JPH0476790B2 - - Google Patents
Info
- Publication number
- JPH0476790B2 JPH0476790B2 JP63187765A JP18776588A JPH0476790B2 JP H0476790 B2 JPH0476790 B2 JP H0476790B2 JP 63187765 A JP63187765 A JP 63187765A JP 18776588 A JP18776588 A JP 18776588A JP H0476790 B2 JPH0476790 B2 JP H0476790B2
- Authority
- JP
- Japan
- Prior art keywords
- color
- leuco dyes
- acid
- mixture
- color developer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
〔産業上の利用分野〕
本発明は、感圧複写紙や感熱記録紙に用いられ
ているロイコ系色素に関し、特に発色性および耐
退色性、耐光性に優れ、白色度の高いロイコ系色
素用顕色剤に関するものである。 〔発明の概要〕 近年、情報産業の急速な発展にともない、産業
用、オフイス用などの情報機器の端末から、容易
に記録出力が得られる感圧複写紙や感熱記録紙の
利用が盛んに行われている。 本発明は、上記感圧複写紙や上記感熱記録紙に
用いられているロイコ系色素用顕色剤として、ア
ルミナと窒化ボロン(BN)の混合物、もしく
は、アルミナと窒化ボロン(BN)とSiO2の混合
物を用いることによつて、発色および耐退色性、
耐光性に優れた記録を得ることができるようにし
たロイコ系色素用顕色剤を提供することを目的と
している。 〔従来の技術〕 従来のロイコ系色素用顕色剤として、α−ナフ
トール、β−ナフトール、2・2′−メチレンビス
(4−メチル−6−ターシヤリ−イソブチルフエ
ノール)、2・2′−メチレンビス(4−クロルフ
エノール)、4フエニルフエノール、4−ターシ
ヤリブチルフエノール、2・2′−ジヒドロキシジ
フエノール、4・4′−セカンダリ−ブチリデンフ
エノール、4、4′ジクロルヘキシリジンジフエノ
ール、4−ヒドロキシジフエノキシド、4・4′−
イソプロピリデンジフエノール、ハイドロキノ
ン、4−ヒドロキシアセトフエノール、4・4′−
イソピリデンビス(2−ターシヤリ−ブチルフエ
ノール)、4−ターシヤリ−オクチルカテコール、
ノボラツク型フエノール樹脂、フエノール重合体
などのフエノール性化合物や、サリチル酸、3−
(α−メチルベン)サリチル酸、3・5−ジ−α
−α−メチルベンジルサリチル酸、3−イソプロ
ピルサリチル酸、3−クロル−5−(α−メチル
ベンジル)サリチル酸、3−フエニル−5−
(α・α−ジメチルベンジル)サリチル酸、3−
ベンジルサリチル酸、3・5−ジターシヤリブチ
ルサリチル酸、3−ターシヤリブチルサリチル
酸、安息香酸、テレフタル酸、3・5−ジメチル
−4−ヒドロキシ安息香酸、パラターシヤリブチ
ル安息香酸、3−セカンダリブチル−4−ヒドロ
キシ安息香酸、トリクロル安息香酸、3−シクロ
ヘキシル−4−ヒドロキシ安息香酸などの芳香族
カルボン酸、及びこれらフエノール性化合物や、
活性白土、酸性白土、ケイ酸アルミニウム、ベン
トナイト、アタパルガイト、コロイダルシリカな
どの固体酸や、マグネシウム、アルミニウム、カ
ルシウム、チタン、マンガン、スズ、ニツケルな
どの多価金属と芳香族カルボン酸との塩などの有
機酸性物質が使用されている。 〔発明が解決しようとしている課題〕 しかし、従来の有機化合物をロイコ系色素用顕
色剤として用いた場合、発色性があまり良好でな
く、退色するという問題があつた。また、光照射
による着色や大気中の窒素化合物による黄変が激
しいなど問題があつた。また、活性白土などは、
黄色味を帯びており良好な画像を得ることができ
なかつた。 そこで、本発明は、従来のこの様な問題点を解
決するために、発色性に優れ、また耐退色性、耐
光性に優れ、白色度の高いロイコ系色素用顕色剤
を提供することを目的としている。 〔課題を解決するための手段〕 本発明は、上記課題を解決するために、ロイコ
系色素用顕色剤としてアルミナと窒化ボロン
(BN)の混合物、もしくは、アルミナと窒化ボ
ロン(BN)とSiO2の混合物を用いることによつ
て、発色性を向上させ、また、耐退色性、耐光性
を向上させるようにしたものである。さらに、ア
ルミナ、窒化ボロン(BN)、及びSiO2は、白色
度も高いために、良好な画像が得られるようにし
たものである。 〔実施例〕 以下に本発明の実施例を示すが、本発明はこれ
に限定されるものではない。 〔実施例1〕 5%(W/W)の濃度のポリビニルアルコール
水溶液50重量部に、アルミナ15重量部、BN15重
量部を加え、ボールミルを用いて約24時間粉砕分
散し、顕色剤分散液とした。この顕色剤分散液を
バーコーターを用いて、40g/m2の上質紙上に、
20g/m2(乾燥重量)となるように塗工し、ロイ
コ系色素用顕色シートとした。このロイコ系色素
用顕色シートを、ロイコ系色素を用いた感圧複写
紙と合わせ、120Kg/cm2の圧力で発色させ、濃度
を測定した。また、耐退色性を調べるために、発
色直後より500時間後に発色濃度を測定した。以
上の測定値を表1に示す。 〔実施例2〕 5%(W/W)の濃度のポリビニルアルコール
水溶液50重量部に、アルミナ10重量部、BN10重
量部、SiO210重量部を加え、ボールミルを用い
て約24時間粉砕分散し、顕色剤分散液とした。こ
の顕色剤分散液をバーコーターを用いて、40g/
m2の上質紙上に、20g/m2(乾燥重量)となるよ
うに塗工し、ロイコ系色素用顕色シートとした。
このロイコ系色素用顕色シートを、ロイコ系色素
を用いた感圧複写紙と合わせ、120Kg/cmの圧力
で発色させ、濃度を測定した。また、耐退色性を
調べるために、発色直後より500時間後に発色濃
度を測定した。以上の測定値を表1に示す。 〔比較例〕 上記の実施例と比較するために、公知のロイコ
系色素用顕色剤のひとつである、ビスフエノール
Aについて、実施例1,2と同様の測定を行い、
測定値を表1に示す。
ているロイコ系色素に関し、特に発色性および耐
退色性、耐光性に優れ、白色度の高いロイコ系色
素用顕色剤に関するものである。 〔発明の概要〕 近年、情報産業の急速な発展にともない、産業
用、オフイス用などの情報機器の端末から、容易
に記録出力が得られる感圧複写紙や感熱記録紙の
利用が盛んに行われている。 本発明は、上記感圧複写紙や上記感熱記録紙に
用いられているロイコ系色素用顕色剤として、ア
ルミナと窒化ボロン(BN)の混合物、もしく
は、アルミナと窒化ボロン(BN)とSiO2の混合
物を用いることによつて、発色および耐退色性、
耐光性に優れた記録を得ることができるようにし
たロイコ系色素用顕色剤を提供することを目的と
している。 〔従来の技術〕 従来のロイコ系色素用顕色剤として、α−ナフ
トール、β−ナフトール、2・2′−メチレンビス
(4−メチル−6−ターシヤリ−イソブチルフエ
ノール)、2・2′−メチレンビス(4−クロルフ
エノール)、4フエニルフエノール、4−ターシ
ヤリブチルフエノール、2・2′−ジヒドロキシジ
フエノール、4・4′−セカンダリ−ブチリデンフ
エノール、4、4′ジクロルヘキシリジンジフエノ
ール、4−ヒドロキシジフエノキシド、4・4′−
イソプロピリデンジフエノール、ハイドロキノ
ン、4−ヒドロキシアセトフエノール、4・4′−
イソピリデンビス(2−ターシヤリ−ブチルフエ
ノール)、4−ターシヤリ−オクチルカテコール、
ノボラツク型フエノール樹脂、フエノール重合体
などのフエノール性化合物や、サリチル酸、3−
(α−メチルベン)サリチル酸、3・5−ジ−α
−α−メチルベンジルサリチル酸、3−イソプロ
ピルサリチル酸、3−クロル−5−(α−メチル
ベンジル)サリチル酸、3−フエニル−5−
(α・α−ジメチルベンジル)サリチル酸、3−
ベンジルサリチル酸、3・5−ジターシヤリブチ
ルサリチル酸、3−ターシヤリブチルサリチル
酸、安息香酸、テレフタル酸、3・5−ジメチル
−4−ヒドロキシ安息香酸、パラターシヤリブチ
ル安息香酸、3−セカンダリブチル−4−ヒドロ
キシ安息香酸、トリクロル安息香酸、3−シクロ
ヘキシル−4−ヒドロキシ安息香酸などの芳香族
カルボン酸、及びこれらフエノール性化合物や、
活性白土、酸性白土、ケイ酸アルミニウム、ベン
トナイト、アタパルガイト、コロイダルシリカな
どの固体酸や、マグネシウム、アルミニウム、カ
ルシウム、チタン、マンガン、スズ、ニツケルな
どの多価金属と芳香族カルボン酸との塩などの有
機酸性物質が使用されている。 〔発明が解決しようとしている課題〕 しかし、従来の有機化合物をロイコ系色素用顕
色剤として用いた場合、発色性があまり良好でな
く、退色するという問題があつた。また、光照射
による着色や大気中の窒素化合物による黄変が激
しいなど問題があつた。また、活性白土などは、
黄色味を帯びており良好な画像を得ることができ
なかつた。 そこで、本発明は、従来のこの様な問題点を解
決するために、発色性に優れ、また耐退色性、耐
光性に優れ、白色度の高いロイコ系色素用顕色剤
を提供することを目的としている。 〔課題を解決するための手段〕 本発明は、上記課題を解決するために、ロイコ
系色素用顕色剤としてアルミナと窒化ボロン
(BN)の混合物、もしくは、アルミナと窒化ボ
ロン(BN)とSiO2の混合物を用いることによつ
て、発色性を向上させ、また、耐退色性、耐光性
を向上させるようにしたものである。さらに、ア
ルミナ、窒化ボロン(BN)、及びSiO2は、白色
度も高いために、良好な画像が得られるようにし
たものである。 〔実施例〕 以下に本発明の実施例を示すが、本発明はこれ
に限定されるものではない。 〔実施例1〕 5%(W/W)の濃度のポリビニルアルコール
水溶液50重量部に、アルミナ15重量部、BN15重
量部を加え、ボールミルを用いて約24時間粉砕分
散し、顕色剤分散液とした。この顕色剤分散液を
バーコーターを用いて、40g/m2の上質紙上に、
20g/m2(乾燥重量)となるように塗工し、ロイ
コ系色素用顕色シートとした。このロイコ系色素
用顕色シートを、ロイコ系色素を用いた感圧複写
紙と合わせ、120Kg/cm2の圧力で発色させ、濃度
を測定した。また、耐退色性を調べるために、発
色直後より500時間後に発色濃度を測定した。以
上の測定値を表1に示す。 〔実施例2〕 5%(W/W)の濃度のポリビニルアルコール
水溶液50重量部に、アルミナ10重量部、BN10重
量部、SiO210重量部を加え、ボールミルを用い
て約24時間粉砕分散し、顕色剤分散液とした。こ
の顕色剤分散液をバーコーターを用いて、40g/
m2の上質紙上に、20g/m2(乾燥重量)となるよ
うに塗工し、ロイコ系色素用顕色シートとした。
このロイコ系色素用顕色シートを、ロイコ系色素
を用いた感圧複写紙と合わせ、120Kg/cmの圧力
で発色させ、濃度を測定した。また、耐退色性を
調べるために、発色直後より500時間後に発色濃
度を測定した。以上の測定値を表1に示す。 〔比較例〕 上記の実施例と比較するために、公知のロイコ
系色素用顕色剤のひとつである、ビスフエノール
Aについて、実施例1,2と同様の測定を行い、
測定値を表1に示す。
以上のように、ロイコ系色素用顕色剤として、
アルミナと窒化ボロン(BN)の混合物、もしく
は、アルミナと窒化ボロン(BN)とSiO2の混合
物を用いることによつて、発色性に優れ、また耐
退色性、耐光性に優れ、白色度の高いロイコ系色
素用顕色剤を提供することができる。
アルミナと窒化ボロン(BN)の混合物、もしく
は、アルミナと窒化ボロン(BN)とSiO2の混合
物を用いることによつて、発色性に優れ、また耐
退色性、耐光性に優れ、白色度の高いロイコ系色
素用顕色剤を提供することができる。
Claims (1)
- 【特許請求の範囲】 1 ロイコ系色素用の顕色剤として、アルミナと
窒化ボロン(BN)の混合物をもちいたことを特
徴とするロイコ系色素用顕色剤。 2 ロイコ系色素用の顕色剤として、アルミナと
窒化ボロン(BN)とSiO2の混合物をもちいたこ
とを特徴とするロイコ系色素用顕色剤。