KR100530077B1 - 내2차가공취성 및 가공성이 우수한 고장력강판과 그제조방법 - Google Patents
내2차가공취성 및 가공성이 우수한 고장력강판과 그제조방법 Download PDFInfo
- Publication number
- KR100530077B1 KR100530077B1 KR10-2001-0082246A KR20010082246A KR100530077B1 KR 100530077 B1 KR100530077 B1 KR 100530077B1 KR 20010082246 A KR20010082246 A KR 20010082246A KR 100530077 B1 KR100530077 B1 KR 100530077B1
- Authority
- KR
- South Korea
- Prior art keywords
- less
- steel sheet
- high tensile
- tensile strength
- workability
- Prior art date
Abstract
Description
Claims (3)
- 중량%로 C:0.01%이하, Mn:0.7%이하, P:0.03%이하 , S:0.015% 이하, Sol-Al: 0.06%이하, N:0.005%이하, Cu 0.5~1.0%, Ti : 0.01 - 0.04%, Nb은 다음의 조건, 6.63[C] + 0.02% ≤Nb ≤ 6.63[C] + 0.04%을 만족하고, 나머지 Fe와 불가피하게 함유되는 불순물로 조성되는 내2차가공취성 및 가공성이 우수한 고장력 강판.
- 제 1항에 있어서, 상기 고장력강판은 인장강도가 40Kg/㎟이상이고, rm값(수직이방성의 평균값)이 2.1이상이고, 연성취성천이온도가 가공비 2.0 하에서 -80℃이하임을 특징으로 하는 내2차가공취성 및 가공성이 우수한 고장력 강판.
- 중량%로 C : 0.01%이하, Mn : 0.7%이하, P : 0.03%이하 , S : 0.015% 이하, Sol-Al : 0.06%이하, N:0.005%이하, Cu 0.5~1.0%, Ti : 0.01 - 0.04%, Nb은 다음의 조건, 6.63[C] + 0.02% ≤Nb ≤ 6.63[C] + 0.04%을 만족하고, 나머지 Fe와 불가피하게 함유되는 불순물로 조성되는 알루미늄 킬드강을 1200∼1250℃의 온도범위에서 균질화처리후, 마무리압연온도 Ar3이상의 온도에서 열간압연하고 550 -700℃에서 권취한 다음, 냉간압연하고, 800℃이상에서 연속소둔한 다음, 조질압연하는 것을 포함하여 이루어지는 내2차가공취성 및 가공성이 우수한 고장력강판의 제조방법.