina de acero de alta resistencia y lámina de acero recubierta con zinc de alta resistencia con excelente ductilidad y capacidad de estiramiento y método de fabricación de estas
JP5884151B2 (ja) * 2010-11-25 2016-03-15 Ｊｆｅスチール株式会社 熱間プレス用鋼板およびそれを用いた熱間プレス部材の製造方法
CN102094149A (zh) 2011-03-08 2011-06-15 攀钢集团钢铁钒钛股份有限公司 一种含铌高强度热镀锌钢板及其生产方法

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2011026674A (ja) * 2009-07-28 2011-02-10 Jfe Steel Corp 耐めっき剥離性に優れる高強度溶融亜鉛めっき鋼板
JP2011256404A (ja) * 2010-05-10 2011-12-22 Sumitomo Metal Ind Ltd 溶融めっき鋼板およびその製造方法
JP2012102359A (ja) * 2010-11-09 2012-05-31 Sumitomo Metal Ind Ltd 熱処理用溶融亜鉛めっき鋼板およびその製造方法

Also Published As

Publication number Publication date
JPWO2014024825A1 (ja) 2016-07-25
CA2879069A1 (en) 2014-02-13
CN104520464B (zh) 2016-08-24
BR112015001774B1 (pt) 2020-11-10
JP5720856B2 (ja) 2015-05-20
TWI484047B (zh) 2015-05-11
US9902135B2 (en) 2018-02-27
WO2014024825A1 (ja) 2014-02-13
KR20150029734A (ko) 2015-03-18
CA2879069C (en) 2016-08-16
BR112015001774A2 (pt) 2017-07-04
MX373551B (es) 2020-05-05
EP2883976A1 (en) 2015-06-17
ES2725831T3 (es) 2019-09-27
IN2015DN00788A (cg-RX-API-DMAC10.html) 2015-07-03
ZA201500490B (en) 2016-01-27
CN104520464A (zh) 2015-04-15
RU2603762C2 (ru) 2016-11-27
TW201413006A (zh) 2014-04-01
MX2015001687A (es) 2015-04-10
US20150314568A1 (en) 2015-11-05
PL2883976T3 (pl) 2019-08-30
EP2883976A4 (en) 2016-02-17
EP2883976B1 (en) 2019-03-13
RU2015105595A (ru) 2016-09-27

Similar Documents

Publication Publication Date Title
KR101705999B1 (ko) 열간 성형용 아연계 도금 강판
CN111936650B (zh) 高强度镀锌钢板、高强度部件和它们的制造方法
KR102331003B1 (ko) 용융 아연 도금 강판
KR102345533B1 (ko) 용융 아연 도금 강판
JP5732907B2 (ja) 熱間三次元曲げ加工用鋼材と熱間三次元曲げ鋼材及びその製造方法
JP4329639B2 (ja) 耐液体金属脆性に優れた熱処理用鋼板
JP4837604B2 (ja) 合金化溶融亜鉛めっき鋼板
CN108603263B (zh) 高屈服比型高强度镀锌钢板及其制造方法
JP3459500B2 (ja) 成型性及びめっき密着性に優れた高強度合金化溶融亜鉛めっき鋼板およびその製造方法
JP5741413B2 (ja) 合金化溶融亜鉛めっき鋼帯およびその製造方法
US20210017621A1 (en) Alloyed hot-dip galvanized steel sheet and alloyed hot-dip galvanized steel sheet production method
KR101304621B1 (ko) 영역별로 상이한 강도를 갖는 프레스 성형품의 제조방법
CN116457481B (zh) 合金化镀锌钢板、电沉积涂装钢板、汽车部件、电沉积涂装钢板的制造方法以及合金化镀锌钢板的制造方法
JP7160204B2 (ja) ホットスタンプ成形体
US20220186351A1 (en) Zinc-plated steel sheet for hot stamping, method of manufacturing zinc-plated steel sheet for hot stamping, and hot-stamping formed body
CN111936649B (zh) 高强度镀锌钢板、高强度部件和它们的制造方法
JP2018090879A (ja) 熱間プレス成形用鋼板、熱間プレス成形品の製造方法、および熱間プレス成形品
JP5092858B2 (ja) 溶融亜鉛めっき用鋼板及び合金化溶融亜鉛めっき鋼板
JP7173368B2 (ja) 熱間プレス部材および熱間プレス用鋼板ならびに熱間プレス部材の製造方法
KR101271802B1 (ko) 균열이 억제된 열간 프레스 성형품의 제조방법
JP3921101B2 (ja) 形状凍結性に優れた高強度高延性溶融亜鉛めっき鋼板の製造方法
KR20130002226A (ko) 도금층의 안정성이 우수한 열간 프레스 성형용 도금강판

Legal Events

Date Code Title Description
A201 Request for examination
PA0105 International application

St.27 status event code: A-0-1-A10-A15-nap-PA0105

PA0201 Request for examination

St.27 status event code: A-1-2-D10-D11-exm-PA0201

PG1501 Laying open of application

St.27 status event code: A-1-1-Q10-Q12-nap-PG1501

E902 Notification of reason for refusal
PE0902 Notice of grounds for rejection

St.27 status event code: A-1-2-D10-D21-exm-PE0902

P11-X000 Amendment of application requested

St.27 status event code: A-2-2-P10-P11-nap-X000

P13-X000 Application amended

St.27 status event code: A-2-2-P10-P13-nap-X000

E902 Notification of reason for refusal
PE0902 Notice of grounds for rejection

St.27 status event code: A-1-2-D10-D21-exm-PE0902

E701 Decision to grant or registration of patent right
PE0701 Decision of registration

St.27 status event code: A-1-2-D10-D22-exm-PE0701

GRNT Written decision to grant
PR0701 Registration of establishment

St.27 status event code: A-2-4-F10-F11-exm-PR0701

PR1002 Payment of registration fee

St.27 status event code: A-2-2-U10-U12-oth-PR1002

Fee payment year number: 1

PG1601 Publication of registration

St.27 status event code: A-4-4-Q10-Q13-nap-PG1601

P22-X000 Classification modified

St.27 status event code: A-4-4-P10-P22-nap-X000

PN2301 Change of applicant

St.27 status event code: A-5-5-R10-R13-asn-PN2301

St.27 status event code: A-5-5-R10-R11-asn-PN2301

PR1001 Payment of annual fee

St.27 status event code: A-4-4-U10-U11-oth-PR1001

Fee payment year number: 4

PR1001 Payment of annual fee

St.27 status event code: A-4-4-U10-U11-oth-PR1001

Fee payment year number: 5

PR1001 Payment of annual fee

St.27 status event code: A-4-4-U10-U11-oth-PR1001

Fee payment year number: 6

PR1001 Payment of annual fee

St.27 status event code: A-4-4-U10-U11-oth-PR1001

Fee payment year number: 7

P22-X000 Classification modified

St.27 status event code: A-4-4-P10-P22-nap-X000

PR1001 Payment of annual fee

St.27 status event code: A-4-4-U10-U11-oth-PR1001

Fee payment year number: 8

PR1001 Payment of annual fee

St.27 status event code: A-4-4-U10-U11-oth-PR1001

Fee payment year number: 9

PR1001 Payment of annual fee

St.27 status event code: A-4-4-U10-U11-oth-PR1001

Fee payment year number: 10

U11 Full renewal or maintenance fee paid

Free format text: ST27 STATUS EVENT CODE: A-4-4-U10-U11-OTH-PR1001 (AS PROVIDED BY THE NATIONAL OFFICE)

Year of fee payment: 10

P22-X000 Classification modified

St.27 status event code: A-4-4-P10-P22-nap-X000