JP6938112B2 - 光学積層体 - Google Patents
光学積層体 Download PDFInfo
- Publication number
- JP6938112B2 JP6938112B2 JP2016016528A JP2016016528A JP6938112B2 JP 6938112 B2 JP6938112 B2 JP 6938112B2 JP 2016016528 A JP2016016528 A JP 2016016528A JP 2016016528 A JP2016016528 A JP 2016016528A JP 6938112 B2 JP6938112 B2 JP 6938112B2
- Authority
- JP
- Japan
- Prior art keywords
- oxide layer
- optical laminate
- polarizer
- base material
- layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
1つの実施形態においては、上記光学積層体は、上記偏光子の少なくとも一方の側に保護層をさらに有する。
1つの実施形態においては、上記第1の酸化物層の厚みは10nm〜100nmである。
1つの実施形態においては、上記第2の酸化物層の厚みは10nm〜100nmである。
1つの実施形態においては、上記光学積層体は、透湿度が3.0×10−2g/m2/24hr以下である。
1つの実施形態においては、上記光学積層体は、ガスバリア性が1.0×10−7g/m2/24hr〜0.5g/m2/24hrである。
1つの実施形態においては、上記光学積層体は、塩酸または水酸化ナトリウム溶液滴下後の透湿度が1.0×10−1g/m2/24hr未満である。
図1は、本発明の1つの実施形態による光学積層体の概略断面図である。本実施形態の光学積層体100は、偏光子41と基材10と第1の酸化物層20と第2の酸化物層30とをこの順に有する。このような構成を有することにより、本発明の実施形態による光学積層体は、画像表示装置のバリアフィルムおよび偏光板の両方として機能し得る。実用的には、偏光子の少なくとも一方の側には保護層42および/または43が設けられる(図示例では、偏光子41の両側に保護層42および43が設けられている)。この場合、代表的には、偏光子41は偏光板40として基材10に積層され、光学積層体に導入され得る。第1の酸化物層20は、ZnO、AlおよびSiO2を含む。第2の酸化物層30は、SiO2で構成されている。第1の酸化物層20の厚みは、好ましくは10nm〜100nmである。第2の酸化物層30の厚みは、好ましくは10nm〜100nmである。
上記のとおり、偏光子41は、代表的には、偏光板40として基材10に積層され、光学積層体に導入され得る。偏光板40(実質的には保護層42、保護層42が存在しない場合には偏光子41)は、任意の適切な粘着剤層(例えば、アクリル系粘着剤層)または接着剤層(PVA系樹脂接着剤層)を介して基材10に貼り合わせられる。
偏光子41としては、任意の適切な偏光子が採用され得る。例えば、偏光子を形成する樹脂フィルムは、単層の樹脂フィルムであってもよく、二層以上の積層体であってもよい。
保護層42は、偏光子の保護層として使用できる任意の適切なフィルムで形成される。当該フィルムの主成分となる材料の具体例としては、トリアセチルセルロース(TAC)等のセルロース系樹脂や、ポリエステル系、ポリビニルアルコール系、ポリカーボネート系、ポリアミド系、ポリイミド系、ポリエーテルスルホン系、ポリスルホン系、ポリスチレン系、ポリノルボルネン系、ポリオレフィン系、(メタ)アクリル系、アセテート系等の透明樹脂等が挙げられる。また、(メタ)アクリル系、ウレタン系、(メタ)アクリルウレタン系、エポキシ系、シリコーン系等の熱硬化型樹脂または紫外線硬化型樹脂等も挙げられる。この他にも、例えば、シロキサン系ポリマー等のガラス質系ポリマーも挙げられる。また、特開2001−343529号公報(WO01/37007)に記載のポリマーフィルムも使用できる。このフィルムの材料としては、例えば、側鎖に置換または非置換のイミド基を有する熱可塑性樹脂と、側鎖に置換または非置換のフェニル基ならびにニトリル基を有する熱可塑性樹脂を含有する樹脂組成物が使用でき、例えば、イソブテンとN−メチルマレイミドからなる交互共重合体と、アクリロニトリル・スチレン共重合体とを有する樹脂組成物が挙げられる。当該ポリマーフィルムは、例えば、上記樹脂組成物の押出成形物であり得る。
基材10は、好ましくは透明である。基材は、可視光(例えば、波長550nmの光)の全光線透過率が、好ましくは85%以上であり、より好ましくは90%以上であり、さらに好ましくは95%以上である。
第1の酸化物層20は、上記のとおり、ZnO、AlおよびSiO2を含む。第1の酸化物層は、全重量に対して、Alを好ましくは2.5重量%〜3.5重量%、SiO2を好ましくは20.0重量%〜62.4重量%の割合で含む。ZnOは、好ましくは残量である。ZnOをこのような範囲で含有することにより、非晶性、バリア性、屈曲性および耐熱性に優れた層を形成することができる。Alをこのような範囲で含有することにより、第1の酸化物層は代表的にはスパッタリングで形成されるところ、ターゲットの導電率を増大させることができる。SiO2をこのような範囲で含有することにより、異常放電を発生させることなく、かつ、バリア性を損なうことなく、第1の酸化物層の屈折率を小さくすることができる。
第2の酸化物層30は、上記のとおり、SiO2で構成される(不可避の不純物も含まれ得る)。このような第2の酸化物層を第1の酸化物層の表面に形成することにより、第1の酸化物層による良好な特性を維持しつつ、光学積層体の耐薬品性および透明性を格段に向上させることができる。さらに、第2の酸化物層は低屈折率層として機能し得るので、光学積層体に良好な反射防止特性を付与し得る。
本発明の光学積層体は、画像表示装置のバリア層(バリアフィルム)および偏光板の両方の機能を有する光学部材として好適に用いられ得る。より詳細には、本発明の光学積層体は、液晶表示装置および有機EL表示装置、好ましくは有機EL表示装置、より好ましくは屈曲可能な有機EL表示装置の光学部材として用いられ得る。
第1の酸化物層および第2の酸化物層の厚みは、透過型電子顕微鏡(日立製作所製H−7650)を用いて断面を観察し、測定を行なった。光学積層体のその他の構成要素の厚みは膜厚計(Peacock社製デジタルダイアルゲージDG−205)を用いて測定した。
(2)表面粗さRa
JIS B 0601に準じて測定した。測定機には、光学式表面粗さ計(Veeco Metrogy Group社製、商品名「Wyko NT9100」)を用いた。
(3)信頼性
実施例および比較例で得られた光学積層体を50mm×50mmサイズに切り出し、測定試料とした。この測定試料を石英ガラスに貼りあわせ、95℃のオーブンに500時間保管し、保管後の透湿度を測定し、以下の基準で評価した。
○:1.0×10−1g/m2/24hr未満
×:1.0×10−1g/m2/24hr以上
(4)透湿度
実施例および比較例で得られた光学積層体を10cmΦの円状に切り出し、測定試料とした。この測定試料について、テクノロックス社製「DELTAPERM」を用いて、40℃、90%RHの試験条件で透湿度を測定した。
(5)耐薬品性
実施例および比較例で得られた光学積層体を100mm×100mmサイズに切り出し、測定試料とした。2%の水酸化ナトリウム溶液(pH13.7)を測定試料に滴下し、10分後に水酸化ナトリウム溶液を拭き取り、透湿度を測定し、以下の基準で評価した。
○:1.0×10−1g/m2/24hr未満
×:1.0×10−1g/m2/24hr以上
(積層バリアフィルムの作製)
市販のCOPフィルム(日本ゼオン株式会社製、商品名「ゼオノア」、厚み40μm)を基材として、Al、SiO2およびZnOを含むスパッタリングターゲットを用いて、DCマグネトロンスパッタリング法により基材上に第1の酸化物層(厚み30nm)を形成した。次に、S(ターゲットを用いて、基材/第1の酸化物層の積層体の第1の酸化物層上に第2の酸化物層(50nm)を形成した。このようにして、基材/第1の酸化物層(AZO)/第2の酸化物層(SiO2)の構成を有する積層バリアフィルムを作製した。基材のスパッタリングされる面にはコロナ処理によりあらかじめ粗面化処理を施した。当該表面の表面粗さRaは0.51nmであった。
厚み30μmのポリビニルアルコール(PVA)系樹脂フィルム(クラレ製、製品名「PE3000」)の長尺ロールを、ロール延伸機により長手方向に5.9倍になるように長手方向に一軸延伸しながら同時に膨潤、染色、架橋、洗浄処理を施し、最後に乾燥処理を施すことにより厚み12μmの偏光子を作製した。
具体的には、膨潤処理は20℃の純水で処理しながら2.2倍に延伸した。次いで、染色処理は得られる偏光子の単体透過率が45.0%になるようにヨウ素濃度が調整されたヨウ素とヨウ化カリウムの重量比が1:7である30℃の水溶液中において処理しながら1.4倍に延伸した。更に、架橋処理は、2段階の架橋処理を採用し、1段階目の架橋処理は40℃のホウ酸とヨウ化カリウムを溶解した水溶液において処理しながら1.2倍に延伸した。1段階目の架橋処理の水溶液のホウ酸含有量は5.0重量%で、ヨウ化カリウム含有量は3.0重量%とした。2段階目の架橋処理は65℃のホウ酸とヨウ化カリウムを溶解した水溶液において処理しながら1.6倍に延伸した。2段階目の架橋処理の水溶液のホウ酸含有量は4.3重量%で、ヨウ化カリウム含有量は5.0重量%とした。また、洗浄処理は、20℃のヨウ化カリウム水溶液で処理した。洗浄処理の水溶液のヨウ化カリウム含有量は2.6重量%とした。最後に、乾燥処理は70℃で5分間乾燥させて偏光子を得た。
上記偏光子の片側に、ポリビニルアルコール系接着剤を介して、TACフィルムの片面にハードコート処理により形成されたハードコート(HC)層を有するHC−TACフィルム(厚み32μm)を、もう一方の側に、ポリビニルアルコール系接着剤を介して、通常のTACフィルム(厚み25μm)をロールトゥロールにより貼り合わせ、保護層/偏光子/保護層の構成を有する長尺状の偏光板を得た。
上記で得られた偏光板のHC−TAC面と上記で得られた積層バリアフィルムの基材面とを、アクリル系粘着剤を介してロールトゥロールにより貼り合わせ、保護層/偏光子/保護層/基材/第1の酸化物層/第2の酸化物層の構成を有する長尺状の光学積層体を得た。得られた光学積層体を上記(3)〜(5)の評価に供した。結果を表1に示す。
基材の第1の酸化物層側の表面の表面粗さRaを0.66nmとしたこと以外は実施例1と同様にして光学積層体を作製した。得られた光学積層体を実施例1と同様の評価に供した。結果を表1に示す。
基材の第1の酸化物層側の表面の表面粗さRaを0.85nmとしたこと以外は実施例1と同様にして光学積層体を作製した。得られた光学積層体を実施例1と同様の評価に供した。結果を表1に示す。
基材の第1の酸化物層側の表面の表面粗さRaを0.20nmとしたこと以外は実施例1と同様にして光学積層体を作製した。得られた光学積層体を実施例1と同様の評価に供した。結果を表1に示す。
基材の第1の酸化物層側の表面の表面粗さRaを0.28nmとしたこと以外は実施例1と同様にして光学積層体を作製した。得られた光学積層体を実施例1と同様の評価に供した。結果を表1に示す。
表1から明らかなように、バリア層(第1の酸化物層および第2の酸化物層)と基材と偏光子とを有する光学積層体において、基材の第1の酸化物層側の表面の表面粗さを所定値以上とすることにより、優れたバリア性および耐薬品性を維持しつつ、信頼性を顕著に改善することができる。より詳細には、偏光子の加熱収縮に起因するクラックを顕著に抑制することができる。
20 第1の酸化物層
30 第2の酸化物層
40 偏光板
41 偏光子
42 保護層
43 保護層
100 光学積層体
Claims (6)
- 偏光子と、該偏光子の視認側となる側に該偏光子側から順に配置された保護層と、ハードコート層と、基材と、ZnO、AlおよびSiO2を含む第1の酸化物層と、SiO2で構成された第2の酸化物層と、を有し、
該基材の該第1の酸化物層側の表面の表面粗さRaが0.30nm〜50nmである、
光学積層体。 - 前記第1の酸化物層の厚みが10nm〜100nmである、請求項1に記載の光学積層体。
- 前記第2の酸化物層の厚みが10nm〜100nmである、請求項1または2に記載の光学積層体。
- 透湿度が3.0×10−2g/m2/24hr以下である、請求項1から3のいずれかに記載の光学積層体。
- ガスバリア性が1.0×10−7g/m2/24hr〜0.5g/m2/24hrである、請求項4に記載の光学積層体。
- 塩酸または水酸化ナトリウム溶液滴下後の透湿度が1.0×10−1g/m2/24hr未満である、請求項1から5のいずれかに記載の光学積層体。