JP6090970B2 - 偏光板、その製造方法、光学フィルムおよび画像表示装置 - Google Patents
偏光板、その製造方法、光学フィルムおよび画像表示装置 Download PDFInfo
- Publication number
- JP6090970B2 JP6090970B2 JP2012110784A JP2012110784A JP6090970B2 JP 6090970 B2 JP6090970 B2 JP 6090970B2 JP 2012110784 A JP2012110784 A JP 2012110784A JP 2012110784 A JP2012110784 A JP 2012110784A JP 6090970 B2 JP6090970 B2 JP 6090970B2
- Authority
- JP
- Japan
- Prior art keywords
- polarizing plate
- polarizer
- film
- transparent protective
- protective film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
前記易接着層は、ポリマー樹脂100重量部に対して、水溶性の還元剤を0.1〜3重量部含有するポリマー樹脂組成物により形成されたものであることを特徴とする偏光板、に関する。
偏光子と、
ポリマー樹脂100重量部に対して、水溶性の還元剤を0.1〜3重量部を含有するポリマー樹脂組成物により形成された易接着層が設けられている透明保護フィルムを、
前記透明保護フィルムに設けられた易接着層と偏光子が対面するように、接着剤により貼り合わせる工程、
を有することを特徴とする偏光板の製造方法、に関する。さらに本発明は、前記製造方法により得られた偏光板、に関する。
本発明の偏光板に用いられる偏光子としては、例えば、ポリビニルアルコール系フィルム、部分ホルマール化ポリビニルアルコール系フィルム、エチレン・酢酸ビニル共重合体系部分ケン化フィルム等の親水性高分子フィルムに、ヨウ素や二色性染料の二色性物質を吸着させて一軸延伸したもの、ポリビニルアルコールの脱水処理物やポリ塩化ビニルの脱塩酸処理物等ポリエン系配向フィルム等が挙げられる。これらの中でも、ポリビニルアルコール系フィルムとヨウ素などの二色性物質からなる偏光子が好適である。これら偏光子の厚さは特に制限されないが、一般的に、1〜80μm程度である。
透明保護フィルムを構成する材料としては、例えば透明性、機械的強度、熱安定性、水分遮断性、等方性などに優れる熱可塑性樹脂が用いられる。このような熱可塑性樹脂の具体例としては、トリアセチルセルロール等のセルロール樹脂、ポリエステル樹脂、ポリエーテルスルホン樹脂、ポリスルホン樹脂、ポリカーボネート樹脂、ポリアミド樹脂、ポリイミド樹脂、ポリオレフィン樹脂、(メタ)アクリル樹脂、環状ポリオレフィン樹脂(ノルボルネン系樹脂)、ポリアリレート樹脂、ポリスチレン樹脂、ポリビニルアルコール樹脂、およびこれらの混合物があげられる。なお、偏光子の片側には、透明保護フィルムが接着剤層により貼り合わされるが、他の片側には、透明保護フィルムとして、(メタ)アクリル系、ウレタン系、アクリルウレタン系、エポキシ系、シリコーン系等の熱硬化性樹脂または紫外線硬化型樹脂を用いることができる。
前記接着剤としては、光学的に透明であり、易接着層から溶出した水溶性の還元剤を偏光子中に浸入させやすいものを用いるものを特に制限されなく使用でき、例えば、水系、溶剤系、ホットメルト系、ラジカル硬化型の各種形態のものが用いられるが、水系接着剤が好適である。
本発明の偏光板は、偏光子と透明保護フィルムが接着剤層を介して設けられているが、透明保護フィルムと接着剤層の間には、易接着層を有する。易接着層は、水溶性の還元剤およびポリマー樹脂を含有するポリマー樹脂組成物により形成されたものである。
本発明の偏光板は、透明保護フィルムと偏光子を、前記接着剤を用いて貼り合わせることにより製造する。また、透明保護フィルムと、接着剤により形成される接着剤層の間には易接着層を形成する。当該易接着層は、通常、透明保護フィルム上に形成した後、当該易接着層と偏光子が対面するように、前記接着剤により貼り合わせる。
平均重合度2400、ケン化度99.9モル%、厚さ75μmのポリビニルアルコールフィルムを、30℃の温水中に60秒間浸漬して膨潤させた。次いで、0.3重量%(重量比:ヨウ素/ヨウ化カリウム=0.5/8)の30℃のヨウ素溶液中で1分間染色しながら、3.5倍まで延伸した。その後、65℃の4重量%のホウ酸水溶液中に0.5分間浸漬しながら総合延伸倍率が6倍まで延伸した。延伸後、70℃のオーブンで3分間乾燥を行い、厚さ26μmの偏光子を得た。偏光子の水分率は13.5重量%であった。
(1):ラクトン化ポリメチルメタクリレートフィルム(ラクトン化率20%,厚み30μm,Re=0nm,Rth=0nm;表1中でLMMAと示す)、
(2):ノルボルネン系樹脂フィルム(日本ゼオン(株)製,商品名ゼオノア,厚み40μm;表1中でゼオノアと示す)、
(3):セルロース樹脂フィルム(コニカミノルタオプト(株)製,商品名KC4UY,厚み40μm;表1中でKC4UYと示す)、を選択して用いた。
(4):ポリエステル樹脂フィルム(三菱樹脂(株)製,商品名S100−38,厚み38μm;表1中でS100−38と示す)、または、
位相差値の測定は、平行ニコル回転法を原理とする位相差計〔王子計測機器(株)製,製品名「KOBRA21−ADH」〕を用いて、波長590nmの値について測定した、nx、ny、nzの値と、フィルム厚み(d)から、正面位相差Re、厚み方向位相差Rth、Nzを求めた。[ただし、フィルムの遅相軸方向、進相軸方向及び厚さ方向の屈折率をそれぞれnx、ny、nzとし、d(nm)はフィルムの厚みとする。遅相軸方向は、フィルム面内の屈折率の最大となる方向とする。]。
アセトアセチル基変性したポリビニルアルコール樹脂100重量部(アセチル化度13%)に対してメチロールメラミン20重量部を含む水溶液を、濃度5%になるように調整した接着剤水溶液を作製した。
(易接着層の形成)
ポリエステル骨格を有するポリマー(スパーフレックスSF210,第一工業製薬(株)製)100重量部(固形分)に対して、アスコルビン酸0.8重量部を配合した形成材(固形分濃度11重量%の水溶液)を調製した。当該形成材を上記透明保護フィルム(1)(ラクトン化ポリメチルメタクリレートフィルム)の片側に、バーコーターを用いて厚さ2μmになるように塗工し、150℃で乾燥して、透明保護フィルム上に易接着層を形成した。乾燥後における易接着層厚みは0.2μmであった。
上記で得られた偏光子の両面に、上記易接着層付き透明保護フィルム(1)と厚さ80μmのケン化処理を施したトリアセチルセルロースフィルムを、上記接着剤を介して積層し、圧延ロールで密着させた後、70℃にて4分間乾燥させて、偏光板を作製した。
実施例1において、透明保護フィルムの種類、易接着層を形成するポリマー樹脂、水溶性の還元剤の種類またはそれらの使用量を表1に示すように変えたこと以外は実施例1と同様にして偏光板を得た。
実施例および比較例で得られた、偏光板について下記評価を行った。結果を表1に示す。
得られた偏光板を、15mm×150mmのサイズに裁断してサンプルとした。サンプルを両面接着テープ(日東電工(株)製,No.500)によりガラス板上に貼り付けた。サンプル(偏光板)には、透明保護フィルムと偏光子の間に予めキッカケを設けておき、そのキッカケを変角度ピール試験機(アサヒセイコウ社製)にチャックしてピール強度(N/15mm)を測定した。測定条件は、常温(23℃)、ピール角:90度、ピール速度:3000mm/minとした。得られた測定データの50mm〜100mm間のデータを平均化した値を表1に示す。
偏光子の単体透過率(Ts)、偏光度(P)は、積分球付き分光光度計(日本分光(株)製のV7100)にて測定した。
なお、偏光度は、2枚の同じ偏光子を両者の透過軸が平行となるように重ね合わせた場合の透過率(平行透過率:Tp)および、両者の透過軸が直交するように重ね合わせた場合の透過率(直交透過率:Tc)を以下の式に適用することにより求められるものである。
偏光度P(%)={(Tp−Tc)/(Tp+Tc)}1/2×100
各透過率は、グランテラープリズム偏光子を通して得られた完全偏光を100%として、JIS Z8701の2度視野(C光源)により視感度補整したY値で示したものである。測定波長は、波長410nmであった。得られた410nmにおける直交透過率を光学特性評価の指標とした。
SF210:ポリエステル骨格を有するポリマー(スパーフレックスSF210,第一工業製薬(株)製);
WLS202:ポリエーテル骨格を有するポリマー(ハイドランWLS202,大日本インキ化学工業(株)製)、を示す。
Claims (10)
- 偏光子の少なくとも一方の面に、偏光子の側から接着剤層および易接着層をこの順で介して透明保護フィルムが設けられている偏光板であって、
前記易接着層は、ポリマー樹脂100重量部に対して、水溶性の還元剤を0.1〜3重量部含有するポリマー樹脂組成物から形成されたものであることを特徴とする偏光板。 - 前記水溶性の還元剤がアスコルビン酸、エリソルビン酸,チオ硫酸、亜硫酸およびこれらの塩の少なくともいずれか1種類を含むことを特徴する請求項1記載の偏光板。
- 前記易接着層を形成するポリマー樹脂が、ポリエステル骨格を有することを特徴とする請求項1または2に記載の偏光板。
- 前記偏光子が、ポリビニルアルコール系フィルムにヨウ素が吸着配向されているヨウ素系偏光子であることを特徴とする請求項1〜3のいずれかに記載の偏光板。
- 前記透明保護フィルムが、セルロース樹脂、ポリカーボネート樹脂、環状ポリオレフィン樹脂、ポリエステル樹脂および(メタ)アクリル樹脂から選ばれるいずれか少なくとも1つであることを特徴とする請求項1〜4のいずれかに記載の偏光板。
- 前記接着剤層が、ポリビニルアルコール系水系接着剤であることを特徴とする請求項1〜5のいずれかに記載の偏光板。
- 偏光子の少なくとも一方の面に、接着剤層および易接着層をこの順で介して透明保護フィルムが設けられている請求項1〜6のいずれかに記載の偏光板の製造方法であって、
偏光子と、
ポリマー樹脂100重量部に対して、水溶性の還元剤を0.1〜3重量部を含有するポリマー樹脂組成物から形成された易接着層が設けられている透明保護フィルムを、
前記透明保護フィルムに設けられた易接着層と偏光子が対面するように、接着剤により貼り合わせる工程、
を有することを特徴とする偏光板の製造方法。 - 請求項7に記載の製造方法により得られた偏光板。
- 請求項1〜6、8のいずれかに記載の偏光板を有すことを特徴とする光学フィルム。
- 請求項1〜6、8のいずれかに記載の偏光板または請求項9記載の光学フィルムを有することを特徴とする画像表示装置。