JP5760574B2 - 着色粘着テープ - Google Patents
着色粘着テープ Download PDFInfo
- Publication number
- JP5760574B2 JP5760574B2 JP2011065764A JP2011065764A JP5760574B2 JP 5760574 B2 JP5760574 B2 JP 5760574B2 JP 2011065764 A JP2011065764 A JP 2011065764A JP 2011065764 A JP2011065764 A JP 2011065764A JP 5760574 B2 JP5760574 B2 JP 5760574B2
- Authority
- JP
- Japan
- Prior art keywords
- colored
- acrylate
- sensitive adhesive
- pressure
- meth
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明に使用する支持体は、着色層を有する支持体であり、着色層のハロゲン含有量が0.3質量%以下、好ましくは0.05質量%以下であり、ハロゲンを実質的に含有しないものが特に好ましい。ここで、ハロゲン含有量は、蛍光X線で分析したときの検出量である。たとえば、蛍光X線の分析装置としてはRigaku社製「ZSX Primus」、「ZSX PrimusII」等が挙げられる。
バーコーターにてポリエステルウレタン樹脂を厚さ50μmに製膜する。次に試料長さ20mmにカットした試験片(試料長20mm、膜厚50μ)を粘弾性試験機を用いて、周波数1Hz、昇温時間3℃/1分の条件で−150℃から250℃までの貯蔵弾性率(G’)と損失弾性率(G”)を測定する。損失正接tanδは、以下の計算式より算出する。
損失正接tanδ=G”/G’
粘弾性試験機としては例えば、セイコーインスツル社製DMS210、DMS220、DMS6100等があげられる。
本発明に使用する粘着剤層は、水性媒体中にアクリル系共重合体エマルジョン粒子が分散した水分散型アクリル系粘着剤組成物を架橋して形成される粘着剤層である。そして、アクリル系共重合体エマルジョン粒子を形成するアクリル系共重合体が、炭素数4〜8のアルキル基を有する(メタ)アクリレート、カルボキシル基含有モノマー、および、窒素含有ビニルモノマーをモノマー成分として所定量含有し、前記炭素数4〜8のアルキル基を有する(メタ)アクリレートとして2−エチルヘキシルアクリレートを含有する。本発明においては、上記支持体の着色層表面と積層する粘着剤層として、当該粘着剤層を使用することで、ハロゲンフリーの着色層を有する支持体を使用し、粘着剤層を水系の粘着剤層とした場合にも、好適な接着性を実現できると共に、支持体と粘着剤層間のアンカリングが良好となり、好適なリワーク性を実現できる。
本発明に使用する水分散型アクリル系粘着剤組成物においては、得られる粘着剤層の強接着性を調整するために粘着付与樹脂を使用することが好ましい。本発明に使用する粘着付与樹脂としては、水分散型の粘着剤組成物に使用する観点から、エマルジョン型の粘着付与樹脂を好ましく使用できる。当該エマルジョン型の粘着付与樹脂としては、ロジン系、重合ロジン系、重合ロジンエステル系、ロジンフェノール系、安定化ロジンエステル系、不均化ロジンエステル系、テルペン系、テルペンフェノール系、石油樹脂系等が例示できる。
本発明に使用する水分散型アクリル系粘着剤組成物においては、得られる粘着剤層の凝集力を向上させる目的で、架橋剤を使用することが好ましい。架橋剤としては、公知のイソシアネート系架橋剤、エポキシ系架橋剤、アジリジン系架橋剤、多価金属塩系架橋剤、金属キレート系架橋剤、ケト・ヒドラジド系架橋剤、オキサゾリン系架橋剤、カルボジイミド系架橋剤、シラン系架橋剤、グリシジル(アルコキシ)エポキシシラン系架橋剤等が使用できる。その中でも、重合終了後に添加し、架橋反応を進行させるタイプの架橋剤が好ましい。例えば、イソシアネート系架橋剤、エポキシ系架橋剤、オキサゾリン系架橋剤、カルボジイミド系架橋剤、グリシジル(アルコキシ)エポキシシラン系架橋剤等が挙げられる。具体的には、イソシアネート系架橋剤では、バーノック DNW−5000[DIC(株)製]、バーノック DNW−5010[DIC(株)製]、バーノック DNW−5100[DIC(株)製]、バーノック DNW−5500[DIC(株)製]、アクアネート100[日本ポリウレタン工業(株)製]、アクアネート105[日本ポリウレタン工業(株)製]、アクアネート110[日本ポリウレタン工業(株)製]、アクアネート120[日本ポリウレタン工業(株)製]、アクアネート130[日本ポリウレタン工業(株)製]、アクアネート200[日本ポリウレタン工業(株)製]、アクアネート210[日本ポリウレタン工業(株)製]、LS2319[住化バイエルウレタン(株)製]、LS2336[住化バイエルウレタン(株)製]、Bayhydur3100[住化バイエルウレタン(株)製]等が挙げられ、エポキシ系架橋剤では、デナコール EX−832[ナガセ化成工業(株)製]、デナコール EX−841[ナガセ化成工業(株)製]、テトラッドC[三菱瓦斯化学(株)製]、テトラッドX[三菱瓦斯化学(株)製]等が挙げられ、オキサゾリン系架橋剤では、エポクロスWS−500[(株)日本触媒製]、エポクロスWS−700[(株)日本触媒製]、エポクロスK−2010E[(株)日本触媒製]、エポクロスK−2020E[(株)日本触媒製]、エポクロスK−2030E[(株)日本触媒製]が挙げられ、カルボジイミド系架橋剤では、カルボジライトSV−02[日清紡績(株)]、カルボジライトV−02[日清紡績(株)]、カルボジライトV−02−L2[日清紡績(株)]、カルボジライトV−04[日清紡績(株)]、カルボジライトE−01[日清紡績(株)]、カルボジライトE−02[日清紡績(株)]、カルボジライトE−03A[日清紡績(株)]、カルボジライトE−04[日清紡績(株)]、グリシジル(アルコキシ)エポキシシラン系架橋剤では、2−(3,4−エポキシシクロヘキシルエチルトリメトキシシラン[KBM−303;信越シリコーン(株)製]、γ−グリシドキシプロピルトリメトキシシラン[KBM−403;信越シリコーン(株)製]、γ−グリシドキシプロピルメチルジエトキシシラン[KBE−402;信越シリコーン(株)製]、γ−グリシドキシプロピルトリエトキシシラン[KBE−403;信越シリコーン(株)製]等が挙げられる。
本発明に使用する水分散型アクリル系粘着剤組成物においては、添加剤として、必要に応じて本発明の所望の効果を阻害しない範囲で、pHを調整するための塩基(アンモニア水など)や酸、可塑剤、軟化剤、酸化防止剤、ガラスやプラスチック製の繊維・バルーン・ビーズ・金属粉末等の充填剤、顔料・染料等の着色剤、pH調整剤、皮膜形成補助剤、レベリング剤、増粘剤、撥水剤、消泡剤等の公知のものを粘着剤組成物に任意で添加することができる。
本発明の着色粘着テープは、上記着色層を有する支持体の着色層表面に、上記水分散型アクリル系粘着剤組成物からなる粘着剤層が設けられた着色粘着テープである。当該構成により、ハロゲンフリーの着色層に水系粘着剤層を適用した場合にも、好適な接着力とリワーク性を実現できる。
本発明の着色粘着テープは、装飾、表示、隠蔽、反射、遮光等の目的で使用される各種産業分野にて使用できる。なかでもハロゲン含有量や溶剤含有量が低く、好ましくは実質的に含有せず、かつ好適な接着力とリワーク性を有することから、各種画像表示装置の部品固定用に好適に使用できる。特に、省スペースにて、部品固定や好適な遮光反射性能の求めら、かつ不良時や修理時にリワーク性の要求される薄型の画像表示装置の遮光テープ、光反射テープ、遮光反射テープとして好適に使用できる。
(ポリエステルウレタン樹脂(A))
攪拌機,温度計,還流冷却器および窒素ガス導入管を備えた四つロフラスコにアジピン酸/テレフタル酸=50/50なる酸成分と3一メチル‐1,5ペンタンジオールから得られる数平均分子量(以下Mnという)2,000のポリエステルジオール256.3部とイソホロンジイソシアネート36.5部を仕込み、窒素気流下に90℃で15時間反応させた。次いでイソホロンジアミン5.0部、ジ‐n‐ブチルアミン2.2部、トルエン175部、メチルエチルケトン350部、イソプロピレンアルコール175部を添加し、攪枠下に40℃で3時間反応させ、樹脂固形分濃度30.0%、ガードナー粘度U−V(25℃)、アミン価=0、質量平均分子量(以下Mwという)67,000のポリエステルウレタン樹脂(A)を得た。得られた樹脂のtanδのピーク温度は−8℃であった。
攪拌機,温度計,還流冷却器および窒素ガス導入管を備えた四つロフラスコにアジピン酸とネオペンチルグリコールから得られるMn=1,000のポリエステルジオール223.1部とイソホロンジイソシアネート64.4部を仕込み、窒素気流下に90℃で15時間反応させた。次いでイソホロンジアミン11.3部、ジ‐n‐ブチルアミン1.2部、トルエン175部、酢酸エチル315部、イソプロピレンアルコール210部を添加し、攪枠下に40℃で3時間反応させ、樹脂固形分濃度30.0%、ガードナー粘度S−T(25℃)、アミン価=0.5、Mw=100,000のポリエステルウレタン樹脂(B)を得た。得られた樹脂のtanδのピーク温度は−20℃であった。
(黒色インキの製造例1)
デグサ社製「カーボンデグサスペシャル4A」を4部、デグサ社製「カーボンスペシャル250P」6部、ポリエステルウレタン樹脂(A)(tanδピーク温度=−8℃)を40部、メチルエチルケトンを23部、トルエンを13部、酢酸エチルを6部、N−プロピルアセテートを3部、イソプロピルアルコール3部を添加し、サンドミルで約1時間湿式分散した物に、DIC社製硬化剤「KR90」(ヘキサメチレンジジイソシアネートのビウレット体)を4部、DIC社製希釈剤「ダイレジューサーV No.20」を35部添加して黒色インキ(A)を作成した。なお、樹脂は固形分比を表す。
製造例1のポリエステルウレタン樹脂(A)の代わりにポリエステルウレタン樹脂(B)(ポリエステルウレタン樹脂、tanδピーク温度=−20℃)を使用して、黒色インキの製造例1と同様に黒色インキ(B)を作成した。
(インキコートフィルム(A))
帝人デュポンフィルム(株)製テフレックスFW2#13(厚さ:13μm、引張強度23N/20mm)に表面状態が50ダイン以上になるようコロナ処理を行い、その上に黒色インキ(A)を乾燥厚みが4μmになるよう2回グラビアコートした。尚、乾燥は常温で2分間放置した。その後40℃で2日間養生し、インキコートフィルム(A)を得た。
黒色インキ(B)を使用した以外はインキコートフィルム(A)と同様にして、インキコートフィルム(B)を得た。
(調整例1)
<乳化液の調製>
容器にイオン交換水75.0gと界面活性剤アクアロンKH−1025[第一工業製薬(株)製;有効成分25%]20.0gと界面活性剤ラテムルPD−104[花王(株)製;有効成分20%]37.5gを入れ、均一に溶解した。そこに、n−ブチルアクリレート227.5g、2−エチルヘキシルアクリレート227.5g、メチルメタクリレート25.0g、N−ビニルピロリドン7.5g、アクリル酸12.5g、ラウリルメルカプタン0.20gを加えて乳化し、乳化液(1)632.7gを得た。
攪拌機、還流冷却管、窒素導入管、温度計、滴下漏斗を備えた反応容器に、イオン交換水340gを入れ、窒素を吹き込みながら60℃まで昇温した。攪拌下、乳化液(1)の一部[3.2g]、過硫酸アンモニウム水溶液5.0g[有効成分3%]、亜硫酸水素ナトリウム水溶液5.0g[有効成分3%]を添加し、60℃を保ちながら1時間で重合させた。引き続き、残りの乳化液(1)629.5gと、過硫酸アンモニウム水溶液40g[有効成分1.25%]を別々の漏斗を使用して、反応容器を60℃に保ちながら8時間かけて滴下重合した。滴下終了後、反応容器を60℃に保ちながら2時間攪拌した後、内容物を冷却し、引き続き、pHが7.5になるようにアンモニア水(有効成分10%)で調整した。これを200メッシュ金網で濾過し、アクリル系共重合体(1)のエマルジョン1013.5gを得た。ここで、得られたアクリル系共重合体(1)のエマルジョンは固形分濃度50%、平均粒子径は338nmであった。
<乳化液(2)の調製>
容器にイオン交換水75.0gと界面活性剤アクアロンKH−1025[第一工業製薬(株)製;有効成分25%]20.0gと界面活性剤ラテムルPD−104[花王(株)製;有効成分20%]37.5gを入れ、均一に溶解した。そこに、n−ブチルアクリレート227.5g、2−エチルヘキシルアクリレート227.5g、メチルメタクリレート25.0g、N−ビニルピロリドン7.5g、アクリル酸1.5g、メタクリル酸11.0g、ラウリルメルカプタン0.2gを加えて乳化し、乳化液(2)632.7gを得た。
攪拌機、還流冷却管、窒素導入管、温度計、滴下漏斗を備えた反応容器に、イオン交換水340gを入れ、窒素を吹き込みながら60℃まで昇温した。攪拌下、乳化液(2)の一部[3.2g]、過硫酸アンモニウム水溶液5.0g[有効成分3%]、亜硫酸水素ナトリウム水溶液5.0g[有効成分3%]を添加し、60℃を保ちながら1時間で重合させた。引き続き、残りの乳化液(2)629.5gと、過硫酸アンモニウム水溶液40g[有効成分1.25%]を別々の漏斗を使用して、反応容器を60℃に保ちながら8時間かけて滴下重合した。滴下終了後、反応容器を60℃に保ちながら2時間攪拌した後、内容物を冷却し、引き続き、pHが7.5になるようにアンモニア水(有効成分10%)で調整した。これを200メッシュ金網で濾過し、アクリル系共重合体(2)のエマルジョン1013.5gを得た。ここで、得られたアクリル系共重合体(2)のエマルジョンは固形分濃度50%、平均粒子径は341nmであった。
<乳化液(3)の調製>
容器にイオン交換水75.0gと界面活性剤アクアロンKH−1025[第一工業製薬(株)製;有効成分25%]20.0gと界面活性剤ラテムルPD−104[花王(株)製;有効成分20%]37.5gを入れ、均一に溶解した。そこに、n−ブチルアクリレート457g、酢酸ビニル25.0g、アクリル酸17.5g、2−ヒドロキシエチルアクリレート0.5g、ラウリルメルカプタン0.2gを加えて乳化し、乳化液(3)632.7gを得た。
攪拌機、還流冷却管、窒素導入管、温度計、滴下漏斗を備えた反応容器に、イオン交換水340gを入れ、窒素を吹き込みながら65℃まで昇温した。攪拌下、乳化液(3)の一部[3.2g]、過硫酸アンモニウム水溶液5.0g[有効成分3%]、亜硫酸水素ナトリウム水溶液5.0g[有効成分3%]を添加し、60℃を保ちながら1時間で重合させた。引き続き、残りの乳化液(3)629.5gと、過硫酸アンモニウム水溶液40g[有効成分1.25%]を別々の漏斗を使用して、反応容器を60℃に保ちながら8時間かけて滴下重合した。滴下終了後、反応容器を60℃に保ちながら2時間攪拌した後、内容物を冷却し、引き続き、pHが7.5になるようにアンモニア水(有効成分10%)で調整した。これを200メッシュ金網で濾過し、アクリル系共重合体(3)のエマルジョン1013.5gを得た。ここで、得られたアクリル系共重合体(3)のエマルジョンは固形分濃度50%、平均粒子径は308nmであった。
(製造例1)
前記のアクリル系共重合体(1)のエマルジョン1000g[dry;500g]に、レベリング剤としてサーフィノールPSA−336[エアー・プロダクツ・ジャパン(株)製;有効成分100%]2.5g、消泡剤としてサーフィノールDF−110D[エアー・プロダクツ・ジャパン(株)製;有効成分100%]2.5g、粘着付与樹脂としてエマルジョン型重合ロジンエステル系粘着付与樹脂スーパーエステルE−865NT[荒川化学工業(株)製;軟化点160℃]固形分で62.5g、エマルジョン型ロジンフェノール系粘着付与樹脂タマノルE−200NT[荒川化学工業(株)製;軟化点150℃]固形分で62.5g、架橋剤としてエポキシ化合物テトラッドC[三菱瓦斯化学(株)製]0.05g(0.01質量部)を添加し、200メッシュ金網で濾過し、水分散型アクリル系粘着剤組成物(1)を得た。
製造例1において、架橋剤としてエポキシ化合物テトラッドC[三菱瓦斯化学(株)製]0.15g(0.03質量部)を添加すること以外は、製造例1と同様にして、水分散型アクリル系粘着剤組成物(2)を製造した。
製造例1において、架橋剤としてエポキシ化合物テトラッドC[三菱瓦斯化学(株)製]0.25g(0.05質量部)を添加すること以外は、製造例1と同様にして、水分散型アクリル系粘着剤組成物(3)を製造した。
前記のアクリル系共重合体(2)のエマルジョン1000g[dry;500g]に、レベリング剤としてサーフィノールPSA−336[エアー・プロダクツ・ジャパン(株)製;有効成分100%]2.5g、消泡剤としてサーフィノールDF−110D[エアー・プロダクツ・ジャパン(株)製;有効成分100%]2.5g、粘着付与樹脂としてエマルジョン型重合ロジンエステル系粘着付与樹脂スーパーエステルE−865NT[荒川化学工業(株)製;軟化点160℃]固形分で62.5g、エマルジョン型ロジンフェノール系粘着付与樹脂タマノルE−200NT[荒川化学工業(株)製;軟化点150℃]固形分で62.5g、架橋剤としてエポキシ化合物テトラッドC[三菱瓦斯化学(株)製]0.05g(0.01質量部)を添加し、200メッシュ金網で濾過し、水分散型アクリル系粘着剤組成物(4)を得た。
製造例5において、架橋剤としてエポキシ化合物テトラッドC[三菱瓦斯化学(株)製]0.15g(0.03質量部)を添加すること以外は、製造例4と同様にして、水分散型アクリル系粘着剤組成物(5)を製造した。
製造例5において、架橋剤としてエポキシ化合物テトラッドC[三菱瓦斯化学(株)製]0.25g(0.05質量部)を添加すること以外は、製造例4と同様にして、水分散型アクリル系粘着剤組成物(6)を製造した。
製造例5において、架橋剤としてエポキシ化合物テトラッドC[三菱瓦斯化学(株)製]0.5g(0.1質量部)を添加すること以外は、製造例4と同様にして、水分散型アクリル系粘着剤組成物(7)を製造した。
前記のアクリル系共重合体(3)のエマルジョン1000g[dry;500g]に、レベリング剤としてサーフィノールPSA−336[エアー・プロダクツ・ジャパン(株)製;有効成分100%]2.5g、消泡剤としてサーフィノールDF−110D[エアー・プロダクツ・ジャパン(株)製;有効成分100%]2.5g、粘着付与樹脂としてエマルジョン型重合ロジンエステル系粘着付与樹脂スーパーエステルE−865NT[荒川化学工業(株)製;軟化点160℃]固形分で62.5g、エマルジョン型ロジンフェノール系粘着付与樹脂タマノルE−200NT[荒川化学工業(株)製;軟化点150℃]固形分で62.5g、架橋剤としてエポキシ化合物テトラッドC[三菱瓦斯化学(株)製]0.05g(0.01質量部)を添加し、200メッシュ金網で濾過し、水分散型アクリル系粘着剤組成物(H1)を得た。
(参考製造例1)
冷却管、攪拌機、温度計、滴下漏斗を備えた反応容器にn−ブチルアクリレート93部、酢酸ビニル3.4部、アクリル酸3.5部、β−ヒドロキシ−エチルアクリレート0.1部と、重合開始剤として2,2’−アゾビスイソブチルニトリル0.2部とを酢酸エチル100部に溶解し、窒素置換後、80℃で8時間重合して質量平均分子量80万のアクリル系共重合体(S1)を得た。上記アクリル系共重合体(S1)を100部に、荒川化学社製「スーパーエステルA100」を10部、及び荒川化学工業製「ペンセルD135」10質量部を、トルエンで希釈し、固形分40%の溶剤系のアクリル系粘着剤組成物(S1)を得た。
(実施例1)
製造例1で得た水分散型アクリル系粘着剤組成物(1)を、離型処理した厚さ75μmのポリエステルフィルム上に、乾燥後の厚さが20μmとなるよう塗工して、85℃で2分間乾燥して粘着剤層を得た。得られた粘着剤層をインキコートフィルム(A)の両面に、転写し、80℃の熱ロールで4kgf/cmの圧力でラミネートし、さらに、40℃で2日間養生して、両面粘着テープを得た。
製造例2〜7で得た水分散型アクリル系粘着剤組成物(2)〜(7)を使用した以外は、実施例1と同様にして、実施例2〜7の両面粘着テープを得た。
製造例2で得た水分散型アクリル系粘着剤組成物(2)を、離型処理した厚さ75μmのポリエステルフィルム上に、乾燥後の厚さが20μmとなるよう塗工して、85℃で2分間乾燥して粘着剤層を得た。得られた粘着剤層をインキコートフィルム(B)の両面に、転写し、80℃の熱ロールで4kgf/cmの圧力でラミネートし、さらに、40℃で2日間養生して、実施例8の両面粘着テープを得た。
製造例6で得た水分散型アクリル系粘着剤組成物(6)を使用した以外は、実施例9と同様にして、実施例9の両面粘着テープを得た。
比較製造例1で得た水分散型アクリル系粘着剤組成物(H1)を使用した以外は、上記実施例1と同様にして、比較例1の両面粘着テープを得た。
参考製造例1で得た溶剤系のアクリル系粘着剤組成物(S1)に日本ポリウレタン工業社製「コロネートL−45」(イソシアネート系架橋剤)を1.2部配合し、充分に撹拌した後、離型処理した厚さ75μmのポリエステルフィルム上に、乾燥後の厚さが20μmとなるよう塗工して、85℃で2分間乾燥して粘着剤層を得た。これをインキコートフィルム(b)の両面に転写し、80℃の熱ロールで4kgf/cmの圧力でラミネートし、さらに、40℃で2日間養生して、参考例1の両面粘着テープを得た。
上記インキコートフィルムに使用した黒色インキを、10mm幅、長さ150mmのインキ塗膜に加工し、環境温度23℃、湿度50%の条件下で、テンシロン万能引張試験機(オリエンテック製、RTA100)を用い、チャック間100mmのときに、300mm/minで引っ張った時の弾性率、引張強度、破断強度、破断伸度を測定した。
接着力はJIS−Z0237(2000)の180度引き剥がし接着力の試験方法に従って下記の手順により求めた。
ステンレス(SUS)板及びガラス板にポリエステルフィルム25μmで裏打ちした20mm幅の実施例及び比較例の粘着テープを、環境温度23℃、湿度50%の条件下において、2kgのローラーで1往復加圧貼付し1時間放置後、テンシロン万能引張試験機(オリエンテック製、RTA100)を用い、同一の温度湿度条件下で300mm/minの速度で引っ張って、180度引き剥がし接着力を測定した。
尚、ガラスに対する接着力が8N/20mm以上のものを良好と判断した。
ステンレス板に白面をポリエステルフィルム25μmで裏打ちした10mm幅の実施例及び比較例の粘着テープを、環境温度23℃、湿度50%RHの条件下において、2kgローラーで1往復加圧貼付し1時間後、60℃の環境試験器で24時間放置する。その後、23℃に1時間放置後、斜め135°方向に300mm/minの速度で剥がし、粘着剤が糊残りせずに剥がせるか否かを評価した。
◎:全く糊残りなく剥離可能であった。
○:わずかに糊残りが発生するが実用上問題無く剥離可能であった。
×:糊残りが発生する。
電通産業(株)製ライトボックス「フラットイルミネーターHF−SL−A48LCG」が10000cd/m2になるよう調整し、その上に遮光性粘着テープを置き、遮光性粘着テープを透過する光を(株)アイ・システム製輝度計「アイスケール3」で測定する。
Claims (9)
- 着色層を有する支持体の着色層表面に粘着剤層が設けられた着色粘着テープであって、
前記着色層のハロゲン含有量が0.3質量%以下であり、前記着色層表面に設けられる粘着剤層が、水性媒体中にアクリル系共重合体エマルジョン粒子が分散した水分散型アクリル系粘着剤組成物からなる粘着剤層であり、前記水分散型アクリル系粘着剤組成物が架橋剤としてエポキシ化合物を含有するものであり、
前記アクリル系共重合体エマルジョン粒子を形成するアクリル系共重合体が、炭素数4〜8のアルキル基を有する(メタ)アクリレート、カルボキシル基含有モノマー、および、窒素含有ビニルモノマーをモノマー成分として含有し、
前記炭素数4〜8のアルキル基を有する(メタ)アクリレートとして2−エチルヘキシルアクリレートを含有し、
前記アクリル系共重合体を形成するモノマー成分中の炭素数4〜8のアルキル基を有する(メタ)アクリレートの含有量が50〜98質量%、カルボキシル基含有モノマーの含有量が1〜10質量%、窒素含有ビニルモノマーの含有量が0.1〜5質量%であることを特徴とする着色粘着テープ。 - 前記着色層が、ポリウレタン系樹脂をバインダー樹脂とする着色インキからなる請求項1に記載の着色粘着テープ。
- 前記ポリウレタン系樹脂が、ガラス転移温度が−30〜30℃のポリエステルポリウレタン樹脂であることを特徴とする請求項2に記載の着色粘着テープ。
- 前記着色インキが、ブロッキング防止剤を含有する請求項2又は3に記載の着色粘着テープ。
- 前記2−エチルヘキシルアクリレートの含有量が、前記炭素数が4〜8のアルキル基を有する(メタ)アクリレート中の20〜90質量%である請求項1〜4のいずれかに記載の着色粘着テープ。
- 前記炭素数4〜8のアルキル基を有する(メタ)アクリレートとして、n−ブチル(メタ)アクリレート、イソブチル(メタ)アクリレート、t−ブチル(メタ)アクリレート、イソオクチル(メタ)アクリレート及びn−オクチル(メタ)アクリレートから選ばれる少なくとも一種を含有する請求項1〜5のいずれかに記載の着色粘着テープ。
- 前記窒素含有ビニルモノマーが、N−ビニルピロリドン、N−ビニルカプロラクタム、アクリロイルモルホリン、アクリロニトリル、アクリルアミド及びN,N−ジメチルアクリルアミドから選ばれる少なくとも一種である請求項1〜6のいずれかに記載の着色粘着テープ。
- 前記カルボキシル基含有モノマーとして、アクリル酸及びメタクリル酸を含有し、アクリル酸とメタクリル酸の含有量の比が、(メタクリル酸/アクリル酸)で表されるモル等量比で1.3以上である請求項1〜7のいずれかに記載の着色粘着テープ。
- 請求項1〜8のいずれかに記載の着色粘着テープにおいて、着色層が、黒色の着色インキからなる遮光層であることを特徴とする遮光テープ。