JPH01313578A - 有機イリジウムインク - Google Patents
有機イリジウムインクInfo
- Publication number
- JPH01313578A JPH01313578A JP63145024A JP14502488A JPH01313578A JP H01313578 A JPH01313578 A JP H01313578A JP 63145024 A JP63145024 A JP 63145024A JP 14502488 A JP14502488 A JP 14502488A JP H01313578 A JPH01313578 A JP H01313578A
- Authority
- JP
- Japan
- Prior art keywords
- resin
- ink
- iridium
- resins
- organoiridium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【発明の詳細な説明】
(産業上の利用分野)
本発明は、セラミック製品やガラス製品の表面に装飾用
や電子工業用等に使用される有機イリジウムインクに関
する。
や電子工業用等に使用される有機イリジウムインクに関
する。
(従来技術とその問題点)
従来の有機イリジウムインクは樹脂酸のイリジウム塩と
ガラスフリット又は樹脂酸のイリジウム塩と他の樹脂酸
の金属塩で構成されたものにバインダとしてエチルセル
ロース等の熱可塑性樹脂が用いられており、その問題点
として電子工業用では抵抗体への利用上でシート抵抗値
100Ω/口〜10にΩ/口の範囲を調製するのが困難
であり、室温にて放置しておくと短期間に固体分と液体
分が分離するという欠点もあり、また微細構造の印刷性
に欠けるなどの問題がある。
ガラスフリット又は樹脂酸のイリジウム塩と他の樹脂酸
の金属塩で構成されたものにバインダとしてエチルセル
ロース等の熱可塑性樹脂が用いられており、その問題点
として電子工業用では抵抗体への利用上でシート抵抗値
100Ω/口〜10にΩ/口の範囲を調製するのが困難
であり、室温にて放置しておくと短期間に固体分と液体
分が分離するという欠点もあり、また微細構造の印刷性
に欠けるなどの問題がある。
(発明の目的)
本発明はこれら従来の問題点を考慮し、シート抵抗値を
100Ω/口〜IOKΩ/口の範囲で自由に調製でき数
ケ月室温にて放置しても固体分と液体分に分離しない均
一性の高い安定したもので、しかも微細構造への印刷性
にも優れた有機イリジウムインクを提供することを目的
とする。
100Ω/口〜IOKΩ/口の範囲で自由に調製でき数
ケ月室温にて放置しても固体分と液体分に分離しない均
一性の高い安定したもので、しかも微細構造への印刷性
にも優れた有機イリジウムインクを提供することを目的
とする。
(問題点を解決するため手段)
本発明は、樹脂酸のイリジウム塩と他の金属成分とバイ
ンダとしてのアルキッド樹脂、尿素樹脂、メラミン樹脂
、ロジン誘導体樹脂及びテルペン樹脂から成る群から選
択される1又は2以上の樹脂及び溶剤を含有することを
特徴とする有機イリジウムインクである。
ンダとしてのアルキッド樹脂、尿素樹脂、メラミン樹脂
、ロジン誘導体樹脂及びテルペン樹脂から成る群から選
択される1又は2以上の樹脂及び溶剤を含有することを
特徴とする有機イリジウムインクである。
以下本発明をより詳細に説明する。
金属成分としてロジウム、鉛、ケイ素、ホウ素、アルミ
ニウム、カルシウム、マグネシウム、マンガン、亜鉛、
ジルコニウム、バリウム、ストロンチウム、カリウムか
ら成る群から選択される1又は2以上の金属の樹脂酸及
び/又は金属微粉末を含有させるのは、基体の種類と膜
厚や線幅の変化にも対応した密着性の高いものが得られ
しかも耐久性のある安定した膜が形成できるからである
。
ニウム、カルシウム、マグネシウム、マンガン、亜鉛、
ジルコニウム、バリウム、ストロンチウム、カリウムか
ら成る群から選択される1又は2以上の金属の樹脂酸及
び/又は金属微粉末を含有させるのは、基体の種類と膜
厚や線幅の変化にも対応した密着性の高いものが得られ
しかも耐久性のある安定した膜が形成できるからである
。
またバインダとしてアルキッド樹脂、尿素樹脂、メラニ
ン樹脂、ロジン誘導体樹脂及びテルペン樹脂から成る群
から選択される1又は2以上の樹脂を含有させるのは、
微細構造の印刷等の時におけるインクのダレを防止させ
る程度の粘度を持ち樹脂酸の金属塩及び/又は金属粉末
を混合させ安定した分散状態を保つためである。
ン樹脂、ロジン誘導体樹脂及びテルペン樹脂から成る群
から選択される1又は2以上の樹脂を含有させるのは、
微細構造の印刷等の時におけるインクのダレを防止させ
る程度の粘度を持ち樹脂酸の金属塩及び/又は金属粉末
を混合させ安定した分散状態を保つためである。
さらに、少ない含有量で求める粘度を得ることができ印
刷焼付作業等が効率よくできる。
刷焼付作業等が効率よくできる。
溶剤は前記物質を溶解し、かつ該物質を含むインクが印
刷された場合比較的短時間で乾くような揮発性物質であ
ることが好ましく、メタノール、テレピネオール、ブチ
ルカルピトール、メチルエチルケトン、プロピレングリ
コール、エチレングリコール、シクロヘキサノン、酢酸
エチル、酢酸ベンジル、アミルアセラード、セルソルブ
、ブチルセルソルブ、ブタノール、シトロベンゼン、ト
ルエン、キシレン、石油エーテル、クロロホルム、四塩
化炭素、ピネン、ジペンテン、ジペンテンオキサイド、
精油のいずれか1又は2以上の物質から成る溶剤を用い
ることで該有機イリジウムインクの特徴を得ることがで
きる。
刷された場合比較的短時間で乾くような揮発性物質であ
ることが好ましく、メタノール、テレピネオール、ブチ
ルカルピトール、メチルエチルケトン、プロピレングリ
コール、エチレングリコール、シクロヘキサノン、酢酸
エチル、酢酸ベンジル、アミルアセラード、セルソルブ
、ブチルセルソルブ、ブタノール、シトロベンゼン、ト
ルエン、キシレン、石油エーテル、クロロホルム、四塩
化炭素、ピネン、ジペンテン、ジペンテンオキサイド、
精油のいずれか1又は2以上の物質から成る溶剤を用い
ることで該有機イリジウムインクの特徴を得ることがで
きる。
本発明の有機イリジウムインクは安定な均一溶液状のた
め、スクリーン印刷の他、スタンプ、スプレ、ディッピ
ング、スピンコーティング、筆塗りなどにより微細部に
まで塗布が可能で、乾燥、焼成工程を経て得られた膜厚
は0.1〜1μmと薄い膜を施すことができシート抵抗
値として100Ω/口〜IOKΩ/口の範囲で自由に調
製が可能である。また含有するバインダの選択により直
接スクリーン印刷で線幅100μmの塗布が可能である
。
め、スクリーン印刷の他、スタンプ、スプレ、ディッピ
ング、スピンコーティング、筆塗りなどにより微細部に
まで塗布が可能で、乾燥、焼成工程を経て得られた膜厚
は0.1〜1μmと薄い膜を施すことができシート抵抗
値として100Ω/口〜IOKΩ/口の範囲で自由に調
製が可能である。また含有するバインダの選択により直
接スクリーン印刷で線幅100μmの塗布が可能である
。
さらに従来の有機イリジウムインクやイリジウムペース
トでは困難とされていた1〜10μmのピンホールや凹
凸の生じたりしない安定した膜厚をも形成することがで
きる。
トでは困難とされていた1〜10μmのピンホールや凹
凸の生じたりしない安定した膜厚をも形成することがで
きる。
以下本発明に係わる有機イリジウムインクの実施例を記
載するが、該実施例は本発明を限定するものではない。
載するが、該実施例は本発明を限定するものではない。
(実施例1)
下記の成分を混合して有機イリジウムインクとした。
樹脂酸イリジウム(Ir15%) 4重量%樹脂酸
ロジウム (Rh27%) 5重量%樹脂酸鉛
(Pb30%)16重量%樹脂酸ケイ素 (Si
14%) 5重量%樹脂酸ホウ素 (87%)
4重量%アルキッド樹脂 14
重滑部尿素樹脂 4重量%メ
ンタノール 14重量%変性ガムロ
ジン 22重量%テルペン樹脂
12重量%このインクは適度の粘性を有
した均一な溶液状であり、スクリーン印刷により基板上
に印刷塗布し、室温にて10分間放置後、200℃にて
10分間乾燥し、850℃にて10分間焼成させた。得
られた抵抗体膜は0.2〜0.6μmの膜厚であり75
0〜950Ω/口のシート抵抗値を有していた。
ロジウム (Rh27%) 5重量%樹脂酸鉛
(Pb30%)16重量%樹脂酸ケイ素 (Si
14%) 5重量%樹脂酸ホウ素 (87%)
4重量%アルキッド樹脂 14
重滑部尿素樹脂 4重量%メ
ンタノール 14重量%変性ガムロ
ジン 22重量%テルペン樹脂
12重量%このインクは適度の粘性を有
した均一な溶液状であり、スクリーン印刷により基板上
に印刷塗布し、室温にて10分間放置後、200℃にて
10分間乾燥し、850℃にて10分間焼成させた。得
られた抵抗体膜は0.2〜0.6μmの膜厚であり75
0〜950Ω/口のシート抵抗値を有していた。
(実施例2)
下記の成分を混合し有機イリジウムインクとした。
樹脂酸イリジウム(Ir15%)31重量%樹脂酸ホウ
素 (88%)18重世%樹脂酸ケイ素 (S i
10%)18重量%樹脂酸鉛 (Pb30%)
12重量%アルキッド樹脂 14重量
%尿素樹脂 4重量%メンタ
ノール 3重量%このインクは三
本ロールミルにて分散性よい有機イリジ・ラムインクと
し、スクリーン印刷により基板上に塗布し室温にて約1
時間放置し、200℃にて10分間乾燥後、850℃に
て10分間焼成した。
素 (88%)18重世%樹脂酸ケイ素 (S i
10%)18重量%樹脂酸鉛 (Pb30%)
12重量%アルキッド樹脂 14重量
%尿素樹脂 4重量%メンタ
ノール 3重量%このインクは三
本ロールミルにて分散性よい有機イリジ・ラムインクと
し、スクリーン印刷により基板上に塗布し室温にて約1
時間放置し、200℃にて10分間乾燥後、850℃に
て10分間焼成した。
得られた抵抗体膜は膜厚3〜8μm、シート抵抗700
Ω/口であった。
Ω/口であった。
(発明の効果)
本発明は、従来の有機イリジウムインクやイリジウムペ
ーストでは得られなかったシート抵抗値を100Ω/口
〜IOKΩ/口の範囲で自由に調製でき、数ケ月室温に
放置しても固体骨と液体分に分離しない均一性の高い安
定したものでしかも微細構造への印刷性にも優れ膜厚0
.1〜10μmと広範囲の厚みを自由に調製でき線幅も
100μmという細い幅がスクリーン印刷で可能となり
工業用とし広く応用できる価値の高いものと言える。
ーストでは得られなかったシート抵抗値を100Ω/口
〜IOKΩ/口の範囲で自由に調製でき、数ケ月室温に
放置しても固体骨と液体分に分離しない均一性の高い安
定したものでしかも微細構造への印刷性にも優れ膜厚0
.1〜10μmと広範囲の厚みを自由に調製でき線幅も
100μmという細い幅がスクリーン印刷で可能となり
工業用とし広く応用できる価値の高いものと言える。
なお、本発明は特許請求の範囲に記載した特徴を有する
ものであるが、その実施態様を例示すると次のとおりで
ある。
ものであるが、その実施態様を例示すると次のとおりで
ある。
(実施態様)
(2)金属成分としてロジウム、鉛、ケイ素、ホウ素、
アルミニウム、カルシウム、マグネシウム、マンガン、
亜鉛、ジルコニウム、バリウム、ストロンチウム、カリ
ウムから成る群から選択される1又は2以上の金属の樹
脂酸及び/又は金属微粉末である請求項1記載の有機イ
リジウムインク。
アルミニウム、カルシウム、マグネシウム、マンガン、
亜鉛、ジルコニウム、バリウム、ストロンチウム、カリ
ウムから成る群から選択される1又は2以上の金属の樹
脂酸及び/又は金属微粉末である請求項1記載の有機イ
リジウムインク。
(3)アルキッド樹脂がアマニ油及び/又はロジン変性
アルキッド樹脂であり、尿素樹脂がn−ブチルエーテル
型ブチル化尿素樹脂及び/又はイソブチルエーテル型ブ
チル尿素樹脂であり、メラミン樹脂がn−ブチル−エー
テル型ブチル化メラミン樹脂及び/又はイソブチルエー
テル型ブチルメラミン樹脂であり、ロジン誘導体樹脂が
ロジンのグリセリンエステル、ロジンのペンタエリスリ
トールエステル、水素添加したロジンのメチルエステル
、水素添加したロジンのトリエチレングリコールエステ
ル、水素添加したロジンのグリセリンエステル、水素添
加したロジンのペンタエリスリトールエステル、重合し
たロジン、重合したロジンのグリセリンエステル、重合
したロジンのペンタエリスリトールエステル、マレイン
酸変性したロジンエステル、マレイン酸変性したロジン
ノヘンタエリスリトールエステル及びマレイン酸変性し
たロジンのグリセリンリスチルから成る群から選択され
る1種又は2種以上の混合物から成るものであり、テル
ペン樹脂がテルペン重合体、α−ピネン重合体、β−ピ
ネン重合体、d−リモネン重合体、ジテルペン樹脂、芳
香族変性テルペン重合体、変性テルペン重合体及びテル
ペンフェノール共重合体から成る群から選択されるもの
である請求項1又は実施態様(2)に記載の有機イリジ
ウムインク。
アルキッド樹脂であり、尿素樹脂がn−ブチルエーテル
型ブチル化尿素樹脂及び/又はイソブチルエーテル型ブ
チル尿素樹脂であり、メラミン樹脂がn−ブチル−エー
テル型ブチル化メラミン樹脂及び/又はイソブチルエー
テル型ブチルメラミン樹脂であり、ロジン誘導体樹脂が
ロジンのグリセリンエステル、ロジンのペンタエリスリ
トールエステル、水素添加したロジンのメチルエステル
、水素添加したロジンのトリエチレングリコールエステ
ル、水素添加したロジンのグリセリンエステル、水素添
加したロジンのペンタエリスリトールエステル、重合し
たロジン、重合したロジンのグリセリンエステル、重合
したロジンのペンタエリスリトールエステル、マレイン
酸変性したロジンエステル、マレイン酸変性したロジン
ノヘンタエリスリトールエステル及びマレイン酸変性し
たロジンのグリセリンリスチルから成る群から選択され
る1種又は2種以上の混合物から成るものであり、テル
ペン樹脂がテルペン重合体、α−ピネン重合体、β−ピ
ネン重合体、d−リモネン重合体、ジテルペン樹脂、芳
香族変性テルペン重合体、変性テルペン重合体及びテル
ペンフェノール共重合体から成る群から選択されるもの
である請求項1又は実施態様(2)に記載の有機イリジ
ウムインク。
(4)溶剤としてメンタノール、テルピネオール、ブチ
ルカルピトール、メチルエチルケトン、プロピレングリ
コール、エチレングリコール、シクロヘキサノン、酢酸
エチル、酢酸ベンジル、アミルアセラード、セルソルブ
、ブチルセルソルブ、ブタノール、ニトロベンゼン、ト
ルエン、キシレン、石油エーテル、クロロホルム、四塩
化炭素、ピネン、ジペンテン、ジペンテンオキサイド、
精油のいずれか1種又は2種以上の物質から成る請求項
1から実施態様(3)に記載の有機イリジウムインク。
ルカルピトール、メチルエチルケトン、プロピレングリ
コール、エチレングリコール、シクロヘキサノン、酢酸
エチル、酢酸ベンジル、アミルアセラード、セルソルブ
、ブチルセルソルブ、ブタノール、ニトロベンゼン、ト
ルエン、キシレン、石油エーテル、クロロホルム、四塩
化炭素、ピネン、ジペンテン、ジペンテンオキサイド、
精油のいずれか1種又は2種以上の物質から成る請求項
1から実施態様(3)に記載の有機イリジウムインク。
出願人 田中貴金属工業株式会社
Claims (1)
- 1.樹脂酸のイリジウム塩と他の金属成分とバインダと
してのアルキッド樹脂、尿素樹脂、メラミン樹脂、ロジ
ン誘導体樹脂及びテルペン樹脂から成る群から選択され
る1種又は2種以上の樹脂及び溶剤を含有することを特
徴とする有機イリジウムインク。