JPS58161974A - 誘電体磁器組成物 - Google Patents
誘電体磁器組成物Info
- Publication number
- JPS58161974A JPS58161974A JP57040396A JP4039682A JPS58161974A JP S58161974 A JPS58161974 A JP S58161974A JP 57040396 A JP57040396 A JP 57040396A JP 4039682 A JP4039682 A JP 4039682A JP S58161974 A JPS58161974 A JP S58161974A
- Authority
- JP
- Japan
- Prior art keywords
- composition
- ceramic composition
- dielectric ceramic
- grain size
- crystal grain
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【発明の詳細な説明】
本発明はｉ壊電圧が高くかつ寿命の長い温度補償用誘電
体磁器組成物に関する。
体磁器組成物に関する。
従米温度補償用鋤電体磁器組成書として１例えばランタ
ン、チタン、カルクラムおよびマグネシウムの酸化物を
それぞれＬａｍ０ｍ ＊ Ｔ ｉ Ｏ＠ ＠ Ｃａ Ｏ
およびＭｇＯに換算して、Ｌｍ＠０＠ ３．０乃至２５
． ＯｗａａＬ憾とＴｉ０１５１．０乃至６２．０ ｌ
１１ｏＬ ％とＣａ０Ｏ，５乃至４５．０ ｗａａＬ
％とＭｇＯ１，０乃至４５．０ ｗＬ ４とからなるＬ
ａｍｂ、−’ｒｉｏ、−ＣａＯ−ＭｇＯ系組成物が公知
となっている。しかしながら、その結晶粒径は５μｍ以
上で大きく、積層コンデンサなどのように電界強度の大
きい製品には不適当である。すなわち。
ン、チタン、カルクラムおよびマグネシウムの酸化物を
それぞれＬａｍ０ｍ ＊ Ｔ ｉ Ｏ＠ ＠ Ｃａ Ｏ
およびＭｇＯに換算して、Ｌｍ＠０＠ ３．０乃至２５
． ＯｗａａＬ憾とＴｉ０１５１．０乃至６２．０ ｌ
１１ｏＬ ％とＣａ０Ｏ，５乃至４５．０ ｗａａＬ
％とＭｇＯ１，０乃至４５．０ ｗＬ ４とからなるＬ
ａｍｂ、−’ｒｉｏ、−ＣａＯ−ＭｇＯ系組成物が公知
となっている。しかしながら、その結晶粒径は５μｍ以
上で大きく、積層コンデンサなどのように電界強度の大
きい製品には不適当である。すなわち。
結晶粒径が大きい場合には、結晶粒子１個あたり和かか
る電界強度は大きくなり、そのため碧壊電圧は低くなり
、ｌＩ＃命４ｂ短くなり、従って信頼性が低下するとい
う欠点があった。また、Ｌａ１ｏ、を含有しているため
に％アルンナ・セッターを用いる必要があり１通常の誘
電体磁器組成物で用いるジルコニア・竜ツメ−と使い別
けをしなければならないという襄造工ｍ画での煩繍さが
あった。
る電界強度は大きくなり、そのため碧壊電圧は低くなり
、ｌＩ＃命４ｂ短くなり、従って信頼性が低下するとい
う欠点があった。また、Ｌａ１ｏ、を含有しているため
に％アルンナ・セッターを用いる必要があり１通常の誘
電体磁器組成物で用いるジルコニア・竜ツメ−と使い別
けをしなければならないという襄造工ｍ画での煩繍さが
あった。
本発明者らは上記の従来の４ＩＩＩＩｔ物の欠点を解決
し、結晶粒・径が５μｍ未満のきわめてＩｉ細であるの
で破壊電圧が鳩くかつ寿命が長く、シかもジルコニア・
セッターにて焼成可能な−電体磁器組成物ｔ−提供すぺ
＜ｍ討した結果、＊化ジルコニウムを添加すると、得ら
れた誘電体磁器組成物の結晶粒子が微細化し、しか４１
１電率１１Ｑ％温度特性を低下させることがなく、更に
ジルコニア・セッターにて焼成可能であることを見出し
、本発明和到達した。すなわち１本発明のｌｌ！旨とす
るところは。
し、結晶粒・径が５μｍ未満のきわめてＩｉ細であるの
で破壊電圧が鳩くかつ寿命が長く、シかもジルコニア・
セッターにて焼成可能な−電体磁器組成物ｔ−提供すぺ
＜ｍ討した結果、＊化ジルコニウムを添加すると、得ら
れた誘電体磁器組成物の結晶粒子が微細化し、しか４１
１電率１１Ｑ％温度特性を低下させることがなく、更に
ジルコニア・セッターにて焼成可能であることを見出し
、本発明和到達した。すなわち１本発明のｌｌ！旨とす
るところは。
Ｌａｖａｓ −Ｔｊｏｙ−ＣａＯ−ＭｇＯ系組成物を主
成分とし、ジルコニウムの酸化物をＺｒＯ，に換ｇして
、該主成分に対し０．１重量憾乃至８．０重量僑含有し
てなる誘電体磁器組成物、にある。
成分とし、ジルコニウムの酸化物をＺｒＯ，に換ｇして
、該主成分に対し０．１重量憾乃至８．０重量僑含有し
てなる誘電体磁器組成物、にある。
本発明の組成物は上記構成によって、実施例に示すよう
に、結晶粒径がきわめて微細であるので。
に、結晶粒径がきわめて微細であるので。
積層コンデンサなどのように電界強度の大きい製品には
好適である。すなわち、ｌｌＩＮａｌ粒径が微細である
ので結１粒子１個あたりにかかる電界強度が小さくなり
、それによって破壊電圧が高くなり、寿命はのびて信槌
性が向上する。また１本発明の組成物は、酸化ジルコニ
ウムを含有しない従来の組成物とｌＷｌ等の結電率、Ｑ
、温度特性を有し、実用的であることは実施例が示す通
りである。
好適である。すなわち、ｌｌＩＮａｌ粒径が微細である
ので結１粒子１個あたりにかかる電界強度が小さくなり
、それによって破壊電圧が高くなり、寿命はのびて信槌
性が向上する。また１本発明の組成物は、酸化ジルコニ
ウムを含有しない従来の組成物とｌＷｌ等の結電率、Ｑ
、温度特性を有し、実用的であることは実施例が示す通
りである。
本発明の組成物の組成において、酸化ジルコニウムの鎗
が０．１重量嘩未満であると、結晶粒径が５μｍ以上に
なるとともにジルコニア・セッターと反応し、また、８
．０重量憾を超えると粒径５μｍ以上の結晶が発生する
。
が０．１重量嘩未満であると、結晶粒径が５μｍ以上に
なるとともにジルコニア・セッターと反応し、また、８
．０重量憾を超えると粒径５μｍ以上の結晶が発生する
。
本発明の組成物は１例えば、１＠成後に本＠例の組成に
なるように秤取された原料配合物をボールミルで湿式１
合・粉砕し、得られた混合・粉砕物を脱水−乾燥後、所
定の形式に加圧成形して焼成することにより得ることが
できる。この場合、Ｎ科として使用するランタン化合物
はＬａ１Ｏ＠、 Ｌａｇ（Ｃ鵞０４）、・９１１，０．
チタン化合物はＴｉｅ、、 ７１１Ｏ，、カルシウム化
合物はＣａｂ、ＣａＣ０＠ 、マグネシウム化合物はＭ
ｇＯ，ＭｇＣｌＯ４・２ Ｈ，Ｏ、ジルコニア化合物ｕ
ｚ ｒｏ、 、 ｓｚ ｒＯ，１１Ｃ０，１１６Ｈ，Ｏ
が好適である。
なるように秤取された原料配合物をボールミルで湿式１
合・粉砕し、得られた混合・粉砕物を脱水−乾燥後、所
定の形式に加圧成形して焼成することにより得ることが
できる。この場合、Ｎ科として使用するランタン化合物
はＬａ１Ｏ＠、 Ｌａｇ（Ｃ鵞０４）、・９１１，０．
チタン化合物はＴｉｅ、、 ７１１Ｏ，、カルシウム化
合物はＣａｂ、ＣａＣ０＠ 、マグネシウム化合物はＭ
ｇＯ，ＭｇＣｌＯ４・２ Ｈ，Ｏ、ジルコニア化合物ｕ
ｚ ｒｏ、 、 ｓｚ ｒＯ，１１Ｃ０，１１６Ｈ，Ｏ
が好適である。
次に１本発＃４を実施例によってさらに具体的に説明す
るが１本発明はその要旨を越えない限り以下の実施例Ｋ
ｉ１定されるものではない。
るが１本発明はその要旨を越えない限り以下の実施例Ｋ
ｉ１定されるものではない。
実施例
Ｉ科として、主成分であるＬａ１０Ｂ 、 Ｔ ４０１
、 Ｃａｂ。
、 Ｃａｂ。
ＭｇＯ、ｆｉびに添加成分であるＺｒ０１を、それぞれ
試＠ＩＩＩ＆のＬａ１Ｏ畠、Ｔｉ０１．Ｃａｂ、ＭｇＯ
およびＺｒＯ２を用い、焼成後に次のｔｌに下す配仔比
になるよう秤取し、ボールイル中で２０時時間式混合・
粉砕し、脱水・乾ｆＩｋ後、成形圧力３ ｔｏｎ／ｃ−
で直径１６ｍｍ厚さ０．６ｍｍの円板に加圧成形し、成
形物を次の表に示す焼成温度で１時間焼成し、試料番号
１〜７とした。
試＠ＩＩＩ＆のＬａ１Ｏ畠、Ｔｉ０１．Ｃａｂ、ＭｇＯ
およびＺｒＯ２を用い、焼成後に次のｔｌに下す配仔比
になるよう秤取し、ボールイル中で２０時時間式混合・
粉砕し、脱水・乾ｆＩｋ後、成形圧力３ ｔｏｎ／ｃ−
で直径１６ｍｍ厚さ０．６ｍｍの円板に加圧成形し、成
形物を次の表に示す焼成温度で１時間焼成し、試料番号
１〜７とした。
これら試料の結晶粒径は光学顕微鏡により倍率４００で
−察し、容量値およびＱ値は試料の両面に銀電極を焼付
け、ＹＨＰデジタルＬＣＲメータモデル４２７４Ａを使
瑣し、測定温度２５°Ｃ，＃Ｊ定電圧１、 ＯＶｒｍｓ
、醐定周ｉ数１００に■２による測定により求めた。温
度時性は２５°Ｃにおける容量値を基準とし８５°Ｃｌ
ＩＣおける容量値にて算出した。これら物性の測定結果
を次の表に併せ示す、。
−察し、容量値およびＱ値は試料の両面に銀電極を焼付
け、ＹＨＰデジタルＬＣＲメータモデル４２７４Ａを使
瑣し、測定温度２５°Ｃ，＃Ｊ定電圧１、 ＯＶｒｍｓ
、醐定周ｉ数１００に■２による測定により求めた。温
度時性は２５°Ｃにおける容量値を基準とし８５°Ｃｌ
ＩＣおける容量値にて算出した。これら物性の測定結果
を次の表に併せ示す、。
得られた試料はいずれも次の表が水すように。
酸化ジルコニウム添加により結晶粒径が５．０μｍ未満
で、かつ実用的な酵電卓、Ｑ値および温度特性１に有し
、しかもジルコニア拳セッターにて焼成ＩｊＴ舵な酵電
体ｉｌ器組成智であり、積層コンデンサのごとき電界強
度の大きい製品には最適である。
で、かつ実用的な酵電卓、Ｑ値および温度特性１に有し
、しかもジルコニア拳セッターにて焼成ＩｊＴ舵な酵電
体ｉｌ器組成智であり、積層コンデンサのごとき電界強
度の大きい製品には最適である。
３６４
手続補正書
昭和５７年４月１４日
特許庁長官 島 １）春 樹 殿
１、事件の表示
昭和５７年特許願第０４０３９６号
２、発明の名称
誘電体磁器組成物
３、補正をする者
事件との関係 特許出願人
４、代理人
Claims (1)
- （１１Ｌａ１０ｇ−Ｔｉ０１−ＣａＯ−ＭｇＯ系組成物
を主成分とし、ジルコニウムの酸化物をＺｒＯ，にＩｌ
Ｉ算して、該生成分に対し０．１重量嗟乃至８．０重量
慢含Ｍしてなる誘電体磁器組成物。