JPH0339238Y2 - - Google Patents
Info
- Publication number
- JPH0339238Y2 JPH0339238Y2 JP6492486U JP6492486U JPH0339238Y2 JP H0339238 Y2 JPH0339238 Y2 JP H0339238Y2 JP 6492486 U JP6492486 U JP 6492486U JP 6492486 U JP6492486 U JP 6492486U JP H0339238 Y2 JPH0339238 Y2 JP H0339238Y2
- Authority
- JP
- Japan
- Prior art keywords
- weight
- unsaturated polyester
- coating
- inorganic filler
- polyester resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
【考案の詳細な説明】
(産業上の利用分野)
本考案は外装防食材に関する。
(従来の技術)
従来、不飽和ポリエステル系樹脂防食材、例え
ば珪砂、タルク、クレー、ガラスフレーク、ガラ
ス繊維等の無機物を添加した不飽和ポリエステル
系樹脂防食材を鋼材に塗装又はライニングする際
には、一般に鋼材を予めサンドブラスト、グリツ
ドブラスト、化成処理等の表面処理をした後に、
鋼材との接着性向上及び防錆、防食等の耐食性を
目的としてプライマーを塗装することが行われて
いる。この場合、使用されるプライマー用樹脂の
成分としては、上塗りと同様、不飽和ポリエステ
ル系樹脂が接着性等の見地より好適である。 しかし、不飽和ポリエステル系樹脂プライマー
は空気中の酸素及び湿気の影響を受けて表面乾燥
性が悪く、塗膜のごく表層のみが粘着性を帯び
る。 この結果例えば大容量の鋼製タンク内面を防食
塗装するか又はライニングする際、鋼材の前処理
であるブラスト処理を連続して行なう必要が生じ
た場合、プライマーの乾燥性が工程に大きく影響
を及ぼす。プライマー塗布はブラスト処理後、短
時間内に行なわないと、鋼面に錆が再発生するに
至るのであるが、前に塗布したプライマーの表面
乾燥性が悪い場合、次いで施工するブラスト処理
で飛散した塵が上記の如く粘着性を帯びたプライ
マー表層に付着し、掃除機等でも簡単に取り除け
ない欠点がある。 このような欠点を除く目的で、本出願人は先に
不飽和ポリエステル系樹脂に特定粒径の鱗片状無
機充填材を配合した耐食性プライマーが著しく改
善された塗膜乾燥性を有し、同一可使用時間のも
ので乾燥時間が1/2以下になる効果を奏すること
を見い出し特許出願した(特開昭56−79160号)。 しかし上記プライマーを塗装した上に、鱗片状
無機充填材を配合した不飽和ポリエステル系樹脂
防食塗材を被覆塗装する場合、優れた防食性及び
耐衝撃性が得られるが、塗膜表面が鱗片状無機充
填材の突出によつて凹凸状となつて平滑性がな
く、このた表面光沢が極めて乏しい、また日光に
よつて塗膜表面が褪色してくるといつた欠点も生
じた。 この欠点を改良するものとして本出願人は金属
基材の表面に不飽和ポリエステル系樹脂と平均粒
径10〜100μの鱗片状無機充填材を主成分とした
プライマー組成物を塗装し、その上に平均粒径40
〜1000μの鱗片状無機充填材を不飽和ポリエステ
ル系樹脂に配合した防食塗材を被覆塗装を行い、
さらに無色または着色した弗素樹脂系塗料を被覆
塗装してなる外装用防食複合構造について出願し
た(実願昭60−109452号)。 (考案が解決しようとする問題点) 本考案の目的は上記従来の外装防食材を更に一
層改良することにあり、優れた防食性及び耐衝撃
性と同時に、優れた表面平滑性及び光沢性を合せ
有する外装防食材を提供することにある。 (問題点を解決するための手段) 本考案は金属基材の表面に不飽和ポリエステル
系樹脂60〜95重量%、平均粒径10〜100μの鱗片
状無機充填材40〜5重量%を主成分としたプライ
マー組成物を20〜100μの厚さに塗装し、その上
に平均粒径40〜1000μの鱗片状無機充填材10〜60
重量%を不飽和ポリエステル系樹脂90〜40重量%
に配合した防食塗材を200μ以上の厚さに被覆塗
装を行い、この上に2官能以上のポリオールとジ
イソシアネートを成分とするポリウレタン塗料を
20〜100μの厚さに塗装し、さらに無色または着
色した弗素樹脂系塗料を20〜100μの厚さに被覆
塗装してなる耐候性、美観性の向上および重防食
性を兼備した外装防食材に係る。 第1図は本考案の防食材の断面概略図であり、
1は金属基材、2はプライマー組成物、3は防食
塗材、4はポリウレタン塗料、5は弗素樹脂系塗
料である。 本考案で使用される金属基材は公知のものなら
いずれも良いが、例えば鋼、アルミニウム、ステ
ンレス鋼などを挙げることができる。 本考案のプライマー組成物及び防食塗材の成分
である不飽和ポリエステル系樹脂も、公知の各種
のものを使用できる。これは不飽和ジカルボン酸
の単独又はこれと飽和ジカルボン酸との混合物と
多価アルコールとを重縮合反応させて得られた不
飽和ポリエステルに、ビニルモノマーを混合した
ものである。不飽和ジカルボン酸としては無水マ
イレン酸、フマル酸、イタコン酸、シトラコン酸
などを、飽和ジカルボン酸としては無水フタル
酸、イソフタル酸、テレフタル酸、アジピン酸な
どを例示できる。多価アルコールとしてはエチレ
ングリコール、ジエチレングリコール、プロピレ
ングリコール、ブチレングリコールなどが挙げら
れる。ビニルモノマーとしてはスチレン、酢酸ビ
ニル、メタクリル酸メチル、ビニルトルエンなど
が使用できる。この不飽和ポリエステル系樹脂の
硬化剤としては通常の有機過酸化物例えばベンゾ
イルパーオキサイド、メチルエチルケトンパーオ
キサイド、クメンパーオキサイド等が用いられ
る。また、これらの樹脂にはナフテン酸コバル
ト、アミン系重合禁止剤等の添加剤、更に着色顔
料、分散剤等が配合される。 本考案のプライマー組成物及び防食塗材にはそ
れぞれ平均粒径が10〜100μ及び40〜1000μの鱗片
状無機充填材が配合される。鱗片状無機充填剤と
してはフレーク状ガラス、天然及び人造グラフア
イト、天然及び人造雲母、鱗片状酸化鉄(MIO)
等が使用される。 プライマー組成物において鱗片状無機充填材の
平均粒径が100μより大きくなると基材とのなじ
みが悪くなり、また塗装作業性も悪くなる。一
方、平均粒径が10μより小さくなると塗膜の乾燥
性が悪くなる。また、鱗片状無機充填材の量が40
重量%を越えると塗装作業が悪くなり、接着力も
低下する。一方5重量%未満ではプライマーの乾
燥性の向上効果が殆ど認められない。 防食塗材において鱗片状無機充填材の平均粒径
が1000μより大きくなると塗装作業性が悪くな
る。一方40μより小さくなると防食性能が著しく
低下する。また、鱗片状無機充填材量が60重量%
を越えると塗装作業性が悪くなり、一方10重量%
未満では防食性能が低下する。 本考案においてポリウレタン塗料はポリオール
として2官能以上のポリエーテルポリオールまた
はポリエステルポリオール、硬化剤としてジイソ
シアネートからなる2液型ポリウレタンである。
ポリウレタン塗料は不飽和ポリエステルからなる
防食材と弗素樹脂系塗料との界面接着層として効
果を発揮する。ポリエーテルポリオールとしては
ポリプロピレン系ポリオール、アクリルポリオー
ル、ポリブタジエンポリオール等が挙げられる。
またポリエステルポリオールとしてはアジピン酸
系や芳香族カルボン酸などを酸成分とし、これに
単量体ポリオール成分(1,6ーヘキサンジオー
ルなど)を用いたもの等が挙げられる。またジイ
ソシアネートとしては各種のものを使用できる
が、1,6ーヘキサメチレンジイソシアネート、
イソホロンジイソシアネート、水添キシリレンジ
イソシアネート、水添ジフエニルメタンジイソシ
アネート(MDI)など比較的耐黄変性のあるも
のが好ましい。 本考案において弗素樹脂系塗料としては例えば
フルオロオレフインとビニルエーテルの共重合体
(ポリフルオロオレフインビニルエーテル)をイ
ソシアネート又はメラミン化合物で架橋したもの
など各種のものを使用できる。この塗料は無色又
は酸化チタン、その他の顔料を添加した着色塗料
でも良く、ベンゾフエノン類、ベンゾトリアゾー
ル類などの紫外線吸収剤、ジスアゾイエロー、ク
ロムパーミリオン、コバルトブルーなどの顔料、
その他の公知の添加剤を配合することも任意であ
る。 本考案の外装用防食構造は金属基材に上記プラ
イマー組成物を20〜100μの厚さに塗装し、その
上に上記防食塗材を200μ以上の厚さに塗装し、
その上にポリウレタン塗料を20〜100μの厚さに
塗装し、更に弗素樹脂系塗料を20〜100μの厚さ
に塗装して、各工程で乾燥、必要により焼付けを
行うことにより得られる。塗装は公知の方法、例
えば刷毛、ローラー、エアレススプレー、エアス
プレーなどにより行うことができ、乾燥は好まし
くは常温でも行われ、現場施工において有効であ
る。焼付けは高温、例えば100℃で30分間の加熱
で硬化が可能であるので、短時間で塗装仕上げを
する場合に好適である。 本考案品の用途は例えばタンク、プール、架構
などの陸上構築物や橋梁、シーバースなどの海洋
構築物、さらに船舶、パイプライン、鋼矢板など
防食性と美観を必要とする分野で広範囲にわた
る。 (実施例) 次に実施例及び比較例により本考案を説明す
る。 実施例 1 鋼板を脱脂、除錆をした後コバルト等の硬化促
進剤及び過酸化物系硬化剤、その他の添加剤を配
合したビニルエステル樹脂に平均粒径40μのマイ
カを樹脂100重量部に対して30重量部を添加して
得られたプライマーを50μの厚さに塗装し、その
上に平均粒径150μのガラスフレークを40重量部
とビスフエノール系ポリエステル樹脂100重量部
を配合して得られる防食塗材を300μの厚さに塗
装し、常温放置して硬化後、ポリプロピレン系ポ
リオールと1,6ーヘキサメチレンジイソシアネ
ートを主成分としたポリウレタン系塗料を厚さ
30μになるように塗装し、常温で24時間放置して
乾燥する。さらにその上にチタン白顔料17重量部
を含むポリフルオロオレフインビニルエーテルを
イソシアネートで架橋した弗素樹脂100重量部か
らなる塗料を50μの厚さに塗装して常温放置して
乾燥硬化させる。ポリウレタン塗料の接着層を設
けたことにより、防食材と弗素樹脂系塗料層の界
面接着力は168Kg/cm2に向上した。 本塗装物を促進耐候性試験機サンシヤインウエ
ザオメーターで3000時間照射試験をした後、光沢
測定器で測定したところ光沢保持率は60%以上で
あつた。また褪色性も殆ど認められなかつた。更
にJISK5400に基づき1000時間塩水噴霧試験を行
つたが特に異状が認められなかつた。 比較例 1 ポリウレタン塗料層の形成を行わなかつた他は
実施例1と同様にして防食材を得た。この場合の
上記界面接着力は75Kg/cm2と低かつた。 本考案品の性能評価の結果を第1表に示す。 【表】
ば珪砂、タルク、クレー、ガラスフレーク、ガラ
ス繊維等の無機物を添加した不飽和ポリエステル
系樹脂防食材を鋼材に塗装又はライニングする際
には、一般に鋼材を予めサンドブラスト、グリツ
ドブラスト、化成処理等の表面処理をした後に、
鋼材との接着性向上及び防錆、防食等の耐食性を
目的としてプライマーを塗装することが行われて
いる。この場合、使用されるプライマー用樹脂の
成分としては、上塗りと同様、不飽和ポリエステ
ル系樹脂が接着性等の見地より好適である。 しかし、不飽和ポリエステル系樹脂プライマー
は空気中の酸素及び湿気の影響を受けて表面乾燥
性が悪く、塗膜のごく表層のみが粘着性を帯び
る。 この結果例えば大容量の鋼製タンク内面を防食
塗装するか又はライニングする際、鋼材の前処理
であるブラスト処理を連続して行なう必要が生じ
た場合、プライマーの乾燥性が工程に大きく影響
を及ぼす。プライマー塗布はブラスト処理後、短
時間内に行なわないと、鋼面に錆が再発生するに
至るのであるが、前に塗布したプライマーの表面
乾燥性が悪い場合、次いで施工するブラスト処理
で飛散した塵が上記の如く粘着性を帯びたプライ
マー表層に付着し、掃除機等でも簡単に取り除け
ない欠点がある。 このような欠点を除く目的で、本出願人は先に
不飽和ポリエステル系樹脂に特定粒径の鱗片状無
機充填材を配合した耐食性プライマーが著しく改
善された塗膜乾燥性を有し、同一可使用時間のも
ので乾燥時間が1/2以下になる効果を奏すること
を見い出し特許出願した(特開昭56−79160号)。 しかし上記プライマーを塗装した上に、鱗片状
無機充填材を配合した不飽和ポリエステル系樹脂
防食塗材を被覆塗装する場合、優れた防食性及び
耐衝撃性が得られるが、塗膜表面が鱗片状無機充
填材の突出によつて凹凸状となつて平滑性がな
く、このた表面光沢が極めて乏しい、また日光に
よつて塗膜表面が褪色してくるといつた欠点も生
じた。 この欠点を改良するものとして本出願人は金属
基材の表面に不飽和ポリエステル系樹脂と平均粒
径10〜100μの鱗片状無機充填材を主成分とした
プライマー組成物を塗装し、その上に平均粒径40
〜1000μの鱗片状無機充填材を不飽和ポリエステ
ル系樹脂に配合した防食塗材を被覆塗装を行い、
さらに無色または着色した弗素樹脂系塗料を被覆
塗装してなる外装用防食複合構造について出願し
た(実願昭60−109452号)。 (考案が解決しようとする問題点) 本考案の目的は上記従来の外装防食材を更に一
層改良することにあり、優れた防食性及び耐衝撃
性と同時に、優れた表面平滑性及び光沢性を合せ
有する外装防食材を提供することにある。 (問題点を解決するための手段) 本考案は金属基材の表面に不飽和ポリエステル
系樹脂60〜95重量%、平均粒径10〜100μの鱗片
状無機充填材40〜5重量%を主成分としたプライ
マー組成物を20〜100μの厚さに塗装し、その上
に平均粒径40〜1000μの鱗片状無機充填材10〜60
重量%を不飽和ポリエステル系樹脂90〜40重量%
に配合した防食塗材を200μ以上の厚さに被覆塗
装を行い、この上に2官能以上のポリオールとジ
イソシアネートを成分とするポリウレタン塗料を
20〜100μの厚さに塗装し、さらに無色または着
色した弗素樹脂系塗料を20〜100μの厚さに被覆
塗装してなる耐候性、美観性の向上および重防食
性を兼備した外装防食材に係る。 第1図は本考案の防食材の断面概略図であり、
1は金属基材、2はプライマー組成物、3は防食
塗材、4はポリウレタン塗料、5は弗素樹脂系塗
料である。 本考案で使用される金属基材は公知のものなら
いずれも良いが、例えば鋼、アルミニウム、ステ
ンレス鋼などを挙げることができる。 本考案のプライマー組成物及び防食塗材の成分
である不飽和ポリエステル系樹脂も、公知の各種
のものを使用できる。これは不飽和ジカルボン酸
の単独又はこれと飽和ジカルボン酸との混合物と
多価アルコールとを重縮合反応させて得られた不
飽和ポリエステルに、ビニルモノマーを混合した
ものである。不飽和ジカルボン酸としては無水マ
イレン酸、フマル酸、イタコン酸、シトラコン酸
などを、飽和ジカルボン酸としては無水フタル
酸、イソフタル酸、テレフタル酸、アジピン酸な
どを例示できる。多価アルコールとしてはエチレ
ングリコール、ジエチレングリコール、プロピレ
ングリコール、ブチレングリコールなどが挙げら
れる。ビニルモノマーとしてはスチレン、酢酸ビ
ニル、メタクリル酸メチル、ビニルトルエンなど
が使用できる。この不飽和ポリエステル系樹脂の
硬化剤としては通常の有機過酸化物例えばベンゾ
イルパーオキサイド、メチルエチルケトンパーオ
キサイド、クメンパーオキサイド等が用いられ
る。また、これらの樹脂にはナフテン酸コバル
ト、アミン系重合禁止剤等の添加剤、更に着色顔
料、分散剤等が配合される。 本考案のプライマー組成物及び防食塗材にはそ
れぞれ平均粒径が10〜100μ及び40〜1000μの鱗片
状無機充填材が配合される。鱗片状無機充填剤と
してはフレーク状ガラス、天然及び人造グラフア
イト、天然及び人造雲母、鱗片状酸化鉄(MIO)
等が使用される。 プライマー組成物において鱗片状無機充填材の
平均粒径が100μより大きくなると基材とのなじ
みが悪くなり、また塗装作業性も悪くなる。一
方、平均粒径が10μより小さくなると塗膜の乾燥
性が悪くなる。また、鱗片状無機充填材の量が40
重量%を越えると塗装作業が悪くなり、接着力も
低下する。一方5重量%未満ではプライマーの乾
燥性の向上効果が殆ど認められない。 防食塗材において鱗片状無機充填材の平均粒径
が1000μより大きくなると塗装作業性が悪くな
る。一方40μより小さくなると防食性能が著しく
低下する。また、鱗片状無機充填材量が60重量%
を越えると塗装作業性が悪くなり、一方10重量%
未満では防食性能が低下する。 本考案においてポリウレタン塗料はポリオール
として2官能以上のポリエーテルポリオールまた
はポリエステルポリオール、硬化剤としてジイソ
シアネートからなる2液型ポリウレタンである。
ポリウレタン塗料は不飽和ポリエステルからなる
防食材と弗素樹脂系塗料との界面接着層として効
果を発揮する。ポリエーテルポリオールとしては
ポリプロピレン系ポリオール、アクリルポリオー
ル、ポリブタジエンポリオール等が挙げられる。
またポリエステルポリオールとしてはアジピン酸
系や芳香族カルボン酸などを酸成分とし、これに
単量体ポリオール成分(1,6ーヘキサンジオー
ルなど)を用いたもの等が挙げられる。またジイ
ソシアネートとしては各種のものを使用できる
が、1,6ーヘキサメチレンジイソシアネート、
イソホロンジイソシアネート、水添キシリレンジ
イソシアネート、水添ジフエニルメタンジイソシ
アネート(MDI)など比較的耐黄変性のあるも
のが好ましい。 本考案において弗素樹脂系塗料としては例えば
フルオロオレフインとビニルエーテルの共重合体
(ポリフルオロオレフインビニルエーテル)をイ
ソシアネート又はメラミン化合物で架橋したもの
など各種のものを使用できる。この塗料は無色又
は酸化チタン、その他の顔料を添加した着色塗料
でも良く、ベンゾフエノン類、ベンゾトリアゾー
ル類などの紫外線吸収剤、ジスアゾイエロー、ク
ロムパーミリオン、コバルトブルーなどの顔料、
その他の公知の添加剤を配合することも任意であ
る。 本考案の外装用防食構造は金属基材に上記プラ
イマー組成物を20〜100μの厚さに塗装し、その
上に上記防食塗材を200μ以上の厚さに塗装し、
その上にポリウレタン塗料を20〜100μの厚さに
塗装し、更に弗素樹脂系塗料を20〜100μの厚さ
に塗装して、各工程で乾燥、必要により焼付けを
行うことにより得られる。塗装は公知の方法、例
えば刷毛、ローラー、エアレススプレー、エアス
プレーなどにより行うことができ、乾燥は好まし
くは常温でも行われ、現場施工において有効であ
る。焼付けは高温、例えば100℃で30分間の加熱
で硬化が可能であるので、短時間で塗装仕上げを
する場合に好適である。 本考案品の用途は例えばタンク、プール、架構
などの陸上構築物や橋梁、シーバースなどの海洋
構築物、さらに船舶、パイプライン、鋼矢板など
防食性と美観を必要とする分野で広範囲にわた
る。 (実施例) 次に実施例及び比較例により本考案を説明す
る。 実施例 1 鋼板を脱脂、除錆をした後コバルト等の硬化促
進剤及び過酸化物系硬化剤、その他の添加剤を配
合したビニルエステル樹脂に平均粒径40μのマイ
カを樹脂100重量部に対して30重量部を添加して
得られたプライマーを50μの厚さに塗装し、その
上に平均粒径150μのガラスフレークを40重量部
とビスフエノール系ポリエステル樹脂100重量部
を配合して得られる防食塗材を300μの厚さに塗
装し、常温放置して硬化後、ポリプロピレン系ポ
リオールと1,6ーヘキサメチレンジイソシアネ
ートを主成分としたポリウレタン系塗料を厚さ
30μになるように塗装し、常温で24時間放置して
乾燥する。さらにその上にチタン白顔料17重量部
を含むポリフルオロオレフインビニルエーテルを
イソシアネートで架橋した弗素樹脂100重量部か
らなる塗料を50μの厚さに塗装して常温放置して
乾燥硬化させる。ポリウレタン塗料の接着層を設
けたことにより、防食材と弗素樹脂系塗料層の界
面接着力は168Kg/cm2に向上した。 本塗装物を促進耐候性試験機サンシヤインウエ
ザオメーターで3000時間照射試験をした後、光沢
測定器で測定したところ光沢保持率は60%以上で
あつた。また褪色性も殆ど認められなかつた。更
にJISK5400に基づき1000時間塩水噴霧試験を行
つたが特に異状が認められなかつた。 比較例 1 ポリウレタン塗料層の形成を行わなかつた他は
実施例1と同様にして防食材を得た。この場合の
上記界面接着力は75Kg/cm2と低かつた。 本考案品の性能評価の結果を第1表に示す。 【表】
第1図は本考案の外装防食材の断面概略図であ
り、1は金属基材、2はプライマー組成物、3は
防食塗材、4はポリウレタン塗料、5は弗素樹脂
系塗料である。
り、1は金属基材、2はプライマー組成物、3は
防食塗材、4はポリウレタン塗料、5は弗素樹脂
系塗料である。
Claims (1)
- 金属基材の表面に不飽和ポリエステル系樹脂60
〜95重量%、平均粒径10〜100μの鱗片状無機充
填材40〜5重量%を主成分としたプライマー組成
物を20〜100μの厚さに塗装し、その上に平均粒
径40〜1000μの鱗片状無機充填材10〜60重量%を
不飽和ポリエステル系樹脂90〜40重量%に配合し
た防食塗材を200μ以上の厚さに被覆塗装を行い、
この上に2官能以上のポリオールとジイソシアネ
ートを成分とするポリウレタン塗料を20〜100μ
の厚さに塗装し、さらに無色または着色した弗素
樹脂系塗料を20〜100μの厚さに被覆塗装してな
る耐候性、美観性の向上および重防食性を兼備し
た外装防食材。