JPS59227029A - 磁気記録媒体 - Google Patents
磁気記録媒体Info
- Publication number
- JPS59227029A JPS59227029A JP58099468A JP9946883A JPS59227029A JP S59227029 A JPS59227029 A JP S59227029A JP 58099468 A JP58099468 A JP 58099468A JP 9946883 A JP9946883 A JP 9946883A JP S59227029 A JPS59227029 A JP S59227029A
- Authority
- JP
- Japan
- Prior art keywords
- fatty acid
- ester
- magnetic layer
- durability
- magnetic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【発明の詳細な説明】
産業上の利用分野
本発明は、基拐の上に磁性層を形成してなる磁気記録媒
体に関づる。
体に関づる。
従来技術の問題点
ビデオテープおよびフロッピーディスクで代表される磁
気記録媒体(以下媒体と称す)は高度の耐久性が東京8
れるものである1、この耐久性の向上のため磁性層に潤
滑性をイ]与ηる方法として、磁性粉、バインダー等か
らなる磁性塗液に潤滑剤を分散さ1!基材に塗布Jるこ
とd3よび磁性層の表面潤滑剤を含む塗液を用いて再m
イ1jせしめることが一般に知られCいる・。ここで
用いられる潤滑剤どしては、シリコーン系化合物、フン
素系化合物。
気記録媒体(以下媒体と称す)は高度の耐久性が東京8
れるものである1、この耐久性の向上のため磁性層に潤
滑性をイ]与ηる方法として、磁性粉、バインダー等か
らなる磁性塗液に潤滑剤を分散さ1!基材に塗布Jるこ
とd3よび磁性層の表面潤滑剤を含む塗液を用いて再m
イ1jせしめることが一般に知られCいる・。ここで
用いられる潤滑剤どしては、シリコーン系化合物、フン
素系化合物。
脂肪酸アミド、脂肪酸エステルおよび炭化水素などが利
用されてぎた。
用されてぎた。
ところで例えば脂肪酸エステルであるブヂルステアレー
トを潤滑剤とする媒体は、通常の使用条イ′1下では、
耐久性がほぼ満足でさる水準にある。
トを潤滑剤とする媒体は、通常の使用条イ′1下では、
耐久性がほぼ満足でさる水準にある。
しかしながら、この媒体は、高温下または逆に低温下C
使用リーる場合には耐久性が著しく低くなることが判明
した。例えば、フロッピーディスクでは筺体(ジャケッ
ト)に収納され、外部から回転駆動を受けて記録再生が
行われるが、記録再生装置の駆動モーター等発熱体の影
響を受り、40〜50℃ないしはそれ以上の温度下に曝
される場合も多い。そのうえ最近の記録再生装置の小型
化、薄型化及び使用環境の多様化に伴ない、媒体に課口
られる保障ずべき耐久性はより高温側またはより低温側
に拡大されつつある。
使用リーる場合には耐久性が著しく低くなることが判明
した。例えば、フロッピーディスクでは筺体(ジャケッ
ト)に収納され、外部から回転駆動を受けて記録再生が
行われるが、記録再生装置の駆動モーター等発熱体の影
響を受り、40〜50℃ないしはそれ以上の温度下に曝
される場合も多い。そのうえ最近の記録再生装置の小型
化、薄型化及び使用環境の多様化に伴ない、媒体に課口
られる保障ずべき耐久性はより高温側またはより低温側
に拡大されつつある。
各種の潤H’l剤を用いた媒体の使用温度条イ′1と耐
久性との関係について述べれば単官能脂肪酸ニスアルど
しCは室温ひはブチシス1アレー1〜が比較的良9fな
耐久性を承りが、40〜50°Cの高温域および0〜・
10°Cの低温域においては耐久性が満足できない。ま
lこ11−キシエチルステアレートひは高温1“i1!
t、 、低温特11Iども幾分向上覆るが、まだ満足で
さる水準ではない。一方、グリセリンや1−リメチII
−ルブロバンの如き多価アルコールと脂肪酸との」ステ
ルCは室温くの耐久性と畠温下にJ3りる耐久性にマ)
しい差はないものの、耐久性のレベルが中宮能脂肪酸■
スプル類よりも低く、実用面C必ずしも満足できない。
久性との関係について述べれば単官能脂肪酸ニスアルど
しCは室温ひはブチシス1アレー1〜が比較的良9fな
耐久性を承りが、40〜50°Cの高温域および0〜・
10°Cの低温域においては耐久性が満足できない。ま
lこ11−キシエチルステアレートひは高温1“i1!
t、 、低温特11Iども幾分向上覆るが、まだ満足で
さる水準ではない。一方、グリセリンや1−リメチII
−ルブロバンの如き多価アルコールと脂肪酸との」ステ
ルCは室温くの耐久性と畠温下にJ3りる耐久性にマ)
しい差はないものの、耐久性のレベルが中宮能脂肪酸■
スプル類よりも低く、実用面C必ずしも満足できない。
これ1う中宮「1シの脂肪酸ニスデルと多官111の脂
肪酸エステルどを配合した多成分系潤滑剤を用いIC媒
体の耐久性は、多官能エステル単独のものとほぼ同程度
に過ぎづ゛、単に脂肪酸エステルの混合系では実用的に
満足しうるちのは得られてぃながっ/j 。
肪酸エステルどを配合した多成分系潤滑剤を用いIC媒
体の耐久性は、多官能エステル単独のものとほぼ同程度
に過ぎづ゛、単に脂肪酸エステルの混合系では実用的に
満足しうるちのは得られてぃながっ/j 。
発明の構成
本発明は、磁気記録媒体、特にウレタン系のバインダー
を用いて磁性層を形成uしめた磁気記録媒体において、
耐久性を改良する目的で、単官能□の脂肪酸ニスミール
、多官能の脂肪酸エステルおよび炭化水素化合物とから
なる多成分系の潤滑剤を磁性層を形成する磁性塗料に分
散uしめるか、または磁性層の表面にオーバー]−アイ
ングリ゛るかの手段により、磁性層に対し含有、11着
uしめたしのである。
を用いて磁性層を形成uしめた磁気記録媒体において、
耐久性を改良する目的で、単官能□の脂肪酸ニスミール
、多官能の脂肪酸エステルおよび炭化水素化合物とから
なる多成分系の潤滑剤を磁性層を形成する磁性塗料に分
散uしめるか、または磁性層の表面にオーバー]−アイ
ングリ゛るかの手段により、磁性層に対し含有、11着
uしめたしのである。
本発明でいう単官能の脂117+酸」ステルとはエステ
ル結合を1個含むものを云い、多官能の脂肪酸ニスデル
とはエステル結合を2個以上含むものを云う。具体的に
は、単官能の脂肪、酸ニスデルは、炭素数8から22の
脂肪酸と炭素数1から18の脂肪族アル」−ルから得ら
れる脂肪酸エステルを云う。
ル結合を1個含むものを云い、多官能の脂肪酸ニスデル
とはエステル結合を2個以上含むものを云う。具体的に
は、単官能の脂肪、酸ニスデルは、炭素数8から22の
脂肪酸と炭素数1から18の脂肪族アル」−ルから得ら
れる脂肪酸エステルを云う。
炭素数8から22の脂肪酸としては直鎖状1分枝状。
不飽和脂肪酸を含む。例えば、ラウリン酸、ミリスチン
酸、パルミヂン酸、ステアリン酸、イソステアリン酸、
オレイン酸、リノール酸等が挙げられる。。
酸、パルミヂン酸、ステアリン酸、イソステアリン酸、
オレイン酸、リノール酸等が挙げられる。。
1シJ素数′1か618の脂肪族、アルコールとしては
、白鎖状1分枝状、不飽和アル」−ルを含む。又、−r
−−−5ル結合をイ」していCもよい。
、白鎖状1分枝状、不飽和アル」−ルを含む。又、−r
−−−5ル結合をイ」していCもよい。
IZIえば、」ニタノール、ブタノール、ヘキサノ−J
し、2−1ブルヘニ1.シルフ7ル]−ル、イソステア
リルアルコール ルノノル」−ル,メ1〜キシエチルアル]ール,■トー
トジエチルアルコール、ブ1へキシエチルアルコール等
を挙げることができる。
し、2−1ブルヘニ1.シルフ7ル]−ル、イソステア
リルアルコール ルノノル」−ル,メ1〜キシエチルアル]ール,■トー
トジエチルアルコール、ブ1へキシエチルアルコール等
を挙げることができる。
また多官能の脂肪酸エステルは2官能,3官能または4
宵1iシの脂肪酸ニスデルが代表的ぐある。
宵1iシの脂肪酸ニスデルが代表的ぐある。
2官能の脂肪酸エステルは2官能のグリコールと長鎖1
1H !I/j 止どのニスデル3または2塩基酸と1
価アル7j−ルどの上スプルである。グリコールとして
は例えばエナレングリコール,10ピレングリコール、
ジ1チレングリコール,ポリエチレングリコール舌を挙
(yることができる。長鎖脂肪酸としくは炭素数ε3か
ら18の直鎖状,分岐状,不飽和脂肪酸を挙げることか
一Cきる。2塩基酸としては、例えばフマール酸,マレ
イン酸,アジピン酸+ ’Lバヂン酸.アゼライン酸等
を挙げることができる。
1H !I/j 止どのニスデル3または2塩基酸と1
価アル7j−ルどの上スプルである。グリコールとして
は例えばエナレングリコール,10ピレングリコール、
ジ1チレングリコール,ポリエチレングリコール舌を挙
(yることができる。長鎖脂肪酸としくは炭素数ε3か
ら18の直鎖状,分岐状,不飽和脂肪酸を挙げることか
一Cきる。2塩基酸としては、例えばフマール酸,マレ
イン酸,アジピン酸+ ’Lバヂン酸.アゼライン酸等
を挙げることができる。
1価のアルコールとしては、炭素数1から18の直鎖状
,分岐状,不飽・和アルコールを挙げることができる。
,分岐状,不飽・和アルコールを挙げることができる。
3官能の脂肪酸エステルとじては1〜リメチロールプロ
パン,1〜リメヂ[1−ルエタン.グリレリン等の3価
アルコールと炭素数8から22の脂肪酸からのコースチ
ルを挙げることができる。4官能の脂肪酸エステルとし
てはソルビトール、ペンタエリスリ1−−ルと直鎖脂肪
酸のエステルを挙げることができる。
パン,1〜リメヂ[1−ルエタン.グリレリン等の3価
アルコールと炭素数8から22の脂肪酸からのコースチ
ルを挙げることができる。4官能の脂肪酸エステルとし
てはソルビトール、ペンタエリスリ1−−ルと直鎖脂肪
酸のエステルを挙げることができる。
更に本発明に使用する炭化水素化合物とは鉱物油.流動
パラフィン、α−オレフィンオリゴマー。
パラフィン、α−オレフィンオリゴマー。
ポリブテン、液状ポリプロピレン等が例示できる。
室温において液状であって分子n1200以上が好まし
く、特に分子量300〜1000程磨のものが好適に使
用し得る。
く、特に分子量300〜1000程磨のものが好適に使
用し得る。
なお上述した単官能の脂肪酸1スプル、多官能の脂肪酸
エステルおよび炭化水素化合物との混合物からなる潤滑
剤の添加量は、磁性粉、バインダーその他成分を含む磁
性層全宙吊の0.3〜12%が好ましい。添加量が0.
3%未満であると、潤滑剤どして、耐久性の効果に乏し
く、また12%を越えると潤滑剤が多づぎて、逆に塗膜
が軟化する等の弊害かで−(耐久性が低下するからであ
る。
エステルおよび炭化水素化合物との混合物からなる潤滑
剤の添加量は、磁性粉、バインダーその他成分を含む磁
性層全宙吊の0.3〜12%が好ましい。添加量が0.
3%未満であると、潤滑剤どして、耐久性の効果に乏し
く、また12%を越えると潤滑剤が多づぎて、逆に塗膜
が軟化する等の弊害かで−(耐久性が低下するからであ
る。
また、上述の)14合系潤滑剤のうち、炭化水素化合物
の流力10nについては、磁性層全重量の0.1〜6%
、望3Lシクは、全潤滑剤量の5〜50%が好ましい。
の流力10nについては、磁性層全重量の0.1〜6%
、望3Lシクは、全潤滑剤量の5〜50%が好ましい。
炭化水素化合物の添加量が多くなり過さ゛るど、バイン
ダーへ安相溶性が低下し、環境の変化Cブルーミングの
生じる恐れがあるためである。
ダーへ安相溶性が低下し、環境の変化Cブルーミングの
生じる恐れがあるためである。
なお本発明においては、磁性粉、バインダーは従来公知
の−bのぐあっ−Cもよく、ま1=伯に分散剤(レシチ
ン等)、帯電防止剤(カニボン等゛)、補強剤(α−F
e203.アルミノ等)等の従来公知の添加剤を添加す
るようにしてもよい。
の−bのぐあっ−Cもよく、ま1=伯に分散剤(レシチ
ン等)、帯電防止剤(カニボン等゛)、補強剤(α−F
e203.アルミノ等)等の従来公知の添加剤を添加す
るようにしてもよい。
実施例
次に本発明の実施例を述べる。以下の実施例および比較
例において「部」はづべて「重量部」を示す。
例において「部」はづべて「重量部」を示す。
実施例1
γ−Fe2O370部
ポリウレタンエラストマーと水[を
有する塩化ビニル−酢酸ビニル共重
合体からなる磁気記録用バインダー 17部カーボン
ブラック 5部分散剤
2部ポリイソシアネートか
らなる架橋剤 2部テ1〜ラヒドロフラン、シクロ
ヘキサン混合溶剤 180部
潤滑剤 ブトキシ王チルステアレー1− 1 、5部オ
リーブメイル 1.5部鉱物油
1部上記組成物を混合
分散した後75μIrL厚のポリエステルフィルム基体
両面に乾燥厚さが片面約3μ肌となるように塗布し、乾
燥後表面をカレンダー処理したうえで加熱架橋し円板状
に打ら抜いて)11ツビーノ゛イスクを冑だ。
ブラック 5部分散剤
2部ポリイソシアネートか
らなる架橋剤 2部テ1〜ラヒドロフラン、シクロ
ヘキサン混合溶剤 180部
潤滑剤 ブトキシ王チルステアレー1− 1 、5部オ
リーブメイル 1.5部鉱物油
1部上記組成物を混合
分散した後75μIrL厚のポリエステルフィルム基体
両面に乾燥厚さが片面約3μ肌となるように塗布し、乾
燥後表面をカレンダー処理したうえで加熱架橋し円板状
に打ら抜いて)11ツビーノ゛イスクを冑だ。
実施例2
実施例1にa5いC、ブトキシ1ヂルスiアレー1−、
.1−リーゾオイルd3よび鉱物油系潤滑剤の代りに、
イソAクチルスデアレ−1〜 1.5部、トリメヂIJ
−ルプロパントリfカッニーh1.5部およびα−Aレ
フインΔリゴマー 1.0部を用い−C実施11i11
1と同様にし−C、フロッピーディスクを得た。
.1−リーゾオイルd3よび鉱物油系潤滑剤の代りに、
イソAクチルスデアレ−1〜 1.5部、トリメヂIJ
−ルプロパントリfカッニーh1.5部およびα−Aレ
フインΔリゴマー 1.0部を用い−C実施11i11
1と同様にし−C、フロッピーディスクを得た。
実施例こ3
実施例1にa3いてブト:Vシ]1−プルスiアレー1
〜。
〜。
オリーブ油および鉱物油系avj滑剤の代りに、ブチル
スフアレー1〜4.0部、1〜リメヂロールブL1パン
2.0部J5よびスフワラ21.0部を用いて実施例1
と11目1こし−()1」ツビーディスクを得た。
スフアレー1〜4.0部、1〜リメヂロールブL1パン
2.0部J5よびスフワラ21.0部を用いて実施例1
と11目1こし−()1」ツビーディスクを得た。
実施例4
実施例1においてブトキシ1ヂルスiアレート。
オリーブ油Jメよひ鉱物油の添加f4%をそれぞれ0.
5部、0.5部および0.5部に変更して、実施例1と
同様にしでフロッピーディスクを百だ。
5部、0.5部および0.5部に変更して、実施例1と
同様にしでフロッピーディスクを百だ。
比較例
実施例1において、ブトキシ」−デルステアレー1〜.
オリーブ油および鉱物油系の潤滑剤を表1の組成に変え
て、実施例1と同様にしCフロッピーディスクを得た。
オリーブ油および鉱物油系の潤滑剤を表1の組成に変え
て、実施例1と同様にしCフロッピーディスクを得た。
(以下余白)
表1 比較例の組成
このようにして製作した各実施例、比較例のフ[lツピ
ーディスクの耐久性の評価を8インチの市販)1]ツビ
ーデイスク装置を用いC以下の通り行った。ヘッドデン
ション30りでヘツドロードを行い、同一トラックで連
続しC回転させて、出力レベルか初期値の80%以下に
なる時間をしって媒体の耐久時間どしIC8なお、通1
iものフロッピーディスク装置のへラドテンションは1
0〜207であり、水沫で用いた309のへラドテンシ
ョンは、フL1ツピーディスクの耐久性評価条件としで
はかなり厳しいものと云える。また雰囲気温度は50℃
および0℃である。
ーディスクの耐久性の評価を8インチの市販)1]ツビ
ーデイスク装置を用いC以下の通り行った。ヘッドデン
ション30りでヘツドロードを行い、同一トラックで連
続しC回転させて、出力レベルか初期値の80%以下に
なる時間をしって媒体の耐久時間どしIC8なお、通1
iものフロッピーディスク装置のへラドテンションは1
0〜207であり、水沫で用いた309のへラドテンシ
ョンは、フL1ツピーディスクの耐久性評価条件としで
はかなり厳しいものと云える。また雰囲気温度は50℃
および0℃である。
耐久11間によって、次の3つのランクに区分した。
耐久性ランクA:耐久時間250時間以−トB:
n 150へ・ 250時間C: n
150時間以下 上記実施例および比較例によっ−U 1’lた耐久性の
評価結果を表2に示す。
n 150へ・ 250時間C: n
150時間以下 上記実施例および比較例によっ−U 1’lた耐久性の
評価結果を表2に示す。
これらの結果によれば、単独系では、それぞれ必ずしし
良好な特性を示さないが、単官能、多官能の脂肪酸コー
スアルの混合系に、炭化水素化合物を加えた潤滑剤系(
・は、高温、低温の特性が署しく改善されることが明ら
かである。
良好な特性を示さないが、単官能、多官能の脂肪酸コー
スアルの混合系に、炭化水素化合物を加えた潤滑剤系(
・は、高温、低温の特性が署しく改善されることが明ら
かである。
実施例巳)
実施例1にi3イ(,7−Fe、0370部の代すニコ
バ/L/ 1−酸化鉄70部を用いた磁+1塗料を作成
し、14μyn、 17のポリ土スjルフィルム基体に
乾燥厚さが約4.5μとなるように塗イ11シ、乾燥後
人mlを7Jレンター処理したうえで加熱架橋さゼ、1
/2インヂrIJにスリットし、ビデオテニブを1がた
。
バ/L/ 1−酸化鉄70部を用いた磁+1塗料を作成
し、14μyn、 17のポリ土スjルフィルム基体に
乾燥厚さが約4.5μとなるように塗イ11シ、乾燥後
人mlを7Jレンター処理したうえで加熱架橋さゼ、1
/2インヂrIJにスリットし、ビデオテニブを1がた
。
比較例7
実施例5において、ブ1〜キシエチルステアレ=1−
、オリーブメイルおよび鉱物油系潤滑剤の代りに、ブヂ
ルスデアレ−1〜 2.0部およびAリーブオイル2.
0部からなる潤滑剤を用い実施例5と同様にしCビf7
1ア〜プを得た。
、オリーブメイルおよび鉱物油系潤滑剤の代りに、ブヂ
ルスデアレ−1〜 2.0部およびAリーブオイル2.
0部からなる潤滑剤を用い実施例5と同様にしCビf7
1ア〜プを得た。
実施例5.比較例7のビデ副テープについて、日本電子
工業会規格V l−I S 3JA格の方法により40
°C雰囲気でスヂル特性を評価した結果を表3に示づ。
工業会規格V l−I S 3JA格の方法により40
°C雰囲気でスヂル特性を評価した結果を表3に示づ。
表 3
ビデオテープにおいても記述のフロッピーディスク同様
本発明の潤滑剤系で磁性層の耐久性が向上していること
が明らかである。
本発明の潤滑剤系で磁性層の耐久性が向上していること
が明らかである。
発明の効果
以上のように本発明では単独系、または2成分系潤滑剤
で果し得なかった高度の耐久11を系統の異なる第3の
成分を添加りることにより高温、低温特性をバランスさ
せつつしかも特異的に向上けしめることがでさた。
で果し得なかった高度の耐久11を系統の異なる第3の
成分を添加りることにより高温、低温特性をバランスさ
せつつしかも特異的に向上けしめることがでさた。
手続補正巴
昭和58年 9月」日
特n午庁長1ヨ゛殿
1、事件の表示
特願昭 58−99468号
2、発明の名称
磁気記録媒体
3、補正をする者
事イ′1との関係 特R1[出願人
東京都千代田区内幸町2丁目1番1号
帝人メモレックス 株式会社
代表者 飯 野 弘 之
4、代 理 人 東京都千代田区内幸町2丁目十
番1号(飯野 ビル)
番1号(飯野 ビル)
Claims (1)
- 【特許請求の範囲】 1)単官能の脂肪酸エステル、多官能の脂肪酸ニスデル
および炭化水素化合物とからなる潤滑剤が磁性層に含イ
ラされてなる磁気記録媒体。 2)前記潤滑剤が磁性層の0,3〜12重呈%の範囲を
占める特、lT請求の範囲第1項記載の磁気記録媒体。