JP6487273B2 - 水硬性組成物用添加剤 - Google Patents
水硬性組成物用添加剤 Download PDFInfo
- Publication number
- JP6487273B2 JP6487273B2 JP2015105657A JP2015105657A JP6487273B2 JP 6487273 B2 JP6487273 B2 JP 6487273B2 JP 2015105657 A JP2015105657 A JP 2015105657A JP 2015105657 A JP2015105657 A JP 2015105657A JP 6487273 B2 JP6487273 B2 JP 6487273B2
- Authority
- JP
- Japan
- Prior art keywords
- mass
- less
- hydraulic composition
- parts
- hydraulic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
特許文献1は、ポルトランドセメントと、アルミナセメントと、石膏とを含有する無機成分Iに、特定のビニル系単量体aとアクリル酸又はメタクリル酸の水溶性塩であるビニル系単量体bの共重合体からなる共重合体成分IIを含有する自己流動性水硬性組成物を開示している。
また特許文献1は、自己流動性水硬性組成物に、炭酸リチウム、酒石酸ナトリウム類及び重炭酸ナトリウムからなる群より選択される一種以上の凝結調整剤をさらに含有することを開示している。
特許文献2は、高性能減水剤を使用したグラウトモルタルのセメント分に対し、特定量のオキシカルボン酸又はその塩を添加することを特徴とするグラウトモルタルの作業性改良法を開示している。
また特許文献2は、グラウトモルタルに、炭酸ナトリウムをさらに含有することを開示している。
特許文献3は、ポリアルキルアリルスルホン酸塩系高性能減水剤、メラミンホルマリン樹脂スルホン酸塩系高性能減水剤、及び芳香族アミノスルホン酸塩系高性能減水剤の一種又は二種以上の高性能減水剤と、ナトリウム又はカリウムの重炭酸塩とを含有してなるセメントコンクリート二次製品用セメント混和剤を開示している。
また、本発明は、流動性に優れた水硬性組成物を提供する。
また、本発明によれば、流動性に優れた水硬性組成物が提供される。
本発明の水硬性組成物用添加剤は、ポリカルボン酸系分散剤を含有する。
R1、R2:それぞれ独立に、水素原子又はメチル基
m1:0以上2以下の整数
AO:炭素数2又は3のアルキレンオキシ基
n1:AOの平均付加モル数であって、4以上300以下の数
X:水素原子又は炭素数1以上3以下のアルキル基
を示す。〕
R3、R4、R5:それぞれ独立に、水素原子、メチル基、又は(CH2)m2COOM2
M1、M2:それぞれ独立に、対イオンを示し、水素イオン、アルカリ金属イオン、アルカリ土類金属イオン(1/2イオン)、有機アンモニウムイオン、又はアンモニウムイオン、
m2:0以上2以下の整数
を示す。〕
m1は、水硬性組成物の流動性の観点から、0以上2以下の整数であり、0が好ましい。
AOは、水硬性組成物の流動性の観点から、炭素数2のアルキレンオキシ基及び炭素数3のアルキレンオキシ基から選ばれるアルキレンオキシ基であり、エチレンオキシ基が好ましい。
n1は、AOの平均付加モル数であり、4以上300以下の数である。n1は水硬性組成物の流動性の観点から、9以上が好ましく、15以上がより好ましく、20以上が更に好ましい。そして、200以下が好ましく、130以下がより好ましく、100以下が更に好ましく、80以下がより更に好ましく、50以下がより更に好ましく、30以下がより更に好ましい。
Xは、水素原子又は炭素数1以上3以下のアルキル基であり、水硬性組成物の流動性の観点から、水素原子又は炭素数1のアルキル基が好ましく、炭素数1のアルキル基がより好ましい。
なお、共重合体(A)の重量平均分子量は、ゲルパーミエーションクロマトグラフィー法(ポリエチレングリコール換算)によるものであり、具体的な条件は下記の通りである。
*ゲルパーミエーションクロマトグラフィー条件
装置:GPC(HLC−8320GPC)東ソー株式会社製
カラム:G4000PWXL+G2500PWXL(東ソー株式会社製)
溶離液:0.2Mリン酸バッファー/CH3CN=9/1
流量:1.0mL/min
カラム温度:40℃
検出:RI
サンプルサイズ:0.2mg/mL
標準物質:ポリエチレングリコール換算(分子量87500、250000、145000、46000、24000の単分散ポリエチレングリコール)
本発明の水硬性組成物は、水硬性粉体、水、ポリカルボン酸系分散剤、炭酸カリウム及び炭酸ナトリウムから選ばれる一種以上の炭酸塩、並びに重炭酸塩を含有する。
ポリカルボン酸系分散剤、炭酸カリウム及び炭酸ナトリウムから選ばれる一種以上の炭酸塩、並びに重炭酸塩の種類及び好ましい態様は、それぞれ本発明の水硬性組成物用添加剤と同じである。
本発明の水硬性組成物において、炭酸カリウム及び炭酸ナトリウムから選ばれる一種以上の炭酸塩の含有量は、水硬性組成物の流動性、及び凝結時間の観点から、水硬性粉体100質量部に対して0.0005質量部以上が好ましく、0.001質量部以上がより好ましく、0.005質量部以上が更に好ましく、0.01質量部以上がより更に好ましい。そして、6.0質量部以下が好ましく、4.0質量部以下がより好ましく、3.0質量部以下が更に好ましく、1.0質量部以下がより更に好ましく、0.1質量部以下がより更に好ましく、0.05質量部以下がより更に好ましい。
本発明の水硬性組成物において、重炭酸塩の含有量は、水硬性組成物の流動性、及び凝結時間の観点から、水硬性粉体100質量部に対して0.0005質量部以上が好ましく、0.001質量部以上がより好ましく、0.005質量部以上が更に好ましく、0.01質量部以上がより更に好ましい。そして、6.0質量部以下が好ましく、4.0質量部以下がより好ましく、3.0質量部以下が更に好ましく、1.0質量部以下がより更に好ましく、0.1質量部以下がより更に好ましく、0.05質量部以下がより更に好ましい。
本発明の水硬性組成物の製造方法は、水硬性粉体、水、ポリカルボン酸系分散剤、炭酸カリウム及び炭酸ナトリウムから選ばれる一種以上の炭酸塩、並びに重炭酸塩を混合して水硬性組成物を得る工程を有する。
この製造方法では、本発明用の水硬性組成物用添加剤、水硬性組成物で述べた事項を、適宜適用することができる。
本発明のより具体的な態様を以下に例示する。これらの態様には、本発明の水硬性組成物用添加剤、水硬性組成物、水硬性組成物の製造方法で述べた事項を適宜適用することができる。
ポリカルボン酸系分散剤、炭酸カリウム及び炭酸ナトリウムから選ばれる一種以上の炭酸塩、並びに重炭酸塩を含有する水硬性組成物用添加剤。
ポリカルボン酸系分散剤が、(1)ポリアルキレングリコールとアクリル酸とのモノエステル、及びポリアルキレングリコールとメタクリル酸とのモノエステルから選ばれる一種以上のモノエステルと、アクリル酸及びメタクリル酸から選ばれる一種以上のカルボン酸との共重合体、(2)ポリアルキレングリコールを有する不飽和アルコールと、アクリル酸及びメタクリル酸から選ばれる一種以上のカルボン酸との共重合体、並びに(3)ポリアルキレングリコールを有する不飽和アルコールと、マレイン酸との共重合体から選ばれる一種以上の共重合体である、前記<1>記載の水硬性組成物用添加剤。
ポリカルボン酸系分散剤が、下記一般式(A1)で表される単量体(A1)と下記一般式(A2)で表される単量体(A2)とを含む単量体を重合して得られる共重合体(A)である、前記<1>記載の水硬性組成物用添加剤。
R1、R2:それぞれ独立に、水素原子又はメチル基
m1:0以上2以下の整数
AO:炭素数2又は3のアルキレンオキシ基
n1:AOの平均付加モル数であって、4以上300以下の数
X:水素原子又は炭素数1以上3以下のアルキル基
を示す。〕
R3、R4、R5:それぞれ独立に、水素原子、メチル基、又は(CH2)m2COOM2
M1、M2:それぞれ独立に、対イオンを示し、水素イオン、アルカリ金属イオン、アルカリ土類金属イオン(1/2イオン)、有機アンモニウムイオン、又はアンモニウムイオン、
m2:0以上2以下の整数
を示す。〕
一般式(A1)中、R1が水素原子であり、R2がメチル基である、前記<3>記載の水硬性組成物用添加剤。
一般式(A1)中、m1が0である、前記<3>又は<4>記載の水硬性組成物用添加剤。
一般式(A1)中、AOがエチレンオキシ基である、前記<3>〜<5>の何れかに記載の水硬性組成物用添加剤。
一般式(A1)中、n1が、好ましくは9以上、より好ましくは15以上、更に好ましくは20以上であり、そして、好ましくは200以下、より好ましくは130以下、更に好ましくは100以下、より更に好ましくは80以下、より更に好ましくは50以下、より更に好ましくは30以下である、前記<3>〜<6>の何れかに記載の水硬性組成物用添加剤。
一般式(A1)中、Xが、好ましくは水素原子又は炭素数1のアルキル基であり、より好ましくは炭素数1のアルキル基である、前記<3>〜<7>の何れかに記載の水硬性組成物用添加剤。
一般式(A2)中、R3、R5が、それぞれ、水素原子であり、R4が、メチル基である、前記<3>〜<8>の何れかに記載の水硬性組成物用添加剤。
一般式(A2)中、M1、M2が、それぞれ、好ましくは水素イオン、又はアルカリ金属イオンであり、より好ましくは水素原子である、前記<3>〜<9>の何れかに記載の水硬性組成物用添加剤。
単量体(A1)が、(1)メトキシポリエチレングリコール、メトキシポリプロピレングリコール、メトキシポリブチレングリコール、メトキシポリスチレングリコール、及びエトキシポリエチレンポリプロピレングリコールから選ばれる片末端アルキル封鎖ポリアルキレングリコールと、アクリル酸、メタクリル酸、及びマレイン酸から選ばれるカルボン酸とのエステル化物、(2)アクリル酸、メタクリル酸、及びマレイン酸から選ばれるカルボン酸へのエチレンオキサイド及びプロピレンオキサイドから選ばれる付加物、から選ばれる一種以上の単量体であり、好ましくはメトキシポリエチレングリコールである、前記<3>記載の水硬性組成物用添加剤。
単量体(A2)が、アクリル酸、メタクリル酸、クロトン酸から選ばれるモノカルボン酸系単量体、及びマレイン酸、イタコン酸、フマル酸から選ばれるジカルボン酸系単量体、並びにこれらの無水物又は、アルカリ金属塩、アルカリ土類金属塩、アンモニウム塩、水酸基が置換されていてもよい炭素数2以上8以下であるモノ、ジ、トリアルキルアンモニウム塩から選ばれる塩、から選ばれる一種以上の単量体であり、好ましくはアクリル酸、メタクリル酸、マレイン酸、及びこれらのアルカリ金属塩、並びに無水マレイン酸から選ばれる単量体であり、より好ましくはアクリル酸、メタクリル酸、及びこれらのアルカリ金属塩から選ばれる単量体であり、更に好ましくはメタクリル酸及びメタクリル酸のアルカリ金属塩から選ばれる単量体である、前記<3>又は<11>記載の水硬性組成物用添加剤。
共重合体(A)の単量体(A1)と単量体(A2)のモル比(A1)/(A2)が、好ましくは10/90以上、より好ましくは20/80以上、そして、好ましくは60/40以下、より好ましくは50/50以下、更に好ましくは35/65以下、より更に好ましくは30/70以下である、前記<3>〜<12>の何れかに記載の水硬性組成物用添加剤。
共重合体(A)の全構成単量体中、単量体(A1)と単量体(A2)の合計量が、好ましくは90質量%以上、より好ましくは95質量%以上、そして、好ましくは100質量%以下であり、あるいは100質量%である、前記<3>〜<13>の何れかに記載の水硬性組成物用添加剤。
単量体(A1)と単量体(A2)の合計質量に対する単量体(A2)の質量の割合が、好ましくは1質量%以上、より好ましくは3質量%以上、更に好ましくは4質量%以上、そして、好ましくは100質量%以下、より好ましくは90質量%以下、更に好ましくは80質量%以下、より更に好ましくは70質量%以下、より更に好ましくは50質量%以下である、前記<3>〜<14>の何れかに記載の水硬性組成物用添加剤。
下記のゲルパーミエーションクロマトグラフィー条件で測定された共重合体(A)の重量平均分子量が、好ましくは10000以上、より好ましくは20000以上、更に好ましくは30000以上、そして、好ましくは200000以下、より好ましくは100000以下である、前記<3>〜<15>の何れかに記載の水硬性組成物用添加剤。
*ゲルパーミエーションクロマトグラフィー条件
装置:GPC(HLC−8320GPC)東ソー株式会社製
カラム:G4000PWXL+G2500PWXL(東ソー株式会社製)
溶離液:0.2Mリン酸バッファー/CH3CN=9/1
流量:1.0mL/min
カラム温度:40℃
検出:RI
サンプルサイズ:0.2mg/mL
標準物質:ポリエチレングリコール換算(分子量87500、250000、145000、46000、24000の単分散ポリエチレングリコール)
炭酸カリウム及び炭酸ナトリウムから選ばれる一種以上の炭酸塩が、炭酸ナトリウムである、前記<1>〜<16>の何れかに記載の水硬性組成物用添加剤。
重炭酸塩が、炭酸水素ナトリウム、炭酸水素カリウム、炭酸水素カルシウム、炭酸水素リチウム、及び炭酸水素アンモニウムから選ばれる一種以上の炭酸水素塩であり、好ましくは炭酸水素ナトリウム、及び炭酸水素カリウムから選ばれる一種以上の炭酸水素塩であり、より好ましくは炭酸水素ナトリウムである、前記<1>〜<17>の何れかに記載の水硬性組成物用添加剤。
ポリカルボン酸系分散剤と炭酸カリウム及び炭酸ナトリウムから選ばれる一種以上の炭酸塩の質量比(分散剤/炭酸塩)が、好ましくは0.5以上、より好ましくは1以上、更に好ましくは1.5以上、より更に好ましくは5以上、そして、好ましくは60以下、より好ましくは30以下、更に好ましくは15以下、より更に好ましくは10以下である、前記<1>〜<18>の何れかに記載の水硬性組成物用添加剤。
ポリカルボン酸系分散剤と重炭酸塩の質量比(分散剤/重炭酸塩)が、好ましくは0.5以上、より好ましくは1以上、更に好ましくは1.5以上、より更に好ましくは5以上、そして、好ましくは60以下、より好ましくは30以下、更に好ましくは15以下、より更に好ましくは10以下である、前記<1>〜<19>の何れかに記載の水硬性組成物用添加剤。
炭酸カリウム及び炭酸ナトリウムから選ばれる一種以上の炭酸塩と重炭酸塩の質量比(炭酸塩/重炭酸塩)が、好ましくは0.25以上、より好ましくは0.5以上、更に好ましくは0.8以上、そして、好ましくは8以下、より好ましくは6以下、更に好ましくは4以下、より更に好ましくは2.0以下である、前記<1>〜<20>の何れかに記載の水硬性組成物用添加剤。
水硬性粉体、水、ポリカルボン酸系分散剤、炭酸カリウム及び炭酸ナトリウムから選ばれる一種以上の炭酸塩、並びに重炭酸塩を含有する水硬性組成物。
水硬性粉体が、セメント、及び石膏から選ばれる一種以上であり、好ましくは、普通ポルトランドセメント、ビーライトセメント、中庸熱セメント、早強セメント、超早強セメント、及び耐硫酸塩セメントからから選ばれる一種以上のセメント、並びに、前記セメントに、ポゾラン作用を有する粉体、潜在水硬性を有する粉体、及び石粉(炭酸カルシウム粉末)から選ばれる一種以上の粉体が添加されたセメント、から選ばれる一種以上のセメントである、前記<22>記載の水硬性組成物。
水硬性粉体として、セメント及び石膏を含有する、あるいは水硬性粉体として、セメント及び石膏を配合してなる、前記<22>記載の水硬性組成物。
セメント100質量部に対して、石膏を、好ましくは5質量部以上、より好ましくは10質量部以上、更に好ましくは20質量部以上、そして、好ましくは100質量部以下、より好ましくは80質量部以下、更に好ましくは70質量部以下配合してなる、前記<24>記載の水硬性組成物。
ポリカルボン酸系分散剤を水硬性粉体100質量部に対して、好ましくは0.0005質量部以上、より好ましくは0.001質量部以上、更に好ましくは0.005質量部以上、より更に好ましくは0.01質量部以上、より更に好ましくは0.05質量部以上、そして、好ましくは6.0質量部以下、より好ましくは4.0質量部以下、更に好ましくは3.0質量部以下、より更に好ましくは1.0質量部以下、より更に好ましくは0.5質量部以下、より更に好ましくは0.2質量部以下含有する、前記<22>〜<25>の何れかに記載の水硬性組成物。
炭酸カリウム及び炭酸ナトリウムから選ばれる一種以上の炭酸塩を水硬性粉体100質量部に対して、好ましくは0.0005質量部以上、より好ましくは0.001質量部以上、更に好ましくは0.005質量部以上、より更に好ましくは0.01質量部以上、そして、好ましくは6.0質量部以下、より好ましくは4.0質量部以下、更に好ましくは3.0質量部以下、より更に好ましくは1.0質量部以下、より更に好ましくは0.1質量部以下、より更に好ましくは0.05質量部以下含有する、前記<22>〜<26>の何れかに記載の水硬性組成物。
重炭酸塩を水硬性粉体100質量部に対して、好ましくは0.0005質量部以上、より好ましくは0.001質量部以上、更に好ましくは0.005質量部以上、より更に好ましくは0.01質量部以上、そして、好ましくは6.0質量部以下、より好ましくは4.0質量部以下、更に好ましくは3.0質量部以下、より更に好ましくは1.0質量部以下、より更に好ましくは0.1質量部以下、より更に好ましくは0.05質量部以下含有する、前記<22>〜<27>の何れかに記載の水硬性組成物。
ポリカルボン酸系分散剤と炭酸カリウム及び炭酸ナトリウムから選ばれる一種以上の炭酸塩の質量比(分散剤/炭酸塩)が、好ましくは0.5以上、より好ましくは1以上、更に好ましくは1.5以上、更に好ましくは5以上、そして、好ましくは60以下、より好ましくは30以下、更に好ましくは15以下、より更に好ましくは10以下である、前記<22>〜<28>の何れかに記載の水硬性組成物。
ポリカルボン酸系分散剤と重炭酸塩の質量比(分散剤/重炭酸塩)が、好ましくは0.5以上、より好ましくは1以上、更に好ましくは1.5以上、より更に好ましくは5以上、そして、好ましくは60以下、より好ましくは30以下、更に好ましくは15以下、より更に好ましくは10以下である、前記<22>〜<29>の何れかに記載の水硬性組成物。
炭酸カリウム及び炭酸ナトリウムから選ばれる一種以上の炭酸塩と重炭酸塩の質量比(炭酸塩/重炭酸塩)が、好ましくは0.25以上、より好ましくは0.5以上、更に好ましくは0.8以上、そして、好ましくは8以下、より好ましくは6以下、更に好ましくは4以下、より更に好ましくは2.5以下、より更に好ましくは2.0以下である、前記<22>〜<30>の何れかに記載の水硬性組成物。
水/水硬性粉体×100(質量%)が、好ましくは20質量%以上、より好ましくは25質量%以上、更に好ましくは30質量%以上、そして、好ましくは80質量%以下、より好ましくは70質量%以下、更に好ましくは65質量%以下である、前記<22>〜<31>の何れかに記載の水硬性組成物。
更に、細骨材及び粗骨材から選ばれる一種以上の骨材を含有する、前記<22>〜<32>の何れかに記載の水硬性組成物。
細骨材が、川砂、陸砂、山砂、海砂、石灰砂、珪砂、及びこれらの砕砂、高炉スラグ細骨材、フェロニッケルスラグ細骨材、人工及び天然の軽量細骨材、並びに再生細骨材から選ばれる一種以上である、前記<33>記載の水硬性組成物。
粗骨材が、川砂利、陸砂利、山砂利、海砂利、石灰砂利、及びこれらの砕石、高炉スラグ粗骨材、フェロニッケルスラグ粗骨材、人工及び天然の軽量粗骨材、並びに再生粗骨材から選ばれる一種以上である、前記<33>又は<34>記載の水硬性組成物。
骨材を水硬性組成物の体積あたり、好ましくは1700kg/m3以上、より好ましくは1720kg/m3以上、そして、好ましくは1800kg/m3以下、より好ましくは1760kg/m3以下含有する、前記<33>〜<35>の何れかに記載の水硬性組成物。
骨材(a)中の細骨材(s)の容積比〔s/a×100(%)〕が、好ましくは45%以上、より好ましくは47%以上、そして、好ましくは55%以下、より好ましくは53%以下である、前記<33>〜<36>の何れかに記載の水硬性組成物。
更に、消泡剤を含有し、好ましくはシリコーン系消泡剤、脂肪酸エステル系消泡剤、及びエーテル系消泡剤から選ばれる一種以上の消泡剤であり、より好ましくはジメチルポリシロキサン、ポリアルキレングリコール脂肪酸エステル、及びポリアルキレングリコールエーテルから選ばれる一種以上の消泡剤である、前記<22>〜<37>の何れかに記載の水硬性組成物。
水硬性粉体、水、ポリカルボン酸系分散剤、炭酸カリウム及び炭酸ナトリウムから選ばれる一種以上の炭酸塩、並びに重炭酸塩を混合して水硬性組成物を得る工程を有する、水硬性組成物の製造方法。
水硬性粉体、水、及び前記<1>〜<21>の何れかに記載の水硬性組成物用添加剤を混合して水硬性組成物を得る工程を有する、水硬性組成物の製造方法。
水硬性組成物用添加剤を、液体組成物、好ましくは水溶液として用いる、前記<40>記載の水硬性組成物の製造方法。
水硬性組成物用添加剤の液体組成物、好ましくは水溶液中のポリカルボン酸系分散剤の含有量が、好ましくは3質量%以上、より好ましくは5質量%以上、更に好ましくは10質量%以上、そして、好ましくは50質量%以下、より好ましくは40質量%以下、更に好ましくは35質量%以下である、前記<41>記載の水硬性組成物の製造方法。
水硬性組成物用添加剤の液体組成物、好ましくは水溶液中の炭酸カリウム及び炭酸ナトリウムから選ばれる一種以上の炭酸塩の含有量が、好ましくは0.05質量%以上、より好ましくは0.1質量%以上、更に好ましくは0.5質量%以上、そして、好ましくは50質量%以下、より好ましくは40質量%以下、更に好ましくは30質量%以下である、前記<41>又は<42>記載の水硬性組成物の製造方法。
水硬性組成物用添加剤の液体組成物、好ましくは水溶液中の重炭酸塩の含有量が、好ましくは0.05質量%以上、より好ましくは0.1質量%以上、更に好ましくは0.5質量%以上、そして、好ましくは25質量%以下、より好ましくは20質量%以下、更に好ましくは15質量%以下である、前記<41>〜<43>の何れかに記載の水硬性組成物の製造方法。
水硬性組成物用添加剤の添加量が、水硬性粉体100質量部に対して固形分換算で、好ましくは0.005質量部以上、より好ましくは0.01質量部以上、更に好ましくは0.05質量部以上、そして、好ましくは6質量部以下、より好ましくは4質量部以下、更に好ましくは3質量部以下である、前記<40>〜<44>の何れかに記載の水硬性組成物の製造方法。
水硬性粉体がセメントと石膏である、前記<39>〜<45>の何れかに記載の水硬性組成物の製造方法。
石膏がセメント100質量部に対して、好ましくは5質量部以上、より好ましくは10質量部以上、更に好ましくは20質量部以上、そして、好ましくは100質量部以下、より好ましくは80質量部以下、更に好ましくは70質量部以下の割合である、前記<46>記載の水硬性組成物の製造方法。
(分散剤)
・PCE:ポリカルボン酸系分散剤(下記製造例で製造、固形分濃度20質量%の水溶液)
・NSF:ナフタレン系分散剤(花王株式会社性、マイテイ150、固形部濃度40質量%の水溶液)
(炭酸塩)
・炭酸ナトリウム:和光純薬工業(株)製、試薬
・炭酸カリウム:和光純薬工業(株)製、試薬
・炭酸リチウム:和光純薬工業(株)製、試薬
(重炭酸塩)
・炭酸水素ナトリウム:和光純薬工業(株)製、試薬
攪拌機付きガラス製反応容器(四つ口フラスコ)に水333gを仕込み、撹拌しながら窒素置換をし、窒素雰囲気中で80℃まで昇温した。ω−メトキシポリエチレングリコールモノメタクリレート(エチレンオキシドの平均付加モル数23:NKエステルM230G、新中村化学工業株式会社製)300g、メタクリル酸(試薬:和光純薬工業株式会社製)69.7g、及び3−メルカプトプロピオン酸6.3gを水200gに混合溶解した水溶液と、過硫酸アンモニウム12.3gを水45gに溶解した水溶液の2者を、それぞれ1.5時間かけて上記反応容器中に滴下した。その後、80℃で1時間熟成し、更に過硫酸アンモニウム4.9gを水15gに溶解した水溶液を30分かけて滴下し、引き続き80℃で1.5時間熟成した。熟成終了後に40℃以下に冷却した後、48%水酸化ナトリウム水溶液50.2gで中和し、重量平均分子量43000の共重合体を得た(中和度0.7)。その後、水を用いて固形分20質量%に調整した。単量体1/[単量体1+単量体2]は75モル%である。
500ml容器に、表1に従いセメント(C)と石膏(G)並びに、分散剤、炭酸塩、及び重炭酸塩を含む水(W)を投入し、ハンドミキサー(National製、型番 MK−H3)の低速で、実施例5及び比較例10〜13は45秒混練し、実施例1〜4、6〜7及び比較例1〜9、14〜19は、105秒混練し、ペーストを得た。
表1中のセメント(C)、石膏(G)、水(W)の成分は以下の通りである。
セメント(C):普通ポルトランドセメント(太平洋セメント(株)製)
石膏(G):焼石膏(吉野石膏(株)製)
水(W):上水道水
W/Pは、[水(W)の含有量]/[水硬性粉体(P)の含有量(セメント(C)の含有量と石膏(G)の含有量の合計)]×100の質量%を示す。
得られたペーストを円筒状コーン(φ50mm×50mm)に充填し、垂直に引き上げた時の広がり(もっとも長い直径の長さとそれと垂直方向の長さの平均値)をペーストフローとして測定した。測定は、混練終了直後(0分後)に測定した。
Claims (7)
- ポリカルボン酸系分散剤、炭酸カリウム及び炭酸ナトリウムから選ばれる一種以上の炭酸塩、並びに重炭酸塩を含有し、炭酸塩と重炭酸塩の質量比(炭酸塩/重炭酸塩)が0.25以上8以下である、水硬性組成物用添加剤。
- 水硬性粉体、水、ポリカルボン酸系分散剤、炭酸カリウム及び炭酸ナトリウムから選ばれる一種以上の炭酸塩、並びに重炭酸塩を含有し、炭酸塩と重炭酸塩の質量比(炭酸塩/重炭酸塩)が0.25以上8以下である、水硬性組成物。
- ポリカルボン酸系分散剤を水硬性粉体100質量部に対して0.0005質量部以上3.0質量部以下含有する、請求項2に記載の水硬性組成物。
- 炭酸塩を水硬性粉体100質量部に対して0.0005質量部以上3.0質量部以下含有する、請求項2又は3に記載の水硬性組成物。
- 重炭酸塩を水硬性粉体100質量部に対して0.0005質量部以上3.0質量部以下含有する、請求項2〜4の何れかに記載の水硬性組成物。
- 水硬性粉体として、セメント及び石膏を配合してなる請求項2〜5の何れかに記載の水硬性組成物。
- セメント100質量部に対して、石膏を5質量部以上100質量部以下配合してなる、請求項6に記載の水硬性組成物。