JP7399189B2 - スズ酸化物形成用組成物 - Google Patents
スズ酸化物形成用組成物 Download PDFInfo
- Publication number
- JP7399189B2 JP7399189B2 JP2021562355A JP2021562355A JP7399189B2 JP 7399189 B2 JP7399189 B2 JP 7399189B2 JP 2021562355 A JP2021562355 A JP 2021562355A JP 2021562355 A JP2021562355 A JP 2021562355A JP 7399189 B2 JP7399189 B2 JP 7399189B2
- Authority
- JP
- Japan
- Prior art keywords
- ruthenium
- tin
- tin oxide
- composition
- precursor
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
陰極(Cathode)反応:2H2O+2e-→2OH-+H2(E0=-0.83V)
全体反応:2Cl-+2H2O→2OH-+Cl2+H2(E0=-2.19V)
本発明の発明者は、スズ前駆体と硫酸イオンが同時に存在し、かつ組成物中の硫酸イオンとスズのモル比が1以上である場合、スズ前駆体からスズ酸化物が形成される過程における中間生成物の揮発を抑えることができ、これにより、最終的に形成されるスズ酸化物の収率が飛躍的に高くなることができることを見出し、本発明を完成した。
本発明は、前述のスズ酸化物形成用組成物を用いてスズ酸化物を形成する方法を提供する。具体的に、本発明は、上述のスズ酸化物形成用組成物を480℃以上の温度で焼成するステップ(S1)を含むスズ酸化物の形成方法を提供する。
溶媒である脱イオン水に塩化スズ(II)二水和物および硫酸(H2SO4)を溶解させてスズ酸化物形成用組成物を製造した。組成物中のスズ成分に対する硫酸イオン(SO4 2-)のモル比は3になるようにした。
スズ前駆体としてスズ2-エチルヘキサノエートを溶解させたことを除き、実施例1と同様に行ってスズ酸化物形成用組成物を製造した。
硫酸スズ(SnSO4)を直接溶解させたことを除き、実施例1と同様に行ってスズ酸化物形成用組成物を製造した。
塩化ルテニウム三水和物、塩化イリジウム三水和物、および塩化スズ(II)二水和物をRu:Ir:Snのモル比が35:20:45となるように、過量の1Mの硫酸水溶液に溶解させ、スズ酸化物形成用組成物を製造した。組成物中のスズ成分に対する硫酸イオン(SO4 2-)のモル比は8になるようにした。
スズ前駆体として硫酸スズを直接溶解させたことを除き、実施例4と同様に行ってスズ酸化物形成用組成物を製造した。
実施例1において、硫酸を溶解させなかったことを除き、同様に行ってスズ酸化物形成用組成物を製造した。
実施例2において、硫酸を溶解させなかったことを除き、同様に行ってスズ酸化物形成用組成物を製造した。
実施例1において、組成物中のスズ成分に対する硫酸イオン(SO4 2-)のモル比が0.7になるようにしたことを除き、同様に行ってスズ酸化物形成用組成物を製造した。
実施例4において、溶媒としてn-ブタノールを使用したことを除き、同様に行ってスズ酸化物形成用組成物を製造した。
前記実施例1~4および比較例1~2で製造したスズ酸化物形成用組成物を焼成し、焼成結果得られたスズ酸化物の重量から収率を計算した。収率は下記式1および2を用いて計算し、その結果を表2に示した。
収率={(焼成後の試料の重量)/(焼成前の試料中のSnモル数XSnO2の分子量)}X100
収率=(焼成後の試料の重量)/{(焼成前の試料中のRuモル数XRuO2の分子量)+(焼成前の試料中のIrモル数XIrO2の分子量)+(焼成前の試料中のSnモル数XSnO2の分子量)}X100
また、焼成温度を450℃、480℃、530℃、550℃、および580℃に変化させてXRDを確認し、純粋なSnO2を対照群として図1に示した。
白色アルミナでブラスト処理したチタン拡張基材を10%のシュウ酸水溶液(90℃)で2時間前処理して凹凸を形成した後、蒸留水で洗浄し、乾燥して金属基材を準備した。準備した金属基材に、実施例4、5、および比較例3のスズ酸化物形成用組成物を塗布した後、70℃で乾燥し、550℃で10分間焼成した。組成物の塗布量が20g/m2になるまで前記塗布、乾燥、および焼成を繰り返した後、最終的に550℃で60分間焼成して電極を製造した。製造された電極の表面をEDS分析し、電極コーティング層中に存在する各金属成分のモル比を計算し、これを表4に示した。
Claims (10)
- スズ前駆体と、硫酸イオンと、溶媒と、を含み、
スズに対する硫酸イオンのモル比(硫酸イオン/スズ)が3~10であり、
前記スズ前駆体は、スズアルコキシド化合物、スズ酢酸塩、硫酸スズ、およびスズ2-エチルヘキサノエートからなる群から選択される1つ以上である、
スズ酸化物形成用組成物。 - ルテニウム前駆体およびイリジウム前駆体からなる群から選択される1つ以上を含む白金族前駆体をさらに含み、
前記ルテニウム前駆体は、ルテニウムヘキサフルオリド(RuF6)、ルテニウム(III)クロリド(RuCl3)、ルテニウム(III)クロリド水和物(RuCl3・xH2O)、ルテニウム(III)ニトロシルクロリド(Ru(NO)Cl3)、ヘキサアンミンルテニウム(III)クロリド(Ru(NH3)6Cl3)、ルテニウム(III)ブロミド(RuBr3)、ルテニウム(III)ブロミド水和物(RuBr3・xH2O)、ルテニウムヨージド(RuI3)、およびルテニウム酢酸塩からなる群から選択される1つ以上の化合物であり、
前記イリジウム前駆体は、イリジウムクロリド水和物(IrCl3・xH2O)およびヘキサクロロイリジウム酸水素六水和物(H2IrCl6・6H2O)からなる群から選択される1種以上の化合物である、
請求項1に記載のスズ酸化物形成用組成物。 - スズハロゲン化化合物と、硫酸イオンと、白金族前駆体と、溶媒と、を含み、
前記白金族前駆体は、ルテニウム前駆体およびイリジウム前駆体を含み、
スズに対する硫酸イオンのモル比(硫酸イオン/スズ)が3~10であり、
前記ルテニウム前駆体は、ルテニウムヘキサフルオリド(RuF6)、ルテニウム(III)クロリド(RuCl3)、ルテニウム(III)クロリド水和物(RuCl3・xH2O)、ルテニウム(III)ニトロシルクロリド(Ru(NO)Cl3)、ヘキサアンミンルテニウム(III)クロリド(Ru(NH3)6Cl3)、ルテニウム(III)ブロミド(RuBr3)、ルテニウム(III)ブロミド水和物(RuBr3・xH2O)、ルテニウムヨージド(RuI3)、およびルテニウム酢酸塩からなる群から選択される1つ以上の化合物であり、
前記イリジウム前駆体は、イリジウムクロリド水和物(IrCl3・xH2O)およびヘキサクロロイリジウム酸水素六水和物(H2IrCl6・6H2O)からなる群から選択される1種以上の化合物である、
スズ酸化物形成用組成物。 - 前記溶媒は、水、アルコール類、およびケトン類からなる群から選択される1つ以上である、請求項1~3のいずれか一項に記載のスズ酸化物形成用組成物。
- 組成物中の硫酸イオンの濃度が0.01~10Mである、請求項1~4のいずれか一項に記載のスズ酸化物形成用組成物。
- 組成物中のスズイオンの濃度が0.01~10Mである、請求項1~5のいずれか一項に記載のスズ酸化物形成用組成物。
- 請求項1~6のいずれか一項に記載のスズ酸化物形成用組成物を480℃以上の温度で焼成するステップ(S1)を含む、スズ酸化物の形成方法。
- 焼成の前に、50~300℃の温度で乾燥するステップ(S0)をさらに含む、請求項7に記載のスズ酸化物の形成方法。
- 前記焼成は30~120分間行う、請求項7または8に記載のスズ酸化物の形成方法。
- 前記焼成の温度は550℃以上である、請求項7~9のいずれか一項に記載のスズ酸化物の形成方法。