JP6750663B2 - 非水電解質二次電池 - Google Patents
非水電解質二次電池 Download PDFInfo
- Publication number
- JP6750663B2 JP6750663B2 JP2018232771A JP2018232771A JP6750663B2 JP 6750663 B2 JP6750663 B2 JP 6750663B2 JP 2018232771 A JP2018232771 A JP 2018232771A JP 2018232771 A JP2018232771 A JP 2018232771A JP 6750663 B2 JP6750663 B2 JP 6750663B2
- Authority
- JP
- Japan
- Prior art keywords
- negative electrode
- active material
- electrode active
- material layer
- particle group
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
負極は負極集電体と、第1空孔率を有する第1負極活物質層と、第2空孔率を有する第2負極活物質層とを含む。負極集電体の表面に第1負極活物質層と第2負極活物質層とがこの順で積層されている。
第1負極活物質層は、第1平均粒径を有する第1黒鉛粒子群を含む。
第2負極活物質層は、第2平均粒径を有する第2黒鉛粒子群と、第3平均粒径を有するセラミック粒子群とを含む。
下記式(1)〜(3):
0.8≦第2平均粒径/第1平均粒径≦1.13 …(1)
第3平均粒径/第2平均粒径≦0.1 …(2)
第2空孔率/第1空孔率>1 …(3)
の関係が満たされている。
図1は本実施形態の非水電解質二次電池の構成の一例を示す概略図である。
電池100はケース80を含む。ケース80は角形である。ケース80は円筒形であってもよい。ケース80は例えば金属製であってもよい。ケース80は例えばアルミラミネートフィルム製のパウチ等であってもよい。ケース80は密閉されている。ケース80は電極群50を収納している。
電極群50は積層型である。電極群50は、正極10と負極20との間にセパレータ30が挟まれつつ、正極10と負極20とが交互にそれぞれ1枚以上積層されることにより形成されている。電極群50には電解液(不図示)が含浸されている。すなわち電池100は正極10と負極20と電解液とを含む。
負極20はシート状の部品である。負極20は負極集電体21と、第1負極活物質層22Aと、第2負極活物質層22Bとを含む。負極集電体21は導電性の電極基材である。負極集電体21は例えば銅(Cu)箔等であってもよい。負極集電体21は例えば5μm以上30μm以下の厚さを有していてもよい。図2のx軸方向において負極集電体21がセパレータ30から突出している部分は外部端子との接続に利用され得る。
負極20では、負極集電体21の表面に第1負極活物質層22Aおよび第2負極活物質層22Bがこの順で積層されている。第1負極活物質層22Aおよび第2負極活物質層22Bは、負極集電体21の片面のみに配置されていてもよい。第1負極活物質層22Aおよび第2負極活物質層22Bは、負極集電体21の表裏両面に配置されていてもよい。
(第1黒鉛粒子群)
第1負極活物質層22Aは第1黒鉛粒子群1を含む。本実施形態の「粒子群」は粒子の集合体を示す。本実施形態の「黒鉛」は黒鉛結晶を含む材料を示す。黒鉛結晶は炭素六角網面が積層された構造を含む。炭素六角網面同士の間隔等は特に限定されるべきではない。したがって本実施形態の第1黒鉛粒子群1〔または第2黒鉛粒子群2(後述)〕は、例えば黒鉛、易黒鉛化性炭素および難黒鉛化性炭素からなる群より選択される少なくとも1種を含んでいてもよい。黒鉛結晶が含まれる限り、無定形炭素等がさらに含まれていてもよい。例えば個々の黒鉛粒子の表面が無定形炭素により被覆されていてもよい。
第1負極活物質層22Aは、例えば酸化珪素粒子群、珪素粒子群等(いずれも不図示)をさらに含んでいてもよい。例えば100質量部の第1黒鉛粒子群1に対して、1質量部以上20質量部以下の酸化珪素粒子群が含まれていてもよい。例えば100質量部の第1黒鉛粒子群1に対して、1質量部以上10質量部以下の酸化珪素粒子群が含まれていてもよい。第1負極活物質層22Aが酸化珪素粒子群をさらに含むことにより、電池容量の増大が期待される。
第2負極活物質層22Bは第2黒鉛粒子群2と、セラミック粒子群3とを含む。第2黒鉛粒子群2は、例えば第1黒鉛粒子群1と実質的に同一材料であってもよい。これによりサイクル特性の向上が期待される。第1負極活物質層22Aおよび第2負極活物質層22Bの全体において負極活物質の反応性が略均一になるためと考えられる。第2黒鉛粒子群2は、例えば第1黒鉛粒子群1と異なる材料であってもよい。
セラミック粒子群3は第2負極活物質層22B内に空孔を形成し得る。圧縮時、第2負極活物質層22Bに硬いセラミック粒子群3が含まれていることにより、粒子間の隙間が潰され難くなるためと考えられる。例えば100質量部の第2黒鉛粒子群2に対して、4質量部以上10質量部以下のセラミック粒子群3が含まれていてもよい。セラミック粒子群3は、例えばアルミナ、ベーマイトおよびジルコニアからなる群より選択される少なくとも1種を含んでいてもよい。
第1負極活物質層22Aおよび第2負極活物質層22Bの各々は、上記の成分に加えて、例えばバインダ等をさらに含んでいてもよい。例えば100質量部の第1黒鉛粒子群1(または第2黒鉛粒子群2)に対して、例えば0.1質量部以上10質量部以下のバインダが含まれていてもよい。バインダは特に限定されるべきではない。バインダは例えばカルボキシメチルセルロース(CMC)、スチレンブタジエンゴム(SBR)およびポリアクリル酸(PAA)からなる群より選択される少なくとも1種を含んでいてもよい。
第1黒鉛粒子群1は第1平均粒径(以下「d1」とも記される)を有する。
第2黒鉛粒子群2は第2平均粒径(以下「d2」とも記される)を有する。
セラミック粒子群3は第3平均粒径(以下「d3」とも記される)を有する。
0.8≦d2/d1≦1.13 …(1)
の関係を満たしている。
d3/d2≦0.1 …(2)
の関係を満たしている。
第1負極活物質層22Aは第1空孔率(以下「p1」とも記される)を有する。
第2負極活物質層22Bは第2空孔率(以下「p2」とも記される)を有する。
空孔率=B/(A+B)
により、各層の空孔率が算出される。
p2/p1>1 …(3)
の関係を満たしている。
第1負極活物質層22Aは第1厚さ(以下「t1」とも記される)を有する。
第2負極活物質層22Bは第2厚さ(以下「t2」とも記される)を有する。
0.1<t2/t1<0.5 …(4)
の関係を満たしていてもよい。
正極10はシート状の部品である。正極10は正極集電体11と正極活物質層12とを含む。正極集電体11は導電性の電極基材である。正極集電体11は例えばアルミニウム(Al)箔等であってもよい。正極集電体11は例えば5μm以上30μm以下の厚さを有していてもよい。図2のx軸方向において正極集電体11がセパレータ30から突出している部分は外部端子との接続に利用され得る。
電解液は溶媒および支持塩を含む。電解液は、溶媒および支持塩に加えて、各種の添加剤(被膜形成剤、ガス発生剤、難燃剤等)をさらに含んでいてもよい。
セパレータ30は正極10および負極20の間に配置されている。セパレータ30は例えばポリオレフィン製の多孔質膜を含んでいてもよい。セパレータ30は例えば5μm以上50μm以下の厚さを有していてもよい。
《実施例1》
1.正極の製造
以下の材料が準備された。
正極活物質:NCA(LiNi0.82Co0.15Al0.03O2)
導電材:AB
バインダ:PVDF
正極集電体:Al箔(厚さ=15μm)
以下の材料が準備された。
第1黒鉛粒子群(第1平均粒径=15μm)
第2黒鉛粒子群(第2平均粒径=15μm)
セラミック粒子群(第3平均粒径=1.5μm)
バインダ:CMC/SBR=1/1
負極集電体:Cu箔(厚さ=10μm)
セパレータ30が準備された。セパレータ30は3層構造(PP層/PE層/PP層)を有する。正極10と負極20とが交互に積層されることにより、電極群50が形成された。正極10と負極20の各間にはセパレータ30がそれぞれ配置された。
溶媒:EC、EMCおよびDMCの混合物
電池100が2枚のステンレス板の間に挟み込まれた。電池100に1MPaの圧力が加わるように、2枚のステンレス板が固定された。
下記表1に示されるように、第2黒鉛粒子群の比率、セラミック粒子群の比率および第2厚さが変更されることを除いては、実施例1と同様に電池が製造され、電池のエージングが実施された。なお第2黒鉛粒子群およびセラミック粒子群の合計は一定(98質量%)である。
下記表1に示されるように、第2平均粒径および第3平均粒径が変更されることを除いては、実施例1と同様に電池が製造され、電池のエージングが実施された。
下記表1に示されるように、第2平均粒径および第2厚さが変更されることを除いては、実施例1と同様に電池が製造され、電池のエージングが実施された。
下記表1に示されるように、セラミック粒子群の材種および第2厚さが変更されることを除いては、実施例1と同様に電池が製造され、電池のエージングが実施された。
下記表1に示されるように、セラミック粒子群の材種が変更されることを除いては、実施例1と同様に電池が製造され、電池のエージングが実施された。
第1黒鉛粒子群の一部(5質量%)が酸化珪素粒子群で置換されることを除いては、実施例1と同様に電池が製造され、電池のエージングが実施された。
下記表1に示されるように単層構造の負極が製造された。比較例1の単層構造は第1負極活物質層のみからなる。第1厚さは111μmである。これらを除いては実施例1と同様に電池が製造され、電池のエージングが実施された。
下記表1に示されるように、第2平均粒径が変更され、かつセラミック粒子群が使用されないことを除いては、実施例1と同様に電池が製造され、電池のエージングが実施された。
下記表1に示されるように、セラミック粒子群が使用されないことを除いては、実施例1と同様に電池が製造され、電池のエージングが実施された。
《入力特性》
電池のSOC(state of charge)が50%に調整された。25℃の温度環境において、1Cの電流により電池が10秒間充電された。充電開始から10秒後の電圧上昇量が測定された。電圧上昇量が充電電流(1C)で除されることにより電池抵抗が算出された。結果は下記表2に示される。下記表2中「入力特性」の欄に示される値は、比較例1の電池抵抗を100とする相対値である。値が小さい程、入力特性が向上していると考えられる。
25℃の温度環境において、充放電が100サイクル繰り返された。1サイクルは以下の充電と放電との一巡を示す。
放電:CC方式、CC電流=1C、カットオフ電圧=2.5V
25℃の温度環境において、電池のSOCが100%に調整された。60℃の温度環境において電池が10日間保存された。保存前後で放電容量が測定された。放電容量の測定条件は以下のとおりである。
放電:CC方式、CC電流=0.2C、カットオフ電圧=2.5V
《比較例1〜3》
比較例2は比較例1に比して入力特性が向上している。比較例2では、表層に平均粒径が相対的に小さい黒鉛粒子群が配置されている。そのため電解液と黒鉛粒子群との反応面積が大きくなっていると考えられる。しかし比較例2では保存特性が低下している。保存時に、電解液と黒鉛粒子群との副反応が起こりやすいためと考えられる。
実施例1〜9は比較例1に比して入力特性が向上している。実施例1〜9では、保存特性の低下が抑制されている。実施例1〜9では下記式(1)〜(3):
0.8≦d2/d1≦1.13 …(1)
d3/d2≦0.1 …(2)
p2/p1>1 …(3)
の関係が満たされている。
実施例1〜4では、「p2/p1」が大きくなる程、入力特性が向上する傾向がみられる。
実施例5は実施例1に比して保存特性が若干低下している。実施例5は実施例1に比して入力特性が若干向上している。第2平均粒径が若干小さいためと考えられる。
実施例7、8では、アルミナに代えて、ベーマイトおよびジルコニアがセラミック粒子群として使用されている。実施例7、8は実施例1と略同等の特性を示している。したがってセラミック粒子群は、例えばアルミナ、ベーマイトおよびジルコニアからなる群より選択される少なくとも1種を含んでいてもよいと考えられる。
実施例9では、第1黒鉛粒子群の一部が酸化珪素粒子群に置換されている。実施例9の構成では、電池容量の増大が期待される。実施例9の入力特性、サイクル特性および保存特性はいずれも良好である。
Claims (1)
- 正極と負極と電解液とを含み、
前記負極は負極集電体と、第1空孔率を有する第1負極活物質層と、第2空孔率を有する第2負極活物質層とを含み、
前記負極集電体の表面に前記第1負極活物質層と前記第2負極活物質層とがこの順で積層されており、
前記第1負極活物質層は、第1平均粒径を有する第1黒鉛粒子群を含み、
前記第2負極活物質層は、第2平均粒径を有する第2黒鉛粒子群と、第3平均粒径を有するセラミック粒子群とを含み、
下記式(1)〜(3):
0.8≦第2平均粒径/第1平均粒径≦1.13 …(1)
第3平均粒径/第2平均粒径≦0.1 …(2)
第2空孔率/第1空孔率>1 …(3)
の関係が満たされている、
非水電解質二次電池。