JP6226923B2 - 鋼管用ねじ継手 - Google Patents
鋼管用ねじ継手 Download PDFInfo
- Publication number
- JP6226923B2 JP6226923B2 JP2015160162A JP2015160162A JP6226923B2 JP 6226923 B2 JP6226923 B2 JP 6226923B2 JP 2015160162 A JP2015160162 A JP 2015160162A JP 2015160162 A JP2015160162 A JP 2015160162A JP 6226923 B2 JP6226923 B2 JP 6226923B2
- Authority
- JP
- Japan
- Prior art keywords
- coating
- curable resin
- film
- resin film
- threaded joint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本願は、2012年06月07日に、日本に出願された特願2012−130134号に基づき優先権を主張し、その内容をここに援用する。
図2は、油井管Aの締結に使用される典型的なねじ継手(特殊ねじ継手とも呼ばれる)のピン−ボックス構造の詳細を模式的に示す図である。ピン1は、雄ねじ11を有する継手要素であって、典型的には油井管Aの端部に形成される。ボックス2は、雌ねじ21を有する継手要素であって、典型的にはねじ継手部品(カップリングB)の内面に形成される。ピン1は、雄ねじ11に加えて、このねじ部より鋼管先端側に位置するシール部13とショルダー部14とを備える。これに対応して、ボックス2は、雌ねじ21に加えて、このねじ部より内側にシール部23と、ピン1のショルダー部14が当接するショルダー部24とを備える。ピン1およびボックス2のそれぞれシール部13、23およびショルダー部14、24が鋼管用ねじ継手のねじ無し金属接触部である。符号12はピン1の先端のリップ部を示し、符号31は、ピン1とボックス2とが接触しない部分(締付け時に滲みだした油分が溜まる部分)を示す。
(1)本発明の一態様に係る鋼管用ねじ継手は、シール部を含むねじ無し金属接触部と、ねじ部とを有する接触表面をそれぞれ備えたピン及びボックスから構成される鋼管用ねじ継手であって、前記ピンおよび前記ボックスの少なくとも一方の部材の前記接触表面に形成された紫外線硬化樹脂被膜と;前記紫外線硬化樹脂被膜の表面の全部に形成されたアクリルシリコーン樹脂被膜と;を有し、前記アクリルシリコーン樹脂被膜の厚さが5〜10μmである。
本実施形態の鋼管用ねじ継手は、ねじ部と、シール部およびショルダー部を含むねじ無し金属接触部とを有する接触表面をそれぞれ備えたピン1及びボックス2から構成されている。つまり、図1及び図2を参照すると、ピン1は、ねじ部として雄ねじ11を備え、ねじ無し金属接触部としてシール部13及びショルダー部14を備えている。また、ボックス2は、ねじ部として雌ねじ21を備え、ねじ無し金属接触部としてシール部23及びショルダー部24を備えている。
本実施形態の鋼管用ねじ継手は、ピン1およびボックス2の少なくとも一方の部材(すなわち、ピン1のみ、ボックス2のみ、またはピン1とボックス2の両方)の接触表面(好ましくは接触表面の全面)に形成された紫外線硬化樹脂被膜と、この紫外線硬化樹脂被膜の表面の少なくとも一部、好ましくはシール部13、23を覆っている部分に形成されたアクリルシリコーン樹脂被膜とを備える。
紫外線硬化樹脂被膜は、鋼材に適用可能な適当な紫外線硬化樹脂塗料を用いて形成することができる。一般に、紫外線硬化樹脂塗料は、少なくともモノマー、オリゴマー、および光重合開始剤を含有し、それ以外に顔料、防錆剤、消泡剤やレベリング剤などの各種添加剤を含有しうる。そのような紫外線硬化樹脂塗料の一例は、上記の特許文献1に光硬化性組成物として開示されているが、それに限られるものではない。また、市販の紫外線硬化性樹脂塗料を使用してもよい。
アクリルシリコーン樹脂被膜は、上記の紫外線硬化樹脂皮膜の表面の少なくとも一部に形成されている。すなわち、本実施形態の鋼管用ねじ継手では、ピン1及びボックス2の少なくとも一方の接触表面の少なくとも一部に、下層の紫外線硬化樹脂被膜と上層のアクリルシリコーン樹脂被膜との二層構造の被膜が形成されている。紫外線硬化樹脂被膜の上層にアクリルシリコーン樹脂被膜を設けることで、上述した補修効果に加え、鋼管用ねじ継手の潤滑性能が向上するので、焼付きがより起こりにくくなる。
アクリルシリコーン樹脂被膜の膜厚は、1〜100μmの範囲内であることが好ましい。
アクリルシリコーン樹脂被膜の膜厚が1μm未満の場合には、防錆性が著しく低下し、アクリルシリコーン樹脂被膜の膜厚が100μmを越える場合には、潤滑性が著しく低下する。
アクリルシリコーン樹脂被膜の膜厚は、防錆性と潤滑性の両立の観点から5〜10μmの範囲内であることがより好ましい。
アクリルシリコーン樹脂被膜の膜厚が5〜10μmの範囲である場合、一定の防錆性能の向上が確認できたが、アクリルシリコーン樹脂被膜の膜厚が10μmよりも厚い場合には、さらなる防錆性能の向上が確認できなかった。一方で、アクリルシリコーン樹脂皮膜の膜厚が厚くなると、耐焼き付き性が阻害され、締め緩めの繰り返しの許容回数が減ることになる。
なお、紫外線硬化樹脂皮膜は、モノマー、オリゴマー及び光重合開始剤等を含有する塗料に、紫外線を照射して光重合開始剤からラジカルを発生させ、このラジカルによりモノマーをポリマーに転換させて塗料を硬化させるという硬化プロセスを経て得られるものである。これに対して、アクリルシリコーン樹脂皮膜は、アクリルシリコーン樹脂、揮発性溶剤及び硬化剤等を含有する塗料(例えば油性シリコーンラッカースプレー)の溶剤を揮発させて塗料を硬化させるという硬化プロセスを経て得られるものである。
つまり、紫外線硬化樹脂皮膜とアクリルシリコーン樹脂皮膜との硬化プロセスは、基本的に全く異なるものである。
紫外線硬化樹脂被膜が形成される鋼管用ねじ継手の接触表面であるねじ部やねじ無し金属接触部は、ねじ切りを含む切削加工により形成され、一般にその表面粗さは3〜5μm程度である。接触表面の表面粗さをこれより大きくすると、その上に形成される被膜の密着性を高めることができ、結果としてねじ継手の締付け性や防錆性といった性能を改善することができる。そのために、紫外線硬化樹脂被膜の形成に先立って、鋼管用ねじ継手の接触表面に、表面粗さを大きくすることができる下地処理を施してもよい。
化成処理は、針状結晶からなる表面粗さの大きな化成被膜を形成することによって、表面粗さを大きくし、その上に形成される固体防食被膜および固体潤滑被膜の密着性を高めることができる。なお、防錆性をより向上させるには、リン酸亜鉛、或いはリン酸マンガンなどで下地層(紫外線硬化樹脂被膜の下層)を形成することが好ましい。
下層の紫外線硬化樹脂被膜と上層のアクリルシリコーン樹脂被膜を、鋼管用ねじ継手のピン1とボックス2の一方の部材(例えば、ピン1)の接触表面だけに形成する場合、他方の部材(例えば、ボックス2)の接触表面に対する処理は特に規定されない。例えば、下層の紫外線硬化樹脂被膜だけを形成してもよい。或いは、従来技術で提案されたか、または今後に提案される各種の鋼管用ねじ継手の表面処理を適用してもよい。
なお、上記実施形態では、ショルダー部14、24を備える鋼管用ねじ継手を例示して説明したが、例えば、楔型ねじ等、ねじ自体に締め付けの回転を停止させるロッキング機能が設けられたねじ継手など、ショルダー部14、24を備えていない鋼管用ねじ継手にも本発明を適用することが可能である。
本実施例では、鋼管用ねじ継手の接触表面を被覆する紫外線硬化被膜の上に各種の樹脂被膜を形成して、防錆性を調査した。参考のために、紫外線硬化樹脂被膜のみ、およびこの紫外線硬化樹脂被膜の上に、高い防錆効果があることが知られている浸透潤滑剤のCRC5−56(呉工業KURE 5-56)を塗布した場合についても同じ試験を実施した。
(1)熱硬化性アクリル樹脂塗料:アクリルラッカースプレーα(大日本塗料)
(2)フッ素樹脂塗料:ヘンケルジャパンより入手したポリテトラフルオロエチレンのスプレー塗料
(3)アクリルシリコーン樹脂塗料:シリコーンラッカースプレー(アクリルシリコーン樹脂塗料)(カンペハピオ社)
塗装後の塗膜の乾燥は、その塗料の指示通りに実施したが、いずれも自然乾燥であった。各種樹脂塗料または浸透潤滑剤CRC5−56はいずれも時間にして5秒間程度塗布した。
実施例1において、下層の紫外線硬化樹脂被膜と上層のアクリルシリコーン樹脂被膜の2層構造の被膜の防錆効果が著しく高いことが実証された。しかし、鋼管用ねじ継手の場合、ねじ継手の締付け特性が最も重要な性能となるが、アクリルシリコーン樹脂被膜の形成がこれらの性能を阻害することも懸念される。そのため、上記2層被膜の締付け性能および気密性への影響を調査した。
紫外線硬化樹脂被膜を形成する前に実施した下地処理は、ピン表面にはリン酸亜鉛処理、ボックス表面には銅−錫−亜鉛3元合金めっき処理であった。
(締付け性能)
締付け性能は、ショルダリングトルクおよびトルクオンショルダー抵抗への影響により評価した。ショルダリングトルクは、ピンとボックスのショルダー部が互いに接触した時(干渉し始めた時)のトルク値である。また、トルクオンショルダー抵抗とは、上記ショルダリングトルクからショルダー部の降伏変形までのトルク差である。このトルクオンショルダー抵抗が大きいほど、ねじ継手の締付け時の規定トルク値を高く設定することができるため、規定トルクで締付けた時のシール部の干渉量、従ってねじ継手の気密性を高めることができる。ねじ継手を最終的に規定のトルク値で締め付けたときに、規定トルク値とショルダリングトルク値の差がピン/ボックスのシール部の接触圧力に影響を与えるため、ショルダリングトルク値およびトルクオンショルダー抵抗値の管理が重要である。
上記のようにピン表面とボックス表面を処理した鋼管用ねじ継手を、規定トルク(7470ft−lbs)で締結した後、ISO13679の方法に従って、継手を180℃に加熱し、内圧/外圧、引張/圧縮の複合荷重下で気密試験を実施した。この気密試験の結果、アクリルシリコーン樹脂被膜の有無で気密性能に差異が無いことを確認した。
B カップリング
1 ピン
2 ボックス
11 雄ねじ
21 雌ねじ
13、23 シール部
14、24 ショルダー部
Claims (2)
- シール部を含むねじ無し金属接触部と、ねじ部とを有する接触表面をそれぞれ備えたピン及びボックスから構成される鋼管用ねじ継手であって、
前記ピンおよび前記ボックスの少なくとも一方の部材の前記接触表面に形成された紫外線硬化樹脂被膜と;
前記紫外線硬化樹脂被膜の表面の全部に形成されたアクリルシリコーン樹脂被膜と;
を有し、
前記アクリルシリコーン樹脂被膜の厚さが5〜10μmであることを特徴とする鋼管用ねじ継手。 - 前記紫外線硬化樹脂皮膜は、着色剤を含有していることを特徴とする請求項1に記載の鋼管用ねじ継手。