JPS61122949A - 光記録媒体およびその製造法 - Google Patents

光記録媒体およびその製造法

Info

Publication number
JPS61122949A
JPS61122949A JP59242925A JP24292584A JPS61122949A JP S61122949 A JPS61122949 A JP S61122949A JP 59242925 A JP59242925 A JP 59242925A JP 24292584 A JP24292584 A JP 24292584A JP S61122949 A JPS61122949 A JP S61122949A
Authority
JP
Japan
Prior art keywords
optical recording
film
recording medium
composite oxide
transparent substrate
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
JP59242925A
Other languages
English (en)
Other versions
JPH0535490B2 (ja
Inventor
Yoshiki Goto
良樹 後藤
Tokihiko Shimizu
清水　時彦
Sanemori Soga
眞守 曽我
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Panasonic Holdings Corp
Original Assignee
Matsushita Electric Industrial Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Matsushita Electric Industrial Co Ltd filed Critical Matsushita Electric Industrial Co Ltd
Priority to JP59242925A priority Critical patent/JPS61122949A/ja
Publication of JPS61122949A publication Critical patent/JPS61122949A/ja
Publication of JPH0535490B2 publication Critical patent/JPH0535490B2/ja
Granted legal-status Critical Current

Abstract

(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。

Description

【発明の詳細な説明】 産業上の利用分野 本発明は、光学的な情報の記録・再生に用いる光記録媒
体に関するものであり、光ディスク、ビデオディスクあ
るいはＤＡＤ用コンパクトディスクに適用される。
従来の技術 レーザー光の照射により光学的に記録・再生を行なう光
記録媒体は、従来、透明性のすぐれたポリメタクリル酸
メチルやポリカーボネートなどの高分子材料を基体とし
て、その片面に光記録膜を作成し、さらに保護膜としで
、基体と同じ材料の膜をは９合わせたり、エポキシ樹脂
等をコーティングしたりして構成している。
発明が解決しようとする問題点 上記のような構成では、常湿ないし多湿環境下では、水
分が容易に保護膜を通過し、光記録膜の成分と反応する
ことにより、結晶核の生成や、光記録膜の変質が起こり
、やがては、記録・再生が不可能になるという致命的欠
陥が生じる。
この対策として、前記の保護膜を構成する有機系材料の
改質が提案されているが、透明性の低下や、防湿性の基
本的な解決がなされていないのが現状である。゛ 一方、無機系材料では、スパッタや蒸着で形成した５ｉ
０２膜が提案されてきたが、前記基体への接着性の弱さ
から剥離が生じたり、クラックが発生したりして長期信
頼性に耐えない。
本発明の目的は、保護膜を改良して、防湿性にすぐれ、
かつ長期安定性を有する光記録媒体を提供することであ
る。
問題点全解決するだめの手段 本発明は、透明性基板にメモリー機能を有する光記録膜
を設けた光記録媒体において、ジルコニア−ノリ力系複
合酸化物被膜を保護膜として備えるものである。
作用 本発明の保護膜を構成するジルコニア−シリカ系複合酸
化物は、その分子構造上ガラス状膜として形成されるた
め、水分透過性が小さく、かつ透明性がきわめて高い材
料である。
これまで無機材料での保護膜として、５ｉＯｚｉスパツ
タ、蒸着等で形成する方法が提案されてきだが、接着性
の問題から剥離が生じたり、クラックが発生したりする
ため、苛酷な環境試験では長期信頼性に耐えないばかり
か、量産性にも不向きでありた。
一方、本発明のジルコニア−シリカ系複合酸化物被膜は
、実施例に述べるように、接着性、透明性、防湿性およ
び量産性においてすぐれており、長期信頼性に耐える光
記録媒体を提供できる。
すなわち、ジルコニア−シリカ系複合酸化物被膜は、複
合酸化物の可溶性溶媒中に溶解した液を、湿式でコーテ
ィングし、適度な温度と湿度で硬化することにより容易
に形成される。
ジルコニア−シリカ系複合酸化物を溶解する溶媒として
は、メタノール、エタノール、イソプロピルアルコール
やブタノール等のアルコール類を応用に合わせて単独ま
たは混合して、適度な希釈度で調合するのみでよい。硬
化の原理は、次式のように、 ｎ−ＺｒＯ２５ｉ０２−　ＯＲ ２Ｏ −（Ｚｒ０２・５ＬＯｚ）ｎ＋ＨＯＲｔＲ：アルキル基 加水分解によって達成され、アンモニア雰囲気では、さ
らに硬化速度を短縮することが可能である。
又、湿式であるため、浸漬、スピンコード、はけ塗り等
が可能であり、量産性においてきわめてすぐれている。
本発明のメモリー機能を有する光記録膜とは、後述する
実施例に限らず、Ｔｅ　、　Ｔｅ１０２　、　Ｓｂ　、
Ｓｓ。
Ｂｉ、又はムＥなどを単独あるいは混合して蒸着した膜
等であり、有機系では、光学的に応答するホトクロミッ
ク材料１色素、染料、界面活性剤等の記録材料金用いる
場合にも適用可能である。そして、透明性基板としては
、プラスチック以外にもガラス等を用いた構成にも良い
ことは言うまでもない。
実施例 第１図は光記録媒体の構成例全示す。
（ａｌＨ透明性基板１の片面だ光記録膜２を設け、向じ
ぐ透明性の基板３をはり合わせ、これらの表面にジルコ
ニアーンリ力系複合酸化物の被膜４を設けた例である。
（ｂｌは基板５つ片面に光記録膜６を設け、その表面全
複合酸化物の被膜７で覆った例である。
次に、具体例を説明する。
まず、１．２既厚のポリカーボネート基板の片面にＴｅ
及びＴｅ０ｚ　ｔ”主成分とする光記録膜を設け、この
膜側にポリカーボネート＆ｌはり合わせる。
次に、ジルコニア−シリカ系複合酸化物の２〜５重量％
イソプロピルアルコール溶液をスピンコードし、適湿環
境条件下で加熱乾燥して硬化させ、第１図已に示す構成
の光記録媒体をつくった。
この実施例のものムと、複合酸化物被膜を設けない比較
例の記録媒体Ｂについて、７０°Ｃ５８０％ＲＨの条件
で耐環境試験全行ない、光透過電全測定した。その結果
を第２図に示す。
図から明らかなように、比較例Ｂでは１０日過ぎからｓ
３ｏｎｍでの光透過率が低下し始め、２０日〜５０日で
は膜そのものも黒化が顕著になり、結晶核の生成を生じ
たりするなど劣化が激しかった。これに対し、実施例で
は１００日以後も光学特性や顕微鏡観察における変化は
なく、光記録媒体として長期信頼性を有することが確認
できた。
発明の効果 以上のように、本発明によれば、防湿性にすぐれ、透明
性の高い信頼性が向上した光記録媒体全実現することが
できる。
【図面の簡単な説明】
第１図は本発明の光記録媒体の構成例を示す縦断面図、
第２図は耐環境試験における光透過率の経時変化の比較
を示す図である。 １．３．５・・・・・・透明性基板、２，６・・・・・
光記録１漠、４．了・・・・・複合酸化物被膜。 代理人の氏名　弁理士　中　尾　敏　男　ほか１名ｆ、
３．６　・・　＼占つド明ノ←４を一黛メ≧ノｉ聾し４
．７・　藪化物翔暎 第２図 ｓ　　ｑ（田

Claims (2)

    【特許請求の範囲】
  1. （１）透明性基板とメモリー機能を有する光記録膜から
    なる光記録媒体であって、ジルコニア−シリカ系複合酸
    化物を保護膜として備えたことを特徴とする光記録媒体
    。
  2. （２）透明性基板とメモリー機能を有する光記録膜を有
    する光記録媒体に、ジルコニア−シリカ系複合酸化物を
    可溶性溶媒に溶解した溶液を塗布し、加熱処理すること
    により、前記酸化物による保護膜を形成することを特徴
    とする光記録媒体の製造法。
JP59242925A 1984-11-16 1984-11-16 光記録媒体およびその製造法 Granted JPS61122949A (ja)