JP7389459B2 - ポリアミドイミド溶液の製造方法および増粘ポリアミドイミド - Google Patents
ポリアミドイミド溶液の製造方法および増粘ポリアミドイミド Download PDFInfo
- Publication number
- JP7389459B2 JP7389459B2 JP2019171751A JP2019171751A JP7389459B2 JP 7389459 B2 JP7389459 B2 JP 7389459B2 JP 2019171751 A JP2019171751 A JP 2019171751A JP 2019171751 A JP2019171751 A JP 2019171751A JP 7389459 B2 JP7389459 B2 JP 7389459B2
- Authority
- JP
- Japan
- Prior art keywords
- pai
- solution
- cdi
- viscosity
- imide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
PAI溶液に、PAI質量に対し、0.1質量%以上、10質量%以下のカルボジイミド(CDI)を加えた後、PAIとCDIとを40℃以上で反応させPAIを鎖延長させることを特徴とするPAI溶液の製造方法。
このようなCDIによる増粘効果は、PAI末端のアミノ基やカルボキシル基が、CDIと反応することにより、PAIの鎖延長が起こり、PAIの分子量が増加するためである。 ここで、増粘率としては、元液の溶液粘度に対し、20%以上とすることが好ましく、50%以上がより好ましく、70%以上がさらに好ましい。このような高い増粘率は、特許文献1で開示されたような方法では達成することができない。
このようにして鎖延長された増粘PAI溶液に、メチルアルコール、水、アセトン等のPAIに対する非溶媒を加え、PAIを再沈殿後、濾別、乾燥することにより、固体状のPAI(粉体等)とすることもできる。
攪拌機およびコンデンサ付きフラスコに、MDI(4,4′-ジフェニルメタンジイソシアネート)255.0g(1.02モル)、TMA192.0g(1.00モル)、NMP670gを仕込み、攪拌しながら3時間で温度を150℃に上昇させ、この温度で5時間保温して重合反応を行った後、降温し、100℃となった時点でNMP1485gを加えた。その後冷却することにより、溶液粘度が0.54Pa・sで、固形分濃度が15質量%の光学的に均一なPAI溶液(PAI-L)を得た。この溶液を密閉容器に入れ、30℃で5日保存後の溶液粘度を測定し、保存前の溶液粘度に対する変化率を算出した結果を表1に示した。
攪拌機およびコンデンサ付きフラスコに、PAI-L 200g、CDI(日清紡社製カルボジライトV-05)1gを仕込み、110℃で5時間反応させることにより、光学的に均一なPAI溶液(PAI-1)を得た。この溶液の溶液粘度および保存時の粘度変化率を表1に示した。
CDIの仕込み量を1.5gとしたこと以外は、実施例1と同様に110℃で5時間反応させることにより、光学的に均一なPAI溶液(PAI-2)を得た。この溶液の溶液粘度および保存時の粘度変化率を表1に示した。
CDIの仕込み量を0.5gとしたこと以外は、実施例1と同様に110℃で5時間反応させることにより、光学的に均一なPAI溶液(PAI-3)を得た。この溶液の溶液粘度および保存時の粘度変化率を表1に示した。
TACと、DADEおよびMDAと、を共重合(共重合モル比:DADE/MDA=7/3)して得られるPAI粉体(ソルベイアドバンストポリマーズ株式会社製トーロン4000T-MV、ガラス転移温度280℃)を、NMP30質量部とテトラグライム70質量部とからなる混合溶媒に、80℃で溶解して、PAIの固形分濃度が対PAI溶液比で15質量%の光学的に均一なPAI溶液を得た。このPAI溶液の溶液粘度は、4.71Pa・sであった。この溶液200gにCDI(日清紡社製カルボジライトV-05)0.6gを仕込み50℃で5時間反応させることにより、均一なPAI溶液(PAI-4)を得た。この溶液の溶液粘度および保存時の粘度変化率を表1に示した。
PAIとCDIとの反応温度を30℃としたこと以外は、実施例1と同様して光学的に均一なPAI溶液(PAI-4)を得た。この溶液の溶液粘度および保存時の粘度変化率を表1に示した。
Claims (1)
- ポリアミドイミド(PAI)溶液に、PAI質量に対し、0.1質量%以上、10質量%以下のカルボジイミド(CDI)を加えた後、PAIとCDIとを40℃以上で反応させPAIを鎖延長させることを特徴とするPAI溶液の製造方法。