JP6345218B2 - リチウム複合遷移金属酸化物製造用前駆体及びその製造方法 - Google Patents
リチウム複合遷移金属酸化物製造用前駆体及びその製造方法 Download PDFInfo
- Publication number
- JP6345218B2 JP6345218B2 JP2016215053A JP2016215053A JP6345218B2 JP 6345218 B2 JP6345218 B2 JP 6345218B2 JP 2016215053 A JP2016215053 A JP 2016215053A JP 2016215053 A JP2016215053 A JP 2016215053A JP 6345218 B2 JP6345218 B2 JP 6345218B2
- Authority
- JP
- Japan
- Prior art keywords
- transition metal
- lithium
- producing
- composite transition
- metal oxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
Aは、OH1−xを除外した一つ以上のアニオンであり、
0<x<0.5、
0.01≦y≦0.5、
nは、Aの酸化数である。
3Lの湿式反応器用タンクに蒸留水2Lを満たした後、窒素ガスをタンクに1L/minの速度で連続的に投入して溶存酸素を除去した。このとき、タンク中の蒸留水の温度を温度維持装置を用いて45〜50℃に維持した。また、タンクの外部に設置されているモーターと連結されているインペラを用いて、タンク内部の蒸留水を1000〜1200rpmの速度で撹拌した。
0.2mol%のNa3PO4を添加した3M水酸化ナトリウム水溶液を使用したこと以外は、実施例1と同様の方法で遷移金属前駆体を製造した。
0.5mol%のNa3PO4を添加した3M水酸化ナトリウム水溶液を使用したこと以外は、実施例1と同様の方法で遷移金属前駆体を製造した。
Na3PO4の代わりに、0.1mol%の(NH4)2HPO4を使用したこと以外は、実施例1と同様の方法で遷移金属前駆体を製造した。
Na3PO4を添加していない3M水酸化ナトリウム水溶液を使用したこと以外は、実施例1と同様の方法で遷移金属前駆体を製造した。
上記実施例1〜4及び比較例1でそれぞれ製造された遷移金属前駆体0.01gを、50ml Corning tubeに正確に測定して入れ、少量の酸を滴加した後、振って混合した。混合された試料が透明に溶解したとき、Ion Chromatograph(Diones社製のモデルDX500)で試料のPO4イオンの濃度を測定する。その結果を下記表1に示す。
上記実施例1〜4及び比較例1でそれぞれ製造された遷移金属前駆体を、Powder Multi Tester(SEISHIN社製)で1000回以上タッピング(tapping)した後、タップ密度を測定した。
実施例1〜4でそれぞれ製造されたニッケル−コバルト−マンガン複合遷移金属前駆体をLi2CO3と1:1の比率(重量比)で混合した後、5℃/分の昇温速度で加熱して、950℃で10時間焼成させて、Li[Ni0.4Co0.2Mn0.4]O2の正極活物質粉末を製造した。
比較例1で製造されたニッケル−コバルト−マンガン複合遷移金属前駆体をLi2CO3と1:1の比率(重量比)で混合した後、5℃/分の昇温速度で加熱して、950℃で10時間焼成させてLi[Ni0.4Co0.2Mn0.4]O2を製造した後、このように製造されたLi[Ni0.4Co0.2Mn0.4]O2にLi3PO4 1重量%を混合して、正極活物質粉末を製造した。
比較例1で製造されたニッケル−コバルト−マンガン複合遷移金属前駆体をLi2CO3と1:1の比率(重量比)で混合した後、5℃/分の昇温速度で加熱して、950℃で10時間焼成させてLi[Ni0.4Co0.2Mn0.4]O2を製造した。このように製造されたLi[Ni0.4Co0.2Mn0.4]O2の表面全体に、メカノフュージョン(mechano fusion)を用いてLi3PO4 1重量%をコーティングして正極活物質粉末を製造した後、比較例2と同様の方法を用いて、2016コイン電池を製造した。
比較例1で製造されたニッケル−コバルト−マンガン複合遷移金属前駆体をLi2CO3と1:1の比率(重量比)で混合した後、5℃/分の昇温速度で加熱して、950℃で10時間焼成させてLi[Ni0.4Co0.2Mn0.4]O2を製造した後、比較例2と同様の方法を用いて、2016コイン電池を製造した。
上記において実施例5〜8及び比較例2〜4でそれぞれ製造されたコイン電池に対して、電気化学分析装置(Toyo System、Toscat 3100U)を用いて、3.0〜4.25Vの領域で正極活物質の電気的特性を評価した。
その結果を下記表3に示す。
上記実施例5〜8及び比較例2〜4でそれぞれ製造されたコイン電池を、0.2Cで充電し、0.2C及び2Cで放電して、レート特性を評価した。
Claims (10)
- リチウム複合遷移金属酸化物の製造に使用される遷移金属前駆体であって、下記化学式2で表される複合遷移金属化合物からなることを特徴とする、遷移金属前駆体。
Ni b Mn c Co 1−(b+c+d) M’ d (OH 1−x ) 2−y A y/n (2)
上記式中、0.3≦b≦0.9、
0.1≦c≦0.6、
0≦d≦0.1、
b+c+d<1、
M’は、Al、Mg、Cr、Ti、Si、Cu、Fe及びZrからなる群から選択される一つまたは2つ以上であり、
AはPO 4 であり、
0<x<0.5、
0.01≦y≦0.5、
nは、3であり、
前記遷移金属前駆体の遷移金属の全量を基準としてNiの含量は30〜90mol%である。 - 前記複合遷移金属化合物は、タップ密度が1.5〜2.5g/cm 3 であることを特徴とする、請求項1に記載の遷移金属前駆体。
- 請求項1に記載の化学式2で表されるリチウム複合遷移金属酸化物の製造用の複合遷移金属化合物を製造する方法であって、前駆体製造用遷移金属塩を0.01〜0.5モル%の範囲で塩基性物質溶液に含まれているZx’Ay’と反応させる過程を含むことを特徴とする、複合遷移金属化合物を製造する方法。
上記において、Zは、Na、NH4、Hからなる群から選択される一つ以上であり、
Aは、PO4 であり、
0<x’<4及び0<y’<4の範囲で、Zの酸化数×x’−3×y’=0である条件を満たす。 - 前記前駆体製造用遷移金属塩は硫酸塩であることを特徴とする、請求項3に記載の複合遷移金属化合物を製造する方法。
- 前記硫酸塩は、硫酸ニッケル、硫酸コバルト及び硫酸マンガンからなる群から選択される一つまたは2つ以上であることを特徴とする、請求項4に記載の複合遷移金属化合物を製造する方法。
- 前記Zx’Ay’は、Na3PO4、(NH4)3PO4、(NH4)2HPO4、(NH4)H2PO4からなる群から選択される一つ以上であることを特徴とする、請求項3に記載の複合遷移金属化合物を製造する方法。
- 前記Zx’Ay’は、水酸化ナトリウム水溶液に溶解した状態で反応槽に投入されることを特徴とする、請求項3に記載の複合遷移金属化合物を製造する方法。
- 請求項1に記載の遷移金属前駆体とリチウム含有物質とを焼成反応させる段階を含むリチウム複合遷移金属酸化物の製造方法であって、アニオンAが該リチウム複合遷移金属酸化物の表面と内部に均一に含まれていることを特徴とする、リチウム複合遷移金属酸化物の製造方法。
- 前記アニオンAは、リチウム複合遷移金属酸化物全体の重量を基準として0.05〜3重量%含まれていることを特徴とする、請求項8に記載のリチウム複合遷移金属酸化物の製造方法。
- 請求項1に記載の遷移金属前駆体とリチウム含有物質とを焼成反応させて、リチウム複合遷移金属酸化物を製造する段階を含み、該リチウム複合遷移金属酸化物を正極活物質として含むことを特徴とする、リチウム二次電池の製造方法。