JPH01280580A - 被記録材 - Google Patents
被記録材Info
- Publication number
- JPH01280580A JPH01280580A JP63109514A JP10951488A JPH01280580A JP H01280580 A JPH01280580 A JP H01280580A JP 63109514 A JP63109514 A JP 63109514A JP 10951488 A JP10951488 A JP 10951488A JP H01280580 A JPH01280580 A JP H01280580A
- Authority
- JP
- Japan
- Prior art keywords
- cellulose
- water
- fine particles
- recording
- recording material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【発明の詳細な説明】
〔産業上の利用分野〕
本発明は被記録材に関し、更に詳しくは非多孔質支持体
の少くとも片面にインクジェットプリンターでの高密度
記録が可能な皮膜を形成させてなるインクジェットプリ
ンターのための被記録材に関する。
の少くとも片面にインクジェットプリンターでの高密度
記録が可能な皮膜を形成させてなるインクジェットプリ
ンターのための被記録材に関する。
インクジェットプリンターは、記録の鮮明さ、音の静か
さ、カラー化の容易なことなどの優れた特徴によシ近年
普及し始めている。インクジェットプリンターはジェッ
トノズルの詰シを防ぐために乾燥しにくいインクが用い
られ、このインクの成分はバインダー、染料、添加剤な
どを水、多価アルコール、多価アルコールエーテル、ピ
ロリドン等に溶解したものが一般的である。
さ、カラー化の容易なことなどの優れた特徴によシ近年
普及し始めている。インクジェットプリンターはジェッ
トノズルの詰シを防ぐために乾燥しにくいインクが用い
られ、このインクの成分はバインダー、染料、添加剤な
どを水、多価アルコール、多価アルコールエーテル、ピ
ロリドン等に溶解したものが一般的である。
このためインクジェットプリンターで印刷記録を行う場
合、記録用シートは吸水性を有する必要があり、通常イ
ンクを十分吸収する性能を付与すべく特別に設計された
紙が用いられている。
合、記録用シートは吸水性を有する必要があり、通常イ
ンクを十分吸収する性能を付与すべく特別に設計された
紙が用いられている。
一方、インクジェットプリンターのカラー化に伴って被
記録材に記録を行い、オーバーヘットプロジェクタ−(
OHIり用原紙として使用したシ、インテリア、エフス
テリア用品として使用する要求が高まっている。これら
の被記録材は、通常プラスチックフィルム、ガラス、金
属板、タイル等よシなるが、このプラスチックフィルム
、ガラス、金属板、タイル等は非多孔質かつ疎水性でイ
ンクジェットプリンター用水性インクを全く吸収しない
ので、その上に直接記録されたインクは容易に乾燥せず
、指でこすったり、重ね合されたシすると記録部分が汚
れて、実用にならない。
記録材に記録を行い、オーバーヘットプロジェクタ−(
OHIり用原紙として使用したシ、インテリア、エフス
テリア用品として使用する要求が高まっている。これら
の被記録材は、通常プラスチックフィルム、ガラス、金
属板、タイル等よシなるが、このプラスチックフィルム
、ガラス、金属板、タイル等は非多孔質かつ疎水性でイ
ンクジェットプリンター用水性インクを全く吸収しない
ので、その上に直接記録されたインクは容易に乾燥せず
、指でこすったり、重ね合されたシすると記録部分が汚
れて、実用にならない。
すなわち、インクジェット記録方式に用いられる被記録
材としては、高解像度、高品質な記録画質を得るために
、 /)インクの吸収が可及的速やかであること、リ イン
クドツトが重なった際に、後で付着したインクが前に付
着したインクドツトに流れ出さないこと、 3)インクドツトの径が必要以上尾大きくならないこと
、 リ インクドツトの形状が真円に近く、マたその周辺が
なめらかであること、 リ インクドツトの濃度が高く、ドツト周辺がぼけない
こと、 6)インクの発色性が優れたものであること等の要求性
能を満たしていることが必要とされる。
材としては、高解像度、高品質な記録画質を得るために
、 /)インクの吸収が可及的速やかであること、リ イン
クドツトが重なった際に、後で付着したインクが前に付
着したインクドツトに流れ出さないこと、 3)インクドツトの径が必要以上尾大きくならないこと
、 リ インクドツトの形状が真円に近く、マたその周辺が
なめらかであること、 リ インクドツトの濃度が高く、ドツト周辺がぼけない
こと、 6)インクの発色性が優れたものであること等の要求性
能を満たしていることが必要とされる。
この様な要求に対応するためプラスチックフィルム上に
特定のポリマーを塗工する方法については種々提案され
ている。例えば特開昭j?−/ダ、0り1号、特開昭5
デー//、51号、特開昭3デー、7 J、/ 7 ?
号、特開昭1.0−/、7コ、7g5号、特開昭6o−
ilIr、g’ir号、特開昭60−220.730号
、特開昭61−/9.3.Ir79号、特開昭62−2
/、!? ? ?号が挙げられる。
特定のポリマーを塗工する方法については種々提案され
ている。例えば特開昭j?−/ダ、0り1号、特開昭5
デー//、51号、特開昭3デー、7 J、/ 7 ?
号、特開昭1.0−/、7コ、7g5号、特開昭6o−
ilIr、g’ir号、特開昭60−220.730号
、特開昭61−/9.3.Ir79号、特開昭62−2
/、!? ? ?号が挙げられる。
しかしながら、最近のプリンター技術の急速な進歩で記
録の高密度化及び高速化か格段と進に高度なインク乾燥
性、発色性ギ皮膜と支持体との接着性か要求されている
が、これらの要求を満たすものは未だ見出されていない
。
録の高密度化及び高速化か格段と進に高度なインク乾燥
性、発色性ギ皮膜と支持体との接着性か要求されている
が、これらの要求を満たすものは未だ見出されていない
。
本発明はこのような問題に鑑み、前述した要求特性を充
分に満足し、特にインク吸収性、発色性及び接着性に優
れ、表面画像観察用としての用途の他、記録画像の透過
光を利用する、スライド、OHP、密着プリンター等の
光学機器での使用も可能であるインクジェット記録用と
して好適である被記録材を提供することIcある。
分に満足し、特にインク吸収性、発色性及び接着性に優
れ、表面画像観察用としての用途の他、記録画像の透過
光を利用する、スライド、OHP、密着プリンター等の
光学機器での使用も可能であるインクジェット記録用と
して好適である被記録材を提供することIcある。
本発明は、非多孔質支持体上に■アクリル系樹脂、■セ
ルロース及び水溶性セルロース誘導体、からなる群の少
くとも一種並びに■有機及び/又は無機微粒子を含有す
る皮膜を形成してなる被記録材を要旨とする。
ルロース及び水溶性セルロース誘導体、からなる群の少
くとも一種並びに■有機及び/又は無機微粒子を含有す
る皮膜を形成してなる被記録材を要旨とする。
本発明に使用するアクリル系樹脂としては(メタノアク
リル酸、(メタ)アクリル酸アンモニウム、(メタ)ア
クリル酸のアミン塩のような(メタコアクリル酸塩の単
量体を通常の重合方法だよシ単独重合或は共重合したも
のの他、これらの単量体と(メタ)アクリル酸メチル、
(メタ2アクリル酸エチル、(メタ)アクリル酸ブチル
、ヒドロキシエチルアクリレートのような(メタコアク
リル酸アルキルエステル等の単量体、スチレン、マレイ
ン酸、メチロールアミ クリルアシド等を適宜に通常の重合方法により共重合さ
せたもので、分子量が!、000〜200.000であ
シ、水に可溶あるいは水中で均一に分散するものが挙げ
られる。特に、水溶性であるものが好ましい。また、こ
のアクリル系樹脂は水溶液あるいは水性エマルジョンの
形で使用される。
リル酸、(メタ)アクリル酸アンモニウム、(メタ)ア
クリル酸のアミン塩のような(メタコアクリル酸塩の単
量体を通常の重合方法だよシ単独重合或は共重合したも
のの他、これらの単量体と(メタ)アクリル酸メチル、
(メタ2アクリル酸エチル、(メタ)アクリル酸ブチル
、ヒドロキシエチルアクリレートのような(メタコアク
リル酸アルキルエステル等の単量体、スチレン、マレイ
ン酸、メチロールアミ クリルアシド等を適宜に通常の重合方法により共重合さ
せたもので、分子量が!、000〜200.000であ
シ、水に可溶あるいは水中で均一に分散するものが挙げ
られる。特に、水溶性であるものが好ましい。また、こ
のアクリル系樹脂は水溶液あるいは水性エマルジョンの
形で使用される。
添加量は皮膜全重量に対してり0−ff0%が好ましい
。
。
尚、アクリル系樹脂と共にポリアミドエポキシ樹脂、ポ
リビニルアルコール、ポリビニルピロリドン、ポリビニ
ルアミン、ポリN−ビニルフォルムアミド等の樹脂を併
用することも可能である。
リビニルアルコール、ポリビニルピロリドン、ポリビニ
ルアミン、ポリN−ビニルフォルムアミド等の樹脂を併
用することも可能である。
又、セルロース、水溶性セルロース誘導体としてはセル
ロースパウダー、ヒドロキシグロビルセルロース、カル
ボキシメチルセルロース、メチルセルロース等のセルロ
ースエーテルカ挙ケラレ、特にはセルロースのヒドロキ
シアルキルエーテルが好ましい。これらのセルロース、
セルロース誘導体は単独あるいは混合でも使用される。
ロースパウダー、ヒドロキシグロビルセルロース、カル
ボキシメチルセルロース、メチルセルロース等のセルロ
ースエーテルカ挙ケラレ、特にはセルロースのヒドロキ
シアルキルエーテルが好ましい。これらのセルロース、
セルロース誘導体は単独あるいは混合でも使用される。
添加量は皮膜全重量に対して10〜30条が望ましい。
本発明に使用する有機微粒子としてはポリスチレン、ポ
リエチレン、ポリエチレン尿素、へ素ホルムアルデヒド
樹脂等の微粒子が挙げられ、それらの粒径としては0.
/〜3μmの範囲が好ましい。
リエチレン、ポリエチレン尿素、へ素ホルムアルデヒド
樹脂等の微粒子が挙げられ、それらの粒径としては0.
/〜3μmの範囲が好ましい。
無機微粒子としてはコロイダルシリカ、二酸化チタン等
の微粒子か挙げられ、コロイダルシリカとしては粒径が
110−1O0n、好ましくはコ0−!;Onmのもの
が挙げられ、二酸化チタンとしては0./ −70μm
5好ましくは0・3〜Sμmの粒径のものが挙げられる
。また、これらの中で不透明の被記録材の場合はゴ酸化
チタン微粒子透明の場合はコロイダルシリカが特に好ま
しい。これらの微粒子は皮膜全重量に対して10−jO
wtチが望ましい。
の微粒子か挙げられ、コロイダルシリカとしては粒径が
110−1O0n、好ましくはコ0−!;Onmのもの
が挙げられ、二酸化チタンとしては0./ −70μm
5好ましくは0・3〜Sμmの粒径のものが挙げられる
。また、これらの中で不透明の被記録材の場合はゴ酸化
チタン微粒子透明の場合はコロイダルシリカが特に好ま
しい。これらの微粒子は皮膜全重量に対して10−jO
wtチが望ましい。
本発明で使用される非多孔質支持体としては通常平板状
のものが用いられ、例えばポリエステル、ジアセテート
、トリアセテート、アクリル系ポリマー、セロハン、セ
ルロイド、ポリ塩化ビニル、ポリカーボネート、ポリイ
ミド、ポリアミド等のプラスチックからなるフィルム若
しくは板、ガラス板、タイル、金属板′f、使用するこ
とができる。
のものが用いられ、例えばポリエステル、ジアセテート
、トリアセテート、アクリル系ポリマー、セロハン、セ
ルロイド、ポリ塩化ビニル、ポリカーボネート、ポリイ
ミド、ポリアミド等のプラスチックからなるフィルム若
しくは板、ガラス板、タイル、金属板′f、使用するこ
とができる。
用いる支持体の厚みは特に限定されるものではなく、使
用目的に応じて種々の厚みのものが使用可能である。
用目的に応じて種々の厚みのものが使用可能である。
インク吸収層として形成される皮膜は、乾燥厚みで/
−/ 00μ、特には弘〜SOμが適当である。皮膜が
薄すぎるとインクの乾燥が遅くなシ実用性に乏しくなり
、−刃厚すぎるとシート1枚当シの価格が上昇し、また
塗布が困難になるのでいずれも好ましくない。
−/ 00μ、特には弘〜SOμが適当である。皮膜が
薄すぎるとインクの乾燥が遅くなシ実用性に乏しくなり
、−刃厚すぎるとシート1枚当シの価格が上昇し、また
塗布が困難になるのでいずれも好ましくない。
皮膜を支持体上に形成するに当っては、塗布液を直接そ
のまま塗布しても良いが、支持体と形成された皮膜の密
着性が不十分である場合には皮膜を形成させる前に支持
体上にプライマーが施されていることが好ましい。
のまま塗布しても良いが、支持体と形成された皮膜の密
着性が不十分である場合には皮膜を形成させる前に支持
体上にプライマーが施されていることが好ましい。
支持体上に皮膜を形成する方法としてはグラビアコート
、バーコード、リバースロールコート、ナイフコートな
ど通常のコーティング手段を用いることが出来る。
、バーコード、リバースロールコート、ナイフコートな
ど通常のコーティング手段を用いることが出来る。
支持体上への皮膜の形成は、支持体の片面Ωみに設けて
も良いし、両面に設けても良い。
も良いし、両面に設けても良い。
以下、実施例を用いて本発明の被記録材を更に詳細に説
明するが以下の実施例は本発明を何等限定するものでは
ない。
明するが以下の実施例は本発明を何等限定するものでは
ない。
実施例1
支持体用基材として、厚さ100μmの透光性の親水処
理ポリエステルフィルム(帝人■製セルロースJ重i一
部、コロイダルシリカ2重量部(粒径:10〜1010
0n及び水90重量部からなる組成物をバーコーター法
によシ乾燥膜厚が70μmとなるように塗布しこれをg
。
理ポリエステルフィルム(帝人■製セルロースJ重i一
部、コロイダルシリカ2重量部(粒径:10〜1010
0n及び水90重量部からなる組成物をバーコーター法
によシ乾燥膜厚が70μmとなるように塗布しこれをg
。
℃10分の条件で乾燥させ記録は像の透過光を利用する
用途に用いることのできる本発明の被記録材を得た。
用途に用いることのできる本発明の被記録材を得た。
この得られた被記録材に、ピエゾ振動子によりてインク
を吐出するインクジェットプリンター1O−720(シ
ャープ■製)を用いてインクジェット記録を行い記録画
像を得た。
を吐出するインクジェットプリンター1O−720(シ
ャープ■製)を用いてインクジェット記録を行い記録画
像を得た。
冷却管、攪拌機を備えた。r o o mtの反応器に
/239のイソプロピルアルコール、メタクリル酸/
Of %エチルアクリレー)jf、エチルメタクリレー
ト!;?、0.jfのアゾビスイソブチロニトリルを入
れ、窒素ガス気流下50℃で3時間攪拌した。冷却後ア
ンモニアで中和したのち乾燥し、油状のアクリル系樹脂
を原料上ツマ−に対し、タテ係の収率で得た。
/239のイソプロピルアルコール、メタクリル酸/
Of %エチルアクリレー)jf、エチルメタクリレー
ト!;?、0.jfのアゾビスイソブチロニトリルを入
れ、窒素ガス気流下50℃で3時間攪拌した。冷却後ア
ンモニアで中和したのち乾燥し、油状のアクリル系樹脂
を原料上ツマ−に対し、タテ係の収率で得た。
上記のようにして得られた記録画像を以下の3項目につ
いて試験し、被記録材の記録適性及び光学機器に用いた
場合の適性の評価全行なった0 (IJ 速乾性 インクジェット記録後、記録物全室温下に放置し、60
秒後、記録された部分に指で触れてもインクが指に付着
せず、充分乾燥していた。
いて試験し、被記録材の記録適性及び光学機器に用いた
場合の適性の評価全行なった0 (IJ 速乾性 インクジェット記録後、記録物全室温下に放置し、60
秒後、記録された部分に指で触れてもインクが指に付着
せず、充分乾燥していた。
(2)画像の品位
得られた画像は、インクの広がシやにじみがなく、高解
像度の画像であった。
像度の画像であった。
(3) 光学機器適正
記録画像をOHPによシスクリーンに投影し、目視によ
シ観察して判定した結果、非記録部が明るく、記録画像
のOD(オプティカルデンシティ−)が高く、コントラ
ストの高い鮮明で見易い投影画像が得られた。
シ観察して判定した結果、非記録部が明るく、記録画像
のOD(オプティカルデンシティ−)が高く、コントラ
ストの高い鮮明で見易い投影画像が得られた。
実施例コ
建材用タイルの片面にケン化度gt、%のポリビニルア
ルコール(ゴーセノールGH−/’7;日本合成化学製
)5重量部、下記重合例によシ製造したアクリル樹脂7
3重量部、セルロースパウダー3重量部、二酸化チタン
微粒子(粒径:0.1〜3μm)70重量部及び水io
o重量部及び水100重量部からなる組成物を用いて、
実施例/と同様にして被記録材を得た。
ルコール(ゴーセノールGH−/’7;日本合成化学製
)5重量部、下記重合例によシ製造したアクリル樹脂7
3重量部、セルロースパウダー3重量部、二酸化チタン
微粒子(粒径:0.1〜3μm)70重量部及び水io
o重量部及び水100重量部からなる組成物を用いて、
実施例/と同様にして被記録材を得た。
実施例1と同様にして記録画像を形成し評価を行った結
果、前記(Ll、 (2+項目に関して良好な結果を得
た。
果、前記(Ll、 (2+項目に関して良好な結果を得
た。
冷却管、攪拌機を備えた。3 o o miの反応器に
水/ 00 ?、メタノール1001!、アクリル酸I
O?、メチルメタアクリL/−ト10?、ヒドロキシエ
チルアクリレート102、マレイン酸!;t、0./?
のアゾビスイソブチロニトリルを入れ窒素ガス気流下6
0℃で3時間攪拌した。
水/ 00 ?、メタノール1001!、アクリル酸I
O?、メチルメタアクリL/−ト10?、ヒドロキシエ
チルアクリレート102、マレイン酸!;t、0./?
のアゾビスイソブチロニトリルを入れ窒素ガス気流下6
0℃で3時間攪拌した。
冷却後トリエタノールアミンで中和した後乾燥し油状の
アクリル系樹脂を原料モノマーに対し9g%の収率で得
た。
アクリル系樹脂を原料モノマーに対し9g%の収率で得
た。
実施例3
下記重合例によシ製造したアクリル系樹脂/ o li
i 部、ヒドロキシグロビルセルロースコ重量部、尿
素ホルマリン樹脂の微粒子コ重量部(粒径:o、l、3
μ771)、水70重量部からなる組成物を用いて基材
としてアルミニウム製板上に実施例/と同様にして塗布
し被記録材を得た。実施例/と同様にして記録画像を形
成し、評価を行った結果、前記(1)、(2)項目に関
して良好な結果を得た。
i 部、ヒドロキシグロビルセルロースコ重量部、尿
素ホルマリン樹脂の微粒子コ重量部(粒径:o、l、3
μ771)、水70重量部からなる組成物を用いて基材
としてアルミニウム製板上に実施例/と同様にして塗布
し被記録材を得た。実施例/と同様にして記録画像を形
成し、評価を行った結果、前記(1)、(2)項目に関
して良好な結果を得た。
実施例1の重合例において、エチルアクリレートの代シ
にブチルアクリレート、又、エチルメタクリレートの代
シにメチロールアクリルアミドを用いた以外は、全く同
様にして重合を行いアクリル系樹脂を得た。
にブチルアクリレート、又、エチルメタクリレートの代
シにメチロールアクリルアミドを用いた以外は、全く同
様にして重合を行いアクリル系樹脂を得た。
本発明の被記録材は、インクジェットプリンターによっ
て非多孔質の支持体上に高密度の記録を行なうための被
記録材であシ、記録後のインクの速乾性及び印字品位等
に優れている。
て非多孔質の支持体上に高密度の記録を行なうための被
記録材であシ、記録後のインクの速乾性及び印字品位等
に優れている。
又、本発明の被記録材は、記録された画像を表面観察用
はもちろんのこと、記録画像の透過光を利用するスライ
ド、OHP、密着プリンター等の光学機器に使用するた
めの被記録材としても透光性に特に優れていて有用であ
る。
はもちろんのこと、記録画像の透過光を利用するスライ
ド、OHP、密着プリンター等の光学機器に使用するた
めの被記録材としても透光性に特に優れていて有用であ
る。
特許出願人 三菱化成工業株式会社
代 理 人 弁理士 長谷用 −
(ほか1名)
Claims (1)
- (1)非多孔質支持体上に[1]アクリル系樹脂、[2
]セルロース及び水溶性セルロース誘導体、からなる群
の少なくとも一種、並びに[3]有機及び/又は無機微
粒子を含有する皮膜を形成してなることを特徴とする被
記録材。