JPS6337992A - 光記録媒体 - Google Patents
光記録媒体Info
- Publication number
- JPS6337992A JPS6337992A JP61182219A JP18221986A JPS6337992A JP S6337992 A JPS6337992 A JP S6337992A JP 61182219 A JP61182219 A JP 61182219A JP 18221986 A JP18221986 A JP 18221986A JP S6337992 A JPS6337992 A JP S6337992A
- Authority
- JP
- Japan
- Prior art keywords
- laser
- wavelength
- optical recording
- regeneration
- substrate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【発明の詳細な説明】
産業上の利用分野
本発明は書込みできる光記録媒体に関するものである。
従来の技術
光記録媒体、中でも光ディスクは近年目覚ましい発展を
遂げつつあり、市場の拡大にともない多種多様な目的、
用途に利用されることが予想される。
遂げつつあり、市場の拡大にともない多種多様な目的、
用途に利用されることが予想される。
光ディスクは大きく分けて、再生専用型、追加記録型、
書換え可能型の３種類に分類される。この中で追加記録
型、いわゆるＤＲＡＷ型のディスクにはヒートモードダ
イブ・相変化タイプ・光磁気タイプなど種々の方式があ
るが、ヒートモード方式が一般的であり、レーザー光の
光エネルギーあるいは熱エネルギーによって、記録媒体
の一部を融解、除去当して、ピットを形成することによ
り書込みを行い、次に微弱なレーザー光を、情報が記録
された前記ピントに照射して、前記ビットの反射光量の
変化を検出してて再生するものである。
書換え可能型の３種類に分類される。この中で追加記録
型、いわゆるＤＲＡＷ型のディスクにはヒートモードダ
イブ・相変化タイプ・光磁気タイプなど種々の方式があ
るが、ヒートモード方式が一般的であり、レーザー光の
光エネルギーあるいは熱エネルギーによって、記録媒体
の一部を融解、除去当して、ピットを形成することによ
り書込みを行い、次に微弱なレーザー光を、情報が記録
された前記ピントに照射して、前記ビットの反射光量の
変化を検出してて再生するものである。
このような追加記録型の光ディスクは第２図のようにあ
らかじめトラッキングのための空溝を形成した透明基板
１上に光記録膜４を形成し、空隙３を設けつつ保護板２
を対向させた二枚貼り構造となっていた。記録材料とし
ては、Ｔｅ系の化合物や酸化物がすでに実用化されてい
るが、大損りな生産設備が必要であることから、最近で
は有機色素が追記型光デイスク材料として注目され盛ん
に研究が行われている。（参考「化学と工業」第３９巻
第３号２４５〜２４７ページ） 発明が解決しようとする問題点 ところが一般に有機色素を用いる場合には長期間の安定
性、特にくりかえし再生に問題のあることが多い。すな
わち、何万回となくくりかえし再生することによって、
その都度半導体レーザー光が光ディスクに照射され、記
録膜色素の劣化が生じ、再生性能がしだいに低下する。
らかじめトラッキングのための空溝を形成した透明基板
１上に光記録膜４を形成し、空隙３を設けつつ保護板２
を対向させた二枚貼り構造となっていた。記録材料とし
ては、Ｔｅ系の化合物や酸化物がすでに実用化されてい
るが、大損りな生産設備が必要であることから、最近で
は有機色素が追記型光デイスク材料として注目され盛ん
に研究が行われている。（参考「化学と工業」第３９巻
第３号２４５〜２４７ページ） 発明が解決しようとする問題点 ところが一般に有機色素を用いる場合には長期間の安定
性、特にくりかえし再生に問題のあることが多い。すな
わち、何万回となくくりかえし再生することによって、
その都度半導体レーザー光が光ディスクに照射され、記
録膜色素の劣化が生じ、再生性能がしだいに低下する。
同一の波長で記録、再生を行う方式のもは色素の吸収率
の高い波長で再生することになりこの影響が大きい。
の高い波長で再生することになりこの影響が大きい。
問題点を解決するための手段
上記問題点を解決するために本発明の光記録媒体は、透
明基板上に再生に用いるレーザー光の波長域に分光吸収
を有さず、再生用レーザーと異なった波長のレーザー光
によって記録できる有機色素よりなる光記録膜を形成し
たものである。なお、透明基板の耐溶剤性を高めるため
、記録膜塗布の前に薄い透明保護層を形成しても良い。
明基板上に再生に用いるレーザー光の波長域に分光吸収
を有さず、再生用レーザーと異なった波長のレーザー光
によって記録できる有機色素よりなる光記録膜を形成し
たものである。なお、透明基板の耐溶剤性を高めるため
、記録膜塗布の前に薄い透明保護層を形成しても良い。
作用
上記の構成および記録材料を用いることにより、本発明
の光記録媒体は書込み用レーザーで記録したピットを再
生用レーザーで再生するとき、再生用レーザー波長域で
の記録膜に用いた有機色素の吸収率が低いため、くりか
えし再生による膜の劣化を防ぐことができる。
の光記録媒体は書込み用レーザーで記録したピットを再
生用レーザーで再生するとき、再生用レーザー波長域で
の記録膜に用いた有機色素の吸収率が低いため、くりか
えし再生による膜の劣化を防ぐことができる。
実施例
以下、本発明の光記録媒体について実施例を用いて詳細
に説明する。
に説明する。
（実施例１）
本発明の光記録媒体の一例の部分断面図を第１図に示す
。厚さが１．２ｍｍで表面に深さ０．０８μｍ１幅０．
８μｍのトラッキング溝が１，６μｍピッチでスパイラ
ル状に形成されたメタクリル樹脂製成型基板１上の溝を
有する面上に、基板１の耐溶剤性を高めるためにＳ ｉ
Ｏｔをスパツクして２０ｎｍの透明保護層５とした。
。厚さが１．２ｍｍで表面に深さ０．０８μｍ１幅０．
８μｍのトラッキング溝が１，６μｍピッチでスパイラ
ル状に形成されたメタクリル樹脂製成型基板１上の溝を
有する面上に、基板１の耐溶剤性を高めるためにＳ ｉ
Ｏｔをスパツクして２０ｎｍの透明保護層５とした。
この面上に下記の色素のクロロホルム溶液を１１００Ｏ
ｒｐでスピンコードして８０ｎ１１１の記録膜４を形成
した。さらに、両面接着テープを用いてメタクリル樹脂
製保護板２を基板１の内外周の記録領域以外の部分と接
着した。その後、トラッキングサーボをかけながら基板
を通して６１で波長６３３ｎｍのＨｅ−Ｎｅガスレーザ
光を３ｍ／ｓｅｃ、の線速で照射した。書込まれた信号
はＩＭｌｌｚでデイ−ティ比５０１５０のパルスであり
、記録された信号を０．５ｍＷ、８３０ｎｍの半導体レ
ーザーで式生したところ再生Ｃ／Ｎ比は５５ｄＢであっ
た。この媒体の分光特性は６３３ｎｓ＋で吸収率７０％
、反射理１３％、８３０ｎｍで吸収率θ％、反射率２４
％であった。
ｒｐでスピンコードして８０ｎ１１１の記録膜４を形成
した。さらに、両面接着テープを用いてメタクリル樹脂
製保護板２を基板１の内外周の記録領域以外の部分と接
着した。その後、トラッキングサーボをかけながら基板
を通して６１で波長６３３ｎｍのＨｅ−Ｎｅガスレーザ
光を３ｍ／ｓｅｃ、の線速で照射した。書込まれた信号
はＩＭｌｌｚでデイ−ティ比５０１５０のパルスであり
、記録された信号を０．５ｍＷ、８３０ｎｍの半導体レ
ーザーで式生したところ再生Ｃ／Ｎ比は５５ｄＢであっ
た。この媒体の分光特性は６３３ｎｓ＋で吸収率７０％
、反射理１３％、８３０ｎｍで吸収率θ％、反射率２４
％であった。
また、くりかえし再生をおこなったところ１００万回の
再生後も何等特性に変化はみられなかった。
再生後も何等特性に変化はみられなかった。
（実施例２）
下記の色素クロロホルム溶液を１１０００ｒｐでスピ１
ンコートして９０ｎｍの記録膜４を形成した実施例
１と同じ構成の光ディスクに同一信号を同一条件で記録
した。記録された信号を０．５ｍＷ、８３０ｎｍの半導
体レーザーで再生したところ再生Ｃ／Ｎ比は５４ｄＢで
あった。この媒体の分光特性は６３３ｎｍで吸収１
率５８％、反射率１５％、８３０ｎｍで吸収率Ｏ％、反
射［率１９％であった。また、くりかえし再生を行った
ところ１００万回の再生後も何等特性に変化はみら［れ
なかった。
ンコートして９０ｎｍの記録膜４を形成した実施例
１と同じ構成の光ディスクに同一信号を同一条件で記録
した。記録された信号を０．５ｍＷ、８３０ｎｍの半導
体レーザーで再生したところ再生Ｃ／Ｎ比は５４ｄＢで
あった。この媒体の分光特性は６３３ｎｍで吸収１
率５８％、反射率１５％、８３０ｎｍで吸収率Ｏ％、反
射［率１９％であった。また、くりかえし再生を行った
ところ１００万回の再生後も何等特性に変化はみら［れ
なかった。
（実施例３）
下記の色素のクロロホルム溶液を１１００Ｏｒｐでスピ
ンコードして９０ｎｍの記録膜４を形成した実施例１と
同じ構成の光ディスクに同一信号を同一条件で記録した
。記録された信号を０．５ｍＷ、８３０ｎｍの半導体レ
ーザーで再生したところ再生Ｃ／Ｎは５３ｄＢであった
。この媒体の分光特性は６３３ｎｍで吸収率６５％、反
射率１３％、８３０ｎｍで吸収率θ％、反射率２５％で
あった。また、くりかえし再生をおこなったところ１０
０万回の再生後も何等特性に変化はみられなかった。
ンコードして９０ｎｍの記録膜４を形成した実施例１と
同じ構成の光ディスクに同一信号を同一条件で記録した
。記録された信号を０．５ｍＷ、８３０ｎｍの半導体レ
ーザーで再生したところ再生Ｃ／Ｎは５３ｄＢであった
。この媒体の分光特性は６３３ｎｍで吸収率６５％、反
射率１３％、８３０ｎｍで吸収率θ％、反射率２５％で
あった。また、くりかえし再生をおこなったところ１０
０万回の再生後も何等特性に変化はみられなかった。
（実施例４）
［化メチルロザニリンのクロロホルム溶液を１１００Ｏ
ｒｐでスピンコードして９０ｎｅ＋の記録膜４を形成し
た実施例１と同じ構成の光ディスクに同一信号を同一条
件で記録した。記録された信号を０．５ａ＋Ｗ、８３０
ｎｍの半導体レーザーで再生したところ再生Ｃ／Ｎ比は
５６ｄＢであった。この媒体の分光特性は６３３ ｎｍ
で吸収率８６％、反射率１２％、８３０ｎｍで吸収率Ｏ
％、反射率２４％であった。また、くりかえし再生をお
こなったところ１００万回の再生後も何等特性に変化は
みられなかった。
ｒｐでスピンコードして９０ｎｅ＋の記録膜４を形成し
た実施例１と同じ構成の光ディスクに同一信号を同一条
件で記録した。記録された信号を０．５ａ＋Ｗ、８３０
ｎｍの半導体レーザーで再生したところ再生Ｃ／Ｎ比は
５６ｄＢであった。この媒体の分光特性は６３３ ｎｍ
で吸収率８６％、反射率１２％、８３０ｎｍで吸収率Ｏ
％、反射率２４％であった。また、くりかえし再生をお
こなったところ１００万回の再生後も何等特性に変化は
みられなかった。
（実施例５）
マラカイトグリーンのエタノール溶液を１１００Ｏｒｐ
でスピンコードして９０ｎｍの記録膜４を形成した実施
例１と同じ構成の光ディスクに同一信号を同一条件で記
録した。記録された信号を０．５ｍＷ、８３０ｎｗの半
導体レーザーで再生したところ再生Ｃ／Ｎ比は５２ｄＢ
であった。この媒体の分光特性は６３３ｎｍで吸収率６
０％、反射率１４％、８３０ｎｍで吸収率Ｏ％、反射率
１８％であった。また、くりかえし再生をおこなったと
ころ１００万回の再生後も何等特性に変化はみられなか
った。
でスピンコードして９０ｎｍの記録膜４を形成した実施
例１と同じ構成の光ディスクに同一信号を同一条件で記
録した。記録された信号を０．５ｍＷ、８３０ｎｗの半
導体レーザーで再生したところ再生Ｃ／Ｎ比は５２ｄＢ
であった。この媒体の分光特性は６３３ｎｍで吸収率６
０％、反射率１４％、８３０ｎｍで吸収率Ｏ％、反射率
１８％であった。また、くりかえし再生をおこなったと
ころ１００万回の再生後も何等特性に変化はみられなか
った。
（実施例６）
フ゛リリアントフ゛ル−６Ｇのエリノール）８液を１１
００Ｏｒｐでスピンコードしてて９０ｎｍの記録膜４を
形成した実施例１と同じ構成の光ディスクに同一信号を
同一条件で記録した。記録された信号を０．５ｍ−１８
３０ｎｍの半導体レーザーで再生したところ再生Ｃ／Ｎ
比は５３ｄＢであった。この媒体の分光特性は６３３ｎ
ｍで吸収率７０％、反射率１２％、８３０ｎｍで吸収率
０％、反射率２３％であった。また、くりかえし再生を
おこなったところ１００万回の再生後も何等特性に変化
はみられなかった。
００Ｏｒｐでスピンコードしてて９０ｎｍの記録膜４を
形成した実施例１と同じ構成の光ディスクに同一信号を
同一条件で記録した。記録された信号を０．５ｍ−１８
３０ｎｍの半導体レーザーで再生したところ再生Ｃ／Ｎ
比は５３ｄＢであった。この媒体の分光特性は６３３ｎ
ｍで吸収率７０％、反射率１２％、８３０ｎｍで吸収率
０％、反射率２３％であった。また、くりかえし再生を
おこなったところ１００万回の再生後も何等特性に変化
はみられなかった。
（比較例）
下図の色素のクロロホルム溶液を１１００Ｏｒｐ＋でス
ピンコードして８０ｎｍの記録膜４を形成した実施例１
と同じ構成の光ディスクに同一信号を６ＩＩＩＷ、８３
０ｎｌｌｌの半導体レーザーを用いて３ｍ／３６（、の
線速で記録した。記録された信号を０．５ｎ＋Ｗ、８３
０ｎｍの半導体レーザーで再生したところ再生Ｃ／Ｎ比
は５１ｄＢであった。この媒体の分光特性は８３０ｎｍ
で吸収率６０％、反射率１６％であり、くりかえし再生
をおこなったところ、再生回数が１０万回に達する前に
再生不能となった。
ピンコードして８０ｎｍの記録膜４を形成した実施例１
と同じ構成の光ディスクに同一信号を６ＩＩＩＷ、８３
０ｎｌｌｌの半導体レーザーを用いて３ｍ／３６（、の
線速で記録した。記録された信号を０．５ｎ＋Ｗ、８３
０ｎｍの半導体レーザーで再生したところ再生Ｃ／Ｎ比
は５１ｄＢであった。この媒体の分光特性は８３０ｎｍ
で吸収率６０％、反射率１６％であり、くりかえし再生
をおこなったところ、再生回数が１０万回に達する前に
再生不能となった。
発明の効果
本発明の光記録媒体は書込みレーザーの波長と再生レー
ザー波長が異なり、記録膜に用いる有機色素が書込みレ
ーザーの波長には吸収を存するが、再生レーザーの波長
では吸収を有さないことにより、１００万回以上のくり
かえし再生にも耐えうるものである。
ザー波長が異なり、記録膜に用いる有機色素が書込みレ
ーザーの波長には吸収を存するが、再生レーザーの波長
では吸収を有さないことにより、１００万回以上のくり
かえし再生にも耐えうるものである。
第１図は、本発明の実施例における光記録媒体の部分断
面図、第２図は、従来のエアーサンドインチ構造の書込
みできる光ディスクの部分断面図である。 １・・・・・・基板、２・・・・・・保護板、３・・・
・・・空隙、４・・・・・・記録膜、５・・・・・・透
明保護膜。
面図、第２図は、従来のエアーサンドインチ構造の書込
みできる光ディスクの部分断面図である。 １・・・・・・基板、２・・・・・・保護板、３・・・
・・・空隙、４・・・・・・記録膜、５・・・・・・透
明保護膜。
Claims (4)
- （１）透明基板と、上記透明基板上に形成され、再生に
用いるレーザー光の波長域に分光吸収を有さず、再生用
レーザーと異なった波長のレーザー光によって記録でき
る有機色素よりなる光記録膜とを備えた光記録媒体。 - （２）記録膜の反射率が透明基板の反射率よりも高いこ
とを特徴とする特許請求の範囲第（１）項記載の光記録
媒体。 - （３）記録膜が、７００ｎｍ以下の波長のレーザー光で
記録ができ、かつ７００〜９００ｎｍでは分光吸光度の
極大となる点を有さないことを特徴とする特許請求の範
囲第（１）項記載の光記録媒体。 - （４）記録用レーザーの波長の光にたいして３０％以上
の分光吸収率を有し、かつ再生用レーザーの波長の光に
たいしては１０％以下の分光吸収率しか有すさないこと
を特徴とする特許請求の範囲第（１）項記載の光記録媒
体。