JP7482678B2 - ラミネートチューブ用積層体 - Google Patents
ラミネートチューブ用積層体 Download PDFInfo
- Publication number
- JP7482678B2 JP7482678B2 JP2020084091A JP2020084091A JP7482678B2 JP 7482678 B2 JP7482678 B2 JP 7482678B2 JP 2020084091 A JP2020084091 A JP 2020084091A JP 2020084091 A JP2020084091 A JP 2020084091A JP 7482678 B2 JP7482678 B2 JP 7482678B2
- Authority
- JP
- Japan
- Prior art keywords
- laminate
- layer
- printed
- tube according
- substrate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
〈態様1〉表層、印刷積層体及び基材が積層されているラミネートチューブ用積層体であって、
前記印刷積層体が、少なくとも部分的に互いに積層されている複数の印刷層を有し、
前記印刷層が、硬化性樹脂、及び色材を含有しており、かつ
前記複数の印刷層のうちの、最表層以外の少なくとも1つの印刷層において、前記硬化性樹脂のガラス転移温度が、80℃以下である、
ラミネートチューブ用積層体。
〈態様2〉前記印刷積層体の厚さが、10~40μmである、態様1に記載のラミネートチューブ用積層体。
〈態様3〉前記印刷積層体が、2~20層の印刷層を有している、態様1又は2に記載のラミネートチューブ用積層体。
〈態様4〉前記複数の印刷層のそれぞれが、1~5μmの厚さを有する、態様1~3のいずれか一項に記載のラミネートチューブ用積層体。
〈態様5〉前記印刷層の、JIS K 5600-5-4に準拠する引っかき硬度(鉛筆法)での硬度が、HB又はFである、態様1~4のいずれか一項に記載のラミネートチューブ用積層体。
〈態様6〉前記印刷層の色材が、光輝性顔料である、態様1~5のいずれか一項に記載のラミネートチューブ用積層体。
〈態様7〉前記印刷層が、脂肪族系ポリウレタンアクリレート及びベンゼン環の数が3個未満であり、かつアミノ基を有さない光重合開始剤を含有している、態様1~6のいずれか一項に記載のラミネートチューブ用積層体。
〈態様8〉前記表層と、前記印刷層との間に、エステル部分を有するポリオールとポリイソシアネートとの2液型接着剤で形成されている接着層を更に有し、かつ前記表層の前記接着層と接している面が、ポリオレフィン系樹脂で構成されている、態様1~7のいずれか一項に記載のラミネートチューブ用積層体。
〈態様9〉態様1~8のいずれか一項に記載のラミネートチューブ用積層体で形成された胴部を有する、ラミネートチューブ容器。
図1(a)に示すように、本発明のラミネートチューブ用積層体10は、表層12、印刷積層体14及び基材16が積層されており、
印刷積層体14が、少なくとも部分的に互いに積層されている複数の印刷層を有し、
印刷層が、硬化性樹脂、及び色材を含有しており、かつ
複数の印刷層のうちの、最表層以外の少なくとも1つの印刷層において、硬化性樹脂のガラス転移温度が、80℃以下である。
表層は、概して、ラミネートチューブ用積層体からラミネートチューブ容器を作製した際に最も外側に位置する層である。表層は、単層であっても積層体であってもよい。
図4に示すように、印刷積層体14は、少なくとも部分的に互いに積層されている複数の印刷層14a、14b、14c、14dを有する。ここで、本発明において、「互いに積層されている」とは、他の層を介することなく積層されていることを意味する。
複数の印刷層のうちの、最表層以外の少なくとも1つの印刷層において、硬化性樹脂は、ガラス転移温度が80℃以下である硬化性樹脂である。このガラス転移温度は、80℃以下、又は75℃以下であってよく、また0℃以上、10℃以上、20℃以上、30℃以上、40℃以上、50℃以上、60℃以上、65℃以上、又は70℃以上であってよい。
色材としては、顔料又は染料を用いることができる。
基材は、インキが印刷される非浸透性の基材である。基材は、単層であってもよく、又は複数の層が積層されている積層体でよく、複数の同じ種類の層を含んでもよい。
・LDPE(75μm)/乳白LDPE(160μm)/LDPE(50μm)/PET(12μm)/LLDPE(100μm)
・LLDPE(55)/透明LDPE(80)/EAA(20)/AL(12)/EMAA(25)/PET(12)/LLDPE(100)
透明樹脂層は、透明な樹脂層である。ここで、「透明」とは、この層を通して物体を視認するのに十分に透明であることを意味するものであり、例えば全光線透過率が、50%以上、60%以上、70%以上、75%以上、80%以上、85%以上、90%以上、95%以上、又は100%であり、かつヘイズ値が25%以下、20%以下、15%以下、又は10%以下であることを意味する。
有色下地層は、黒色下地層、赤色下地層、青色下地層、白色下地層であってよい。有色下地層のうち、白色下地層としては、透明樹脂層に関して挙げた樹脂に酸化チタン等の白色顔料を分散させた層であってもよく、又は白色印刷層であってもよい。この場合、有色下地層と印刷層との間には、透明な層以外の層、例えば金属箔層が存在していないことが、意匠性の観点から好ましい。
バリア層としては、例えば無機物蒸着層、金属箔層、有機物コート層等を用いることができる。
補強層は、延伸フィルムから構成されている層であってよい。
シーラント層としては、例えば上記のポリオレフィン系樹脂を用いることができる。ポリオレフィン系樹脂を、例えば、延伸又は無延伸フィルム、押出積層用の溶融樹脂、ホットメルト用の塗料等の形態で与えることができる。シーラント層は、表層のうちの最も外側に位置する部分と同じ樹脂で構成されていることが好ましく、特に表層と同じ層であってよい。
基材接着層は、基材を構成する上記の層の間に存在することができる随意の接着層である。かかる基材接着層としては、例えばドライラミネート接着剤、ホットメルト接着剤、水溶性接着剤、エマルション接着剤、ノンソルベントラミネート接着剤、及び押出ラミネート用の熱可塑性樹脂等であってよい。
印刷層と表層との間、及び表層と基材との間には、接着層が存在していてよい。接着層としては、例えば基材接着層として挙げた接着層を用いることができる。
ラミネートチューブ容器は、上記のラミネートチューブ用積層体で形成された胴部を有する容器である。
ラミネートチューブ用積層体を、基材、特に基材のシーラント層が内側となるように丸めながら、積層体の端部同士を重ね合せてシールして、胴部を得る工程;及び
胴部の開口部の周縁に、肩部及びキャップ部を有する頭部を結合させて、ラミネートチューブ容器を得る工程。
〈実施例〉
以下の層構成を有する積層体を準備した:
LDPE(75μm)/乳白LDPE(160μm)/LDPE(50μm)/PET(12μm)/LLDPE(100μm)
印刷機:フレキシプルーフ
アニロックスロール:180線/inch
UV照射条件:160W
上記の樹脂の代わりに、脂肪族系ポリウレタンアクリレート樹脂(UVフレキュアーパール、女神インキ工業社、Tg:100℃)を用いたことを除き、実施例と同様にして、比較例1の積層体を作製した。得られた印刷積層体の厚さは、28.0μmであった。
印刷層を単層で積層させたことを除き、実施例と同様にして、比較例2の評価用積層体を作製した。得られた印刷積層体の厚さは、3.5μmであった。
〈密着性〉
評価用積層体の印刷積層体にセロテープ(登録商標)を貼付し、これを剥がした際の印刷積層体の剥離を目視により観察した。
〇:剥離が生じた。
×:剥離が生じなかった。
評価用積層体を円筒状に丸めて扱き、印刷積層体の割れの有無を目視により観察した。
〇:割れが生じた。
×:割れが生じなかった。
評価用積層体を、練り歯磨き粉(クリアクリーン エクストラクール、花王社)に1週間浸漬した後、塗膜の剥離の有無を目視により観察した。別の評価用積層体を用い、UVクリーム(ビオレUVアクアリッチ、花王社)、トリートメント(HIMAWARI、クラシエ社)にも1週間それぞれ浸漬させて、同様の試験を行った。
〇:全ての試験で剥離が生じなかった。
△:一部の試験で剥離が生じた。
×:全ての試験で剥離が生じた。
印刷積層体のJIS K 5600-5-4に準拠する引っかき硬度(鉛筆法)での硬度を評価した。
作製した評価用積層体のパール光沢感を、目視により評価した。
〇:強いパール光沢感があった。
△:パール光沢感がやや弱かった。
×:パール光沢感が殆どなかった。
10X ラミネートチューブ容器の胴部
12 表層
14 印刷積層体
14a、14b、14c、14d 印刷層
16 基材
16a、16a’ 基材の暴露されている部分
161 有色下地層
162 透明樹脂層
163 バリア層
164 シーラント層
165 補強層
Claims (10)
- 表層、印刷積層体及び基材が積層されているラミネートチューブ用積層体であって、
前記印刷積層体が、少なくとも部分的に互いに積層されている複数の印刷層を有し、
前記印刷層が、硬化性樹脂、及び色材を含有しており、
前記印刷層が、脂肪族系ポリウレタンアクリレート及びベンゼン環の数が3個未満であり、かつアミノ基を有さない光重合開始剤を含有しており、
前記複数の印刷層のうちの、最表層以外の少なくとも1つの印刷層において、前記硬化性樹脂のガラス転移温度が、80℃以下であり、かつ
前記複数の印刷層のうちの、最表層以外の少なくとも1つの印刷層は、ポリイソシアネートを含有していない、ラミネートチューブ用積層体。 - 前記複数の印刷層のうちの、最表層の印刷層は、ポリイソシアネートを含有している、請求項1に記載のラミネートチューブ用積層体。
- 前記印刷積層体の厚さが、10~40μmである、請求項1又は2に記載のラミネートチューブ用積層体。
- 前記印刷積層体が、2~20層の印刷層を有している、請求項1~3のいずれか一項に記載のラミネートチューブ用積層体。
- 前記複数の印刷層のそれぞれが、1~5μmの厚さを有する、請求項1~4のいずれか一項に記載のラミネートチューブ用積層体。
- 前記印刷層の、JIS K 5600-5-4に準拠する引っかき硬度(鉛筆法)での硬度が、HB又はFである、請求項1~5のいずれか一項に記載のラミネートチューブ用積層体。
- 前記印刷層の色材が、光輝性顔料である、請求項1~6のいずれか一項に記載のラミネートチューブ用積層体。
- 前記基材は、有色下地層及びシーラント層を有している、請求項1~7のいずれか一項に記載のラミネートチューブ用積層体。
- 前記表層と、前記印刷層との間に、エステル部分を有するポリオールとポリイソシアネートとの2液型接着剤で形成されている接着層を更に有し、かつ前記表層の前記接着層と接している面が、ポリオレフィン系樹脂で構成されている、請求項1~8のいずれか一項に記載のラミネートチューブ用積層体。
- 請求項1~9のいずれか一項に記載のラミネートチューブ用積層体で形成された胴部を有する、ラミネートチューブ容器。