JPS63289085A - シ−リング材組成物 - Google Patents
シ−リング材組成物Info
- Publication number
- JPS63289085A JPS63289085A JP12682787A JP12682787A JPS63289085A JP S63289085 A JPS63289085 A JP S63289085A JP 12682787 A JP12682787 A JP 12682787A JP 12682787 A JP12682787 A JP 12682787A JP S63289085 A JPS63289085 A JP S63289085A
- Authority
- JP
- Japan
- Prior art keywords
- compsn
- urethane prepolymer
- sound insulation
- metallic lead
- amt
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【発明の詳細な説明】
本発明はシーリング材組成物、更に詳しくは。
充填剤として金属鉛を配合することにより遮音効果を付
与したシーリング材組成物に関する。
与したシーリング材組成物に関する。
飛行場や高速道路に隣接した騒音地域の建物や音響効果
の求められる建物にあっては、遮音もしくは防音のため
の壁または仕切板として、遮音性のある特殊なサイディ
ングボードが設けられ、その目地にシーリング材が施工
されている。
の求められる建物にあっては、遮音もしくは防音のため
の壁または仕切板として、遮音性のある特殊なサイディ
ングボードが設けられ、その目地にシーリング材が施工
されている。
しかしながら、かかるシーリング材として、−波型の弾
性、耐候性に良好な、分子末端にイソシアネート基(N
CO基)を含有するウレタンプレポリマーを主成分とす
るものが使用されているが、この目地のシール部から音
の伝播があり、所期の十分な遮音効果を成しえないとい
う問題があった。
性、耐候性に良好な、分子末端にイソシアネート基(N
CO基)を含有するウレタンプレポリマーを主成分とす
るものが使用されているが、この目地のシール部から音
の伝播があり、所期の十分な遮音効果を成しえないとい
う問題があった。
そこで本発明者らは、この問題を解決するため鋭意検討
を進めたところ、充填剤として金属鉛を添加すれば、音
の伝播を有効に防止し、遮音効果を付与しうろことを見
出し、本発明を完成させるに至った。
を進めたところ、充填剤として金属鉛を添加すれば、音
の伝播を有効に防止し、遮音効果を付与しうろことを見
出し、本発明を完成させるに至った。
発明の構成と効果
すなわち、本発明は、分子末端にNGO基を含プレ
有スルウレタンポリマーを主成分とするシーリンへ
グ材組成物において、金属鉛を添加したことを特徴とす
るシーリング材組成物を提供するものである。
るシーリング材組成物を提供するものである。
本発明で用いるウレタンプレポリマーとは、ポリオール
と過剰のポリイソシアネートとの反応生成物を指称し、
一般にその分子末端に05〜5%(重量外、以下同様〕
のNCO基を含有する。
と過剰のポリイソシアネートとの反応生成物を指称し、
一般にその分子末端に05〜5%(重量外、以下同様〕
のNCO基を含有する。
上記ポリオールとしては、エチレングリコール、プロピ
レングリコール、ジエチレングリコール、ジプロピレン
グリコール、1.3−ブタンジオール、1.4−ブタン
ジオール、4.4−ジヒドロキシジフェニルプロパン、
4.4−ジヒドロキシジフェニルメタン、グリセリン、
1.2.6−ヘキサントリオ−/L’% lel
、1− トリメチロールプロパン、ペンタエリスリット
、ンルビット、ショ糖等の少なくとも1種にエチレンオ
キサイド、プロピレンオキサイド、ブチレンオキサイド
等のアルキレンオキサイドを寸加重合したポリエーテル
ポリオール、その他ポリテトラメチレンエーテルポリオ
ール、ポリマーポリオール、ポリブタジェンポリオール
が挙げられる。必要に応じて、エチレングリコール、プ
ロピレングリコール、ジエチレンクリコール、ジプロピ
レングリコール、ネオペンチルグリコール、トリエチレ
ングリコール、トリプロピレンゲリコール、1.3−ブ
タンジオール、1.4−ブタンジオール、ビスヒドロキ
シエチルハイドロキノン、グリセリン、1.2.6−ヘ
キサントリオール、 1.1.1−トリメチロールプ
ロパン、ペンタエリスリット、ジグリセリンなどの多価
アルコール類を加えてもよい。
レングリコール、ジエチレングリコール、ジプロピレン
グリコール、1.3−ブタンジオール、1.4−ブタン
ジオール、4.4−ジヒドロキシジフェニルプロパン、
4.4−ジヒドロキシジフェニルメタン、グリセリン、
1.2.6−ヘキサントリオ−/L’% lel
、1− トリメチロールプロパン、ペンタエリスリット
、ンルビット、ショ糖等の少なくとも1種にエチレンオ
キサイド、プロピレンオキサイド、ブチレンオキサイド
等のアルキレンオキサイドを寸加重合したポリエーテル
ポリオール、その他ポリテトラメチレンエーテルポリオ
ール、ポリマーポリオール、ポリブタジェンポリオール
が挙げられる。必要に応じて、エチレングリコール、プ
ロピレングリコール、ジエチレンクリコール、ジプロピ
レングリコール、ネオペンチルグリコール、トリエチレ
ングリコール、トリプロピレンゲリコール、1.3−ブ
タンジオール、1.4−ブタンジオール、ビスヒドロキ
シエチルハイドロキノン、グリセリン、1.2.6−ヘ
キサントリオール、 1.1.1−トリメチロールプ
ロパン、ペンタエリスリット、ジグリセリンなどの多価
アルコール類を加えてもよい。
上記ポリイソシアネートとしては、2.4−)リレンジ
イソシアネートもしくは2.6−トリレンジイソシアネ
ートまたはこれらの混合物、粗製トリレンジイソシアネ
ート% 4.4−ジフェニルメタンジイソシアネートも
しくは2.4−ジフェニルメタンジイソシアネートまた
はこれらの混合物、ポリメチレンポリフェニルポリイソ
シア不一ト(粗製ジフェニルメタンジイソシアネート〕
、キシリレンジイソシアネート、ヘキサメチレンジイソ
シアネート、ジシクロヘキシルメタンジイソシア不一ト
、インホロンジイソシアネート、ヘキサヒドロキシリレ
ンジイソシアネートが挙げられる。
イソシアネートもしくは2.6−トリレンジイソシアネ
ートまたはこれらの混合物、粗製トリレンジイソシアネ
ート% 4.4−ジフェニルメタンジイソシアネートも
しくは2.4−ジフェニルメタンジイソシアネートまた
はこれらの混合物、ポリメチレンポリフェニルポリイソ
シア不一ト(粗製ジフェニルメタンジイソシアネート〕
、キシリレンジイソシアネート、ヘキサメチレンジイソ
シアネート、ジシクロヘキシルメタンジイソシア不一ト
、インホロンジイソシアネート、ヘキサヒドロキシリレ
ンジイソシアネートが挙げられる。
本発明に係るシーリング材組成物は、上記ウレタンプレ
ポリマーを主成分とし、必要に応じて通常の可塑剤(ジ
ブチルフタレート、ジオクチルフタレート、ジオクチル
アジペート、ジブチルセバケート、トリスクロロエチル
ホスフェート、塩化パラフィンなど)、チタン性付与剤
(微粉末シリカなど)、有機溶剤()ノyエン、キシレ
ン、脂肪族灰化水素類などノ、触媒(ジブチル錫ジラウ
レート、錫オクトエート、鉛オクトエートなど)、安定
剤、着色剤(酸化チタン、カーボンブラックなど)、充
填剤(炭酸カルシウム、タルク、硫酸バリウムなど)等
を配合し、これに金属鉛を加え中20〜70%の範囲で
選定すればよい。
ポリマーを主成分とし、必要に応じて通常の可塑剤(ジ
ブチルフタレート、ジオクチルフタレート、ジオクチル
アジペート、ジブチルセバケート、トリスクロロエチル
ホスフェート、塩化パラフィンなど)、チタン性付与剤
(微粉末シリカなど)、有機溶剤()ノyエン、キシレ
ン、脂肪族灰化水素類などノ、触媒(ジブチル錫ジラウ
レート、錫オクトエート、鉛オクトエートなど)、安定
剤、着色剤(酸化チタン、カーボンブラックなど)、充
填剤(炭酸カルシウム、タルク、硫酸バリウムなど)等
を配合し、これに金属鉛を加え中20〜70%の範囲で
選定すればよい。
上記金属鉛の使用量は、組成物全量中20〜70%、好
ましくは30〜50%の範囲で選定すればよい。20%
未満であると、所望の遮音効果を付与しえず、また70
呪を越えると、ウレタン系シーリング材としての弾性、
耐候性を損なう傾向にある。
ましくは30〜50%の範囲で選定すればよい。20%
未満であると、所望の遮音効果を付与しえず、また70
呪を越えると、ウレタン系シーリング材としての弾性、
耐候性を損なう傾向にある。
以上の構成から成る本発明組成物は、金属鉛の配合によ
り、当初の良好な弾性、耐候性を損なうことなく遮音効
果が付与されており、特に遮音性のある石コウボード、
ケイカル板などのサイディングボードのワーキングジヨ
イントに適用することができる。
り、当初の良好な弾性、耐候性を損なうことなく遮音効
果が付与されており、特に遮音性のある石コウボード、
ケイカル板などのサイディングボードのワーキングジヨ
イントに適用することができる。
次に実施例および比較例を挙げて本発明を具体的に説明
する。
する。
実施例1
数平均分子量2000のポリエーテルポリオール(三洋
化成工業(株)製、PP2000ノア0部(重量部、以
下同様〕と、粗製ジフェニルメタンジイソシアネート3
0部を75℃で3時間反応させて、2.0%のNCO基
含有ウレタンプレポリマーを得る。
化成工業(株)製、PP2000ノア0部(重量部、以
下同様〕と、粗製ジフェニルメタンジイソシアネート3
0部を75℃で3時間反応させて、2.0%のNCO基
含有ウレタンプレポリマーを得る。
シーリング材
上記ウレタンプレポリマー50部、ジオクチルフタレー
ト10部、微粉末シリカ(日本アエロジル(株〕製「ア
エロジル200J)3部に、金属鉛(粒径100〜35
0メツシユ)37部を加え、攪拌混合してシーリング材
を得る。
ト10部、微粉末シリカ(日本アエロジル(株〕製「ア
エロジル200J)3部に、金属鉛(粒径100〜35
0メツシユ)37部を加え、攪拌混合してシーリング材
を得る。
比較例1
実施例1において、金属鉛の代わりに同−Iの炭酸カル
シウムを使用する以外は、同様にしてシーリング材を得
る。
シウムを使用する以外は、同様にしてシーリング材を得
る。
比較例2
実施例1において、金属鉛の代わりに同量の硫酸バリウ
ムを使用する以外は、同様にしてシーリング材1を得る
。
ムを使用する以外は、同様にしてシーリング材1を得る
。
試験法
各側のシーリング材を下記試験に供し、結果を表1に示
す。
す。
■シーリング材を目地中15闘、目地厚1Offに充填
し、JIS A1416に準じ遮音効果を測定する。
し、JIS A1416に準じ遮音効果を測定する。
■シーリング材を剥離紙上で約2.0H厚となるように
シート化して、20℃で2週間養生硬化させた後、JI
S K2SO3に準するダンベル物性試験を行う。
シート化して、20℃で2週間養生硬化させた後、JI
S K2SO3に準するダンベル物性試験を行う。
■シーリング材を約2.0H厚・となるようにシート化
して、ウエザーオメータで光照射し、500時間の耐候
性試験を行う。OK:表面にキレン、クラックの発生な
し。
して、ウエザーオメータで光照射し、500時間の耐候
性試験を行う。OK:表面にキレン、クラックの発生な
し。
■JIS A3758に準じ、スランプ試@を行う。
■B型回転粘度計により粘度を測定する。
表1
Claims (1)
- 【特許請求の範囲】 1、分子末端にイソシアネート基を含有するウレタンプ
レポリマーを主成分とするシーリング材組成物において
、金属鉛を添加したことを特徴とするシーリング材組成
物。 2、金属鉛の添加量がシーリング材組成物全量に対して
20〜70重量%である前記第1項記載のシーリング材
組成物。