JPS62238383A - 防食剤 - Google Patents
防食剤Info
- Publication number
- JPS62238383A JPS62238383A JP8034986A JP8034986A JPS62238383A JP S62238383 A JPS62238383 A JP S62238383A JP 8034986 A JP8034986 A JP 8034986A JP 8034986 A JP8034986 A JP 8034986A JP S62238383 A JPS62238383 A JP S62238383A
- Authority
- JP
- Japan
- Prior art keywords
- metals
- formula
- corrosion
- substituted
- ferrous
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【発明の詳細な説明】
更に詳しくは、一般式：
％式％：
（式中Ｒは水素原子又は低級アルキル基を示し又は水素
、塩素、臭素又は沃素原子をＲ１はフェニル基、ベンジ
ルＭ、置換ベンジル基、ナフチル基、置換ナフチル基を
示す。） で表される芳香族置換イミダゾール類の１種ないし２Ｆ
１以上を有効成分とする揮発性の金属防食剤に関するも
のである。
、塩素、臭素又は沃素原子をＲ１はフェニル基、ベンジ
ルＭ、置換ベンジル基、ナフチル基、置換ナフチル基を
示す。） で表される芳香族置換イミダゾール類の１種ないし２Ｆ
１以上を有効成分とする揮発性の金属防食剤に関するも
のである。
従来、気化性の防食剤としては、多くの物質が提案され
、実用に供されているが、これらは鉄系金属に対する防
食剤が多く、非鉄金属に対しては、優れた防食剤がなく
、鉄系、非鉄両糸に有効なものの開発が望まれていた。
、実用に供されているが、これらは鉄系金属に対する防
食剤が多く、非鉄金属に対しては、優れた防食剤がなく
、鉄系、非鉄両糸に有効なものの開発が望まれていた。
従来から使用されている気化性の薬剤には、例えば次に
政げるごときものがある。
政げるごときものがある。
（１）気化性の最も代表的な防食剤である亜１１１酸ア
ミン塩類は鉄系の金属には優れた防食効果が認められる
が、銅をはじめとする非鉄金属には防錆力が全く認めら
れない。
ミン塩類は鉄系の金属には優れた防食効果が認められる
が、銅をはじめとする非鉄金属には防錆力が全く認めら
れない。
（２）脂肪酸のアミン塩も同様に、鉄系金属に対しては
効果が認められるが、非鉄金属に対しては全く効果がな
い。
効果が認められるが、非鉄金属に対しては全く効果がな
い。
（３）非鉄金属に浸れた防食効果を示すベンゾトリアゾ
ールをはじめとするトリアゾール類は気化性が弱く、ア
ルカリ側では全く気化せず、従って防食効果を期待する
ことができない。特にナトリウム、カリウム、マグネシ
ュウムなどのアルカリ性金属の共存する系においては全
く気化しない。
ールをはじめとするトリアゾール類は気化性が弱く、ア
ルカリ側では全く気化せず、従って防食効果を期待する
ことができない。特にナトリウム、カリウム、マグネシ
ュウムなどのアルカリ性金属の共存する系においては全
く気化しない。
このような背景のもと、本発明者は、アルカリ性領域に
おいて、充分な揮発性を有し、熱安定性もよく、シかも
鉄系金属および非鉄金属に対する防食性の優れた薬剤の
研究開発を進め本発明を完成させた。
おいて、充分な揮発性を有し、熱安定性もよく、シかも
鉄系金属および非鉄金属に対する防食性の優れた薬剤の
研究開発を進め本発明を完成させた。
本発明の目的は芳香族＠換イミダゾール類が温時ないし
、水の沸点下で適切な蒸気圧を有しナトリウムをはじめ
とするアルカリ性金属が共存しても、揮交力を持続し、
しかも熱安定性も優ねており、鉄系金属および銅をはじ
めとする非鉄金属の腐食を防止する効果が優ねているこ
とにある。
、水の沸点下で適切な蒸気圧を有しナトリウムをはじめ
とするアルカリ性金属が共存しても、揮交力を持続し、
しかも熱安定性も優ねており、鉄系金属および銅をはじ
めとする非鉄金属の腐食を防止する効果が優ねているこ
とにある。
−・方、アルキル１１イミダゾール項は常温付近では優
れた防食力を有するものである。しかし、水の沸点およ
びそれ以」二の温度で（ま熱分解を受け、防食力を失い
本発明の目的に合致せず、そしてまたナトリウムなどの
アルカリ性金属が共存すると、熱分解が一層促進され好
士しくないのである。
れた防食力を有するものである。しかし、水の沸点およ
びそれ以」二の温度で（ま熱分解を受け、防食力を失い
本発明の目的に合致せず、そしてまたナトリウムなどの
アルカリ性金属が共存すると、熱分解が一層促進され好
士しくないのである。
エンジン冷却系や、ボイラーかん水系など高湿になるよ
うな′防食系では熱安定性が良いことが必須の条件とな
る。これらの防食系には、鉄鋼をはじめ多種類の金属が
組込まれており、多種類の金属を防食しなければならな
い。なかでも鉄系金属と銅系金属は防食の重要な因子と
なる。そのために液性は常にアルカリ性領域に設定され
ており、アルカリ性領域において気化、揮発することが
必要な条件となる。本発明に係る芳香族置換イミダゾー
ル類は、塩基性物質であるため、ナトリウム、カリウム
などのアルカリ金属、そしてまた、カルシウム、マタネ
シウム、などのアルカリ土類金属と塩を生成しないため
、アミン類と同じように挙動し、アルカリ性領域におい
ても揮発性を有し、この用途に最も良く適合しているの
である。
うな′防食系では熱安定性が良いことが必須の条件とな
る。これらの防食系には、鉄鋼をはじめ多種類の金属が
組込まれており、多種類の金属を防食しなければならな
い。なかでも鉄系金属と銅系金属は防食の重要な因子と
なる。そのために液性は常にアルカリ性領域に設定され
ており、アルカリ性領域において気化、揮発することが
必要な条件となる。本発明に係る芳香族置換イミダゾー
ル類は、塩基性物質であるため、ナトリウム、カリウム
などのアルカリ金属、そしてまた、カルシウム、マタネ
シウム、などのアルカリ土類金属と塩を生成しないため
、アミン類と同じように挙動し、アルカリ性領域におい
ても揮発性を有し、この用途に最も良く適合しているの
である。
揮発性を有することの利点は言うまでもなく、液と接し
ない部分の金属、そしてまた、蒸気が通過するパイプや
熱交換器などの防食に有効に作用するものであり工業的
な意義が誠に大きいのである。
ない部分の金属、そしてまた、蒸気が通過するパイプや
熱交換器などの防食に有効に作用するものであり工業的
な意義が誠に大きいのである。
芳香族置換イミダゾール類の防食機構は、金属表面にイ
ミダゾールが吸着して緻密な吸着被膜を形成して、金属
を腐食から保護するものと推定することができる。
ミダゾールが吸着して緻密な吸着被膜を形成して、金属
を腐食から保護するものと推定することができる。
本発明に係る芳香族置換イミダゾール類は１．２−ジア
ミンと芳香族シアニドにトリル）とから常法のイミダゾ
ール合成方法によって、容易に製造することができる。
ミンと芳香族シアニドにトリル）とから常法のイミダゾ
ール合成方法によって、容易に製造することができる。
芳香族イミダゾール類は実質的には水に不溶であるため
、使用にあたっては、アルコール、グリコール、ケトン
やアミドなどの溶剤で可溶化するか、リン酸塩酸、さく
酸、クエン酸などの酸で可溶化する方法をとることがで
きる。許容される添加濃度は０．０１ないし２０． Ｏ
ＯＯｐｐｍの屍囲内であるが、望ましくは０．５ないし
５． ＯＯＯｐｐｍの範囲である。０．０１ｐｐＩ１１
以下の使用濃度では防食率が充分でなく２、 ＯＯＯｐ
ｐｍ以上いくら添加しても、もはやそれ以上防食率の向
上が望めないのである。
、使用にあたっては、アルコール、グリコール、ケトン
やアミドなどの溶剤で可溶化するか、リン酸塩酸、さく
酸、クエン酸などの酸で可溶化する方法をとることがで
きる。許容される添加濃度は０．０１ないし２０． Ｏ
ＯＯｐｐｍの屍囲内であるが、望ましくは０．５ないし
５． ＯＯＯｐｐｍの範囲である。０．０１ｐｐＩ１１
以下の使用濃度では防食率が充分でなく２、 ＯＯＯｐ
ｐｍ以上いくら添加しても、もはやそれ以上防食率の向
上が望めないのである。
本発明に係る芳香族置換イミダゾールの例としては
例えば
２−フェニールイミダゾール、２−フェニール−４−メ
チルイミダゾール、２−フェニール−４−プロピルイミ
ダゾール、２−フェニール−５−ヨードイミダゾール、
２−ベンジルイミダゾール、２−ベンジル−４−メチル
イミダゾール、２−（３−クロール）ベンジルイミダゾ
ール、２−（３−ヨード）ペンジルイミダゾール、２−
ナフチルイミダゾール−２−ナフチル番−メチルイミダ
ゾール、２−ナフチル−４−メチル−５−ブロムイミダ
ゾール、２−（３，５−ジブロム）ナフチルイミダゾー
ル、２−（２，６−ジクロル）ナフチル、４−メチルイ
ミダゾールなどをあげることができる。
チルイミダゾール、２−フェニール−４−プロピルイミ
ダゾール、２−フェニール−５−ヨードイミダゾール、
２−ベンジルイミダゾール、２−ベンジル−４−メチル
イミダゾール、２−（３−クロール）ベンジルイミダゾ
ール、２−（３−ヨード）ペンジルイミダゾール、２−
ナフチルイミダゾール−２−ナフチル番−メチルイミダ
ゾール、２−ナフチル−４−メチル−５−ブロムイミダ
ゾール、２−（３，５−ジブロム）ナフチルイミダゾー
ル、２−（２，６−ジクロル）ナフチル、４−メチルイ
ミダゾールなどをあげることができる。
本発明に係る防食剤は従来から使用されている防食剤、
例えばリン酸塩、ケイ酸塩、硝醗塩炭酸塩、亜硝酸塩、
リン酸エステル類、アミン類、アミド類、カルボン醜塩
などと併用して更に効果の完全を期することができる。
例えばリン酸塩、ケイ酸塩、硝醗塩炭酸塩、亜硝酸塩、
リン酸エステル類、アミン類、アミド類、カルボン醜塩
などと併用して更に効果の完全を期することができる。
以下実施例をあげて本発明を具体的に１悦明するが、こ
れによって本発明が限定されるものではない。
れによって本発明が限定されるものではない。
実施例１
重炭酸ソーダ２ｏ、 ＯＯＯｐｐｍとアンモニア ２０
ｐｐｍと表コ、に示した防錆剤メタノールに溶解したも
のを加えた水２１を３１のフラスコに採り加熱した。
ｐｐｍと表コ、に示した防錆剤メタノールに溶解したも
のを加えた水２１を３１のフラスコに採り加熱した。
発生する蒸気を２０ｍ＋ｎ Ｘ １００ｍｍの純銅帯を
入れた径３０＋ｎｍのガラス管に誘導した。４８時間蒸
気を通して銅の変色度合と腐食減量Ｅｉ！ｊｌ定した。
入れた径３０＋ｎｍのガラス管に誘導した。４８時間蒸
気を通して銅の変色度合と腐食減量Ｅｉ！ｊｌ定した。
結果を表２に示す。
なお、フラスコに水がなくなったら同じ組成の水を追加
した。
した。
表−１
以上の結果より明らかなごとく本発明品は優れた防錆力
を有することが判明した。
を有することが判明した。
実施例２
防錆剤として表−３に示すイミダゾール類の有機ヌは無
機塩を使用いテストピースとして２０ｍｍ Ｘ １００
ｍ＋ｎの黄銅帯を用いろ他は実施例１と同じ操作を行っ
た。
機塩を使用いテストピースとして２０ｍｍ Ｘ １００
ｍ＋ｎの黄銅帯を用いろ他は実施例１と同じ操作を行っ
た。
結果を表−４に示す。
れた防錆力を有することが判明した。
実施例３
表−５に示す防錆剤を使用しテストピースとして２０ｍ
ｍ Ｘ ｌｏｏｍ＋＋＋のＳ８−４１軟鋼帯を用いる他
は実施例２に同じ操作を行った。
ｍ Ｘ ｌｏｏｍ＋＋＋のＳ８−４１軟鋼帯を用いる他
は実施例２に同じ操作を行った。
結果を表−６に示す。
表−６
以上の結果より明らかなごとく本発明品は優れた防錆力
を有することが判明した。
を有することが判明した。
Claims (1)
- 【特許請求の範囲】 一般式 ▲数式、化学式、表等があります▼ （式中Ｒは水素原子又は低級アルキル基を示しＸは水素
、塩素、臭素又は沃素原子を、Ｒ′はフエニル基、置換
フエニル基、ベンジル基、置換ベンジル基、ナフチル基
、置換ナフチル基を示す。） で表わされるイミダゾール類の１種ない２ 種以上を有効成分とすることよりなる揮発性の金属防食
剤。