JPS6325665B2 - - Google Patents
Info
- Publication number
- JPS6325665B2 JPS6325665B2 JP9025880A JP9025880A JPS6325665B2 JP S6325665 B2 JPS6325665 B2 JP S6325665B2 JP 9025880 A JP9025880 A JP 9025880A JP 9025880 A JP9025880 A JP 9025880A JP S6325665 B2 JPS6325665 B2 JP S6325665B2
- Authority
- JP
- Japan
- Prior art keywords
- resin
- photoreceptor
- electrophotographic
- trade name
- manufactured
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
本発明は光導電材料としてα型銅フタロシアニ
ンを用いる電子写真用感光体に関するものであ
る。 従来より電子写真用感光体としては、セレンや
硫化カドミウムなどの無機化合物が主に用いられ
てきているが、これらの材料の多くは毒物や劇物
あるいは特定化学物質に指定され、その取扱い、
特に廃棄には注意を要するという欠点を持つてい
る。一方、これらの無機物を使つた感光体に対し
て、最近では毒性のない安価な感光体として、有
機光導電体を用いた電子写真用感光体が提案され
ている。その代表例として、たとえば、増感され
たポリ−Ｎ−ビニルカルバゾール、ポリビニルア
ントラセン、ポリアセナフチレン、各種フタロシ
アニン化合物など多数の有機化合物が知られてい
る。 これらのうちフタロシアニン化合物、なかでも
α型銅フタロシアニンは、安価、無毒であり、感
度の点でも優れている。 一般に分散型電子写真用感光体は、バインダー
樹脂に光導電材料や増感剤などを適当な方法で混
合し、導電性基板上にロールコーター等を用い塗
布し、乾燥することによつて得られる。ここにお
いて、バインダー樹脂には、単に光導電材料を基
板に結着させるという性能のみならず、被膜形成
能や耐摩耗性および転写性が良好であり、かつ適
正な電気抵抗を有しているということや、帯電特
性、暗減衰、感度、残留電位、繰り返し特性など
の光導電材料の電子写真特性を損わないことが要
求される。 これまでバインダー樹脂としては、ケイ素樹
脂、エポキシ樹脂、アルキツド樹脂、ポリエステ
ル樹脂、ポリカーボネート樹脂、アクリル樹脂、
ビニル樹脂、ポリウレタン樹脂など多数知られて
おり、適当に組み合わせて用いられているが、上
記の諸特性を全て満足させるものは少ない。 本発明の目的は、上記欠点を克服し、電子写真
特性の優れた実用可能な、α型銅フタロシアニン
を用いる電子写真用感光体を提供することにあ
る。 本発明はα型銅フタロシアニンとバインダー樹
脂とからなる分散型感光体において、前記バイン
ダー樹脂をポリウレタン樹脂、アクリル樹脂、お
よびOR基（ただし、ＲはＨまたはCH3を示す）
を含むケイ素樹脂でもつて構成することにより、
前記感光体の電子写真特性が著しく改善されるこ
とを見出したことにもとづいている。 以下に本発明の詳細について実施例にもとづい
て説明する。 実施例 １ α型銅フタロシアニン（東洋インキ(株)、商品名
「シアニンブルーＢ」）を、酢酸ブチル、酢酸エチ
レングリコールモノエチルエーテル、トルエンの
混合溶剤（重量比２：２：１）とともに200時間
ボールミルにより混合粉砕したのち、ポリウレタ
ン樹脂、ポリシロキサン樹脂、およびアクリル樹
脂を加え、第１表に示すような組成の分散液を
得、それをアルミニウミ板上に塗布して電子写真
用感光板を作製した。ポリウレタン樹脂としては
「タケラツクＵ−25」（武田薬品工業(株)製ウレタン
樹脂用ポリオールの商品名）と「タケネートＤ−
110N」（武田薬品工業(株)製ウレタン樹脂用イソシ
アネートの商品名）との等モル比混合塗料を用
い、ポリシロキサン樹脂としては、「信越シリコ
ーンKR−214」（信越化学工業(株)製OH基を含む
ケイ素樹脂の商品名）を、アクリル樹脂としては
「三菱ダイヤナールLR−1065（三菱レイヨン(株)製
アクリル樹脂の商品名）を用いた。
ンを用いる電子写真用感光体に関するものであ
る。 従来より電子写真用感光体としては、セレンや
硫化カドミウムなどの無機化合物が主に用いられ
てきているが、これらの材料の多くは毒物や劇物
あるいは特定化学物質に指定され、その取扱い、
特に廃棄には注意を要するという欠点を持つてい
る。一方、これらの無機物を使つた感光体に対し
て、最近では毒性のない安価な感光体として、有
機光導電体を用いた電子写真用感光体が提案され
ている。その代表例として、たとえば、増感され
たポリ−Ｎ−ビニルカルバゾール、ポリビニルア
ントラセン、ポリアセナフチレン、各種フタロシ
アニン化合物など多数の有機化合物が知られてい
る。 これらのうちフタロシアニン化合物、なかでも
α型銅フタロシアニンは、安価、無毒であり、感
度の点でも優れている。 一般に分散型電子写真用感光体は、バインダー
樹脂に光導電材料や増感剤などを適当な方法で混
合し、導電性基板上にロールコーター等を用い塗
布し、乾燥することによつて得られる。ここにお
いて、バインダー樹脂には、単に光導電材料を基
板に結着させるという性能のみならず、被膜形成
能や耐摩耗性および転写性が良好であり、かつ適
正な電気抵抗を有しているということや、帯電特
性、暗減衰、感度、残留電位、繰り返し特性など
の光導電材料の電子写真特性を損わないことが要
求される。 これまでバインダー樹脂としては、ケイ素樹
脂、エポキシ樹脂、アルキツド樹脂、ポリエステ
ル樹脂、ポリカーボネート樹脂、アクリル樹脂、
ビニル樹脂、ポリウレタン樹脂など多数知られて
おり、適当に組み合わせて用いられているが、上
記の諸特性を全て満足させるものは少ない。 本発明の目的は、上記欠点を克服し、電子写真
特性の優れた実用可能な、α型銅フタロシアニン
を用いる電子写真用感光体を提供することにあ
る。 本発明はα型銅フタロシアニンとバインダー樹
脂とからなる分散型感光体において、前記バイン
ダー樹脂をポリウレタン樹脂、アクリル樹脂、お
よびOR基（ただし、ＲはＨまたはCH3を示す）
を含むケイ素樹脂でもつて構成することにより、
前記感光体の電子写真特性が著しく改善されるこ
とを見出したことにもとづいている。 以下に本発明の詳細について実施例にもとづい
て説明する。 実施例 １ α型銅フタロシアニン（東洋インキ(株)、商品名
「シアニンブルーＢ」）を、酢酸ブチル、酢酸エチ
レングリコールモノエチルエーテル、トルエンの
混合溶剤（重量比２：２：１）とともに200時間
ボールミルにより混合粉砕したのち、ポリウレタ
ン樹脂、ポリシロキサン樹脂、およびアクリル樹
脂を加え、第１表に示すような組成の分散液を
得、それをアルミニウミ板上に塗布して電子写真
用感光板を作製した。ポリウレタン樹脂としては
「タケラツクＵ−25」（武田薬品工業(株)製ウレタン
樹脂用ポリオールの商品名）と「タケネートＤ−
110N」（武田薬品工業(株)製ウレタン樹脂用イソシ
アネートの商品名）との等モル比混合塗料を用
い、ポリシロキサン樹脂としては、「信越シリコ
ーンKR−214」（信越化学工業(株)製OH基を含む
ケイ素樹脂の商品名）を、アクリル樹脂としては
「三菱ダイヤナールLR−1065（三菱レイヨン(株)製
アクリル樹脂の商品名）を用いた。
【表】
【表】
得られたそれぞれの感光板を川口電機製静電記
録紙試験装置「SP−428改良型」を用いて電子写
真特性を測定した。＋6kVのコロナ放電処理を10
秒間行なつたときの表面電位V0、帯電後暗所に
10秒間放置したときの表面電位V10、帯電後白色
タングステンランプを用いて感光板に５ルクスの
光を照射し、表面電位が1/2，1/5に減衰するとき
の露光量（E1/2，E1/5）、また、光照射後10秒後の
表面電位（残留電位とする）Vrを、それぞれ測
定した。測定結果を第２表に示す。
録紙試験装置「SP−428改良型」を用いて電子写
真特性を測定した。＋6kVのコロナ放電処理を10
秒間行なつたときの表面電位V0、帯電後暗所に
10秒間放置したときの表面電位V10、帯電後白色
タングステンランプを用いて感光板に５ルクスの
光を照射し、表面電位が1/2，1/5に減衰するとき
の露光量（E1/2，E1/5）、また、光照射後10秒後の
表面電位（残留電位とする）Vrを、それぞれ測
定した。測定結果を第２表に示す。
【表】
【表】
第２表より明らかなように、ポリウレタン樹
脂、アクリル樹脂、およびケイ素樹脂を適当量混
合することによつて得られるバインダー樹脂と、
α型銅フタロシアニンとからなる電子写真用感光
体は、帯電特性、感度に優れ、暗減衰や残留電位
も小さく実用上優れた感光体である。 また、バインダー樹脂の構成割合については、
電子写真特性をはじめ、耐摩耗性、転写効率、繰
り返し特性などを検討した結果、バインダー樹脂
100重量部において、ポリウレタン樹脂は５〜90
重量部、アクリル樹脂は５〜90重量部、ケイ素樹
脂は５〜90重量部が好ましいということがわかつ
た。 次に実施例で得られた組成番号４，７，９の感
光板を用いて、常法に従い約6kVのコロナ放電器
により正電荷を与えた後、ポジテイブパターンを
通して30ルクスの照度で１秒間露光を行ない、現
像用トナーを磁気ブラシにより付着させたとこ
ろ、いづれも原画に忠実な良好な画像が得られ
た。 実施例 ２ α型銅フタロシアニン（東洋インキ(株)製、商品
名「シアニンブルーＢ」）、ウレタン樹脂用ポリオ
ール（日本ポリウレタン(株)製、商品名「ニツポラ
ン125」）、OCH3基を含む珪素樹脂（東レ(株)製、
商品名「トーレシリコーンSH−6188」）、アクリ
ル樹脂（三菱レーヨン(株)製、商品名「三菱ダイヤ
ナールLR−574」）、および混合溶剤（酢酸ブチル
40重量部、酢酸エチレングリコールモノエチルエ
ーテル40重量部、トルエン20重量部）を、ボール
ミルを用いて200時間混合分散したのち、ウレタ
ン樹脂用イソシアネート（日本ポリウレタン(株)
製、商品名「コロネートHL」）を加えて、第３
表に示すような分散液を得、それをアルミニウム
板上に塗布して電子写真用感光板を作製した。
脂、アクリル樹脂、およびケイ素樹脂を適当量混
合することによつて得られるバインダー樹脂と、
α型銅フタロシアニンとからなる電子写真用感光
体は、帯電特性、感度に優れ、暗減衰や残留電位
も小さく実用上優れた感光体である。 また、バインダー樹脂の構成割合については、
電子写真特性をはじめ、耐摩耗性、転写効率、繰
り返し特性などを検討した結果、バインダー樹脂
100重量部において、ポリウレタン樹脂は５〜90
重量部、アクリル樹脂は５〜90重量部、ケイ素樹
脂は５〜90重量部が好ましいということがわかつ
た。 次に実施例で得られた組成番号４，７，９の感
光板を用いて、常法に従い約6kVのコロナ放電器
により正電荷を与えた後、ポジテイブパターンを
通して30ルクスの照度で１秒間露光を行ない、現
像用トナーを磁気ブラシにより付着させたとこ
ろ、いづれも原画に忠実な良好な画像が得られ
た。 実施例 ２ α型銅フタロシアニン（東洋インキ(株)製、商品
名「シアニンブルーＢ」）、ウレタン樹脂用ポリオ
ール（日本ポリウレタン(株)製、商品名「ニツポラ
ン125」）、OCH3基を含む珪素樹脂（東レ(株)製、
商品名「トーレシリコーンSH−6188」）、アクリ
ル樹脂（三菱レーヨン(株)製、商品名「三菱ダイヤ
ナールLR−574」）、および混合溶剤（酢酸ブチル
40重量部、酢酸エチレングリコールモノエチルエ
ーテル40重量部、トルエン20重量部）を、ボール
ミルを用いて200時間混合分散したのち、ウレタ
ン樹脂用イソシアネート（日本ポリウレタン(株)
製、商品名「コロネートHL」）を加えて、第３
表に示すような分散液を得、それをアルミニウム
板上に塗布して電子写真用感光板を作製した。
【表】
得られた電子写真用感光体を実施例１で用いた
静電記録紙試験装置にて、コロナ印加電圧＋
6kV、帯電速度10ｍ／分、暗減衰時間２秒、光減
衰時間１秒、光強度50ルクスの各条件にて、連続
繰り返し1500回の測定を行なつたところ、初期の
帯電電位に対する1500回目の帯電電位の比率が91
％であり、暗減衰変化率は５％以内であり、感度
は半減露光量が11.0ルクス・秒であり、繰り返し
測定を行なつてもほとんど変化しなかつた。 次に、実施例２で得られた感光体を用い、実施
例１と同様の方法にてカールソンプロセスによる
現像を行なつたところ、原画に忠実な良好な画像
が得られた。また、この感光体は転写性能やウレ
タンブレードを用いたクリーニング時の耐摩耗性
にも優れているなど、実用上優れた感光体であつ
た。 以上のように本発明の感光体は、電子写真特性
をはじめ、耐摩耗性、転写性、繰り返し特性に優
れており、また、その製造も容易であるので、そ
の実用的価値は非常に高い。
静電記録紙試験装置にて、コロナ印加電圧＋
6kV、帯電速度10ｍ／分、暗減衰時間２秒、光減
衰時間１秒、光強度50ルクスの各条件にて、連続
繰り返し1500回の測定を行なつたところ、初期の
帯電電位に対する1500回目の帯電電位の比率が91
％であり、暗減衰変化率は５％以内であり、感度
は半減露光量が11.0ルクス・秒であり、繰り返し
測定を行なつてもほとんど変化しなかつた。 次に、実施例２で得られた感光体を用い、実施
例１と同様の方法にてカールソンプロセスによる
現像を行なつたところ、原画に忠実な良好な画像
が得られた。また、この感光体は転写性能やウレ
タンブレードを用いたクリーニング時の耐摩耗性
にも優れているなど、実用上優れた感光体であつ
た。 以上のように本発明の感光体は、電子写真特性
をはじめ、耐摩耗性、転写性、繰り返し特性に優
れており、また、その製造も容易であるので、そ
の実用的価値は非常に高い。
Claims (1)
- １ α型銅フタロシアニンとバインダー樹脂とか
らなる分散型感光体において、前記バインダー樹
脂がポリウレタン樹脂、アクリル樹脂、および
OH基または−OCH3基を含むケイ素樹脂からら
なることを特徴とする電子写真用感光体。