JP6491004B2 - 排ガス浄化触媒および排ガス浄化用ハニカム触媒構造体 - Google Patents
排ガス浄化触媒および排ガス浄化用ハニカム触媒構造体 Download PDFInfo
- Publication number
- JP6491004B2 JP6491004B2 JP2015060045A JP2015060045A JP6491004B2 JP 6491004 B2 JP6491004 B2 JP 6491004B2 JP 2015060045 A JP2015060045 A JP 2015060045A JP 2015060045 A JP2015060045 A JP 2015060045A JP 6491004 B2 JP6491004 B2 JP 6491004B2
- Authority
- JP
- Japan
- Prior art keywords
- exhaust gas
- gas purification
- supported
- catalyst
- oxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
また、前記表面沈殿膜が、アルミナまたはシリカを含むことも出来る。アルミナやシリカは焼結しにくいので、表面沈殿膜に含有させることで、製品の耐熱性が向上する。
基材粒子であるセリアジルコニア系複合酸化物(比表面積85m2/g)10gに対して、硝酸パラジウム水溶液を添加し、エバポレータで真空引きしながら70℃で加熱、蒸発乾固し、600℃で1時間焼成して、Pd担持セリアジルコニア系複合酸化物を得た(第1段階)。得られたPd担持セリアジルコニア系複合酸化物に水を加えて50mLのスラリーとし、撹拌しながら酸化セリウム1.3g相当を含む塩化セリウム溶液を添加し、アンモニア水でpHを6.5に調整、セリウムイオンをPd担持セリアジルコニア系複合酸化物に吸着させた(第2段階)。前記第2段階に続き、前記セリウムイオンを吸着させたPd担持セリアジルコニア系複合酸化物にさらにアンモニア水を添加、pHを9に調整して、Pd担持セリアジルコニア系複合酸化物の表面に水酸化セリウムを沈殿固定させた(第3段階)。
実施例1−1と同じ基材粒子に対して0.23重量%のPdに相当する硝酸パラジウム水溶液を基材粒子に添加し、エバポレータで真空引きしながら70℃で加熱、蒸発乾固し、600℃で1時間焼成し、さらに、実施例1−1と同じ熱履歴とするため、700℃で3時間焼成して、Pd担持セリアジルコニア系複合酸化物を得た。
実施例1と同じ基材粒子10gに対して、硝酸パラジウム水溶液を添加し、エバポレータで真空引きしながら70℃で加熱、蒸発乾固し、600℃で1時間焼成して、Pd担持セリアジルコニア系複合酸化物を得た。得られたPd担持セリアジルコニア系複合酸化物に水を加え、50mLのスラリーとし、撹拌しながら、酸化イットリウム0.8g相当を含む塩化イットリウム溶液を添加し、アンモニア水でpHを一旦6.5に保持してイットリウムイオンを基材粒子表面に吸着させた後、さらにpHを9に調整、基材粒子の表面に水酸化イットリウムを沈殿固定させた。
実施例2−1と同じ基材粒子に対して0.28重量%のPdに相当する硝酸パラジウム水溶液を基材粒子に添加し、エバポレータで真空引きしながら70℃で加熱、蒸発乾固し、600℃で1時間焼成し、Pd担持セリアジルコニア系複合酸化物を得た。
基材粒子であるアルミナ(比表面積203m2/g)10gに対して、硝酸パラジウム水溶液を添加し、エバポレータで真空引きしながら70℃で加熱、蒸発乾固し、600℃で1時間焼成して、Pd担持アルミナを得た。得られたPd担持アルミナに水を加え、50mLのスラリーとし、撹拌しながら、酸化セリウム1.5g相当を含む塩化セリウム溶液を添加し、アンモニア水を添加し、pHを一旦6.5に保持してセリウムイオンを基材粒子表面に吸着させた後、さらにpHを9に調整、水酸化セリウムをPd担持アルミナの表面に沈殿固定させた。前段階で得られたスラリーをヌッチェでろ過し、得られた水酸化セリウム被覆Pd担持アルミナをアンモニア水50mLで2回リパルプ洗浄した。
実施例3−1と同じ基材粒子に対して0.27重量%のPdに相当する硝酸パラジウム水溶液を基材粒子に添加し、エバポレータで真空引きしながら70℃で加熱、蒸発乾固し、600℃で1時間焼成し、さらに、実施例3−1と同じ熱履歴とするため、700℃で3時間焼成して、Pd担持アルミナを得た。
基材粒子であるジルコニア(比表面積60m2/g)10gに対して、硝酸パラジウム水溶液を添加し、エバポレータで真空引きしながら70℃で加熱、蒸発乾固し、600℃で1時間焼成して、Pd担持ジルコニアを得た。得られたPd担持ジルコニアに水を加え、50mLのスラリーとし、撹拌しながら、酸化セリウム1.5g相当を含む塩化セリウム溶液を添加し、アンモニア水を添加し、pHを一旦6.5に保持してセリウムイオンを基材粒子表面に吸着させた後、さらにpHを9に調整、水酸化セリウムをPd担持ジルコニアの表面に沈殿固定させた。
前段階で得られたスラリーをヌッチェでろ過し、得られた水酸化セリウム被覆Pd担持ジルコニアをアンモニア水50mLで2回リパルプ洗浄した。
実施例4−1と同じ基材粒子に対して0.30重量%のPdに相当する硝酸パラジウム水溶液を基材粒子に添加し、エバポレータで真空引きしながら70℃で加熱、蒸発乾固し、600℃で1時間焼成し、さらに、実施例4−1と同じ熱履歴とするため、700℃で3時間焼成して、Pd担持ジルコニアを得た。
基材粒子であるイットリア安定化ジルコニア(比表面積50m2/g)10gに対して、硝酸パラジウム水溶液を添加し、エバポレータで真空引きしながら70℃で加熱、蒸発乾固し、600℃で1時間焼成して、Pd担持イットリア安定化ジルコニアを得た。得られたPd担持イットリア安定化ジルコニアに水を加え、50mLのスラリーとし、撹拌しながら、酸化セリウム1.5g相当を含む塩化セリウム溶液を添加し、アンモニア水を添加し、pHを一旦6.5に保持してセリウムイオンを基材粒子表面に吸着させた後、さらにpHを9に調整、水酸化セリウムをPd担持ジルコニアの表面に沈殿固定させた。
前段階で得られたスラリーをヌッチェでろ過し、得られた水酸化セリウム被覆Pd担持イットリア安定化ジルコニアをアンモニア水50mLで2回リパルプ洗浄した。
実施例5−1と同じ基材粒子に対して0.33重量%のPdに相当する硝酸パラジウム水溶液を基材粒子に添加し、エバポレータで真空引きしながら70℃で加熱、蒸発乾固し、600℃で1時間焼成し、さらに、実施例5−1と同じ熱履歴とするため、700℃で3時間焼成して、Pd担持イットリア安定化ジルコニアを得た。
実施例1と同じ基材粒子10gに対して、硝酸パラジウム水溶液を添加し、エバポレータで真空引きしながら70℃で加熱、蒸発乾固し、600℃で1時間焼成して、Pd担持セリアジルコニア系複合酸化物を得た。得られたPd担持セリアジルコニア系複合酸化物に水を加え、50mLのスラリーとし、撹拌しながら、酸化アルミニウム0.7g相当を含む塩化アルミニウム溶液を添加し、アンモニア水を用いて基材粒子の表面に水酸化アルミニウムを沈殿固定させた。水酸化アルミニウムの沈殿固定pHは7.5とした。
実施例6−1と同じ基材粒子に対して0.34重量%のPdに相当する硝酸パラジウム水溶液を基材粒子に添加し、エバポレータで真空引きしながら70℃で加熱、蒸発乾固し、600℃で1時間焼成し、さらに、実施例6−1と同じ熱履歴とするため、700℃で3時間焼成して、Pd担持セリアジルコニア系複合酸化物を得た。
また、実施例2−1において、表面沈殿膜として水酸化イットリウムに換えて、水酸化セリウム、水酸化アルミニウムとしたが、実施例2−1と同様に貴金属粒子の粗大化は抑制できた。
また、実施例4−1において、表面沈殿膜としてセリアに換えて、セリアジルコニア、イットリア、イットリア安定ジルコニアとしたが、実施例4−1と同様に貴金属粒子の粗大化は抑制できた。
また、実施例6−1において、表面沈殿膜としてアルミナに換えて、シリカとしたが、実施例6−1と同様に貴金属粒子の粗大化は抑制できた。
Claims (9)
- 貴金属が担持された基材粒子にさらに基材粒子の比表面積径に基づき、基材粒子の表面を計算上0.001〜3nm覆い、粒子径10nm以下サイズの担持貴金属が埋没していない表面沈殿膜を有することを特徴とする排ガス浄化触媒。
- 表面沈殿膜が、酸素イオン伝導酸化物を含むことを特徴とする請求項1記載の排ガス浄化触媒。
- 表面沈殿膜が、酸素吸放出可能な酸化物を含むことを特徴とする請求項1又は2記載の排ガス浄化触媒。
- 表面沈殿膜の成分が、水酸化セリウム単独またはセリア単独、であることを特徴とする請求項1〜3のいずれかに記載の排ガス浄化触媒。
- 表面沈殿膜の成分が、イットリウム及び原子番号57から71までの希土類元素(セリウム、プロメチウムを除く)から選ばれた1種以上の希土類の水酸化物または希土類の酸化物を含むことを特徴とする請求項1〜4のいずれかに記載の排ガス浄化触媒。
- 表面沈殿膜が、水酸化アルミニウム、またはアルミナ、またはシリカを含むことを特徴とする請求項1〜5のいずれかに記載の排ガス浄化触媒。
- 基材粒子が、セリアジルコニア系複合酸化物、またはジルコニア、またはイットリア安定化ジルコニア、またはアルミナであることを特徴とする請求項1〜6のいずれかに記載の排ガス浄化触媒。
- 基材粒子が、酸素吸放出可能な酸化物であることを特徴とする請求項1〜7のいずれかに記載の排ガス浄化触媒。
- 請求項1〜8のいずれかに記載の排ガス浄化触媒を、金属又はセラミックスハニカム内壁に被覆したことを特徴とする排ガス浄化用ハニカム触媒構造体。