JPH0416857B2 - - Google Patents
Info
- Publication number
- JPH0416857B2 JPH0416857B2 JP57115213A JP11521382A JPH0416857B2 JP H0416857 B2 JPH0416857 B2 JP H0416857B2 JP 57115213 A JP57115213 A JP 57115213A JP 11521382 A JP11521382 A JP 11521382A JP H0416857 B2 JPH0416857 B2 JP H0416857B2
- Authority
- JP
- Japan
- Prior art keywords
- layer
- recording
- optical
- changing
- substrate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【発明の詳細な説明】
本発明は光記録装置に関する。
従来、光デイスク等では、基板の上の記録層に
収束したレーザービームを照射し、記録層中に吸
収された光エネルギーから変換された熱エネルギ
ーによつて、記録層の光学定数を変化させて情報
を書き込む。情報の読み出しは低パワーのレーザ
ービームを照射して、反射光量等の変化により行
なう。このような光記録装置を小型化・低価格化
するためには書き込み用レーザーとして半導体レ
ーザーを使用することが強く望まれている。した
がつて、出力の小さい半導体レーザーを用いても
充分高速で書き込める高感度な記録媒体及び記録
装置を必要とするが、未だ望ましい媒体及び装置
は開発されていない。媒体感度は媒体を支持する
基板の熱特性に大きく依存するので、できるだけ
熱伝導度の小さな基板が使用されている。それで
も基板に流出する熱量は大きく、このことが媒体
感度を低めている主な原因となつている。
収束したレーザービームを照射し、記録層中に吸
収された光エネルギーから変換された熱エネルギ
ーによつて、記録層の光学定数を変化させて情報
を書き込む。情報の読み出しは低パワーのレーザ
ービームを照射して、反射光量等の変化により行
なう。このような光記録装置を小型化・低価格化
するためには書き込み用レーザーとして半導体レ
ーザーを使用することが強く望まれている。した
がつて、出力の小さい半導体レーザーを用いても
充分高速で書き込める高感度な記録媒体及び記録
装置を必要とするが、未だ望ましい媒体及び装置
は開発されていない。媒体感度は媒体を支持する
基板の熱特性に大きく依存するので、できるだけ
熱伝導度の小さな基板が使用されている。それで
も基板に流出する熱量は大きく、このことが媒体
感度を低めている主な原因となつている。
本発明の目的は、高感度の光記録を可能とする
光記録装置を提供することにある。
光記録装置を提供することにある。
本発明は収束したレーザービームを照射するこ
とによる記録層の光学定数変化により光記録を行
なう光記録装置において、基板の上に積層された
層の中の第一の層と、該第一の層の直上にありか
つ該記録層の下にある第二の層の間に気泡があ
り、該気泡の上の部分の該記録層の形状を変化さ
せずに該記録層自体の光学定数を変化させて記録
を行なうことを特徴とするものである。
とによる記録層の光学定数変化により光記録を行
なう光記録装置において、基板の上に積層された
層の中の第一の層と、該第一の層の直上にありか
つ該記録層の下にある第二の層の間に気泡があ
り、該気泡の上の部分の該記録層の形状を変化さ
せずに該記録層自体の光学定数を変化させて記録
を行なうことを特徴とするものである。
以下、本発明の光記録装置について実施例を用
いて説明する。第１図は本発明の一実施例におけ
る光記録媒体の断面図である。まず、ポリメチル
メタクリレート（PMMA）基板１の上に、反射
層２としてアルミニウム（Al）膜を30nm、透過
層３として高分子膜を200nm、支持層４としてチ
タン（Ti）膜を10nm順次積層し、しかる後、波
長514nmのアルゴンガスレーザービーム（図示せ
ず）を収束照射し、支持層４を透過層３より剥離
させ、最大ギヤツプ長が約200nmの気泡５を形成
した。次に、支持層４の上全面に記録層６として
テルル低酸化物（TeO1.1）膜を35nm被着した。
このような記録媒体の気泡５の上の部分に波長
830nmの半導体レーザービーム７を収束照射して
第２図のように黒化（光学定数が変化）した部分
２０を形成した。このときに必要であつたレーザ
ーパワーは、PMMA基板の上に10nm厚のTi膜、
35nm厚のTeO1.1膜を順次積層した記録媒体に記
録するに必要であつたレーザーパワーの半分以下
であつた。このように記録が高感度化された主な
原因は、記録層の支持層の下が気泡であることに
より、記録層及び支持層からの熱の流出が阻止さ
れたためである。
いて説明する。第１図は本発明の一実施例におけ
る光記録媒体の断面図である。まず、ポリメチル
メタクリレート（PMMA）基板１の上に、反射
層２としてアルミニウム（Al）膜を30nm、透過
層３として高分子膜を200nm、支持層４としてチ
タン（Ti）膜を10nm順次積層し、しかる後、波
長514nmのアルゴンガスレーザービーム（図示せ
ず）を収束照射し、支持層４を透過層３より剥離
させ、最大ギヤツプ長が約200nmの気泡５を形成
した。次に、支持層４の上全面に記録層６として
テルル低酸化物（TeO1.1）膜を35nm被着した。
このような記録媒体の気泡５の上の部分に波長
830nmの半導体レーザービーム７を収束照射して
第２図のように黒化（光学定数が変化）した部分
２０を形成した。このときに必要であつたレーザ
ーパワーは、PMMA基板の上に10nm厚のTi膜、
35nm厚のTeO1.1膜を順次積層した記録媒体に記
録するに必要であつたレーザーパワーの半分以下
であつた。このように記録が高感度化された主な
原因は、記録層の支持層の下が気泡であることに
より、記録層及び支持層からの熱の流出が阻止さ
れたためである。
なお、本実施例では記録層としてTeO1.1膜を
用いたが、金属フタロシアニンの非晶質から結晶
質への変化を用いてもよいことはいうまでもな
い。また、気泡形成のための層構造としてここで
は、Ti膜／高分子膜／Al膜を用いたが、他の気
泡形成層構造を用いてもよいこともいうまでもな
い。
用いたが、金属フタロシアニンの非晶質から結晶
質への変化を用いてもよいことはいうまでもな
い。また、気泡形成のための層構造としてここで
は、Ti膜／高分子膜／Al膜を用いたが、他の気
泡形成層構造を用いてもよいこともいうまでもな
い。
以上述べたように本発明によれば、高感度の光
記録を可能とする光記録装置が得られる。
記録を可能とする光記録装置が得られる。
第１図は本発明の一実施例をにおける記録媒体
を示す断面図であり、第２図はこの記録媒体に記
録した後の状態を示す断面図である。 図において、１は基板、２は反射層、３は透過
層、４は支持層、５は気泡、６は記録層、７はレ
ーザービーム、２０は光学定数が変化した部分を
表わす。
を示す断面図であり、第２図はこの記録媒体に記
録した後の状態を示す断面図である。 図において、１は基板、２は反射層、３は透過
層、４は支持層、５は気泡、６は記録層、７はレ
ーザービーム、２０は光学定数が変化した部分を
表わす。
Claims (1)
- １ 収束したレーザービームを照射することによ
る記録層の光学定数変化により光記録を行なう光
記録装置において、基板の上に積層された層の中
の第一の層と、該第一の層の直上にありかつ該記
録層の下にある第二の層の間に気泡があり、該気
泡の上の部分の該記録層の形状を変化させずに該
記録層自体の光学定数を変化させて記録を行なう
ことを特徴とする光記録装置。