JPS60226037A - 情報記録媒体 - Google Patents

情報記録媒体

Info

Publication number
JPS60226037A
JPS60226037A JP59081443A JP8144384A JPS60226037A JP S60226037 A JPS60226037 A JP S60226037A JP 59081443 A JP59081443 A JP 59081443A JP 8144384 A JP8144384 A JP 8144384A JP S60226037 A JPS60226037 A JP S60226037A
Authority
JP
Japan
Prior art keywords
recording
disks
recording medium
recorded
information recording
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP59081443A
Other languages
English (en)
Inventor
Kenjiro Watanabe
健次郎 渡辺
Junichi Akamatsu
赤松　順一
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Sony Corp
Original Assignee
Sony Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Sony Corp filed Critical Sony Corp
Priority to JP59081443A priority Critical patent/JPS60226037A/ja
Publication of JPS60226037A publication Critical patent/JPS60226037A/ja
Pending legal-status Critical Current

Abstract

(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。

Description

【発明の詳細な説明】 産業上の利用分野 本発明は、光照射例えばレーザー光を用いてその記録を
行い光学的にその読み出しを行うようにした光学式ビデ
オディスク、デジタルオーディオディスク、各種メモリ
ーカード等の画像ファイルや大容量メモリーに適用して
好適な情報の記録と読み出しとを行うことのできる、い
わゆるＤＲＡＩＩ（Ｄｉｒｅｃｔ　Ｒｅａｄ　Ａｆｔｅ
ｒ　１１ｒｉｔｅ　）型の情報記録媒体に係わる。
背景技術とその問題点 近時ビデオディスク、デジタルオーディオディスク等の
情報記録媒体において、例えば一般ユーザーによって簡
便に情報の記録ができる情報記録媒体の要求が高まって
いる。
記録可能な情報記録媒体として、レーザー光を情報信号
に応じて照射してその記録層を溶融、或いは蒸発ないし
は気化させて記録ピットを形成するようにしたものが提
案され、その多くの開発が注目されている。
この種の情報記録媒体の記録層は、ビスマスＢｉ、テル
ルＴｅなどの低融点金属薄膜を用いるものであるが、こ
のような金属薄膜によるものは、その情報記録に比較的
大きなパワーを必要とする。
一方、このような形状変化による記録態様を採らずに光
学的特性の変化によってその記録及び読み出しを行うよ
うにした情報記録媒体が提案された。この種の情報記録
媒体としては、例えばＳｂ２　Ｓｅ３、ＢｌｚＴｅ３と
の２層構造によるものがある（　Ｊｏｕｒｎａｌｏｆ　
ＡｐｐＨｅｄ　Ｐｙｓｉｃｓ　、　５４．　１２５６．
　１９８３参照）。
ところが、このような２層構造に基く記録層は、各層の
膜厚の僅かなずれが反射率に大きな変化をもたらすので
製造上大きな難点を有する。
発明の目的 本発明は記録層が単層構造をとり、製造が容易で、しか
も半導体レーザー光によって低パワー、高速記録を可能
にしたＤＲＡ−型の情報記録媒体を提供するものである
。
発明の概要 本発明においては、情報信号に応じた光照射によって記
録層に光学的特性の変化、すなわち透過率を低下させ、
反射率を高める光学的特性の変化を得てその記録を行う
ものである。
すなわち、本発明においては、Ｓｂ−Ｍｇ、或いはＳｂ
Ｓｂ−３ｅ−化合物薄膜に光照射、例えば半導体レーザ
ーを集束照射するとき、これが黒色ないしは暗色に光学
的に変化することを見出し、これに基いて種々の実験考
察を重ねた結果、低パワー、高速記録が可能な情報記録
媒体を得るに至った。
すなわち本発明においては、ｓｂもしくは５ｂ−３ｅ化
合物に、５〜９５原子九のＭｇを含ませて成る薄膜記録
層を有して成り、この薄膜記録層に光照射により情報の
記録を行うものである。
実施例 実施例１ 案内溝付の厚さ１．２ｆｉのインジェクション法により
形成したアクリル基板上にＭｇ−Ｓｂ化合物の薄膜記録
層を形成した。この薄膜記録層は、Ｍｇ蒸着源と、ｓｂ
蒸着源とを用い夫々の蒸発の割合を制御して両者の共蒸
着により　９００λ程度の厚さの夫々異る組成比に形成
した。このようにして夫々アクリル基板上に形成された
各組成の記録層上に夫々、同様に１．２■の厚さのアク
リル板を、紫外線硬化型樹脂によって密着接合し硬化し
た。この場合、この紫外線硬化樹脂は記録層の保護膜を
兼ねしめる。このようにして作製した直径２００ｍのデ
ィスクに対し、半導体レーザー光をアクリル基板側から
照射して記録を行った。この時のディスクの回転数は９
００ｒｐｍ、半導体レーザーパワー変調周波数は２　Ｍ
ｇ２とした。このようにして記録した記録部は、記録前
に比して透過率が低下して黒化し、また反射率は増加し
た。第１図中曲線（１）は、この実施例のディスクのＳ
ｂ−Ｍｇの組成比を変えたものにおける記録前の半導体
レーザー光に対する透過率Ｔを測定したもので、同図中
曲線（２）は、これら各ディスクに対して夫々最適のレ
ーザーパワーをもって記録を行った部分のＣ／Ｎを測定
したものである。これによれば、Ｍｇが３０〜９０原子
％で、好ましくは５０〜８０原子％でＣ／Ｎが４０ｄＢ
以上とすることができるが、ｓｂにＭｇを５〜９５原子
％含ましめるとき実用上記録可能な媒体が得られること
が確められた。
実施例２ この実施例では、実施例１における薄膜記録層の組成に
変えて、この薄膜記録層をＳｂ　−Ｍｇ　−Ｓｅ薄膜に
よって構成したもので、この場合、　５ｂｚＳ８３蒸着
源とＭｇ５Ｓ　ｂ２蒸着源とを用いて共蒸着を行った。
そして、５ｂ２ＳｅａとＭｇ５Ｓ　ｂｚとの組成比を変
えた各記録層によるディスクを作製した第２図中曲線（
３）はこの５ｂ２Ｓｅａの量を１とし、これに対するＭ
ｇ：１ＳｂｚＯ量をＸとした場合のその組成比Ｘを変え
た場合の、夫々　１８００ｒｐｍの回転数で、半導体レ
ーザーを５　ＭＨｚの信号で変調して記録したときのＣ
／Ｎの測定結果で、同図曲線（４は、夫々の記録レーザ
ーパワーを示したものである。これによれば、Ｓｅ量が
相対的に多い場合、Ｃ／Ｎが極めて良好になるが、半導
体レーザー光に対する透過率が上るために、記録時の半
導体レーザー光の吸収率が下り大きなパワー、例えばデ
ィスク面上で１５ｍＷ程度必要となる。他方相対的にＭ
ｇＯ量を大とすると、半導体レーザー光の吸収率は増す
が、熱伝導率が高くなることによって記録感度が低下し
てくる。この測定結果によれば、Ｓｂ４Ｓｅ３Ｍｇ３付
近の組成が低いレーザーパワーで記録できることがわか
る。
尚、この実施例においては、Ｓｂ２Ｓｅ３とＭｇ１Ｓ　
ｂｚとの共蒸着によったので、ｓｂの含有量は、４０原
子％という一定の量に設定されているが、５ｂＳｅの各
組成の蒸着源を用意し、Ｓｂ　−ＳｅとＭｇとの共蒸着
を行った。この場合、５ｂｓＳ　ｅ２Ｍｇ２付近で再生
Ｃ／Ｎの良好な記録媒体が得られた。第３図は、Ｓｂ　
−Ｓｅ−Ｍｇの三元図で、ディスクすなわち記録媒体を
１８００ｒｐ−で回転させた状態で、半導体レーザー光
によって４　Ｍｇ２の信号を記録した場合の再生Ｃ／Ｎ
が４０ｄＢ以上となるときの組成範囲を斜線を付して示
したものである。
実施例３ 実施例２における薄膜記録層を構成する蒸着源として５
ｂＳｅ化合物以外の５ｂ２０３を用いこれと１１ｇ３Ｓ
ｂ２の共蒸着を行った。この場合においても、記録がで
きた。
尚、上述した各側においてはディスクを構成した場合で
あるが、この形態に限られるものではなく、カード、シ
ート、テープその外の形態を採る場合においても有効で
あることが確められた。
発明の効果 上述したように本発明による情報記録媒体においては、
その記録が溶融、蒸発によるピットの形成によるもので
はなく、光学的特性の変化による態様を採るものである
ので、低パワーでの記録が可能となり、またその記録層
が単層構造を採り得るので冒頭に述べた反射率変化など
の不都合も回避でき、特性の安定した媒体を再現性良く
得ることができる。また、その記録も上述した実施例で
説明したような１８００ｒｐａ＋の高速回転での記録、
すなわち高速記録ができ、また高いＣ／Ｎが得られるの
で、ビデオディスクを始めとして各種の用途に用いて好
適なものである。
【図面の簡単な説明】
第１図はＳｂ−Ｍｇ記録層による媒体の各組成比に対す
る透過率Ｔと、Ｃ／Ｎの測定曲線図、第２図はＳｂｘ　
Ｓｅ３とＭｇ５Ｓ　ｂ２の組成に対するＣ／Ｎの測定曲
線と、この時の記録レーザーパワーを示した曲線図、第
３図はＳｂＳｂ−３ｅ−三元図における良好なＣ／Ｎを
得る組成範囲を示す図である。

Claims (1)

    【特許請求の範囲】
  1. ｓｂもしくは５ｂ−３ｓ化合物に、５〜９５原子％のＭ
    ｇを含ませて成る薄膜記録層を有し、該薄膜記録層に光
    照射により情報を記録することを特徴とする情報記録媒
    体。
JP59081443A 1984-04-23 1984-04-23 情報記録媒体 Pending JPS60226037A (ja)