JPH01119255A - 脱臭剤組成物 - Google Patents
脱臭剤組成物Info
- Publication number
- JPH01119255A JPH01119255A JP62277995A JP27799587A JPH01119255A JP H01119255 A JPH01119255 A JP H01119255A JP 62277995 A JP62277995 A JP 62277995A JP 27799587 A JP27799587 A JP 27799587A JP H01119255 A JPH01119255 A JP H01119255A
- Authority
- JP
- Japan
- Prior art keywords
- ferrous salt
- deodorant composition
- deodorizing
- iron
- sugar
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【発明の詳細な説明】
（産業上の利用分野）
本発明は、便所、冷蔵片、ごみ箱、自動車内等の悪臭、
特にアンモニア臭気、メルカプタン類の除去に優れた効
果を有する脱臭剤に関する。
特にアンモニア臭気、メルカプタン類の除去に優れた効
果を有する脱臭剤に関する。
（従来の技術）
従来、工業的に上記のような悪臭を除去するに際し、悪
臭ガスをスクラッピングしたり、燃焼することが行われ
ているが、操作が複雑で大規模な装置を要する。それ故
一般家庭や事務所等では次のような脱臭方法が行われて
いる。
臭ガスをスクラッピングしたり、燃焼することが行われ
ているが、操作が複雑で大規模な装置を要する。それ故
一般家庭や事務所等では次のような脱臭方法が行われて
いる。
ｉ）香料によるマスキング。
１１）活性炭による吸着。
１ｉｉ）クエン酸、マレイン酸を主成分とした物７１を
化学的に反応させて除去する。
化学的に反応させて除去する。
ｉｖ） Ｍ化剤を散布する。オゾンや炭酸ソーダと過酸
化水素系の分子結合したものが一般的に使用されている
。
化水素系の分子結合したものが一般的に使用されている
。
■）ビタミンＣと硫酸第一鉄を原料とする脱臭方法。
（発明が解決しようとする問題点）
しかしながら上記ｉ）〜■）の方法は次のような欠点を
有している。
有している。
ｉ）の方法はマスキングのため、臭気を他の香料の６つ
に変えただ【プで本質的に変化なく、また異臭が残る。
に変えただ【プで本質的に変化なく、また異臭が残る。
１１）の方法は吸着容量が限定され吸着能力の低下が早
い。１ｉｉ）の方法はアンモニア。
い。１ｉｉ）の方法はアンモニア。
アミン類には有効であるが、メルカプタン類を除くこと
はできない。ｉｖ）の方法については酸化剤を用いる関
係上、二次公害を生じる。また保存方法によっては自然
発火する場合がおる。■）の方法はアンモニアの脱臭法
で主として冷蔵庫等に刊用されているが、Ｌ−アスコル
ビン酸を使用している関係−Ｌ温度の変化（特に５０℃
以上）に対して非常に弱い。
はできない。ｉｖ）の方法については酸化剤を用いる関
係上、二次公害を生じる。また保存方法によっては自然
発火する場合がおる。■）の方法はアンモニアの脱臭法
で主として冷蔵庫等に刊用されているが、Ｌ−アスコル
ビン酸を使用している関係−Ｌ温度の変化（特に５０℃
以上）に対して非常に弱い。
この様な点から、従来の脱臭剤は脱臭効果は優れていて
も食品衛生上や安定性の面で問題があった。
も食品衛生上や安定性の面で問題があった。
（問題点を解決するための手段）
本発明者らは従来の脱臭剤の欠点を克服するため鋭意研
究を重ねた結果、本発明を完成した。すなわら本発明は
第一鉄塩と、亜硫酸アルカ１ハ尿素及び砂糖よりなる群
より選ばれた少くとも１種の物質とを含有する脱臭剤組
成物である。第一鉄塩はどのような塩でも使用しうるが
、硫酸第一鉄。
究を重ねた結果、本発明を完成した。すなわら本発明は
第一鉄塩と、亜硫酸アルカ１ハ尿素及び砂糖よりなる群
より選ばれた少くとも１種の物質とを含有する脱臭剤組
成物である。第一鉄塩はどのような塩でも使用しうるが
、硫酸第一鉄。
塩化第一鉄、硝酸第−鉄等がより好ましい。
第一鉄塩と上記物質との組成割合は１：０．０２〜０．
３（重量比）、好ましくは１：０．０３〜０．１である
。第一鉄塩に対する亜ＵＡｆｆｔアルカ１ハ尿素又は砂
糖の含有比率がこの範囲を越えるときは組成物が着色し
、かつ経済的でなくなり、またこの範囲未満では十分な
脱臭効果が得られず、第一鉄塩の安定効果も不足してく
る。
３（重量比）、好ましくは１：０．０３〜０．１である
。第一鉄塩に対する亜ＵＡｆｆｔアルカ１ハ尿素又は砂
糖の含有比率がこの範囲を越えるときは組成物が着色し
、かつ経済的でなくなり、またこの範囲未満では十分な
脱臭効果が得られず、第一鉄塩の安定効果も不足してく
る。
本発明におＣプる脱臭剤組成物はいずれの形態でも使用
し得るが、粉末として用いる他、任意の濃度の水溶液と
して用いたり、活性炭、硅ソウ土。
し得るが、粉末として用いる他、任意の濃度の水溶液と
して用いたり、活性炭、硅ソウ土。
アルミナ、シリカゲル、軽石、セピオライト、ゼオライ
ト、モレキュラーシーブ、ケイ酸カルシウム等に担持し
て使用することができる。
ト、モレキュラーシーブ、ケイ酸カルシウム等に担持し
て使用することができる。
これらの担体は、脱臭剤組成物の水溶液に粉末状２粒状
の担体を浸漬し、あるいは水溶液を担体に塗布、スプレ
ー等の手段で担持させる。担持させつる脱臭剤組成物の
吊は、担体１００重量部に対し０．１〜３０手ｍ部、好
ましくは１〜２０重量部である。これらは湿潤状態で用
いることもできるが、乾燥して用いる方が好ましい。ま
た潤臭剤組成物をイｆｉや紙に含有さ−Ｕるには、水溶
液に１１ｉや紙を含浸したり、水溶液を布や紙に塗布又
は散イトして展着させる。湿潤状態のままあるいは乾燥
して用いることができる。布や紙に含浸できる脱臭剤組
成物の間は特に制限はないが、布や紙１００市量部に対
し１〜１０重母部が通常である。
の担体を浸漬し、あるいは水溶液を担体に塗布、スプレ
ー等の手段で担持させる。担持させつる脱臭剤組成物の
吊は、担体１００重量部に対し０．１〜３０手ｍ部、好
ましくは１〜２０重量部である。これらは湿潤状態で用
いることもできるが、乾燥して用いる方が好ましい。ま
た潤臭剤組成物をイｆｉや紙に含有さ−Ｕるには、水溶
液に１１ｉや紙を含浸したり、水溶液を布や紙に塗布又
は散イトして展着させる。湿潤状態のままあるいは乾燥
して用いることができる。布や紙に含浸できる脱臭剤組
成物の間は特に制限はないが、布や紙１００市量部に対
し１〜１０重母部が通常である。
（作 用）
本発明脱臭剤組成物の作用は明白ではないが、メルカプ
タン類については亜硫酸アルカ１ハ尿素。
タン類については亜硫酸アルカ１ハ尿素。
砂糖と第一鉄塩との間に酸化還元反応が起り、窒素化合
物は第−鉄塩によりアミン鉄錯化合物を生成することに
より脱臭されるものと考えられる。
物は第−鉄塩によりアミン鉄錯化合物を生成することに
より脱臭されるものと考えられる。
実施例１
粉末状の砂糖５（］、 Ｆｅ５Ｏａ ・７Ｈ２０２，８
０ｇを計但し、これを水１ｇに溶解し脱臭剤組成物の原
液とした。次にサンプル口の付いた丸底フラスコ１００
０ｄを２個用意して、アンモニア濃度１ｏｏｏｐｐｍに
なるように注射器にてアンモニアを内部に注入した。
０ｇを計但し、これを水１ｇに溶解し脱臭剤組成物の原
液とした。次にサンプル口の付いた丸底フラスコ１００
０ｄを２個用意して、アンモニア濃度１ｏｏｏｐｐｍに
なるように注射器にてアンモニアを内部に注入した。
このフラスコのうら１個に、先に作成した原液５ｍｌを
加え他の１個は加えずに、５０℃の恒温槽中で１０時間
放置後、内部ガスを採集し吸光度法にて測定したところ
次のようであった。
加え他の１個は加えずに、５０℃の恒温槽中で１０時間
放置後、内部ガスを採集し吸光度法にて測定したところ
次のようであった。
脱臭剤添加 ｏ、ｏｌｐｐｍ
脱臭剤なし ９００ｐｐｍ
実施例２
実施例１におけるアンモニアの代りに、メチルメルカプ
タン１１０００ｐｐどした以外は全く同様の操作で実験
を行った。メチルメルカプタン淵度の分析はガスクロマ
トグラフによる。
タン１１０００ｐｐどした以外は全く同様の操作で実験
を行った。メチルメルカプタン淵度の分析はガスクロマ
トグラフによる。
脱臭剤添加 ０．０１ｐｐｍ
脱臭剤なし ９８０ｐｐｍ
実施例３
実施例１と同じ原液を粒状セピオライト（粒度８〜２０
メツシユ）に重量比（セピオライ１〜：原液）１：０．
３で含浸させ５０℃にて真空乾燥を行った。
メツシユ）に重量比（セピオライ１〜：原液）１：０．
３で含浸させ５０℃にて真空乾燥を行った。
１ｑられた脱臭剤組成物担体を直径１００ｍｍのガラス
カラムに充＠（２００ｒｎｉ） Ｌ、メチルメルカプタ
ン２００ｐｐｍを含む悪臭ガスを、線速度ＬＶ＝５ｍ／
分の割合で通気したところ、その分析結果は第１表のと
おりであった。
カラムに充＠（２００ｒｎｉ） Ｌ、メチルメルカプタ
ン２００ｐｐｍを含む悪臭ガスを、線速度ＬＶ＝５ｍ／
分の割合で通気したところ、その分析結果は第１表のと
おりであった。
第 １ 表
実施例４
尿素６Ｑ、 Ｆｅ５Ｏａ ・７１２０ ２８０ｇを計量
し、これを水１．ｌ！に溶解し脱臭剤組成物の原液とし
た。これを実施例１と同様の操作でアンモニア１１００
０１）Ｅ）を作用させて測定したところ次のようであっ
た。
し、これを水１．ｌ！に溶解し脱臭剤組成物の原液とし
た。これを実施例１と同様の操作でアンモニア１１００
０１）Ｅ）を作用させて測定したところ次のようであっ
た。
脱臭剤添加 ０．０２ｐｐＨｌ
脱臭剤なし ９２０ｐｐｍ
実施例５
Ｎａ２３０３ １２（Ｊ、 ＦｅＣＪ１２１２７ｇを計
量し、これを水１、Ｉ！に溶解し、脱臭剤組成物の原液
とした。これを実施例２と同様にしてメルカプタン１１
０００ｐｐを作用させて測定したところ次のようであっ
た。
量し、これを水１、Ｉ！に溶解し、脱臭剤組成物の原液
とした。これを実施例２と同様にしてメルカプタン１１
０００ｐｐを作用させて測定したところ次のようであっ
た。
脱臭剤添加 ０． Ｏ２ｐｐｍ
脱臭剤なし ９６０ｐｐｍ
（発明の効果）
本発明の脱臭剤組成物はアンモニア、アミン類及びメル
カプタン類等の悪臭除去に有効であり、また人体に有害
な成分を含まぬので、食品関係の包装材料に用いたり、
冷蔵庫内の脱臭に用いることができる。また持続性ある
脱臭効果が期待されるので事務所内、家庭内の各程良い
の除去に有効である。
カプタン類等の悪臭除去に有効であり、また人体に有害
な成分を含まぬので、食品関係の包装材料に用いたり、
冷蔵庫内の脱臭に用いることができる。また持続性ある
脱臭効果が期待されるので事務所内、家庭内の各程良い
の除去に有効である。
さらに熱安定性に優れているので自動車内等５０℃以上
の高温になり易い個所の脱臭に’ｂイｉ用性が期待され
る。
の高温になり易い個所の脱臭に’ｂイｉ用性が期待され
る。
Claims (2)
- （１）第一鉄塩と、亜硫酸アルカリ、尿素及び砂糖より
なる群より選ばれた少くとも１種の物質とを含有する脱
臭剤組成物。 - （２）第一鉄塩が硫酸第一鉄、塩化第一鉄及び硝酸第一
鉄よりなる群より選ばれた少くとも１種である特許請求
の範囲第１項記載の脱臭剤組成物。