JP6031818B2 - ステンレス鋼スラグの冷却方法 - Google Patents
ステンレス鋼スラグの冷却方法 Download PDFInfo
- Publication number
- JP6031818B2 JP6031818B2 JP2012108425A JP2012108425A JP6031818B2 JP 6031818 B2 JP6031818 B2 JP 6031818B2 JP 2012108425 A JP2012108425 A JP 2012108425A JP 2012108425 A JP2012108425 A JP 2012108425A JP 6031818 B2 JP6031818 B2 JP 6031818B2
- Authority
- JP
- Japan
- Prior art keywords
- slag
- stainless steel
- cooling
- steel slag
- mold
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
ところが、近年、土壌環境基準の項目にホウ素(B)が加えられたことから、スラグを路盤材等地面下に埋める場合には、B溶出量は、1.0mg/L以下に規制される。スラグ中のB含有量が0.05質量%以上になると、B溶出量は1.0mg/Lを超える場合があるが、粉化防止のためには、スラグ中のB含有量を0.1質量%以上にすることを要する。
したがって、Bの溶出量規制の観点から、溶融スラグにホウ素化合物を添加する方法を用いることができなくなった。
すなわち、本発明は、以下の(1)〜(3)を提供する。
(i) Y≧−154.5X+2988
(i) Y≧−154.5X+2988
すなわち、高温レーザー顕微鏡は、比較的広範囲で冷却速度を制御可能であり、かつ、粉化現象等について、オンサイトでクリアな観察画像が得られるという理由から、本試験に適した装置であると判断した。
(i) Y≧−154.5X+2988
このようなステンレス鋼スラグ中において、CaO含有量は、30〜50質量%が好ましく、35〜45質量%がより好ましい。また、SiO2含有量は、10〜25質量%が好ましく、15〜22質量%がより好ましい。また、MgO含有量は、15〜30質量%が好ましく、20〜25質量%がより好ましい。これらの成分の含有量が上記範囲内であれば、本発明の効果がより優れる。
なお、チェーンホイル4は、無段変速可能で動力として変速可能なモーター(図示せず)と、これに連結する減速機(図示せず)とによって、回転駆動される。このようなモーターおよび減速機を駆動することにより、チェーンホイル4の回転駆動速度が制御される。
なお、溶融スラグ5の冷却速度は、本来は、溶融スラグ5(凝固スラグ5′)の内部温度に基づいて求めるのが好ましいが、循環移動するモールド2内の溶融スラグ5(凝固スラグ5′)の内部温度を測定するのが困難であることから、ここでは、自由表面温度により求めるものである。
また、凝固スラグ5′は、放射温度計9bで測定される自由表面温度が、1000℃以下まで冷却を行なった。その結果、いずれの例においても、落下した凝固スラグ5′に溶融スラグ5が含まれないことが確認された。
さらに、放射温度計9cで測定されるモールド2の凹面2a温度が、250℃になるように、散水ノズル8の散水量を調整した。
2 メタルモールド
2a 凹面
3 チェーンコンベア
4 チェーンホイル
5 溶融スラグ
5′ 凝固スラグ
6 スラグ鍋
7 スラグ樋
8 散水ノズル
9 放射温度計
Claims (3)
- 水砕処理または風砕処理を用いることなくステンレス鋼スラグを冷却する、ステンレス鋼スラグの冷却方法であって、
前記ステンレス鋼スラグ中のAl2O3含有量をX(単位:質量%)とした場合に、Xが12.4〜14.6であり、下記式(i)を満たす冷却速度Y(単位:℃/min)で前記冷却を行うことを特徴とする、ステンレス鋼スラグの冷却方法。
(i) Y≧−154.5X+2988 - 前記ステンレス鋼スラグが、30〜50質量%のCaO、10〜25質量%のSiO2、および、15〜30質量%のMgOを含有する、請求項1に記載のステンレス鋼スラグの冷却方法。
- 前記冷却速度が、50000℃/min未満である、請求項1または2に記載のステンレス鋼スラグの冷却方法。