JP6634543B2 - 蓄電デバイス用セパレータ及びその製造方法、並びに蓄電デバイス及びその製造方法 - Google Patents
蓄電デバイス用セパレータ及びその製造方法、並びに蓄電デバイス及びその製造方法 Download PDFInfo
- Publication number
- JP6634543B2 JP6634543B2 JP2019532159A JP2019532159A JP6634543B2 JP 6634543 B2 JP6634543 B2 JP 6634543B2 JP 2019532159 A JP2019532159 A JP 2019532159A JP 2019532159 A JP2019532159 A JP 2019532159A JP 6634543 B2 JP6634543 B2 JP 6634543B2
- Authority
- JP
- Japan
- Prior art keywords
- storage device
- separator
- mass
- ionic compound
- power storage
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
[1]
ポリオレフィン樹脂と表面処理されたイオン性化合物とを含有する多孔質層を有し、前記多孔質層中の前記イオン性化合物の含有量が5質量%以上99質量%以下であって、前記イオン性化合物の表面親水性度が0.10以上0.80以下であることを特徴とする蓄電デバイス用セパレータ。
[2]
ポリオレフィン樹脂と表面処理されたイオン性化合物とを含有する多孔質層を有し、前記多孔質層中の前記イオン性化合物の含有量が5質量%以上99質量%以下であって、前記イオン性化合物の350℃及び550℃の重量減少量比が0.03以上0.70以下であることを特徴とする蓄電デバイス用セパレータ。
[3]
前記多孔質層中の前記イオン性化合物の含有量が5質量%以上50質量%未満である、[1]又は[2]に記載の蓄電デバイス用セパレータ。
[4]
前記多孔質層中の前記イオン性化合物の含有量が86質量%以上99質量%以下である、[1]又は[2]に記載の蓄電デバイス用セパレータ。
[5]
前記イオン性化合物は、飽和脂肪酸、不飽和脂肪酸、飽和脂肪酸塩、及び不飽和脂肪酸塩からなる群より選ばれる一種以上で表面処理されている、[1]〜[4]のいずれか1項に記載の蓄電デバイス用セパレータ。
[6]
前記イオン性化合物の表面処理量は、表面処理されたイオン性化合物を100質量%とした場合に0.1質量%以上10質量%以下である、[1]〜[5]のいずれか1項に記載の蓄電デバイス用セパレータ。
[7]
前記イオン性化合物は、硫酸イオン、硝酸イオン、リン酸イオン、及びハロゲン化物イオンから成る群から選ばれる1種以上のアニオンを有する、[1]〜[6]のいずれか1項に記載の蓄電デバイス用セパレータ。
[8]
前記イオン性化合物は、アルカリ金属イオン及びアルカリ土類金属イオンから成る群から選ばれる1種以上のカチオンを有する、[1]〜[7]のいずれか1項に記載の蓄電デバイス用セパレータ。
[9]
前記イオン性化合物は、硫酸バリウムである、[1]〜[8]のいずれか1項に記載の蓄電デバイス用セパレータ。
[10]
前記イオン性化合物の平均粒径が、5nm以上600nm以下である、[1]〜[9]のいずれか1項に記載の蓄電デバイス用セパレータ。
[11]
前記ポリオレフィン樹脂は、粘度平均分子量が600,000以上のポリエチレンを含有する、[1]〜[10]のいずれか1項に記載の蓄電デバイス用セパレータ。
[12]
平均孔径が10nm以上150nm以下である、[1]〜[11]のいずれか1項に記載の蓄電デバイス用セパレータ。
[13]
透気度が10秒/100ml以上500秒/100mL以下である、[1]〜[12]のいずれか1項に記載の蓄電デバイス用セパレータ。
[14]
突刺強度が100gf以上600gf以下である、[1]〜[13]のいずれか1項に記載の蓄電デバイス用セパレータ。
[15]
赤外線(IR)吸光度比A1700~1800/A2700が0.01以上0.25以下である可塑剤と、ポリオレフィン樹脂と、イオン性化合物とを含有する混練物から、前記可塑剤を抽出することを特徴とする蓄電デバイス用セパレータの製造方法。
[16]
機械方向(MD)に4倍以上15倍以下、幅方向(TD)に4倍以上15倍以下の延伸を前記混練物のシート状成形体に行う、[15]に記載の蓄電デバイス用セパレータの製造方法。
[17]
前記混練物のシート状成形体をMD及びTDに同時に延伸する工程を含む、[15]又は[16]に記載の蓄電デバイス用セパレータの製造方法。
[18]
正極と、負極と、[1]〜[14]のいずれか1項に記載の蓄電デバイス用セパレータ、又は[15]〜[17]のいずれか1項に記載の方法で製造された蓄電デバイス用セパレータとを備える蓄電デバイス。
[19]
以下の工程:
(1)正極と負極を、[1]〜[14]のいずれか1項に記載の蓄電デバイス用セパレータ、又は[15]〜[17]のいずれか1項に記載の方法で製造された蓄電デバイス用セパレータを介して重ね合せて外装体に装填する工程;及び
(2)非水電解液を前記外装体に注入して、前記外装体を封止する工程;
を含む蓄電デバイスの製造方法。
本実施形態に係る蓄電デバイス用セパレータは、ポリオレフィン樹脂と表面処理されたイオン性化合物とを含有する多孔質層を有する。多孔質層は、ポリオレフィン樹脂とイオン性化合物を併用し、イオン性化合物に特定の表面処理を施すことで、蓄電デバイス用セパレータのイオン透過性及び耐熱性を高め、ひいては蓄電デバイスの入出力特性及び安全性の向上に資する。
本実施形態に係る蓄電デバイス用セパレータは、ポリオレフィン樹脂を含有する多孔質層を有する。本実施形態において用いられるポリオレフィン樹脂とは、通常の押出、射出、インフレーション、及びブロー成形などに使用されるポリオレフィン樹脂であって、オレフィン炭化水素をモノマー成分として含むポリマーであり、例えば、エチレン、プロピレン、1−ブテン、2−ブテン、4−メチル−1−ペンテン、1−ヘキセン、及び1−オクテンなどのホモ重合体、共重合体、及び多段重合体である。また、これらのホモ重合体、共重合体、及び多段重合体から成る群から選ばれた少なくとも1つのポリオレフィンを単独で、又は混合して使用することもできる。
ポリエチレンについては、次式によりMvを算出できる。
[η]=6.77×10-4Mv0.67
ポリプロピレンについては、次式によりMvを算出できる。
[η]=1.10×10-4Mv0.80
本実施形態に係る蓄電デバイス用セパレータは、イオン性化合物を含有する。本実施形態において用いられるイオン性化合物とは、一つ以上のカチオン及び一つ以上のアニオンの組み合わせからなり、イオン結合性の高い化学結合に基づき、電気的に中性である化合物を指す。
また、イオン性化合物のカチオンは、蓄電デバイス内部での安定性及びコストの両面を考慮すると、好ましくはアルカリ金属イオン及び/又はアルカリ土類金属イオンであって、より好ましくはリチウムイオン、ナトリウムイオン、カリウムイオン、マグネシウムイオン、カルシウムイオン、ストロンチウムイオン、及びバリウムイオンから成る群から選ばれる一種以上であり、更に好ましくは、マグネシウムイオン、カルシウムイオン、及びバリウムイオンから成る群から選ばれる一種以上であって、特にバリウムイオンが好ましい。すなわち、イオン性化合物としては、蓄電デバイス内部での安定性を考慮すると、硫酸バリウムが最も好ましい。また、イオン性化合物は、1種を単独で用いてもよく、2種以上を併用してもよい。
また、この割合は、99質量%以下、より好ましくは98質量%以下、更に好ましくは97質量%以下である。イオン性化合物の割合が99質量%以下である場合、多孔質層の形成が容易になる上に、多孔質層に物理的強度を付与することができる。一方で、物理的強度を更に高める観点からは、50質量%未満が好ましく、45質量%以下がより好ましく、40質量%以下が更に好ましい。
蓄電デバイス用セパレータとは、蓄電デバイスの正極と負極の間に配置される電子絶縁性の隔膜であって、非常に小さな孔が多数集まって緻密な連通孔を形成した多孔構造を有しているため、電解液を含浸することでイオン伝導性を発現することができる。本実施形態の方法によって製造された蓄電デバイス用セパレータは、単独でも蓄電デバイスのセパレータとして十分に機能するが、必要に応じて、無機材料及び/又は有機材料を塗布して積層膜としてもよい。本実施形態の蓄電デバイスセパレータは、イオン伝導性及び耐熱性が高く、金属不純物量が少ないため、蓄電デバイスの入出力特性及び安全性を向上させることができる。
この場合、多孔膜の平均孔径d(μm)と曲路率τa(無次元)は、空気の透過速度定数Rgas(m3/(m2・秒・Pa))、水の透過速度定数Rliq(m3/(m2・秒・Pa))、空気の分子速度ν(m/秒)、水の粘度η(Pa・秒)、標準圧力Ps(=101325Pa)、気孔率ε(%)、膜厚L(μm)から、次式を用いて求めた。
d=2ν×(Rliq/Rgas)×(16η/3Ps)×106
τa=(d×(ε/100)×ν/(3L×Ps×Rgas))1/2
ここで、Rgasは透気度(秒)から次式を用いて求めた。
Rgas=0.0001/(透気度×(6.424×10-4)×(0.01276×101325))
また、Rliqは透水度(cm3/(cm2・秒・Pa))から次式を用いて求めた。
Rliq=透水度/100
なお、透水度は次のように求めた。直径41mmのステンレス製の透液セルに、あらかじめエタノールに浸しておいたセパレータをセットし、該セパレータのエタノールを水で洗浄した後、約50000Paの差圧で水を透過させ、120秒間の透水量(cm3)より、単位時間・単位圧力・単位面積当たりの透水量を計算し、これを透水度とした。
また、νは気体定数R(=8.314J/(K・mol))、絶対温度T(K)、円周率π、空気の平均分子量M(=2.896×10-2kg/mol)から次式を用いて求めた。
ν=((8R×T)/(π×M))1/2
《蓄電デバイス用セパレータの製造方法》
本実施形態に係る蓄電デバイス用セパレータの製造方法では、赤外線(IR)吸光度比A1700~1800/A2700が0.01以上0.25以下である可塑剤と、ポリオレフィン樹脂と、イオン性化合物とを含有する混練物から可塑剤を抽出する。このような混練物からの可塑剤の抽出は、製造設備からの金属溶出を抑制し、蓄電デバイス用セパレータに混入する金属不純物量を少なくして、蓄電デバイスの安全性を向上することができる。また、市販されている可塑剤を利用して、セパレータの製造容易性を向上させることもできる。可塑剤の抽出により形成された微多孔は、非水電解液が含浸されたセパレータがイオン伝導性を発現することに寄与する。
(1)ポリオレフィン樹脂、イオン性化合物、及び可塑剤を溶融混練して混練物を得る工程、
(2)混練物を移送し、シート状に成形した後、冷却固化する工程、
(3)シート状成形体を面倍率20倍以上200倍未満で、少なくとも一軸方向に延伸する工程、並びに
(4)延伸工程の後に、シート状成形体から可塑剤を抽出する工程
を含んでよい。
A1700~1800は、可塑剤の透過IRスペクトルの1700〜1800cm-1の範囲内での吸光度の最大値と定義する。分解能を向上させる観点から、2700cm-1の吸光度は、0.5以上1.0以下になるように測定条件を調整して、可塑剤の透過IRスペクトルを測定することが望ましい。なお、透過IRスペクトルは、一般的なフーリエ変換赤外分光光度計を用いて容易に測定することができる。
本実施形態の蓄電デバイスは、正極と、負極と、本実施形態の方法によって製造された蓄電デバイス用セパレータとを備える。蓄電デバイスとしては、具体的には、リチウム二次電池、リチウムイオン二次電池、ナトリウム二次電池、ナトリウムイオン二次電池、マグネシウム二次電池、マグネシウムイオン二次電池、カルシウム二次電池、カルシウムイオン二次電池、アルミニウム二次電池、アルミニウムイオン二次電池、ニッケル水素電池、ニッケルカドミウム電池、電気二重層キャパシタ、リチウムイオンキャパシタ、レドックスフロー電池、リチウム硫黄電池、リチウム空気電池、亜鉛空気電池などが挙げられる。上記の中でも、実用性の観点から、リチウム二次電池、リチウムイオン二次電池、ニッケル水素電池、又はリチウムイオンキャパシタが好ましく、より好ましくはリチウムイオン二次電池である。
(1)正極と負極を、上記の蓄電デバイス用セパレータを介して重ね合せて外装体に装填する工程;及び
(2)非水電解液を前記外装体に注入して、外装体を封止する工程;
を含む方法により、製造することができる。
具体的には、上述の正極と負極とを、セパレータを介して重ね合わせて、必要に応じて捲回して、積層電極体又は捲回電極体とした後、これを外装体に装填し、正負極と外装体の正負極端子とをリード体などを介して接続し、さらに、環状カーボネート及び/又は鎖状カーボネートなどの非水溶媒とリチウム塩などの電解質を含有する非水電解液を外装体内に注入した後に外装体を封止して作製することができる。蓄電デバイスの外装体としては、特に限定されないが、金属製の缶容器、又は金属箔ラミネートフィルムから成るラミネート容器などを好適に用いることができる。なお、蓄電デバイスの形状としては、特に限定されず、一例を挙げると、円筒形、角型、コイン型、扁平形、シート状などの形状が採用される。
正極は、正極活物質に、アセチレンブラックなどの導電助剤、ポリフッ化ビニリデンなどの結着剤を適量加えて、正極合剤を調製し、これをアルミニウム箔などの集電材料に塗布乾燥後に加圧することで、集電材料上に正極合剤層を固着させて作製される。ただし、正極の作製方法は、上記例示の方法に限定されない。
負極は、負極活物質に、カルボキシメチルセルロースなどの増粘剤、スチレンブタジエンゴムなどの結着剤を適量加えて、負極合剤を調製し、これを銅箔などの集電材料に塗布乾燥後に加圧することで、集電材料上に負極合剤層を固着させて作製することができる。ただし、負極の作製方法は、上記例示の方法に限定されない。
微小測厚器(東洋精機社製,タイプKBM)を用いて、試料の膜厚を室温23℃で測定した。
10cm×10cm角の試料をセパレータから切り取り、その体積(cm3)と質量(g)を求め、それらと膜密度(g/cm3)より、次式を用いて気孔率を計算した。
気孔率(%)=(体積−質量/膜密度)/体積×100
なお、膜密度は、用いたポリオレフィン樹脂とイオン性化合物の各々の密度と混合比より計算で求められる値を用いた。
JIS P−8117準拠のガーレー式透気度計(東洋精機社製)にて、試料の透気度を測定した。
ハンディー圧縮試験器「KES−G5」(カトーテック社製)を用いて、開口部の直径11.3mmの試料ホルダーでセパレータを固定した。固定されたセパレータの中央部に対して、針先端の曲率半径0.5mm、突刺速度2mm/秒の条件下で、25℃雰囲気下にて突刺試験を行うことにより、最大突刺荷重として突刺強度(gf)を測定した。
後述の実施例及び比較例に記載の方法で作製された混練物よりブリードしてきた可塑剤の透過IRスペクトルを、フーリエ変換赤外分光光度計「670FTIR」(アジレント・テクノロジー社製)を用いて測定した。得られた透過IRスペクトルの1700〜1800cm-1の範囲内での吸光度の最大値をA1700~1800、2700cm-1での吸光度をA2700として、A1700~1800をA2700で除することでIR吸光度比A1700~1800/A2700を算出した。
後述の実施例及び比較例に記載の方法で作製された混練物を50g測り取り、セパレータの製造設備を模擬した試験片(炭素鋼,幅:10mm,長さ:50mm,厚み:5mm)を混練物で包み込み、PFAボトルに封入した。200℃に設定した恒温槽「PLM−73S」(二葉科学社製)にて、PFAボトルを1週間保管した。1週間後に試験片を取り出して、試験片の表面を顕微鏡で観察し、金属が溶け出して形成された穴の個数をカウントした。具体的には、試験片の任意の1mm2中に形成された穴が0個のときは○(良好)、1〜9個のときは△(許容)、10個以上のときは×(不良)として評価した。
《正極シートの作製》
正極活物質としてLiNi1/3Mn1/3Co1/3O2(日本化学工業社製)と、導電助剤としてアセチレンブラック粉末(電気化学工業社製)と、結着剤としてポリフッ化ビニリデン溶液(クレハ社製)とを、90:6:4の固形分質量比で混合し、分散溶媒としてN−メチル−2−ピロリドンを固形分40質量%となるように添加し、更に混合して、スラリー状の溶液を調製した。このスラリー状の溶液を、厚さ20μmの集電材料としてのアルミニウム箔の両面に塗布し、溶剤を乾燥除去し、その後、塗布されたアルミニウム箔をロールプレスで圧延して、正極シートを得た。
負極活物質としてグラファイト粉末(大阪ガスケミカル社製)と、結着剤としてスチレンブタジエンゴム及びカルボキシメチルセルロース水溶液とを、100:1.5:1.8の固形分質量比で混合し、分散溶媒として水を固形分45質量%となるように添加し、更に混合して、スラリー状の溶液を調製した。このスラリー状の溶液を、厚さ18μmの集電材料としての銅箔の両面に塗布し、溶剤を乾燥除去し、その後、塗布された銅箔をロールプレスで圧延して、負極シートを得た。
非水溶媒としてのエチレンカーボネートとエチルメチルカーボネートとを体積比1:2で混合した混合溶媒に、LiPF6を1mol/L含有させた溶液を調製した。
上述のようにして作製した正極シートと負極シートとを、後述の実施例及び比較例で得られたセパレータの両側に重ね合わせて積層体を得た。得られた積層体を、アルミニウム箔(厚さ40μm)の両面を樹脂層で被覆したアルミラミネートフィルムから成る袋(外装体)内に正負極の端子を突設させながら挿入した。その後、上述のようにして作製した非水電解液を袋内に注入し、袋に真空封止を行うことによって、パウチ型リチウムイオン二次電池を作製した。
パウチ型リチウムイオン二次電池を、25℃に設定した恒温槽「PLM−73S」(二葉科学社製)に収容し、充放電装置「ACD−01」(アスカ電子社製)に接続した。次いで、その二次電池を、0.1Cの定電流で4.2Vの電圧に達するまで充電して、4.2Vの定電圧で1時間充電した、その後、0.1Cの定電流で3.0Vまで放電するという充放電サイクルを、3回繰り返した。その後、0.1Cの定電流で4.2Vの電圧に達するまで充電して、リチウムイオン二次電池を満充電の状態とした。なお、1Cとは、電池の全容量を1時間で放電させる場合の電流値を表し、0.1Cとは、その1/10の電流値を表す。
初充放電後のパウチ型リチウムイオン二次電池を、25℃に設定した恒温槽「PLM−73S」(二葉科学社製)に収容し、充放電装置「ACD−01」(アスカ電子社製)に接続した。次いで、その二次電池を、1/3Cの定電流で4.2Vの電圧に達するまで充電後、4.2Vの定電圧で1時間充電し、1Cの定電流で3.0Vまで放電した。その後、1/3Cの定電流で4.2Vの電圧に達するまで充電後、4.2Vの定電圧で1時間充電し、20Cの定電流で3.0Vまで放電した。上記一連の充放電の結果から、20C容量維持率(%)を、以下の式によって算出した。
20C容量維持率(%)=20C放電容量/1C放電容量×100
20C放電試験後のパウチ型リチウムイオン二次電池を、50℃に設定した恒温槽「PLM−73S」(二葉科学社製)に収容し、充放電装置「ACD−01」(アスカ電子社製)に接続した。次いで、その二次電池を、1Cの定電流で4.2Vの電圧に達するまで充電後、4.2Vの定電圧で1時間充電し、1Cの定電流で3.0Vまで放電した。上記一連の充放電を1サイクルとして、これを100サイクル実施し、100サイクル後の容量維持率(%)を測定した。なお、100サイクル後容量維持率(%)は、以下の式で求めた。
100サイクル後容量維持率(%)=100サイクル目の放電容量/1サイクル目の放電容量×100
イオン性化合物をガラス管に0.5g量り取り、0.001mmHg以下の圧力下、150℃で18時間真空脱気を行った。次に、多検体高性能比表面積・細孔分布測定装置「3Flex」(Micromeritics社製)にて、JIS Z 8830:2013に準じて、吸着質として窒素又は水蒸気を用いて、イオン性化合物の比表面積を測定した。吸着質として水蒸気を使用したときに得られた比表面積(SWater)を、吸着質として窒素を使用したときに得られた比表面積(SNitrogen)で除することで、イオン性化合物の表面親水性度(SWater/SNitrogen)を算出した。
示差熱熱重量同時測定装置「TG/DTA6200」(日立ハイテクサイエンス社製)にて、窒素雰囲気下で室温(23℃)から600℃まで10℃/分の速度で、イオン性化合物を昇温し、350℃及び550℃の重量減少量を計測した。次いで、350℃での重量減少量を、550℃での重量減少量で除することで、重量減少量比を算出した。
セパレータを一辺100mmの正方形状に切り出し、予め150℃に熱してある熱風乾燥機にサンプルを入れ、1時間後の寸法収縮率(%)を求めた。サンプルは、乾燥機の内壁等に付着しないよう、またサンプル同士が融着しないようコピー紙等の上に乗せた。
《イオン性化合物の表面処理》
200mLの水に、50gの硫酸バリウム(平均粒径50nm)を投入し、撹拌しながら70℃に温度調整した。硫酸バリウムの8質量%に相当するステアリン酸を含有する、2−イソプロパノール溶液を少しずつ添加して、70℃で30分間撹拌した。次いで、ステアリン酸の1/2の物質量に相当する水酸化バリウムを含有する水溶液を少しずつ滴下して、30分間撹拌した。その後、固体を濾別して乾燥した後に、粉砕して微粉化することで、表面処理された硫酸バリウム粉末を得た。得られた粉体の表面親水性度及び重量減少量比を測定した結果を表1に示す。
《セパレータの製造》
粘度平均分子量70万の高密度ポリエチレン(UH650,旭化成社製)と、上述のようにして作製した硫酸バリウム粉末と、可塑剤として40℃の動粘度が70.6cStである流動パラフィンと、及び酸化防止剤としてテトラキス−[メチレン−(3’,5’−ジ−t−ブチル−4’−ヒドロキシフェニル)プロピオネート]メタンとを表1に示す割合で混合し、ラボプラストミル(東洋精機社製)を用いて200℃で混練した。
なお、混練物からブリードしてきた可塑剤のIRスペクトルを測定した。得られたIRスペクトルを図1に示し、IR吸光度比を表1に示す。また、混練物を用いて実施した金属溶出量の評価結果を表1に示す。
次に、混練物を150℃で10MPaの圧力でプレスして成形した後に、25℃で冷却して、厚さ1mmの原反シートを作製した。原反シートを同時二軸延伸機にセットして、120℃環境下で7×7倍に同時二軸延伸した。次いで、延伸された原反シートを取り出し、塩化メチレンに浸漬して可塑剤を抽出して、セパレータを得た。得られたセパレータの評価結果を表1に示す。
実施例1で用いたステアリン酸に代えて、オレイン酸を使用したこと以外、実施例1と同様にして、セパレータを作製した。得られたセパレータの評価結果を表1に示す。なお、得られたIRスペクトルを図2に示す。
実施例1で用いた硫酸バリウム(平均粒径50nm)に代えて、リン酸ナトリウム(平均粒径500nm)を使用して、リン酸ナトリウムの5質量%に相当するステアリン酸を用いたこと以外、実施例1と同様にして、セパレータを作製した。得られたセパレータの評価結果を表1に示す。なお、得られたIRスペクトルを図3に示す。
実施例1の混合物原料に代えて、粘度平均分子量70万の高密度ポリエチレン(UH650,旭化成社製)と、可塑剤として40℃の動粘度が70.6cStである流動パラフィンと、酸化防止剤としてテトラキス−[メチレン−(3’,5’−ジ−t−ブチル−4’−ヒドロキシフェニル)プロピオネート]メタンとを表1に示す割合で混合した原料を用いたこと以外、実施例1と同様にして、セパレータを作製した。得られたセパレータの評価結果を表1に示す。比較例1ではイオン性化合物を使用しなかったので、イオン性化合物を含有しない混練物からブリードしてきた可塑剤の透過IRスペクトルを測定してIR吸光度比を表1に示した。なお、得られたIRスペクトルを図4に示す。
実施例1のイオン性化合物の表面処理を室温(23℃)で行ったこと以外、実施例1と同様にして、セパレータを作製した。得られた粉体の表面親水性度及び重量減少量比を測定した結果を表1に示す。また、得られたセパレータの評価結果を表1に示す。なお、得られたIRスペクトルを図5に示す。
《イオン性化合物の表面処理》
300mLの水に、50gの硫酸バリウム(平均粒径50nm)を投入し、撹拌しながら70℃に温度調整した。硫酸バリウムの4質量%に相当するステアリン酸を含有する、2−イソプロパノール溶液を少しずつ添加して、70℃で30分間撹拌した。次いで、ステアリン酸の1/2の物質量に相当する水酸化バリウムを含有する水溶液を少しずつ滴下して、60分間撹拌した。その後、固体を濾別して乾燥した後に、粉砕して微粉化することで、表面処理された硫酸バリウム粉末を得た。得られた粉体の表面親水性度及び重量減少量比を測定した結果を表2に示す。
《セパレータの製造》
粘度平均分子量70万の高密度ポリエチレン(UH650,旭化成社製)と、上述のようにして作製した硫酸バリウム粉末と、可塑剤として40℃の動粘度が70.6cStである流動パラフィンと、及び酸化防止剤としてテトラキス−[メチレン−(3’,5’−ジ−t−ブチル−4’−ヒドロキシフェニル)プロピオネート]メタンとを表2に示す割合で混合し、ラボプラストミル(東洋精機社製)を用いて200℃で混練した。
なお、混練物からブリードしてきた可塑剤のIRスペクトルを測定した。得られたIR吸光度比を表2に示す。また、混練物を用いて実施した金属溶出量の評価結果を表2に示す。
次に、混練物を150℃で10MPaの圧力でプレスして成形した後に、25℃で冷却して、厚さ1mmの原反シートを作製した。原反シートを同時二軸延伸機にセットして、120℃環境下で7×7倍に同時二軸延伸した。次いで、延伸された原反シートを取り出し、塩化メチレンに浸漬して可塑剤を抽出して、セパレータを得た。得られたセパレータの評価結果を表2に示す。
実施例4で用いた硫酸バリウムの4質量%に相当するステアリン酸に代えて、硫酸バリウムの2質量%に相当するステアリン酸を使用したこと以外、実施例4と同様にして、セパレータを作製した。得られたセパレータの評価結果を表2に示す。
実施例4で用いた硫酸バリウム(平均粒径50nm)に代えて、リン酸ナトリウム(平均粒径500nm)を使用して、リン酸ナトリウムの2.5質量%に相当するステアリン酸を用いたこと以外、実施例4と同様にして、セパレータを作製した。得られたセパレータの評価結果を表2に示す。
実施例5で用いたリン酸ナトリウムの2.5質量%に相当するステアリン酸に代えて、リン酸ナトリウムの1.25質量%に相当するステアリン酸を用いたこと以外、実施例5と同様にして、セパレータを作製した。得られたセパレータの評価結果を表2に示す。
実施例4で用いたステアリン酸に代えて、ラウリン酸を使用したこと以外、実施例4と同様にして、セパレータを作製した。得られたセパレータの評価結果を表2に示す。
実施例4で用いたステアリン酸に代えて、カプリル酸を使用したこと以外、実施例4と同様にして、セパレータを作製した。得られたセパレータの評価結果を表2に示す。
実施例4で用いたステアリン酸に代えて、ミリストレイン酸を使用したこと以外、実施例4と同様にして、セパレータを作製した。得られたセパレータの評価結果を表2に示す。
実施例4でセパレータ作製に用いた表面処理された硫酸バリウムに代えて、表面処理を行わずに硫酸バリウムをそのまま用いて、セパレータを作製した。得られたセパレータは、硫酸バリウムが顕著に凝集しており、品質が劣っていた。
実施例4でセパレータ作製に用いた表面処理された硫酸バリウムに代えて、後述の方法で表面処理を行った硫酸バリウムを用いたこと以外、実施例4と同様にして、セパレータを作製した。得られたセパレータの評価結果を表2に示す。
《イオン性化合物の表面処理》
300mLの水に、50gの硫酸バリウム(平均粒径50nm)を投入し、撹拌しながら70℃に温度調整した。硫酸バリウムの4.3質量%に相当するステアリン酸ナトリウムを含有する水溶液を少しずつ添加して、70℃で30分間撹拌した。次いで、ステアリン酸ナトリウムの2倍の物質量に相当する塩化水素を含有する塩酸を少しずつ滴下して、60分間撹拌した。その後、固体を濾別して乾燥した後に、粉砕して微粉化することで、表面処理された硫酸バリウム粉末を得た。得られた粉体の表面親水性度及び重量減少量比を測定した結果を表2に示す。
実施例4で用いた硫酸バリウムの4質量%に相当するステアリン酸に代えて、硫酸バリウムの16質量%に相当するステアリン酸を使用したこと以外、実施例4と同様にして、セパレータを作製した。得られたセパレータの評価結果を表2に示す。
《イオン性化合物の表面処理》
実施例4と同様にして、表面処理された硫酸バリウム粉末を作製した。得られた粉体の表面親水性度及び重量減少量比を測定した結果を表3に示す。
《セパレータの製造》
粘度平均分子量200万の超高分子量ポリエチレン(UH850,旭化成社製)と、上述のようにして作製した硫酸バリウム粉末と、可塑剤として40℃の動粘度が70.6cStである流動パラフィンと、及び酸化防止剤としてテトラキス−[メチレン−(3’,5’−ジ−t−ブチル−4’−ヒドロキシフェニル)プロピオネート]メタンとを表3に示す割合で混合し、ラボプラストミル(東洋精機社製)を用いて200℃で混練した。
なお、混練物からブリードしてきた可塑剤のIRスペクトルを測定した。得られたIR吸光度比を表3に示す。また、混練物を用いて実施した金属溶出量の評価結果を表3に示す。
次に、混練物を180℃で10MPaの圧力でプレスして成形した後に、25℃で冷却して、厚さ1mmの原反シートを作製した。原反シートを同時二軸延伸機にセットして、105℃環境下で7×7倍に同時二軸延伸した。次いで、延伸された原反シートを取り出し、塩化メチレンに浸漬して可塑剤を抽出して、セパレータを得た。得られたセパレータの評価結果を表3に示す。
実施例11で用いたセパレータ原料に代えて、表3に示した原料を用いた以外、実施例11と同様にして、セパレータを作製した。得られたセパレータの評価結果を表3に示す。
実施例11で用いたセパレータ原料に代えて、表3に示した原料を用いた以外、実施例11と同様にして、セパレータを作製した。得られたセパレータの評価結果を表3に示す。
実施例11で用いたセパレータ原料に代えて、表3に示した原料を用いた以外、実施例11と同様にして、セパレータを作製した。得られたセパレータの評価結果を表3に示す。
実施例11で用いたセパレータ原料に代えて、表3に示した原料を用いた以外、実施例11と同様にして、セパレータを作製した。得られたセパレータの評価結果を表3に示す。
実施例11で用いた表面処理された硫酸バリウムに代えて、実施例6で作製した表面処理されたリン酸ナトリウムを用いたこと以外、実施例11と同様にして、セパレータを作製した。得られたセパレータの評価結果を表3に示す。
実施例13で用いた表面処理された硫酸バリウムに代えて、実施例6で作製した表面処理されたリン酸ナトリウムを用いたこと以外、実施例13と同様にして、セパレータを作製した。得られたセパレータの評価結果を表3に示す。
実施例14でセパレータ作製に用いた表面処理された硫酸バリウムに代えて、表面処理を行わずに硫酸バリウムをそのまま用いて、セパレータの作製を試みたところ、延伸工程で原反シートが破れ、セパレータを作製することができなかった。
実施例14でセパレータ作製に用いた表面処理された硫酸バリウムに代えて、比較例4で作製した表面処理された硫酸バリウムを用いたこと以外、実施例14と同様にして、セパレータを作製した。得られたセパレータの評価結果を表3に示す。
実施例14でセパレータ作製に用いた表面処理された硫酸バリウムに代えて、比較例5で作製した表面処理された硫酸バリウムを用いたこと以外、実施例14と同様にして、セパレータを作製した。得られたセパレータの評価結果を表3に示す。
したがって、本実施形態のセパレータは、金属不純物を含まず、蓄電デバイスの安全性を向上する観点から優れていることが分かる。
Claims (15)
- ポリオレフィン樹脂と表面処理されたイオン性化合物とを含有する多孔質層を有し、前記多孔質層中の前記イオン性化合物の含有量が5質量%以上99質量%以下であって、前記イオン性化合物の表面親水性度が0.10以上0.80以下であることを特徴とする蓄電デバイス用セパレータ。
- ポリオレフィン樹脂と表面処理されたイオン性化合物とを含有する多孔質層を有し、前記多孔質層中の前記イオン性化合物の含有量が5質量%以上99質量%以下であって、前記イオン性化合物の350℃及び550℃の重量減少量比が0.03以上0.70以下であることを特徴とする蓄電デバイス用セパレータ。
- 前記多孔質層中の前記イオン性化合物の含有量が5質量%以上50質量%未満である、請求項1又は2に記載の蓄電デバイス用セパレータ。
- 前記多孔質層中の前記イオン性化合物の含有量が86質量%以上99質量%以下である、請求項1又は2に記載の蓄電デバイス用セパレータ。
- 前記イオン性化合物は、飽和脂肪酸、不飽和脂肪酸、飽和脂肪酸塩、及び不飽和脂肪酸塩からなる群より選ばれる一種以上で表面処理されている、請求項1〜4のいずれか1項に記載の蓄電デバイス用セパレータ。
- 前記イオン性化合物の表面処理量は、表面処理されたイオン性化合物を100質量%とした場合に0.1質量%以上10質量%以下である、請求項1〜5のいずれか1項に記載の蓄電デバイス用セパレータ。
- 前記イオン性化合物は、硫酸イオン、硝酸イオン、リン酸イオン、及びハロゲン化物イオンから成る群から選ばれる1種以上のアニオンを有する、請求項1〜6のいずれか1項に記載の蓄電デバイス用セパレータ。
- 前記イオン性化合物は、アルカリ金属イオン及びアルカリ土類金属イオンから成る群から選ばれる1種以上のカチオンを有する、請求項1〜7のいずれか1項に記載の蓄電デバイス用セパレータ。
- 前記イオン性化合物は、硫酸バリウムである、請求項1〜8のいずれか1項に記載の蓄電デバイス用セパレータ。
- 前記イオン性化合物の平均粒径が、5nm以上600nm以下である、請求項1〜9のいずれか1項に記載の蓄電デバイス用セパレータ。
- 前記ポリオレフィン樹脂は、粘度平均分子量が600,000以上のポリエチレンを含有する、請求項1〜10のいずれか1項に記載の蓄電デバイス用セパレータ。
- 平均孔径が10nm以上150nm以下である、請求項1〜11のいずれか1項に記載の蓄電デバイス用セパレータ。
- 透気度が10秒/100ml以上500秒/100mL以下である、請求項1〜12のいずれか1項に記載の蓄電デバイス用セパレータ。
- 突刺強度が100gf以上600gf以下である、請求項1〜13のいずれか1項に記載の蓄電デバイス用セパレータ。
- 正極と、負極と、請求項1〜14のいずれか1項に記載の蓄電デバイス用セパレータとを備える蓄電デバイス。