JPS63317279A - Gold alloy filler metal for brazing - Google Patents
Gold alloy filler metal for brazingInfo
- Publication number
- JPS63317279A JPS63317279A JP15170287A JP15170287A JPS63317279A JP S63317279 A JPS63317279 A JP S63317279A JP 15170287 A JP15170287 A JP 15170287A JP 15170287 A JP15170287 A JP 15170287A JP S63317279 A JPS63317279 A JP S63317279A
- Authority
- JP
- Japan
- Prior art keywords
- brazing
- filler metal
- alloy
- gold
- solder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【発明の詳細な説明】 （産業上の利用分野） 本発明は、金ろう合金の改良に関するものである。[Detailed description of the invention] (Industrial application field) The present invention relates to improvements in gold solder alloys.
（従来技術とその問題点）
一般に真空遮断器、電子管、サイリスター、ＩＣパッケ
ージ等におけるろう材用金ろう合金としては、金に銅を
２０〜６３重量％の範囲で添加した金−銅合金が主に用
いられている。(Prior art and its problems) In general, gold brazing alloys for brazing materials in vacuum circuit breakers, electron tubes, thyristors, IC packages, etc. are mainly gold-copper alloys in which 20 to 63% by weight of copper is added to gold. It is used in
然し乍ら、このろう材にてろう付を行った場合、ろう付
後のろう表面が荒れ、凹凸が発生するものである。従っ
てこのろう材を用いてろう付を行った部品を酸洗浄した
り、めっき処理したりすると、前記凹凸に洗浄液等が浸
入する。この洗浄液は完全に除去することが困難である
為、凹凸の部分に洗浄液が残存し、その結果残存した洗
浄液等によりろう材部が変色、腐蝕したり、めっきにふ
くれが生じたりする等の欠点があった。However, when brazing is performed using this brazing material, the solder surface after brazing becomes rough and uneven. Therefore, when parts brazed using this brazing material are acid-cleaned or plated, the cleaning liquid or the like will penetrate into the irregularities. Since this cleaning solution is difficult to remove completely, it may remain on uneven areas, resulting in disadvantages such as discoloration and corrosion of the brazing metal or blistering of the plating due to the remaining cleaning solution. was there.
（発明の目的）
本発明は上記欠点を解消すべくなされたものであり、ろ
う付後のろう表面の荒れが少なく、凹凸の発生も少ない
金ろう合金を提供せんとするものである。(Object of the Invention) The present invention has been made in order to eliminate the above-mentioned drawbacks, and aims to provide a gold solder alloy that has less roughness on the solder surface after brazing and less occurrence of irregularities.
（問題点を解決するための手段）
本発明の金ろう合金は、銅ｌＯ〜８０重量％、クロム、
パラジウム、マンガンの少なくとも１種０．００１〜１
．０重量％、残部金より成るものである。(Means for Solving the Problems) The gold brazing alloy of the present invention contains copper lO to 80% by weight, chromium,
At least one of palladium and manganese 0.001 to 1
．． 0% by weight, the balance being gold.
本発明の金ろう合金において、クロム、パラジウム、マ
ンガンの少なくとも１種を金−銅合金に含有させる理由
は、ろう付時溶融したろう材の表面張力を小さくし、そ
れによりろう付後のろう表面の荒れを小さくし、凹凸の
発生を抑制する為である。In the gold solder alloy of the present invention, the reason why at least one of chromium, palladium, and manganese is contained in the gold-copper alloy is to reduce the surface tension of the solder metal melted during brazing, thereby reducing the surface tension of the solder material after brazing. This is to reduce roughness and suppress the occurrence of unevenness.
そしてそれの含有量を０．００１〜１．０重量％と限定
した理由は、０．００１重量％未満ではろう付後のろう
表面の荒れ及び凹凸の発生を抑制することができず、ま
た１、０重量％を超えると極端にろう流れが悪く、ろう
付強度に悪影響を及ぼすからである。The reason for limiting the content to 0.001 to 1.0% by weight is that if it is less than 0.001% by weight, it is not possible to suppress the occurrence of roughness and unevenness on the solder surface after brazing, and 1. This is because if it exceeds 0% by weight, the flow of the solder will be extremely poor and the brazing strength will be adversely affected.
次に本発明の金ろう合金の効果を明瞭ならしめる為にそ
の具体的な実施例と従来例について説明する。Next, in order to clarify the effects of the gold brazing alloy of the present invention, specific examples and conventional examples thereof will be described.
（実施例）
下記の表の左欄に示す実施例と従来例１〜２の金ろうを
水素雰囲気中で、ＩＣパッケージ用アルミナにＭｏ−Ｍ
ｎをメタライズし、さらにその上にニッケルめっきを５
μ施し、その部分に鉄−ニッケル４２重量％から成るリ
ードフレームのろう付を行い、ろう付後のろう表面の凹
凸（溝）の個数及び凹凸（溝）の深さを測定したところ
下記の表の右欄に示すような結果を得た。(Example) The gold solders of Examples and Conventional Examples 1 and 2 shown in the left column of the table below were applied to Mo-M on alumina for IC packages in a hydrogen atmosphere.
metallize n and further nickel plating on top of it.
A lead frame made of 42% iron-nickel by weight was brazed to that part, and the number of unevenness (grooves) and the depth of the unevenness (grooves) on the soldering surface after brazing were measured, and the results are shown in the table below. The results shown in the right column were obtained.
（以下余白）
上記の表の右欄の数値で明らかなように本発明の余ろう
合金は、従来の余ろう合金に比較して凹凸（溝）の発生
数が少なく、また凹凸（溝）の深さが浅いものである。(Left below) As is clear from the numbers in the right column of the table above, the residual filler alloy of the present invention has fewer unevenness (grooves) than conventional residual filler alloys, and also has fewer unevenness (grooves). The depth is shallow.
（発明の効果）
以上詳記した通り本発明による金ろう合金は、ろう付後
のろう表面の荒れが少なく、凹凸の発生も少なく、従っ
てろう付を行った部品を酸洗浄したり、めっき処理した
りしてもろう表面の凹凸に浸入する洗浄液等の量が少な
く、その結果それらを除去後の残存量も少なく、それだ
けろう材部の変色、腐蝕を抑制することができるという
優れた効果がある。(Effects of the Invention) As detailed above, the gold brazing alloy according to the present invention has less roughness on the solder surface after brazing and less occurrence of unevenness, so brazed parts can be cleaned with acid or subjected to plating treatment. The amount of cleaning liquid that penetrates into the unevenness of the solder metal surface is small, and as a result, the amount remaining after removal is also small, which has the excellent effect of suppressing discoloration and corrosion of the solder metal part. be.
Claims (1)
少なくとも１種０．００１〜１．０重量％、残部金より
成る金ろう合金。A gold brazing alloy consisting of 10 to 80% by weight of copper, 0.001 to 1.0% by weight of at least one of chromium, palladium, and manganese, and the balance gold.