JP6788150B2 - プレス成形品用粉状液晶性樹脂、プレス成形品及びその製造方法 - Google Patents
プレス成形品用粉状液晶性樹脂、プレス成形品及びその製造方法 Download PDFInfo
- Publication number
- JP6788150B2 JP6788150B2 JP2020524653A JP2020524653A JP6788150B2 JP 6788150 B2 JP6788150 B2 JP 6788150B2 JP 2020524653 A JP2020524653 A JP 2020524653A JP 2020524653 A JP2020524653 A JP 2020524653A JP 6788150 B2 JP6788150 B2 JP 6788150B2
- Authority
- JP
- Japan
- Prior art keywords
- liquid crystal
- press
- crystal resin
- molded product
- particle size
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
[1]嵩密度が0.05g/cm3を超え0.5g/cm3以下である、プレス成形品用粉状液晶性樹脂。
[2]JIS Z8825:2013に定義される粒子径分布の幅が3.0以上12以下である、[1]に記載の粉状液晶性樹脂。
[3]平均粒径が10μm以上300μm以下である、[1]又は[2]に記載の粉状液晶性樹脂。
[4]結晶化度が20%以上70%以下である、[1]から[3]のいずれかに記載の粉状液晶性樹脂。
[5]示差走査熱量計で測定される融点Tm2と融点Tm1のオンセット温度との差ΔTm(Tm2−Tm1オンセット温度)が30℃以上90℃以下である、[1]から[4]のいずれかに記載の粉状液晶性樹脂。
[6]示差走査熱量計で測定される融点Tm2が250℃以上400℃以下である、[1]から[5]のいずれかに記載の粉状液晶性樹脂。
[7]示差走査熱量計で測定される融点Tm2よりも10〜30℃高いシリンダー温度及びせん断速度100sec−1で測定した溶融粘度が、10Pa・s以上1000Pa・s以下である、[1]から[6]のいずれかに記載の粉状液晶性樹脂。
[8]最大粒径と平均粒径との比(最大粒径/平均粒径)が5以下である、[1]から[7]のいずれかに記載の粉状液晶性樹脂。
[9][1]から[8]のいずれかに記載の粉状液晶性樹脂のプレス成形品。
[10][1]から[8]のいずれかに記載の粉状液晶性樹脂を、(示差走査熱量計で測定される融点Tm2−60)℃以上の温度でプレス成形する熱プレス工程を有する、プレス成形品の製造方法。
[11][1]から[8]のいずれかに記載の粉状液晶性樹脂をガラス転移点以下の温度でプレス成形する冷プレス工程と、前記冷プレス工程で得られた成形品を、前記粉状液晶性樹脂の(示差走査熱量計で測定される融点Tm2−60)℃以上の温度でプレス成形する熱プレス工程と、を備える、プレス成形品の製造方法。
本明細書において、「粉状」との用語は、0.1μm〜1000μm程度の平均粒径を有する微粒子で構成されていることをいい、「平均粒径」とは、レーザー回折/散乱式粒度分布測定法による体積基準の算術平均粒子径を意味する。平均粒径は、例えば、株式会社堀場製作所製レーザー回折/散乱式粒度分布測定装置LA−960を用いて測定することができる。「液晶性」とは、光学異方性溶融相を形成し得る性質を有することをいう。異方性溶融相の性質は、直交偏光子を利用した慣用の偏光検査法により確認することができる。より具体的には、異方性溶融相の確認は、Leitz偏光顕微鏡を使用し、Leitzホットステージに載せた溶融試料を窒素雰囲気下で40倍の倍率で観察することにより実施できる。液晶性を有する樹脂は、直交偏光子の間で検査したときに、たとえ溶融静止状態であっても偏光は通常透過し、光学的に異方性を示す。
(1)主として芳香族ヒドロキシカルボン酸及びその誘導体の1種又は2種以上からなるポリエステル;
(2)主として
(a)芳香族ヒドロキシカルボン酸及びその誘導体の1種又は2種以上と、(b)芳香族ジカルボン酸、脂環族ジカルボン酸、及びそれらの誘導体の1種又は2種以上とからなるポリエステル;
(3)主として(a)芳香族ヒドロキシカルボン酸及びその誘導体の1種又は2種以上と、(b)芳香族ジカルボン酸、脂環族ジカルボン酸、及びそれらの誘導体の1種又は2種以上と、(c)芳香族ジオール、脂環族ジオール、脂肪族ジオール、及びそれらの誘導体の1種又は2種以上、とからなるポリエステル;
(4)主として(a)芳香族ヒドロキシカルボン酸及びその誘導体の1種又は2種以上と、(b)芳香族ヒドロキシアミン、芳香族ジアミン、及びそれらの誘導体の1種又は2種以上と、(c)芳香族ジカルボン酸、脂環族ジカルボン酸、及びそれらの誘導体の1種又は2種以上、とからなるポリエステルアミド;
(5)主として(a)芳香族ヒドロキシカルボン酸及びその誘導体の1種又は2種以上と、(b)芳香族ヒドロキシアミン、芳香族ジアミン、及びそれらの誘導体の1種又は2種以上と、(c)芳香族ジカルボン酸、脂環族ジカルボン酸、及びそれらの誘導体の1種又は2種以上と、(d)芳香族ジオール、脂環族ジオール、脂肪族ジオール、及びそれらの誘導体の1種又は2種以上、とからなるポリエステルアミド等、を挙げることができる。さらに上記の構成成分に必要に応じ分子量調整剤を併用してもよい。
粉粒状充填剤としては、カーボンブラック、黒鉛、シリカ、石英粉末、ガラスビーズ、ガラスバルーン、ガラス粉、硅酸カルシウム、ケイ酸アルミニウム、カオリン、クレー、硅藻土、ウォラストナイト等の硅酸塩、酸化鉄、酸化チタン、酸化亜鉛、三酸化アンチモン、アルミナ等の金属の酸化物、炭酸カルシウム、炭酸マグネシウム等の金属の炭酸塩、硫酸カルシウム、硫酸バリウム等の金属の硫酸塩、その他フェライト、炭化ケイ素、窒化ケイ素、窒化硼素、各種金属粉末等が挙げられる。
板状充填剤としては、マイカ、ガラスフレーク、タルク、各種の金属箔等が挙げられる。
これらの無機及び有機充填剤は一種又は二種以上併用することができる。
充填剤の含有量は、液晶性樹脂100質量部に対して、0〜100質量部とすることができる。
また、液晶性樹脂には、その他の成分として、酸化防止剤、熱安定剤、紫外線吸収剤、滑剤、顔料、結晶核剤等の添加剤が配合されていてもよい。
結晶化度の調整は、特に限定されず、例えば、ガラス転移点以上の温度で熱処理することにより調整することができる。
なお、融点Tm2は、JIS K−7121(1999)に基づいた方法により、室温から20℃/分の昇温速度で加熱(1stRUN)した際に観測される吸熱ピークにおけるピークトップの温度(融点Tm1)の測定後、(融点Tm1+40)℃で2分間保持し、次いで20℃/分の降温速度で室温まで冷却し、再度室温から20℃/分の昇温速度で加熱(2ndRUN)した際に観測される2ndRUNの吸熱ピークにおけるピークトップの温度とする。後述する融点Tm1のオンセット温度(ピークの立ち上がり開始温度)は、上記1stRUNの吸熱ピークにおけるオンセットの温度とする。
本実施形態に係るプレス成形品は、上記した粉状液晶性樹脂を用いて形成される。すなわち、プレス成形品は、嵩密度が0.05g/cm3を超え0.5g/cm3以下である粉状液晶性樹脂のプレス成形品である。このプレス成形品は、上記のような所定の嵩密度を有する粉状液晶性樹脂を用いて形成されるので、機械強度が優れている。粉状液晶性樹脂のその他の特徴については上記の通りであるのでここでは記載を省略する。
<第1実施形態>
第1実施形態に係るプレス成形品の製造方法は、粉状液晶性樹脂を(融点−60)℃以上の金型温度でプレス成形する熱プレス工程を有する。
熱プレス工程では、粉状液晶性樹脂を、(示差走査熱量計で測定される融点Tm2−60)℃以上の金型温度でプレス成形する。(融点Tm2−60)℃以上の金型温度にすることで、熱プレス成形時の樹脂の配向性を小さくすることができ、異方性が小さい熱プレス成形品を製造することができる。例えば、粉状液晶性樹脂を投入したプレス成形機の金型温度を(Tm2−30)℃以上(Tm2+30)℃以下、好ましくは(Tm2−10)℃以上(Tm2+15)℃以下として、加圧成形する。この場合の圧力は特に限定されず、所望の厚みに成形できる圧力とすることができる。例えば、0.5MPa以上10MPa以下、好ましくは1MPa以上5MPa以下の圧力とすることができる。
第1実施形態におけるプレス成形品の製造方法において、熱プレス工程の前に、冷プレス工程を有していてもよい。すなわち、第2実施形態に係るプレス成形品の製造方法は、粉状液晶性樹脂をガラス転移点以下の温度でプレス成形する冷プレス工程と、前記冷プレス工程で得られた成形品を、前記粉状液晶性樹脂の(示差走査熱量計で測定される融点Tm2−60)℃以上の金型温度でプレス成形する熱プレス工程と、を有する。
冷プレス工程では、上記所定の平均アスペクト比を有する粉状液晶性樹脂を、粉状液晶性樹脂のガラス転移点(Tg)以下の金型温度でプレス成形(コールドプレス成形)する。冷プレス工程を経て熱プレス成形することでより高機械強度のプレス成形品にすることができる。例えば、粉状液晶性樹脂をプレス成形機の金型内に入れ、0℃以上100℃以下、好ましくは10℃以上40℃以下の金型温度で加圧成形する。この場合の圧力は特に限定されず、所望の厚みに成形できる圧力とすることができる。例えば、1MPa以上30MPa以下、好ましくは5MPa以上20MPa以下の圧力とすることができる。
上記所定の嵩密度を有する粉状液晶性樹脂を粉状液晶性樹脂のガラス転移点(Tg)以下の金型温度でプレス成形して得られる成形品は、内部に在留する空気等のガスが少なく高密度となる。その結果、後述する熱プレス工程で得られるプレス成形品の機械強度をより高めることができる。
熱プレス工程では、冷プレス工程で得られた成形品を、粉状液晶性樹脂の(示差走査熱量計で測定される融点Tm2−60)℃以上の金型温度でプレス成形する。(融点Tm2−60)℃以上の金型温度にすることで、粉状液晶性樹脂が流動して金型の再現性よく成形品を得ることができる。例えば、冷プレス工程に引き続き、プレス成形機の金型温度を(Tm2−30)℃以上(Tm2+30)℃以下、好ましくは(Tm2−10)℃以上(Tm2+15)℃以下として、加圧成形する。この場合の圧力は特に限定されず、所望の厚みに成形できる圧力とすることができる。例えば、0.5MPa以上10MPa以下、好ましくは1MPa以上8.5MPa以下、より好ましくは1MPa以上5MPa以下の圧力とすることができる。
<その他の工程>
上記した第1実施形態及び第2実施形態に係るプレス成形品の製造方法は、プレス成形品用の粉体材料を準備する工程(粉体材料準備工程)等のその他の工程を有していても良い。粉体材料準備工程は、例えば、上記した嵩密度を有する1種以上の液晶性樹脂と、必要に応じて無機充填剤等の添加剤とを、振とうによる混合方法、ボールミル等の粉砕を伴う混合方法、ヘンシェルミキサー等の攪拌翼による混合方法等の従来の方法を用いて混合して混合材料を得る工程とすることができる。
混合材料にする場合の粉状液晶性樹脂の総含有量は、プレス成形用粉体材料中50質量%以上であることが好ましく、70質量%以上であることがより好ましい。上限値は、特に限定されず、例えば、95質量%以下とすることができる。
粉状液晶性樹脂と混合する無機添加剤としては、平均粒径が500nm以下、又は400nm以下の無機微粒子や、平均粒径が1μm以上100μm以下の無機強化材等を挙げることができる。無機添加剤の材質は、特に限定されず、例えば、上記した液晶性樹脂に配合することができる無機充填剤と同様のものを用いることができる。上記平均粒径を有する無機微粒子を用いることで、上記液晶性樹脂微粒子の粉体流動性や分散性を高めることができる。上記平均粒径を有する無機強化材を用いることで、得られるプレス成形品の強度をより高めることができる。なお、平均粒径は、上記と同じ方法で測定することができる。無機添加剤の含有量は、粉体材料中50質量%以下であることが好ましく、30質量%以下であることがより好ましい。
実施例及び比較例で用いた液晶性樹脂LCP1〜4を以下のようにして製造した。
重合容器に下記の原料を仕込んだ後、反応系の温度を140℃に上げ、140℃で1時間反応させた。その後、更に360℃まで5.5時間かけて昇温し、そこから30分かけて5Torr(即ち667Pa)まで減圧して、酢酸、過剰の無水酢酸、及びその他の低沸分を留出させながら溶融重合を行った。撹拌トルクが所定の値に達した後、窒素を導入して減圧状態から常圧を経て加圧状態にして、重合容器の下部からポリマーを排出し、ストランドをペレタイズしてペレットを得た。得られたペレットを、窒素雰囲気下で室温から290℃まで20分かけて昇温し、3時間保持した後、放冷し、LCP1ペレットを得た。
(原料)
4−ヒドロキシ安息香酸(HBA);37g(2モル%)
2−ヒドロキシ−6−ナフトエ酸(HNA);1218g(48モル%)
テレフタル酸(TA);560g(25モル%)
4,4’−ジヒドロキシビフェニル(BP);628g(25モル%)
金属触媒(酢酸カリウム触媒);165mg
アシル化剤(無水酢酸);1432g
重合容器に下記の原料を仕込んだ後、反応系の温度を140℃に上げ、140℃で1時間反応させた。その後、更に340℃まで4.5時間かけて昇温し、そこから15分かけて10Torr(即ち1330Pa)まで減圧して、酢酸、過剰の無水酢酸、及びその他の低沸分を留出させながら重縮合を行った。撹拌トルクが所定の値に達した後、窒素を導入して減圧状態から常圧を経て加圧状態にして、重合容器の下部からポリマーを排出し、ストランドをペレタイズしてLCP2ペレットを得た。
(原料)
4−ヒドロキシ安息香酸(HBA);1380g(60モル%)
2−ヒドロキシ−6−ナフトエ酸(HNA);157g(5モル%)
テレフタル酸(TA);484g(17.5モル%)
4,4’−ジヒドロキシビフェニル(BP);388g(12.5モル%)
4−アセトキシアミノフェノール(APAP);160g(5モル%)
金属触媒(酢酸カリウム触媒);110mg
アシル化剤(無水酢酸);1659g
重合容器に下記の原料を仕込んだ後、反応系の温度を140℃に上げ、140℃で1時間反応させた。その後、更に330℃まで3.5時間かけて昇温し、そこから15分かけて10Torr(即ち1330Pa)まで減圧して、酢酸、過剰の無水酢酸、及びその他の低沸分を留出させながら重縮合を行った。撹拌トルクが所定の値に達した後、窒素を導入して減圧状態から常圧を経て加圧状態にして、重合容器の下部からポリマーを排出し、ストランドをペレタイズしてLCP3ペレットを得た。
(原料)
4−ヒドロキシ安息香酸(HBA);2524g(79.3モル%)
2−ヒドロキシ−6−ナフトエ酸(HNA);867g(20モル%)
テレフタル酸(TA);27g(0.3モル%)
金属触媒(酢酸カリウム触媒);150mg
アシル化剤(無水酢酸);2336g
LCP1をマスコロイダー(増幸産業株式会社製、MKZA10−15JP)を用いて、水温35℃の環境下で湿式粉砕処理した後、スプレードライして粉状液晶性樹脂を得た。この粉状液晶性樹脂の嵩密度、粒子径分布の幅、平均粒径及び最大粒径、結晶化度、融点(Tm2,Tm1オンセット温度)、並びに溶融粘度について、以下に示す方法で測定した。
得られた粉状液晶性樹脂2.8gを使用して、錠剤成形圧縮機(株式会社前川試験機製作所製「TYPE.M.No.30」)を用いて、金型温度23℃、圧力8.5MPaの条件で、半径40mm×厚さ1mmである成形品を作製した(冷プレス工程)。引き続き、熱プレス成形機の金型温度を上昇させ、金型温度355℃、圧力2MPaの条件で、半径40mm×厚さ1mmである成形品を作製した(熱プレス工程)。得られた成形品について、以下に示す方法で落下試験を行った。
LCP1に替えてLCP2を用い、熱プレス工程の温度を表1に記載のように変更した以外は、実施例1と同様にしてプレス成形品を得た。得られた粉状液晶性樹脂及び成形品について、実施例1と同様にして、各種物性を測定した。
冷プレス工程を行わなかった以外は、実施例2と同様にしてプレス成形品を得た。得られた粉状液晶性樹脂及び成形品について、実施例1と同様にして、各種物性を測定した。
LCP3を100質量部に対して、ポリスチレン(PSジャパン株式会社製、「SGP10」、ガラス転移点Tg100℃、溶融粘度27Pa・s(シリンダー温度340℃、せん断速度1000sec−1))を900質量部となるように、株式会社日本製鋼所製二軸押出機「TEX−α」(ノズル開口部の数と各開口部の面積との積300mm2)を用い、シリンダー温度340℃、スクリュー回転数125rpmで溶融混練して組成物を得た。組成物を円形ノズルから、樹脂押出速度10kg/hrで押出ストランドを得て、カットしてペレット化した。この際、ノズル開口部の数nと各開口部の面積Sとの積nS(mm2)と1時間あたりの樹脂押出量Q(kg/hr)との比(nS/Q)は、30であった。
得られた組成物ペレット100gを、2Lフラスコ中で40℃に加熱したトルエン900g中に投入し、30分間攪拌し、ポリスチレンをトルエン中に溶解させた。吸引ろ過により不溶成分を回収し、40℃のトルエン90gでよく追加洗浄した。追加洗浄は3度行った。追加洗浄後の不溶成分を1μmのフィルターでろ過して回収し乾燥して粉状液晶性樹脂を得た。
得られた粉状液晶性樹脂を用い、熱プレス工程の温度を変更した以外は、実施例1と同様にしてプレス成形品を得た。得られた粉状液晶性樹脂及び成形品について、実施例1と同様にして、各種物性を測定した。
LCP2をメッシュミル型粉砕機(株式会社ホーライ製、HA−2542)を用いて凍結粉砕処理して粉状液晶性樹脂を得た。
得られた粉状液晶性樹脂を用い、実施例2と同様にしてプレス成形品を得た。得られた粉状液晶性樹脂及び成形品について、実施例1と同様にして、各種物性を測定した。
粉状液晶性樹脂の嵩密度、粒子径分布の幅、平均粒径及び最大粒径、結晶化度、融点(Tm2,Tm1オンセット温度)、溶融粘度の測定方法、並びにプレス成形品の落下試験の方法は、以下のとおりである。結果を表1に示した。
粉体流動性分析装置(フリーマンテクノロジー社製、「パウダーレオメータFT4」)を用いて、直径50mmの筒状容器に容積85mLの粉状液晶性樹脂を充填し、重量を測定した。その後、直径48mmのVented Pistonを用いて15KPaの圧力で圧縮し、圧縮後の容積で重量を除した値を嵩密度として算出した。
キャピラリー式レオメーター(株式会社東洋精機製作所製キャピログラフ1D:ピストン径10mm)を用いて、以下の条件で、ISO 11443に準拠し、見かけの溶融粘度を測定した。測定には、内径1mm、長さ20mmのオリフィスを用いた。
シリンダー温度:
370℃(LCP1)
350℃(LCP2)
340℃(LCP3)
せん断速度:100sec−1
レーザー回折/散乱式粒度分布測定装置(株式会社堀場製作所製、LA−960)を用い、分散溶媒としてメタノールを用いて、粒子径分布の幅、平均粒径及び最大粒径を測定した。なお、平均粒径は、体積基準の算術平均粒子径である。
X線回折装置(ブルカー社製、D2 PHASER)を用いて、得られる回折情報(広角X線回折図形または広角X線回折プロファイル)から、非晶に由来する散乱領域と結晶に由来する散乱領域とを分け、W.Ruland,Acta Cryst.,14,1180(1961)に記載の方法に準拠し、以下の式(I)により、結晶化度を測定した。
結晶化度(%)=[結晶由来散乱強度/(結晶由来散乱強度+非結晶由来散乱強度)]×100・・・(I)
示差走査熱量計(株式会社日立ハイテクサイエンス製、DSC7000X)を用いて、室温から20℃/分の昇温速度で加熱(1stRUN)した際に観測される吸熱ピークにおけるピークトップの温度(融点Tm1)の測定後、(融点Tm1+40)℃の温度で2分間保持し、次いで20℃/分の降温速度で室温まで冷却し、再度室温から20℃/分の昇温速度で加熱した際に観測される2ndRUNの吸熱ピークにおけるピークトップの温度を融点Tm2として測定した。また、1stRUNの吸熱ピークにおけるオンセットの温度(ピークが立ち上がり始める温度)を融点Tm1オンセット温度として測定した。
動的粘弾性測定装置(ティー・エイ・インスツルメント社製、RSA−III)を用いて、ガラス転移点を測定した。
成形品を50cmの高さから落下させ、以下の基準に従って評価した。
3:成形品が割れなかった。
2:成形品が割れなかったが、ひびがあった。
1:成形品が割れた。
Claims (2)
- 嵩密度が0.05g/cm 3 を超え0.5g/cm 3 以下である、粉状液晶性樹脂を、(示差走査熱量計で測定される融点Tm2−60)℃以上の金型温度でプレス成形する熱プレス工程を有する、プレス成形品の製造方法であって、前記嵩密度は、粉体流動性分析装置を用いて、直径50mmの筒状容器に容積85mLの粉状液晶性樹脂を充填してその重量を測定したのち、直径48mmのVented Pistonを用いて15KPaの圧力で圧縮し、圧縮後の容積で前記重量を除した値である、プレス成形品の製造方法。
- 嵩密度が0.05g/cm 3 を超え0.5g/cm 3 以下である、粉状液晶性樹脂を、ガラス転移点以下の温度でプレス成形する冷プレス工程と、前記冷プレス工程で得られた成形品を、前記粉状液晶性樹脂の(示差走査熱量計で測定される融点Tm2−60)℃以上の金型温度でプレス成形する熱プレス工程と、を有する、プレス成形品の製造方法であって、前記嵩密度は、粉体流動性分析装置を用いて、直径50mmの筒状容器に容積85mLの粉状液晶性樹脂を充填してその重量を測定したのち、直径48mmのVented Pistonを用いて15KPaの圧力で圧縮し、圧縮後の容積で前記重量を除した値である、プレス成形品の製造方法。