KR100786939B1 - 신선성 및 피로특성이 우수한 강선재 및 그 제조방법 - Google Patents
신선성 및 피로특성이 우수한 강선재 및 그 제조방법 Download PDFInfo
- Publication number
- KR100786939B1 KR100786939B1 KR1020060035729A KR20060035729A KR100786939B1 KR 100786939 B1 KR100786939 B1 KR 100786939B1 KR 1020060035729 A KR1020060035729 A KR 1020060035729A KR 20060035729 A KR20060035729 A KR 20060035729A KR 100786939 B1 KR100786939 B1 KR 100786939B1
- Authority
- KR
- South Korea
- Prior art keywords
- steel wire
- inclusions
- sio
- steel
- cao
- Prior art date
Abstract
Description
Claims (7)
- C:0.4~1.3 질량%(이하 질량%), Si:0.1~2.5%, Mn:0.2~1.0%, Al:0.003% 이하(0% 제외)를 함유하고,또한 추가적으로 Ni:0.01~1%, Cu:0.01~1%, Cr:0.01~1.5%, Li:0.02~20ppm, Na:0.02~20ppm, Ce:3~100ppm, La:3~100ppm으로 이루어지는 그룹으로부터 선택되는 하나 이상의 성분원소를 함유하고, 나머지는 Fe 및 불가피불순물로 이루어지는 강선재로서, 이 강선재는 이 강선재의 축을 포함하는 횡단면에서 100㎟당 개재물의 수가 5개 이하이고; 이 개재물은 상기 강선재에 함유되어 압연방향에 직각방향으로 폭 5㎛ 이상의 크기를 가진 산화물 개재물로 되고; 상기 개재물의 성분조성은 Al2O3+MgO+CaO+SiO2+MnO를 100%로 하였을 때 MgO+MnO≤30%를 만족하며, 또한 Al2O3+CaO+SiO2를 100%로 하였을 때 다음의 식(A) 또는 식(B)을 만족하는 것을 특징으로 하는 강선재(A steel wire rod).(A) : SiO2 ≥ 75%(B) : Al2O3 ≥ 35%, SiO2 ≥ 10%, CaO ≥ 10%
- 삭제
- 삭제
- 삭제
- 삭제
- 삭제
- C:0.4~1.3 질량%(이하 질량%), Si:0.1~2.5%, Mn:0.2~1.0%, Al:0.003% 이하(0% 제외)를 함유하고,또한 추가적으로 Ni:0.01~1%, Cu:0.01~1%, Cr:0.01~1.5%, Li:0.02~20ppm, Na:0.02~20ppm, Ce:3~100ppm, La:3~100ppm으로 이루어지는 그룹으로부터 선택되는 하나 이상의 성분원소를 함유하고, 나머지는 Fe 및 불가피불순물로 이루어지는 강선재로서, 이 강선재는 이 강선재의 축을 포함하는 횡단면에서 100㎟당 개재물의 수가 5개 이하이고; 이 개재물은 상기 강선재에 함유되어 압연방향에 직각방향으로 폭 5㎛ 이상의 크기를 가진 산화물 개재물로 되고; 상기 개재물의 성분조성은 Al2O3+MgO+CaO+SiO2+MnO를 100%로 하였을 때 MgO+MnO≤30%를 만족하며, 또한 Al2O3+CaO+SiO2를 100%로 하였을 때 다음의 식(A) 또는 식(B)을 만족하는 것을 특징으로 하는 강선재(A steel wire rod)를 제조하기 위하여,(A) : SiO2 ≥ 75%(B) : Al2O3 ≥ 35%, SiO2 ≥ 10%, CaO ≥ 10%압연해야 할 상기 강선재의 모재인 주강을 가열하여 열간압연 작업시 이 주강의 가열온도를 올리는 작업시간을 1,000℃로부터 1,100℃로 상승시키는데 걸리는 시간이 60분 이하로 작업되게 하는 것을 특징으로 하는 강선재의 제조방법.