JP6569982B2 - 積層不織布 - Google Patents
積層不織布 Download PDFInfo
- Publication number
- JP6569982B2 JP6569982B2 JP2015234224A JP2015234224A JP6569982B2 JP 6569982 B2 JP6569982 B2 JP 6569982B2 JP 2015234224 A JP2015234224 A JP 2015234224A JP 2015234224 A JP2015234224 A JP 2015234224A JP 6569982 B2 JP6569982 B2 JP 6569982B2
- Authority
- JP
- Japan
- Prior art keywords
- nonwoven fabric
- adhesive
- laminated
- fibers
- particles
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
前記第1不織布に積層され、第2繊維を含む第2不織布と、
前記第2不織布の前記第1不織布とは反対側の主面に積層され、かつ第3繊維を含む第3不織布と、
接着剤と、を備え、
前記第2繊維に前記接着剤の粒子が付着しており、
前記第2不織布と前記第1不織布および前記第3不織布とが前記接着剤の粒子を介して接着しており、
前記第1繊維の平均繊維径D1と前記第2繊維の平均繊維径D2とが、D1>D2の関係を満たし、
前記接着剤の粒子の平均粒径Dpと前記第1繊維の平均繊維径D1とが、D1>Dpの関係を満たす、積層不織布に関する。
本発明の一実施形態に係る積層不織布は、第1繊維を含む第1不織布と、第1不織布に積層され、第2繊維を含む第2不織布と、第2不織布の第1不織布とは反対側の主面に積層され、かつ第3繊維を含む第3不織布と、接着剤と、を備える。第2繊維には、接着剤の粒子が付着しており、第2不織布と第1不織布および第3不織布とが前記接着剤の粒子を介して接着している。第1繊維の平均繊維径D1と第2繊維の平均繊維径D2とは、D1>D2の関係を満たし、接着剤の粒子の平均粒径Dpと第1繊維の平均繊維径D1とは、D1>Dpの関係を満たす。
接着剤粒子の平均粒径Dpがこのような範囲である場合、不織布間の剥離をさらに抑制し易くなる。
(第1不織布)
第1不織布は、積層不織布の形状を保持する基材として機能する。なお、積層不織布をプリーツ加工する場合、第1不織布が基材となって、プリーツの形状を保持する。
第1不織布は、第1繊維を含む。第1繊維の材質は特に限定されず、例えば、ガラス繊維、セルロース、アクリル樹脂、ポリオレフィン、ポリエステル、ポリアミド(PA)などが挙げられる。ポリオレフィンとしては、ポリプロピレン(PP)、ポリエチレン(PE)などが例示される。ポリエステルとしては、例えば、ポリエチレンテレフタレート(PET)、ポリブチレンテレフタレートなどが挙げられる。第1繊維は、これらの材質を一種含んでもよく、二種以上含んでもよい。形状保持の観点からは、これらの材質のうち、セルロース、ポリエステル、および/またはPAが好ましい。
なお、本明細書中、圧力損失は、例えば、JISB9908形式1の規格に準拠した測定機を用いて測定できる。
第2不織布は、第1繊維の平均繊維径D1よりも小さい平均繊維径D2を有する第2繊維を備えており、ダストを捕捉する機能を有する。第2不織布は、第1不織布の一方の主面に積層される。
このように、比較的厚い(または単位面積当たりの質量が大きい)第2不織布を用いる場合であっても、平均粒径が小さな接着剤粒子が第2繊維に付着していることで、不織布間の剥離を抑制することができる。
第3不織布は、比較的大きなダストを集塵する機能を有するとともに、種々の外部負荷から第2不織布を保護する保護材として機能する。第3不織布は、第2不織布の他方の主面(第1不織布とは反対側の主面)に積層される。集塵効率の観点から、第3不織布には帯電処理が施されていることが好ましい。
第3繊維の平均繊維径D3は、特に限定されない。平均繊維径D3は、例えば、0.5μm以上、20μm以下であり、1μm以上、20μm以下である。
積層不織布において、第2繊維には、接着剤粒子が付着しており、この接着剤粒子を介して、第2不織布と第1不織布および第3不織布とはそれぞれ接着している。このように、接着剤粒子の点接着を利用して、不織布間を接着させるため、不織布間の剥離を抑制しながらも、積層不織布の圧力損失を抑制できる。積層不織布は、前述のように、さらに、接着剤粒子に連結した接着剤の糸状体を含んでもよい。
なお、接着剤粒子が第1粒子および第2粒子を含む場合、接着剤粒子の平均粒径Dpは、第2粒子について算出するものとする。
積層不織布は、第1不織布と、第2不織布と、第3不織布とを、この順序で配置し、第2繊維に付着した接着剤粒子を介して、第2不織布と、第1不織布および第3不織布とをそれぞれ接着させることにより製造できる。第2繊維は、原料樹脂をエレクトロスピニング処理により紡糸して、第1不織布に堆積させ、これにより第1不織布に第2不織布を積層することが好ましい。接着剤粒子は、接着剤を含む溶液をエレクトロスピニング処理することにより形成することが好ましい。第2繊維の原料樹脂と接着剤とを含む溶液をエレクトロスピニング処理することにより、接着剤粒子が付着した第2繊維を形成することがさらに好ましい。
第1繊維を含む第1不織布と、第2繊維の原料となる原料樹脂と接着剤とを含む原料液と、第3繊維を含む第3不織布と、を準備する工程(第1工程)、
電界紡糸(エレクトロスピニング)法により、原料液をノズルから吐出させて接着剤粒子が付着した第2繊維を生成させ、第1不織布に接着剤の粒子が付着した第2繊維を堆積させて、第1不織布に前記第2不織布を積層する工程(第2工程)、
第2不織布の第1不織布とは反対側の主面に、第3繊維を含む第3不織布を配置して積層物を得る工程(第3工程)、ならびに
積層物を厚み方向に押圧して、第2不織布と第1不織布および第3不織布とを圧着させることにより積層不織布を得る工程(第4工程)、を備える。
(第1工程)
第1工程では、第1不織布、上記の原料液、および第3不織布を準備する。
第1不織布および第3不織布は、前述の方法などにより準備することができる。
原料液は、第2繊維の原料樹脂および接着剤に加え、通常、溶媒を含む。溶媒は、原料樹脂の種類や製造条件に応じて適切なものを選択すればよい。
第2工程では、第1不織布の一方の主面に、原料液を電界紡糸することにより、接着剤粒子が付着した第2繊維を堆積させ、第2不織布を積層する。電界紡糸では、原料液に、高電圧を印加し、電荷をもった原料液をノズルから吐出することにより、第2繊維が生成する。このとき、接着剤もノズルから吐出されて、第2繊維に付着する。
第3工程では、第1不織布に積層された第2不織布に、さらに第3不織布を配置して積層物を得る。第3不織布は、第3不織布の一方の主面が、第2不織布の第1不織布とは反対側の主面に接触するように重ねて配置される。
第4工程(圧着工程)では、第3工程で得られた積層物を、厚み方向に押圧して不織布同士を圧着させる。圧着を行うことで、積層不織布を得ることができる。第3工程で接着剤を溶融させた状態で、第4工程で積層物を押圧すると、溶融した接着剤を介して、第2不織布と、第1不織布および第3不織布とが接着される。第4工程では、必要に応じて加熱下で圧着を行ってもよい。第3工程で接着剤を溶融させずに、第3不織布を配置した場合には、第4工程で加熱を行うことが好ましい。第3工程で接着剤を溶融させずに、第4工程で加熱する場合、第3工程において、接着剤を溶融するためのヒータや溶融工程を省略できるため、工程を簡略化できるとともに、装置を省スペース化できる。
加熱下で圧着を行う場合、加熱温度は、例えば、40〜200℃である。ローラで圧着させる場合には、加熱可能なローラを用いることで、圧着を加熱下で行うことができる。加熱可能なローラとしては、ヒータを内蔵するローラや接続したヒータから加熱可能なローラなどが例示される。
また、接着性を高め易い観点から、エンボス加工面における凸部の高さは、100〜5000μmであることが好ましく、200〜1000μmであることがさらに好ましい。
積層不織布は、例えば、製造ラインの上流から下流に第1不織布を搬送し、搬送される第1不織布の主面に第2不織布を形成した後、第3不織布を積層する製造装置(または製造システム)により製造することができる。このような製造装置は、例えば、(1)製造ラインに第1不織布を供給する第1不織布供給部、(2)第2繊維の原料となる原料樹脂と接着剤とを含む原料液を収容するタンク、(3)タンクから供給される原料液を電界紡糸することにより、第2繊維を生成させ、接着剤が付着した第2繊維を第1不織布に堆積させて第1不織布に第2不織布を積層する電界紡糸機構、(4)第2不織布に第3不織布を供給する第3不織布供給部、ならびに(5)第2不織布と第1不織布および第3不織布とを圧着させる圧着部、を備える。
接着剤溶液タンク39や原料液タンク29では、接着剤溶液32や原料液22を連続的または完結的に攪拌することで、接着剤4のゲル化を抑制してもよい。
本発明に係る積層不織布10を用いた空気清浄機100は、図6に例示されるように、気体の吸い込み部101と、気体の吐き出し部102と、気体の吸い込み部101と吐き出し部102との間に配置される積層不織布10と、を備える。積層不織布10は、蛇腹状にプリーツ加工されて配置されても良い。積層不織布10は、大気中のダストを捕捉する濾材である。積層不織布10を備える空気清浄機は、圧力損失が小さく、集塵効率に優れる。集塵効率の点で、積層不織布10は、第2不織布3が吸い込み部101側に位置するように、吸い込み部101と吐き出し部102との間に配置されることが好ましい。
下記の手順で、積層不織布を作製した。
まず、セルロース繊維、ポリエステル繊維およびアクリル繊維で形成した第1不織布(厚み:300μm、D1:15μm、単位面積当たりの質量:42g/m2)を準備した。
図2に示すような製造装置を用いて、搬送される第1不織布に接着剤粒子および接着剤の糸状体が付着した第2繊維を堆積させて第2不織布を積層した。第2繊維の原料液は、接着剤(ポリエステル系ホットメルト樹脂、融点:約100℃)を20質量%の濃度で含むDMAc溶液(第1溶液)と、PESを20質量%濃度で含むDMAc溶液(第2溶液)とを、質量比1:1で混合した溶液を用いた。得られた第2繊維の平均繊維径D2は273nmであり、第2不織布の単位面積当たりの平均の質量は0.93g/m2であった。
別途、積層不織布から、幅25mm×長さ200mmの試料を切り取った。JISZ0237に準拠した方法により、試料の第1不織布と第3不織布との間の剥離強度を測定した。剥離強度は、88mN/25mmであった。
実施例1と同じ第1不織布の一方の主面に、接着剤(ポリエステル系ホットメルト樹脂、融点:約100℃)を20質量%の濃度で含むDMAc溶液を用いて、エレクトロスピニングにより接着剤を吐出した。次いで、PESを20質量%濃度で含むDMAc溶液を原料液として用いて、実施例1と同様にして、接着剤が付着した第1不織布の主面に、第2繊維を堆積させることにより、第2不織布を積層した。
実施例1と同じ第1不織布の一方の主面に、PESを20質量%濃度で含むDMAc溶液を原料液として用いて、実施例1と同様にして、第2繊維を堆積させることにより、第2不織布を積層した。次いで、第2不織布の主面に、接着剤(ポリエステル系ホットメルト樹脂、融点:約100℃)を20質量%の濃度で含むDMAc溶液を用いて、エレクトロスピニングにより接着剤を吐出した。
Claims (5)
- 第1繊維を含む第1不織布と、
前記第1不織布に積層され、第2繊維を含む第2不織布と、
前記第2不織布の前記第1不織布とは反対側の主面に積層され、かつ第3繊維を含む第3不織布と、
接着剤と、を備え、
前記第2繊維に前記接着剤の粒子が付着しており、
前記第2不織布と前記第1不織布および前記第3不織布とが前記接着剤の粒子を介して接着しており、
前記第1繊維の平均繊維径D1と前記第2繊維の平均繊維径D2とが、D1>D2の関係を満たし、
前記接着剤の粒子の平均粒径Dpと前記第1繊維の平均繊維径D1とが、D1>Dpの関係を満たす、積層不織布。 - 前記積層不織布は、さらに前記接着剤の糸状体を含み、
前記糸状体の平均繊維径は、前記第2繊維よりも細く、
前記糸状体は、前記接着剤の粒子に連結している、請求項1に記載の積層不織布。 - 前記第2繊維は、ナノファイバである、請求項1または2に記載の積層不織布。
- 前記接着剤の粒子の平均粒径Dpと前記第2繊維の平均繊維径D2とが、Dp>D2の関係を満たす、請求項1〜3のいずれか1項に記載の積層不織布。
- 前記接着剤の粒子の平均粒径Dpは、1〜200μmである、請求項1〜4のいずれか1項に記載の積層不織布。