JPH0535490B2 - - Google Patents
Info
- Publication number
- JPH0535490B2 JPH0535490B2 JP59242925A JP24292584A JPH0535490B2 JP H0535490 B2 JPH0535490 B2 JP H0535490B2 JP 59242925 A JP59242925 A JP 59242925A JP 24292584 A JP24292584 A JP 24292584A JP H0535490 B2 JPH0535490 B2 JP H0535490B2
- Authority
- JP
- Japan
- Prior art keywords
- optical recording
- film
- recording medium
- composite oxide
- zirconia
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【発明の詳細な説明】
産業上の利用分野
本発明は、光学的な情報の記録・再生に用いる
光記録媒体に関するものであり、光デイスク、ビ
デオデイスクあるいはDAD用コンパクトデイス
クに適用される。
光記録媒体に関するものであり、光デイスク、ビ
デオデイスクあるいはDAD用コンパクトデイス
クに適用される。
従来の技術
レーザー光の照射により光学的に記録・再生を
行なう光記録媒体は、従来、透明性のすぐれたポ
リメタクリル酸メチルやポリカーボネートなどの
高分子材料を基体として、その片面に光記録膜を
作成し、さらに保護膜として、基体と同じ材料の
膜をはり合わせたり、エポキシ樹脂等をコーテイ
ングしたりして構成している。
行なう光記録媒体は、従来、透明性のすぐれたポ
リメタクリル酸メチルやポリカーボネートなどの
高分子材料を基体として、その片面に光記録膜を
作成し、さらに保護膜として、基体と同じ材料の
膜をはり合わせたり、エポキシ樹脂等をコーテイ
ングしたりして構成している。
発明が解決しようとする問題点
上記のような構成では、常湿ないし多湿環境下
では、水分が容易に保護膜を通過し、光記録膜の
成分と反応することにより、結晶核の生成や、光
記録膜の変質が起こり、やがては、記録・再生が
不可能になるという致命的欠陥が生じる。
では、水分が容易に保護膜を通過し、光記録膜の
成分と反応することにより、結晶核の生成や、光
記録膜の変質が起こり、やがては、記録・再生が
不可能になるという致命的欠陥が生じる。
この対策として、前記の保護膜を構成する有機
系材料の改質が提案されているが、透明性の低下
や、防湿性の基本的な解決がなされていないのが
現状である。
系材料の改質が提案されているが、透明性の低下
や、防湿性の基本的な解決がなされていないのが
現状である。
一方、無機系材料では、スパツタや蒸着で形成
したSiO2膜が提案されてきたが、前記基体への
接着性の弱さから剥離が生じたり、クラツクが発
生したりして長期信頼性に耐えない。
したSiO2膜が提案されてきたが、前記基体への
接着性の弱さから剥離が生じたり、クラツクが発
生したりして長期信頼性に耐えない。
本発明の目的は、保護膜を改良して、防湿性に
すぐれ、かつ長期安定性を有する光記録媒体を提
供することである。
すぐれ、かつ長期安定性を有する光記録媒体を提
供することである。
問題点を解決するための手段
本発明は、透明性基板にメモリー機能を有する
光記録膜を設けた光記録媒体において、ジルコニ
ア−シリカ系複合酸化物被膜を保護膜として備え
るものである。
光記録膜を設けた光記録媒体において、ジルコニ
ア−シリカ系複合酸化物被膜を保護膜として備え
るものである。
作 用
本発明の保護膜を構成するジルコニア−シリカ
系複合酸化物は、その分子構造上ガラス状膜とし
て形成されるため、水分透過性が小さく、かつ透
明性がきわめて高い材料である。
系複合酸化物は、その分子構造上ガラス状膜とし
て形成されるため、水分透過性が小さく、かつ透
明性がきわめて高い材料である。
これまで無機材料での保護膜として、SiO2を
スパツタ、蒸着等で形成する方法が提案されてき
たが、接着性の問題から剥離が生じたり、クラツ
クが発生したりするため、苛酷な環境試験では長
期信頼性に耐えないばかりか、量産性にも不向き
であつた。
スパツタ、蒸着等で形成する方法が提案されてき
たが、接着性の問題から剥離が生じたり、クラツ
クが発生したりするため、苛酷な環境試験では長
期信頼性に耐えないばかりか、量産性にも不向き
であつた。
一方、本発明のジルコニア−シリカ系複合酸化
物被膜は、実施例に述べるように、接着性、透明
性、防湿性および量産性においてすぐれており、
長期信頼性に耐える光記録媒体を提供できる。
物被膜は、実施例に述べるように、接着性、透明
性、防湿性および量産性においてすぐれており、
長期信頼性に耐える光記録媒体を提供できる。
すなわち、ジルコニア−シリカ系複合酸化物被
膜は、複合酸化物の可溶性溶媒中に溶解した液
を、湿式でコーテイングし、適度な温度と湿度で
硬化することにより容易に形成される。
膜は、複合酸化物の可溶性溶媒中に溶解した液
を、湿式でコーテイングし、適度な温度と湿度で
硬化することにより容易に形成される。
ジルコニア−シリカ系複合酸化物を溶解する溶
媒としては、メタノール、エタノール、イソプロ
ピルアルコールやブタノール等のアルコール類を
応用に合わせて単独または混合して、適当な希釈
度で調合するのみでよい。硬化の原理は、次式の
通りである。
媒としては、メタノール、エタノール、イソプロ
ピルアルコールやブタノール等のアルコール類を
応用に合わせて単独または混合して、適当な希釈
度で調合するのみでよい。硬化の原理は、次式の
通りである。
ｎ・ZrO2SiO2・OR
H2O
――→
（ZrO2・SiO2）o＋HOR↑
Ｒ：アルキル基
つまり加水分解、ゲル化、硬化を経て分子間結
合したガラス状膜となる。アンモニア雰囲気では
さらに硬化速度を短縮することが可能である。
又、湿式であるため、浸漬、スピンコート、はけ
塗り等が可能であり、量産性においてきわめてす
ぐれている。
合したガラス状膜となる。アンモニア雰囲気では
さらに硬化速度を短縮することが可能である。
又、湿式であるため、浸漬、スピンコート、はけ
塗り等が可能であり、量産性においてきわめてす
ぐれている。
本発明のメモリー機能を有する光記録膜とは、
後述する実施例に限らず、Te、TeO2、Sb、Se、
Bi、又はAlなどを単独あるいは混合して蒸着し
た膜等であり、有機系では、光学的に応答するホ
トクロミツク材料、色素、染料、界面活性等の記
録材料を用いる場合にも適用可能である。そし
て、透明性基板としては、プラスチツク以外にも
ガラス等を用いた構成にも良いことは言うまでも
ない。
後述する実施例に限らず、Te、TeO2、Sb、Se、
Bi、又はAlなどを単独あるいは混合して蒸着し
た膜等であり、有機系では、光学的に応答するホ
トクロミツク材料、色素、染料、界面活性等の記
録材料を用いる場合にも適用可能である。そし
て、透明性基板としては、プラスチツク以外にも
ガラス等を用いた構成にも良いことは言うまでも
ない。
実施例
第１図は光記録媒体の構成例を示す。
(a)は透明性基板１の片面に光記録膜２を設け、
同じく透明性の基板３をはり合わせ、これらの表
面にジルコニア−シリカ系複合酸化物の被膜４を
設けた例である。(b)は基板５の片面に光記録膜６
を設け、その表面を複合酸化物の被膜７で覆つた
例である。
同じく透明性の基板３をはり合わせ、これらの表
面にジルコニア−シリカ系複合酸化物の被膜４を
設けた例である。(b)は基板５の片面に光記録膜６
を設け、その表面を複合酸化物の被膜７で覆つた
例である。
次に、具体例を説明する。
まず、1.2mm厚のポリカーボネート基板の片面
にTe及びTeO2を主成分とする光記録膜を設け、
この膜側にポリカーボネート板をはり合わせる。
次に、ジルコニア−シリカ系複合酸化物の２〜５
重量％イソプロピルアルコール溶液をスピンコー
トし、適湿環境条件下で加熱乾燥して硬化させ、
第１図ａに示す構成の光記録媒体をつくつた。
にTe及びTeO2を主成分とする光記録膜を設け、
この膜側にポリカーボネート板をはり合わせる。
次に、ジルコニア−シリカ系複合酸化物の２〜５
重量％イソプロピルアルコール溶液をスピンコー
トし、適湿環境条件下で加熱乾燥して硬化させ、
第１図ａに示す構成の光記録媒体をつくつた。
この実施例のものＡと、複合酸化物被膜を設け
ない比較例の記録媒体Ｂについて、70℃、80％
RHの条件で耐環境試験を行ない、光透過率を測
定した。その結果を第２図に示す。
ない比較例の記録媒体Ｂについて、70℃、80％
RHの条件で耐環境試験を行ない、光透過率を測
定した。その結果を第２図に示す。
図から明らかなように、比較例Ｂでは10日過ぎ
から830nｍでの光透過率が低下し始め、20日〜
50日では膜そのものも黒化が顕著になり、結晶核
の生成を生じたりするなど劣化が激しかつた。こ
れに対し、実施例では100日以後も光学特性や顕
微鏡観察における変化はなく、光記録媒体として
は長期信頼性を有することが確認できた。
から830nｍでの光透過率が低下し始め、20日〜
50日では膜そのものも黒化が顕著になり、結晶核
の生成を生じたりするなど劣化が激しかつた。こ
れに対し、実施例では100日以後も光学特性や顕
微鏡観察における変化はなく、光記録媒体として
は長期信頼性を有することが確認できた。
発明の効果
以上のように、本発明によれば、防湿性にすぐ
れ、透明性の高い信頼性が向上した光記録媒体を
実現することができる。
れ、透明性の高い信頼性が向上した光記録媒体を
実現することができる。
第１図は本発明の光記録媒体の構成例を示す縦
断面図、第２図は耐環境試験における光透過率の
経時変化の比較を示す図である。 １，３，５……透明性基板、２，６……光記録
膜、４，７……複合酸化物被膜。
断面図、第２図は耐環境試験における光透過率の
経時変化の比較を示す図である。 １，３，５……透明性基板、２，６……光記録
膜、４，７……複合酸化物被膜。
Claims (1)
- 【特許請求の範囲】 １ 透明性基板とメモリー機能を有する光記録膜
からなる光記録媒体であつて、分子間結合したガ
ラス状のジルコニア−シリカ系複合酸化物を保護
膜として備えたことを特徴とする光記録媒体。 ２ 透明性基板とメモリー機能を有する光記録膜
を有する光記録媒体に、ジルコニア−シリカ系複
合酸化物を可溶性溶媒に溶解した溶液を塗布し、
加熱処理することにより、前記酸化物による保護
膜を分子間結合したガラス状に形成することを特
徴とする光記録媒体の製造法。