JPH04245971A - 親水性アクリル繊維及びその製法 - Google Patents
親水性アクリル繊維及びその製法Info
- Publication number
- JPH04245971A JPH04245971A JP1195191A JP1195191A JPH04245971A JP H04245971 A JPH04245971 A JP H04245971A JP 1195191 A JP1195191 A JP 1195191A JP 1195191 A JP1195191 A JP 1195191A JP H04245971 A JPH04245971 A JP H04245971A
- Authority
- JP
- Japan
- Prior art keywords
- acrylic fiber
- fiber
- metal ion
- group
- amidoxime
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【０００１】
【産業上の利用分野】本発明はアクリル繊維の疎水性を
改善し、親水性、制電性に優れた親水性アクリル繊維及
びその製法に関する。
改善し、親水性、制電性に優れた親水性アクリル繊維及
びその製法に関する。
【０００２】
【従来の技術】従来から親水性アクリル繊維としてはポ
リエチレングリコール系誘導体などの親水性化合物を繊
維中に含有させた繊維あるいは親水性化合物を繊維表面
に付着させた繊維が提案されている。しかしながら親水
性化合物を含有させた繊維は強力低下し、又親水性化合
物を付着させた繊維は親水性化合物が洗濯によって脱落
し、問題がある。
リエチレングリコール系誘導体などの親水性化合物を繊
維中に含有させた繊維あるいは親水性化合物を繊維表面
に付着させた繊維が提案されている。しかしながら親水
性化合物を含有させた繊維は強力低下し、又親水性化合
物を付着させた繊維は親水性化合物が洗濯によって脱落
し、問題がある。
【０００３】
【発明が解決しようとする課題】本発明がかかる従来の
親水性アクリル繊維の問題点を解決し、優れた親水性、
制電性を有するアクリル繊維及びその製法を提供するも
のである。
親水性アクリル繊維の問題点を解決し、優れた親水性、
制電性を有するアクリル繊維及びその製法を提供するも
のである。
【０００４】
【課題を解決するための手段】本発明はアミドオキシム
基を含有し、該基にはチタン、ジルコニウム、コバルト
、ニッケル、亜鉛、カルシウム及びアルミニウムからな
る群から選ばれる少なくとも一つの金属イオンが０．０
２ｍｍｏｌ／ｇ以上１ｍｍｏｌ／ｇ未満配位されている
ことを特徴とする親水性アクリル繊維及び０．０２ｍｍ
ｏｌ／ｇ以上１ｍｍｏｌ／ｇ未満のアミドオキシム基含
有アクリル繊維をチタン、ジルコニウム、コバルト、ニ
ッケル、亜鉛、カルシウム及びアルミニウムからなる群
から選ばれる少なくとも一つの金属イオンを含む水溶液
に浸漬し熱処理することを特徴とする親水性アクリル繊
維の製法にある。
基を含有し、該基にはチタン、ジルコニウム、コバルト
、ニッケル、亜鉛、カルシウム及びアルミニウムからな
る群から選ばれる少なくとも一つの金属イオンが０．０
２ｍｍｏｌ／ｇ以上１ｍｍｏｌ／ｇ未満配位されている
ことを特徴とする親水性アクリル繊維及び０．０２ｍｍ
ｏｌ／ｇ以上１ｍｍｏｌ／ｇ未満のアミドオキシム基含
有アクリル繊維をチタン、ジルコニウム、コバルト、ニ
ッケル、亜鉛、カルシウム及びアルミニウムからなる群
から選ばれる少なくとも一つの金属イオンを含む水溶液
に浸漬し熱処理することを特徴とする親水性アクリル繊
維の製法にある。
【０００５】本発明においてはアクリル繊維に含有する
アミドオキシム基に特定の金属イオンが配位して、従来
に無い耐久性のある優れた親水性、制電性効果を奏する
。更に金属イオンを繊維表層に配位させるので、親水性
、制電性の効率がよく、繊維の強度への影響をなくした
ものである。
アミドオキシム基に特定の金属イオンが配位して、従来
に無い耐久性のある優れた親水性、制電性効果を奏する
。更に金属イオンを繊維表層に配位させるので、親水性
、制電性の効率がよく、繊維の強度への影響をなくした
ものである。
【０００６】本発明でいうアミドオキシム基は、
【００
０７】
０７】
【化１】
【０００８】の互変異性体が考えられる。アミドオキシ
ム基はアクリル繊維重合体のニトリル側鎖を公知の方法
でヒドロキシルアミンで変成して得られる。アミドオキ
シム基の含有量は０．０２ｍｍｏｌ／ｇである。アミド
オキシム基と金属イオンの配位の状態は明らかでないが
、金属イオンは２個の窒素及び又は酸素原子とキレート
結合して安定化していると思われる。
ム基はアクリル繊維重合体のニトリル側鎖を公知の方法
でヒドロキシルアミンで変成して得られる。アミドオキ
シム基の含有量は０．０２ｍｍｏｌ／ｇである。アミド
オキシム基と金属イオンの配位の状態は明らかでないが
、金属イオンは２個の窒素及び又は酸素原子とキレート
結合して安定化していると思われる。
【０００９】本発明でいう金属イオンとしては金属単体
として存在する場合以外をいいアミドオキシム基と配位
結合をし、かつ酸化物、硫化物等になり存在しているも
のと思われる。金属イオンの含有量としては０．０２ｍ
ｍｏｌ／ｇ以上１ｍｍｏｌ／ｇ未満配位することが必要
である。 本発明でアミドオキシム基に配位させる金属イオンとし
てはチタン、ジルコニウム、コバルト、ニッケル、亜鉛
又はアルミニウムが好ましく用いられる。
として存在する場合以外をいいアミドオキシム基と配位
結合をし、かつ酸化物、硫化物等になり存在しているも
のと思われる。金属イオンの含有量としては０．０２ｍ
ｍｏｌ／ｇ以上１ｍｍｏｌ／ｇ未満配位することが必要
である。 本発明でアミドオキシム基に配位させる金属イオンとし
てはチタン、ジルコニウム、コバルト、ニッケル、亜鉛
又はアルミニウムが好ましく用いられる。
【００１０】金属イオンとアミドオキシム基との配位結
合は硫酸第一チタン、硫酸ジルコニウム、硫酸コバルト
、塩化ニッケル、塩化亜鉛、硫酸アルミニウム等の水溶
液中にアミドオキシム基含有アクリル繊維を浸漬し熱処
理して行なわれる。熱処理は４０〜１２０℃で行なわれ
る。熱処理と金属イオンの含有水溶液の浸漬とは別工程
で行なってもよい。
合は硫酸第一チタン、硫酸ジルコニウム、硫酸コバルト
、塩化ニッケル、塩化亜鉛、硫酸アルミニウム等の水溶
液中にアミドオキシム基含有アクリル繊維を浸漬し熱処
理して行なわれる。熱処理は４０〜１２０℃で行なわれ
る。熱処理と金属イオンの含有水溶液の浸漬とは別工程
で行なってもよい。
【００１１】
【実施例】以下、本発明を実施例により説明する。なお
、実施例中の％は重量％を意味する。またアミドオキシ
ム基の含有量はオレンジＩＩ（酸性染料）の染着量より
求め金属の含有量は炭化物の原子吸光分析で行なった。
、実施例中の％は重量％を意味する。またアミドオキシ
ム基の含有量はオレンジＩＩ（酸性染料）の染着量より
求め金属の含有量は炭化物の原子吸光分析で行なった。
【００１２】実施例１
アクリロニトリル９１．２％／メチルアクリレート８．
０％／メタクリルスルフォン酸ソーダ０．８％の重合体
からなるアクリル繊維３ｄ×５１ｍｍを１／５２番で紡
績し２８Ｇのインターロックを編成し、硫酸ヒドロキシ
ルアミン２０％（対繊維）及び第二リン酸ソーダ３０％
（対繊維）の浴比１：２０の水溶液中で沸騰下で６０分
間浸漬同時熱処理をし、水洗してアミドオキシム基量０
．２３ｍｍｏｌ／ｇのアミドオキシム基含有アクリル繊
維を得た。この繊維を表１に示す金属塩の浴比１：２０
の水溶液中で沸騰下３０分処理し、７０℃で湯洗し、約
７０℃で乾燥して金属イオンを表１に示す量含有の繊維
を得た。これらの繊維の性能を表１に示す。本発明の繊
維（Ｎｏ．４〜１３）は表１から明らかなように耐久性
に優れた親水性、制電性を奏するものであった。また本
発明の繊維（Ｎｏ．４〜１３）の強度は未処理のアクリ
ル繊維（Ｎｏ．１）の強度３．１ｇ／ｄと比べても遜色
のないものであった。
０％／メタクリルスルフォン酸ソーダ０．８％の重合体
からなるアクリル繊維３ｄ×５１ｍｍを１／５２番で紡
績し２８Ｇのインターロックを編成し、硫酸ヒドロキシ
ルアミン２０％（対繊維）及び第二リン酸ソーダ３０％
（対繊維）の浴比１：２０の水溶液中で沸騰下で６０分
間浸漬同時熱処理をし、水洗してアミドオキシム基量０
．２３ｍｍｏｌ／ｇのアミドオキシム基含有アクリル繊
維を得た。この繊維を表１に示す金属塩の浴比１：２０
の水溶液中で沸騰下３０分処理し、７０℃で湯洗し、約
７０℃で乾燥して金属イオンを表１に示す量含有の繊維
を得た。これらの繊維の性能を表１に示す。本発明の繊
維（Ｎｏ．４〜１３）は表１から明らかなように耐久性
に優れた親水性、制電性を奏するものであった。また本
発明の繊維（Ｎｏ．４〜１３）の強度は未処理のアクリ
ル繊維（Ｎｏ．１）の強度３．１ｇ／ｄと比べても遜色
のないものであった。
【００１３】なお、表中の吸水長はバイレック法で１０
分後の吸水長、制電性はロータリースタチックメーター
で２０℃×３０％ＲＨで対綿布で測定、洗濯はＪＩＳＬ
−０２０８の１０３法の４０℃の家庭洗濯を実施。
分後の吸水長、制電性はロータリースタチックメーター
で２０℃×３０％ＲＨで対綿布で測定、洗濯はＪＩＳＬ
−０２０８の１０３法の４０℃の家庭洗濯を実施。
【００１４】
【表１】
【００１５】
【発明の効果】本発明によれば親水性、制電性に優れた
アクリル繊維を得ることが可能であり、衣料として用い
ると快適な着用感が得られる。
アクリル繊維を得ることが可能であり、衣料として用い
ると快適な着用感が得られる。
Claims (2)
- 【請求項１】 アミドオキシム基を含有し、該基には
チタン、ジルコニウム、コバルト、ニッケル、亜鉛、ア
ルシウム及びアルミニウムからなる群から選ばれる少な
くとも一つの金属イオンが０．０２ｍｍｏｌ／ｇ以上１
ｍｍｏｌ／ｇ未満配位していることを特徴とする親水性
アクリル繊維。 - 【請求項２】 ０．０２ｍｍｏｌ／ｇ以上１ｍｍｏｌ
／ｇ未満のアミドオキシム基含有アクリル繊維をチタン
、ジルコニウム、コバルト、ニッケル、亜鉛、カルシウ
ム及びアルミニウムからなる群から選ばれる少なくとも
一つの金属イオンを含む水溶液に浸漬し熱処理すること
を特徴とする親水性アクリル繊維の製法。