JP5707898B2 - (メタ)アクリロイル基を有するウレタン樹脂及び該ウレタン樹脂を含有する活性エネルギー線硬化性接着剤、並びに太陽電池用裏面保護シート - Google Patents
(メタ)アクリロイル基を有するウレタン樹脂及び該ウレタン樹脂を含有する活性エネルギー線硬化性接着剤、並びに太陽電池用裏面保護シート Download PDFInfo
- Publication number
- JP5707898B2 JP5707898B2 JP2010262004A JP2010262004A JP5707898B2 JP 5707898 B2 JP5707898 B2 JP 5707898B2 JP 2010262004 A JP2010262004 A JP 2010262004A JP 2010262004 A JP2010262004 A JP 2010262004A JP 5707898 B2 JP5707898 B2 JP 5707898B2
- Authority
- JP
- Japan
- Prior art keywords
- meth
- active energy
- energy ray
- acryloyl group
- sheet
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
さらに、本発明は、シート状部材間の接着力と耐湿熱性とに優れ、接着剤層中の気泡発生による外観不良やデラミネーションが生じない太陽電池用裏面保護シートを、高い歩留まり且つ低コストで生産性良く、製造可能とする活性エネルギー線硬化性接着剤に関する。
ところで、複数のシート状部材を積層し、太陽電池用裏面保護シートを工業的に生産する場合、長尺状態のものをロール状に巻き取る。しかし、ポリウレタン系接着剤は硬化反応が遅いので、ロール状に巻き取った積層体中の接着剤層の硬化が不十分となり易く、巻き取った後、シート状部材がずれ易く、不良品発生率が高く、歩留まりが悪いという問題があった。
また、十分に硬化させる為に高温に維持した倉庫にて数日エージングさせる必要があり、その点でも生産性が悪く、倉庫の温度を維持する為の電気代コストがかかるなど生産コストが大きくなるという問題もあった。
さらに、硬化剤であるイソシアネート化合物は、主剤である水酸基含有樹脂と反応するだけでなく、空気中の水とも反応する。水と反応した後、脱炭酸反応が起きるために、シート状部材を積層した後に接着剤層に気泡が発生し、外観不良やデラミネーションが生じるという問題もあった。
ポリカーボネートジオールの1級水酸基と、分子中に2個の水酸基と2個のエチレン性不飽和基とを含有する2官能エポキシ(メタ)アクリレートの2級水酸基とでは、ポリイソシアネートとの反応性が異なる為に、不飽和基がウレタン樹脂中に均一に導入されず、これを用いた接着剤を硬化させた時の架橋が不均一となり耐湿熱性の弱い部位ができる為ではないかと考察している。
R 1 はジイソシアネート化合物(b2−1)からイソシアネート基を除いた残基を表し、
R 2 は(メタ)アクリロイル基及び水酸基を有する化合物(b1)から水酸基を除いた残基を表す。)
本発明の(メタ)アクリロイル基を有するウレタン樹脂(C)は、カーボネート構造を有するジオール成分を必須とする(メタ)アクリロイル基を有しないジオール成分(A)と、(メタ)アクリロイル基と2個以上のイソシアネート基とを有するポリイソシアネート成分(B)とを反応させて得ることができる。
なお、ウレタン樹脂(C)のガラス転移温度の測定は、セイコーインスツルメンツ社製DSC「RDC220」を用いて行った。ウレタン樹脂溶液を乾燥した試料、約10mgをアルミニウムパンに量り採り、DSC装置にセットして液体窒素で−100℃まで冷却した後、10℃/minで昇温して得られたDSCチャートからガラス転移温度を算出した。
硬化後の接着剤層の凝集力が低くなり、耐湿熱性試験時にシート状部材間の接着力が低下しやすくなる。数平均分子量が150000より大きいと、活性エネルギー線硬化性接着剤が高粘度になりやすくなったり、活性エネルギー線硬化性接着剤を構成する他の成分との溶解性が悪くなりやすくなったり、硬化性接着剤層に又は硬化接着剤層にシート状部材を重ねた際、シート状部材に対する接着剤層の濡れ性が乏しくなり、その結果シート状部材間の接着力が不十分となりやすくなったり、するなどの問題が生じやすくなる。
なお、(メタ)アクリロイル基を有するウレタン樹脂(C)の数平均分子量の測定は、東ソー社製GPC(ゲルパーミエーションクロマトグラフィー)「HPC−8020」を用い、溶媒はテトラヒドロフランを用いた。数平均分子量の計算は標準ポリスチレン換算で行った。
(メタ)アクリロイル基当量が500よりも小さいと、活性エネルギー線硬化時の硬化収縮によりシート状部材間の接着力が不十分となる傾向にある。一方、(メタ)アクリロイル基当量が40000よりも大きいと、接着剤層の架橋が不十分となり、耐湿熱性試験時にシート状部材間の接着力が低下する傾向にある。
ウレタン結合当量が200よりも小さいと、硬化性接着剤層に又は硬化接着剤層の凝集力が大きくなり、硬化性接着剤層に又は硬化接着剤層にシート状部材を重ねた際、シート状部材に対する接着剤層の濡れ性が乏しくなり、接着力が低下する傾向にある。一方、ウレタン結合当量が3000よりも大きいと、耐湿熱性の良好なウレタン結合が少なくなり、耐湿熱性試験後にシート状部材間の接着力が低下する傾向にある。
カーボネート構造は、カーボネート基(−O−CO−O−基)を含んだ構造である。ウレタン樹脂(C)は、ジオール成分(A)に由来するカーボネート基を含んでいる。
ウレタン樹脂(C)において、ジオール成分(A)と、ポリイソシアネート成分(B)の合計の固形分に対するカーボネート基の濃度が2mmol/g乃至8mmol/g範囲内にあることが好ましく、3mmol/g乃至7mmol/gの範囲内にあることがより好ましい。ここで言うカーボネート基の濃度とは、ジオール成分(A)と、ポリイソシアネート成分(B)の合計の固形分1g中に含まれるカーボネート基の量のことである。この濃度が2mmol/gより小さい場合、ウレタン樹脂の溶剤に対する溶解性が悪くなったり、十分な耐湿熱性が得られなくなる傾向があり、また8mmol/gより大きい場合、十分な接着力が得られない傾向にある。
原料として用いるジオールとしては、例えば、エチレングリコール、1,3−プロパンジオール、1,4−ブタンジオール、1,5−ペンタンジオール、1,6−ヘキサンジオール、1,7−ヘプタンジオール、1,8−オクタンジオール、1,9−ノナンジオール、1,10−デカンジオール、1,5−ヘキサンジオール、2−メチル−1,8−オクタンジオール、ネオペンチルグリコール、2−イソプロピル−1,4−ブタンジオール、2−エチル−1,6−ヘキサンジオール、3−メチル−1,5−ペンタンジオール、2,4−ジメチル−1,5−ペンタンジオール、2,4−ジエチル−1,5−ペンタンジオール、1,3−ブタンジオール、2−エチルー1,3−ヘキサンジオール、2−ブチル−2−エチル−1,3−プロパンジオール、1,3−シクロヘキサンジオール、1,4−シクロヘキサンジオール、1,4−シクロヘキサンジメタノール、2−ビス(4−ヒドロキシシクロヘキシル)−プロパン、水添ビスフェノールA、水添ビスフェノールFなどが挙げられ、これらは単独又は2種以上の組み合わせを使用することができる。このようなジオール成分(A1)としては例えば宇部興産株式会社製ETERNACOLL UC−100、ETERNACOLL UM−90(3/1)、ETERNACOLL UM−90(1/1)、ETERNACOLL UM−90(1/3)、ETERNACOLL UC−100、クラレ株式会社製C−1090、C−2050、C−2090、C−3090、宇部興産株式会社製ETERNACOLL UH−50、ETERNACOLL UH−100、ETERNACOLL UH−200、ETERNACOLL UH−300、ETERNACOLL UH−50−200、ETERNACOLL UH−50−100、旭化成ケミカルズ株式会社製T6002、T6001、T5652.T4672、ダイセル化学株式会社製プラクセルCD CD205、プラクセルCD CD205PL、プラクセルCD CD210、プラクセルCD CD210PL、プラクセルCD CD220、プラクセルCD CD220PLなどが挙げられこれらは単独でも、2種類以上を併用しても良い。
ジオール成分(A1)〜(A2)を併用する場合、それらの合計量に占めるジオール成分(A2)の割合は、20重量%以下であることが好ましく、10重量%以下であることがより好ましい。この割合が大きい場合、ポリカーボネート骨格及び脂環骨格の耐湿熱性及び接着力に対する効果が小さくなり、優れた耐湿熱性と優れた接着力との両立が困難となる傾向にある。
本発明で使用されるポリイソシアネート成分(B)はアロファネート結合を有する。ポリイソシアネート成分(B)は、特表2002−533542号公報に記載される方法に従い、(メタ)アクリロイル基及び水酸基を有する化合物(b1)と、ポリイソシアネート化合物(b2)との反応によって得ることができる。
ジイソシアネート化合物(b2−1)としては、脂肪族ジイソシアネート、脂環式ジイソシアネート、芳香族ジイソシアネート等が挙げられる。
脂肪族ジイソシアネートとしては、例えばテトラメチレンジイソシアネート、ヘキサメチレンジイソシアネート(1,6−ジイソシアナトヘキサン)、オクタメチレンジイソシアネート、デカメチレンジイソシアネート、ドデカメチレンジイソシアネート、テトラデカメチレンジイソシアネート;リシンジイソシアネート、テトラメチルキシリレンジイソシアネート、トリメチルヘキサンジイソシアネート又はテトラメチルヘキサンジイソシアネートの誘導体が例示できる。
上記ジイソシアネートの混合物が含まれていても良い。ヘキサメチレンジイソシアネート、1,3−ビス(イソシアナトメチル)シクロヘキサン、イソホロンジイソシアネート、テトラメチルキシリレンジイソシアネート、及びジ(イソシアナトシクロヘキシル)メタンが好ましい。
即ち、水酸基とイソシアネート基との反応によって生じたウレタン結合と、ウレタン反応後に残ったイソシアネート基とを、アロファネート結合の形成を促進する触媒を加え、反応させることにより、ポリイソシアネート成分(B)を得ることができる。
あるいは、ウレタン反応後イソシアネート基が残らない場合には、ジイソシアネート化合物(b2−1)や3官能以上のポリイソシアネート化合物を追加し、アロファネート結合の形成を促進する触媒を加え、ウレタン結合とイソシアネート基とを反応させることにより、ポリイソシアネート成分(B)を得ることができる。
有機亜鉛化合物としては、例えば、亜鉛アセチルアセトネート、亜鉛2−エチルカプロネートが例示できる。
テトラアルキルアンモニウム化合物としては、例えば、N,N,N−トリメチル−N−2−ヒドロキシプロピルアンモニウムヒドロオキシド、N,N,N−トリメチル−N−2−ヒドロキシプロピルアンモニウム2−エチルヘキサノエートが例示できる。
(メタ)アクリロイル基及び水酸基を有する化合物(b1)とジイソシアネート化合物(b2−1)とは、0〜280℃で反応させることが好ましく、20〜250℃で反応させることがより好ましく、80〜200℃で反応させることがさらに好ましい。
R 1 はジイソシアネート化合物(b2−1)からイソシアネート基を除いた残基を表し、
R 2 は(メタ)アクリロイル基及び水酸基を有する化合物(b1)から水酸基を除いた残基を表す。)
なお、一般式(I)における−NHR1−は−NHR1CH3の意ではなく、一般式(II
)における>NR1−は>NR1CH3の意ではない。
本発明で使用されるポリイソシアネート成分(B)として、入手可能な市販品として、例えば、LaromerLR9000(BASF社製)などが挙げられる。
(メタ)アクリロイル基と2個以上のイソシアネート基とを有するポリイソシアネート成分(B)以外にも、ウレタン樹脂(C)中の(メタ)アクリロイル基当量を調整する為に、(メタ)アクリロイル基を有さない2個以上のイソシアネート基とを有するポリイソシアネート成分を併用することもできる。
例えば、2,4−トリレンジイソシアネート、2,6−トリレンジイソシアネート、キシリレンジイソシアネート、ジフェニルメタンジイソシアネート、イソホロンジイソシアネート、1,5−ナフタレンジイソシアネート、ヘキサメチレンジイソシアネート、水添化ジフェニルメタンジイソシアネートなどのジイソシアネート、上記ジイソシアネートとトリメチロールプロパン等のポリオール化合物とのアダクト体、上記ジイソシアネートのビュレット体やイソシアヌレート体、更には上記ジイソシアネートと公知のポリエーテルポリオールやポリエステルポリオール、アクリルポリオール、ポリブタジエンポリオール、ポリイソプレンポリオール等とのアダクト体等が挙げられる。これらは単独でも2種類以上を併用してもよい。耐候性の点から前記ジイソシアネート成分としては、脂環式ジイソシアネートが好ましい。
有機溶剤としては、アセトン、メチルエチルケトン、メチルイソブチルケトン、シクロヘキサノン等のケトン系化合物、酢酸メチル、酢酸エチル、酢酸ブチル、乳酸エチル、酢酸メトキシエチル等のエステル系化合物、ジエチルエーテル、エチレングリコールジメチルエーテル等のエーテル系化合物、トルエン、キシレン等の芳香族化合物、ペンタン、ヘキサン等の脂肪族化合物、塩化メチレン、クロロベンゼン、クロロホルム等のハロゲン化炭化水素化合物などの各種溶剤を使用することができる。
また、必要に応じて触媒を添加することができ、たとえばジブチルチンジアセテート、ジブチルチンジラウレート、ジオクチルチンジラウレート、ジブチルチンジマレート等金属系触媒;1 ,8−ジアザ−ビシクロ(5,4,0)ウンデセン−7、1,5−ジアザビシクロ(4,3,0)ノネン−5、6−ジブチルアミノ−1,8−ジアザビシクロ(5,4,0)ウンデセン−7等の3級アミン;トリエタノールアミンのような反応性3級アミン等が挙げられ、これらは単独でも、2種類以上を併用してもよい。
本発明の活性エネルギー線硬化性接着剤は、前記の(メタ)アクリロイル基を有するウレタン樹脂(C)のうち、ガラス転移温度が−60〜−10℃のウレタン樹脂と、エポキシ樹脂(D)とを含有するものである。
アジリジン系化合物(E)としては、2,2−ビスヒドロキシメチルブタノール−トリス[3-(1-アジリジニル)プロピオネート]、4,4−ビス(エチレンイミノカルボニルアミノ)ジフェニルメタンなどが挙げられ、これらは単独でも、2種類以上を併用してもよい。
なお、太陽電池モジュールには、それを搭載する製品又は用途に応じて様々な構成のものがある。用いるべき裏面保護シートは、太陽電池モジュールを搭載する製品又は用途に応じて適宜選択され得る。従って、シート状部材間の接着力の大きさがさほど重要視されない場合には、活性エネルギー線硬化性接着剤はアジリジン系化合物(E)を含有していなくてもよい。
比較的低分子量の(メタ)アクリレートモノマーとしては、例えば、4−ヒドロキシブチル(メタ)アクリレート、イソボルニル(メタ)アクリレート、ラウリル(メタ)アクリレート、及びアクリロイルモルフォリンなどの単官能(メタ)アクリレートモノマー;並びに、1,9−ノナンジオールジ(メタ)アクリレート、ビスフェノールAジ(メタ)アクリレート、ペンタエリスリトールトリ(メタ)アクリレート、トリス((メタ)アクリロキシエチル)イソシアヌレート、及びジペンタエリスリトールヘキサ(メタ)アクリレートなどの多官能(メタ)アクリレートモノマーを例示することができる。
プレポリマー及びポリマーとしては、例えば、ポリエステル(メタ)アクリレート、ポリウレタン(メタ)アクリレート、エポキシ(メタ)アクリレート、及び(メタ)アクリル化マレイン酸変性ポリブタジエンなどの(メタ)アクリロイル基を有するラジカル重合性プレポリマー又はポリマーを挙げることができる。
これらは単独で使用してもよく、2種類以上を併用してもよい。
また、光重合開始剤とともに、増感剤としてn-ブチルアミン、トリエチルアミン、p-ジメチルアミノ安息香酸エチル等の脂肪族アミン、芳香族アミンを併用しても良い。
ウレタン樹脂(C)が、50重量%よりも少ないと接着剤層の凝集力が低下し、接着力および耐湿熱性が不十分となる傾向にある。85重量%よりも多いと耐湿熱性が低下する傾向にある。
エポキシ樹脂(D)が2.5重量%未満だと、耐湿熱性を向上させる効果が得られず、34重量%を越えると接着剤層の架橋密度が低下するために耐湿熱性が低下する傾向にある。
アジリジン系化合物(E)が5重量%よりも多いと耐湿熱性が低下する傾向にある。
ウレタン樹脂(C)以外の(メタ)アクリロイル基を有する化合物が30重量%より多いと硬化時の収縮により接着力が不十分となりやすい。
ガラス転移温度が20℃を超える場合には、硬化性接着剤層に又は硬化接着剤層にシート状部材を重ねた場合、シート状部材に対する接着剤層の濡れ性が乏しくなり、その結果シート状部材間の接着力が低下する傾向にある。一方、ガラス転移温度が−20℃未満の場合には接着剤層の凝集力が低下し、接着力および耐湿熱性が不十分となりやすい。
本発明の太陽電池用裏面保護シートを構成するシート状部材は特に限定されるものではなく、プラスチックフィルム、金属箔、前記プラスチックフィルムに金属酸化物もしくは非金属酸化物が蒸着されてなるもの等が挙げられる。
ポリエチレン系樹脂フィルム、ポリプロピレン系樹脂フィルム、ポリ塩化ビニル系樹脂フィルム、ポリカーボネート系樹脂フィルム、ポリスルホン系樹脂フィルム、ポリ(メタ)アクリル系樹脂フィルム、
ポリフッ化ビニル、ポリフッ化ビニリデン、ポリクロロトリフルオロエチレン、ポリエチレンテトラフルオロエチレン、ポリテトラフルオロエチレン、テトラフルオロエチレンパーフルオロアルキルビニルエーテル共重合体、テトラフルオロエチレン−ヘキサフルオロプロピレン共重合体などのフッ素系樹脂フィルム等が挙げられる。
単層構造のプラスチックフィルムの代わりに、多層構造のプラスチックフィルムを使用してもよい。例えば、上述したプラスチックフィルムを支持体とし、アクリル系、フッ素系塗料がコーティングされてなるフィルムや、ポリフッ化ビニリデンやアクリル樹脂などが共押出しにより積層されてなる多層フィルムなどを使用することができる。あるいは、ウレタン系接着剤層などを介して上記のプラスチックフィルムが複数積層されたシート状部材を用いても良い。
蒸着される金属酸化物もしくは非金属無機酸化物としては、例えば、ケイ素、アルミニウム、マグネシウム、カルシウム、カリウム、スズ、ナトリウム、ホウ素、チタン、鉛、ジルコニウム、イットリウムなどの酸化物が使用できる
これらの中でも、太陽電池モジュールとして使用する際の耐候性、水蒸気透過性、電気絶縁性、機械特性、実装作業性など観点では、温度に対する耐性を有する、ポリエチレンテレフタレート及びポリナフタレンテレフタレートなどのポリエステル系樹脂フィルム又はポリカーボネート系樹脂フィルムを使用することが好ましい。
また、太陽電池セルの水の影響による出力低下を防止する観点では、水蒸気バリア性を有する金属酸化物若しくは非金属無機酸化物が蒸着されたプラスチックフィルム又はアルミニウム箔などの金属箔を使用することが好ましい。
そして、光劣化による外観不良発生を防止する観点では、耐候性の良好なフッ素系樹脂フィルムを使用することが好ましい。
これらを積層した場合、特に優れた太陽電池用裏面保護シートが得られる。
[1] 一(「任意の」の意)のシート状部材に活性エネルギー線硬化性接着剤を塗工し、形成された活性エネルギー線硬化性接着剤層に他のシート状部材を重ねる。次いで、一方のシート状部材側から又は両シート状部材側から、活性エネルギー線を照射し、両シート状部材間に活性エネルギー線硬化接着剤層を形成する。
[2]の方法は、[1]の方法とは全く反対の特徴を有する。即ち、酸素阻害を受けやすい状況で活性エネルギー線を照射することになる反面、使用し得るシート状部材の選択肢が広がるという長所を有する。
[3]の方法は、最初の工程で酸素阻害を受けやすい状況で活性エネルギー線を照射することになる反面、形成された接着剤層に他のシート状部材形成用塗液を塗工し、他のシート状部材を形成するので、接着剤層と他のシート状部材との接着力を確保しやすいという長所を有する。
太陽電池用裏面保護シートとして要求される性能、価格、生産性等を勘案して、種々の製造方法を選択したり、さらに組み合わせたりすることができる。
なお、[1]、[2]の場合、硬化性接着剤層に又は硬化接着剤層に他のシート状部材を重ねる際に、加熱及び/又は加圧条件下に重ね合わせることができる。
溶剤としては、アセトン、メチルエチルケトン、メチルイソブチルケトン、シクロヘキサノン等のケトン系化合物、酢酸メチル、酢酸エチル、酢酸ブチル、乳酸エチル、酢酸メトキシエチル等のエステル系化合物、ジエチルエーテル、エチレングリコールジメチルエーテル等のエーテル系化合物、トルエン、キシレン等の芳香族化合物、ペンタン、ヘキサン等の脂肪族化合物、塩化メチレン、クロロベンゼン、クロロホルム等のハロゲン化炭化水素化合物、エタノール、イソプロピルアルコール、ノルマルブタノール等のアルコール類、水等が挙げられる。これら溶剤は単独でも、2種類以上を併用してもよい。
以下に(メタ)アクリロイル基を有するウレタン樹脂の合成、活性エネルギー線硬化性接着剤、および太陽電池用裏面保護シートの作成方法について示す。
重合槽、攪拌機、温度計、還流冷却器、窒素導入管、滴下槽を備えた重合反応装置の重合槽に、トルエンを1000.0部、クラレポリオールC−2050(クラレ社製)を854.0部、ヒドロキノンを0.3部仕込み、窒素気流下、攪拌しながら重合槽内の温度を80℃に上げた。80℃になったらジブチル錫ジラウレート(DBTDL)を0.5部加えた。
次に、Laromer LR9000(BASF社製)86.6部とイソホロンジイソシアネート(IPDI)59.4部との混合物を滴下槽から、2時間かけて重合槽に滴下した。その後、赤外分光光度計でイソシアネート基の赤外吸収ピークが消滅するまで反応を続け、イソシアネート基の吸収ピークが完全に消滅したことを確認し、反応を終了した。重合槽の温度を40℃まで下げて、トルエンを500.0部加えて(メタ)アクリロイル基を有するウレタン樹脂(C−1)溶液を得た。(C−1)の性状を表−1に示す。
表1−1、2の組成に従って、実施例1と同様にして(メタ)アクリロイル基を有するウレタン樹脂(C−2)〜(C−16)溶液を得た。各(メタ)アクリロイル基を有するウレタン樹脂の性状を表−1、2に示す。
重合槽、攪拌機、温度計、還流冷却器、窒素導入管、滴下槽を備えた重合反応装置の重合槽に、メチルエチルケトン(MEK)を869.4部、クラレポリオールC−3090(クラレ社製)を834.1部、シクロヘキサンジメタノール(CHDM)を41.7部仕込み、窒素気流下、攪拌しながら重合槽内の温度を80℃に上げた。80℃になったらジブチル錫ジラウレート(DBTDL)を0.5部加えた。次に、イソホロンジイソシアネート(IPDI)124.2部とMEK124.2部とを混合して、滴下槽に入れ、2時間かけて重合槽に滴下した。滴下終了1時間後にDBTDLを0.05部加え、その後、赤外分光光度計でイソシアネート基の赤外吸収ピークが消滅するまで反応を続け、イソシアネート基の吸収ピークが完全に消滅したことを確認し、数平均分子量44000、重量平均分子量76000、水酸基価2.55mgKOH/gのウレタン樹脂を得た。
次いで、重合槽の温度を60℃に下げて、1個のイソシアネート基と1個のアクリロイル基とを有する2−アクリロイルオキシエチルイソシアネート(カレンズAOI、昭和電工社製)を6.4部とMEKを6.4部との混合物を重合槽に添加して、60℃で反応を行い、赤外分光光度計でイソシアネート基の赤外吸収ピークが完全に消滅するまで反応を続けた。重合槽の温度を40℃まで下げて、MEKを500.0部加えて、固形分40%の(メタ)アクリロイル基を有するウレタン樹脂(C−17)溶液を得た。(C−17)の性状を表−2に示す。
重合槽、攪拌機、温度計、還流冷却器、窒素導入管、滴下槽を備えた重合反応装置の重合槽に、メチルエチルケトン(MEK)を862.5部、クラレポリオールC−3090(クラレ社製)を826.7部、シクロヘキサンジメタノール(CHDM)を41.3部仕込み、窒素気流下、攪拌しながら重合槽内の温度を80℃に上げた。80℃になったらジブチル錫ジラウレート(DBTDL)を0.5部加えた。次に、イソホロンジイソシアネート(IPDI)132.0部とMEK132.0部とを混合して、滴下槽に入れ、2時間かけて重合槽に滴下した。滴下終了1時間後にDBTDLを0.05部加えて3時間反応を続けて、数平均分子量42000、重量平均分子量72000、NCO価2.67mgKOH/gのウレタン樹脂を得た。
次いで、重合槽の温度を60℃に下げて、ヒドロキシエチルアクリレート(HEA)を5.5部とMEKを5.5部とを混合したものを重合槽に添加して、60℃で反応を行い、赤外分光光度計でイソシアネート基の赤外吸収ピークが完全に消滅するまで反応を続けた。重合槽の温度を40℃まで下げて、MEKを500.0部加えて、固形分40%の(メタ)アクリロイル基を有するウレタン樹脂(C−18)溶液を得た。(C−18)の性状を表−3に示す。
表−3の組成に従って、実施例1と同様にして(メタ)アクリロイル基を有するウレタン樹脂(C−19)〜(C−21)溶液を得た。各(メタ)アクリロイル基を有するウレタン樹脂の性状を表−2に示す。
Mn、Mwの測定は東ソー社製GPC(ゲルパーミエーションクロマトグラフィー)「HPC−8020」を用い、溶媒はテトラヒドロフランを用いた。MnとMwはポリスチレン換算で行った。
ガラス転移温度の測定は、セイコーインスツルメンツ社製DSC「RDC220」を用いて行った。(メタ)アクリロイル基を有するウレタン樹脂溶液を乾燥した、試料約10mgをアルミニウムパンに量り採り、DSC装置にセットして液体窒素で−100℃まで冷却した後、10℃/minで昇温して得られたDSCチャートからガラス転移温度を算出した。
C−1090:クラレ社製、ポリカーボネートジオール 数平均分子量=1000
C−2050:クラレ社製、ポリカーボネートジオール 数平均分子量=2000
C−2090R:クラレ社製、ポリカーボネートジオール 数平均分子量=2000
C−3090:クラレ社製、ポリカーボネートジオール 数平均分子量=3000
P−3010:クラレ社製、ポリエステルジオール 数平均分子量=3000
CHDM:シクロヘキサンジメタノール
MPD:3−メチル−1,5−ペンタンジオール
1,9−ND:1,9−ノナンジオール
DMBA:ジメチロールブタン酸
エポキシエステル70A:共栄化学(株)製、プロピレングリコールジグリシジルエーテルに2モルのアクリル酸が付加した化合物。
Laromer LR9000:BASF社製、ヘキサメチレンジイソシアネートとヒドロキシエチルアクリレートとを原料とする、分子量約800、アクリロイル基が約2.5官能、NCO含有量が約15重量%、アクリロイル基含有ポリイソシアネート成分
IPDI:イソホロンジイソシアネート
DBTDL:ジブチル錫ジラウレート
AOI:2−アクリロイルオキシエチルイソシアネート(カレンズAOI、昭和電工社製)
HEA:ヒドロキシエチルアクリレート
MEK:メチルエチルケトン
上記合成により得られた(メタ)アクリロイル基を有するウレタン樹脂(C)の樹脂溶液、エポキシ樹脂(D)、(メタ)アクリロイル基を有するウレタン樹脂(C)以外の活性エネルギー線硬化性化合物、光重合開始剤およびその他の成分を表4に示す重量部に従って配合し、活性エネルギー線硬化性接着剤1〜21を得た。
エピコート1001:エポキシ樹脂(ジャパンエポキシレジン社製) 数平均分子量900
エピコート1009:エポキシ樹脂(ジャパンエポキシレジン社製) 数平均分子量3800
IBXA:イソボルニルアクリレート(大阪有機化学社製)
M305:ペンタエリスリトールトリアクリレート(東亞合成社製)
イルガキュア184:1−ヒドロキシーシクロヘキシルーフェニルーケトン(チバ・スペシャリティ・ケミカルズ製)
イルガキュア819:ビス(2,4,6−トリメチルベンゾイル)−フェニルフォスフィンオキサイド(チバ・スペシャリティ・ケミカルズ社製)
厚み約200μの接着剤硬化物シートを作成し、動的粘弾性測定装置DVA−200(アイティー計測制御社製)を用いて測定し、tanδのピーク値の温度をガラス転移温度とした。
作成方法1
シート状部材(S1)に活性エネルギー線硬化性接着剤を塗布し、溶剤を揮散させた後、他のシート状部材(S2)を重ねつつ、60℃に設定した2つのロール間を通過させ、積層後、他のシート状部材(S2)側から紫外線(120Wメタルハライドランプ、UV−A領域の積算光量500mJ/cm2)を照射し活性エネルギー線硬化接着剤層を形成させ太陽電池用裏面保護シートを作成した。なお、接着剤層の量は8〜10g/平方メートルとした。
シート状部材(S1)に活性エネルギー線硬化性接着剤を塗布し、溶剤を揮散させた後、塗布面側から紫外線(120W高圧水銀ランプ、UV−A領域の積算光量200mJ/cm2)を照射し活性エネルギー線硬化接着剤層を硬化させた後、他のシート状部材(S2)を重ねつつ、60℃に設定した2つのロール間を通過させ、積層後、太陽電池用裏面保護シートを作成した。なお、接着剤層の量は8〜10g/平方メートルとした。
シート状部材(S1)に活性エネルギー線硬化性接着剤を塗布し、溶剤を揮散させた後、塗布面側から紫外線(120W高圧水銀ランプ、UV−A領域の積算光量200mJ/cm2)を照射し活性エネルギー線硬化接着剤層を硬化させた後、他のシート状部材(S2)を重ねつつ、60℃に設定した2つのロール間を通過させ、積層後、積層物を作成した。
次にこの積層物に活性エネルギー線硬化性接着剤を塗布し、溶剤を揮散させた後、塗布面側から紫外線(120W高圧水銀ランプ、UV−A領域の積算光量200mJ/cm2)を照射し活性エネルギー線硬化接着剤層を硬化させた後、もう一つのシート状部材(S3)を重ねつつ、60℃に設定した2つのロール間を通過させ、積層後、太陽電池用裏面保護シートを作成した。なお、2つの接着剤層の量はいずれも8〜10g/平方メートルとした。
表5〜7に示す活性エネルギー線硬化性接着剤と、太陽電池用裏面保護シートの作成方法、シート部材の組合せで、太陽電池用裏面保護シートを得た。後述する方法に従い、接着性、耐湿熱性、生産性、気泡の有無を評価した。結果を表5〜7に示す。
・PET(1):無色透明のポリエチレンテレフタレートフィルム(厚さ188μm)
・蒸着PET:ポリエチレンテレフタレートフィルム(厚さ12μm)の片面に、珪素酸化物とフッ化マグネシウムの比率(モル%)が90/10の混合物を500Åの厚さに蒸着したフィルム。
・AL(1):アルミニウム箔(厚さ30μm)の片面に10μの耐候性樹脂層*を設けたもの。
耐候性樹脂層*:オブリガートPS2012(白) 主剤:硬化剤(13:1)(AGCコーテック社製)
・AL(2):アルミニウム箔(厚さ30μm)。
・白色PET:白色ポリエチレンテレフタレートフィルム(厚さ50μm)
・黒PET:黒色ポリエチレンテレフタレートフィルム(厚さ50μm)
・PVF:デュポン社製ポリフッ化ビニルフィルム「テドラー」(厚さ38μm)
・KFC:クレハエクステック社製多層フィルム「FT−50Y」(厚さ50μm)
・EVA:エチレン・酢酸ビニル共重合樹脂フィルム(厚さ100μm)
(1)接着性
太陽電池用裏面保護シートを200mm×15mmの大きさに切断し、ASTM D1876−61の試験法に準じ、引張り試験機を用いて荷重速度300mm/分でT型剥離試験を行った。各シート状部材間の剥離強度(N/15mm巾)を5個の試験片の平均値で示した。
◎・・・4N以上
○・・・2N以上〜4N未満
△・・・1N以上〜2N未満
×・・・1N未満
太陽電池用裏面保護シートを85℃、85%RH雰囲気下に1000および2000時間保存した。保存した太陽電池用裏面保護シートを200mm×15mmの大きさに切断し、ASTM D1876−61の試験法に準じ、引張り試験機を用いて荷重速度300mm/分でT型剥離試験を行った。各シート状部材間の剥離強度(N/15mm巾)を5個の試験片の平均値で示した。
◎・・・4N以上
○・・・2N以上〜4N未満
△・・・1N以上〜2N未満
×・・・1N未満
50cm巾、500m長の太陽電池用裏面保護シートのロール状物を作成し、巻芯を天地方向にした状態に立て、外周をつかみ持ち上げた。
○・・・接着したシート内にズレが生じることはなく、ロールの形状も維持できた。
×・・・接着したシート内にズレが生じ、ロールの形状も維持できなかった。
50cm巾、500m長の太陽電池用裏面保護シートのロール状物を作成し、巻芯を天地方向にした状態に立て、60℃の環境に1週間保存した。
透明なシート状部材を通して接着剤層の状態を観察したり、シート状部材の浮きの有無を観察したりした。
○・・・異常なし
△・・・小さな気泡発生又は小さな浮きが発生。
×・・・大きな気泡発生又は大きな浮きが発生。
Claims (11)
- カーボネート構造を有するジオール成分を必須とする(メタ)アクリロイル基を有しないジオール成分(A)と、(メタ)アクリロイル基と2個以上のイソシアネート基とを有するポリイソシアネート成分(B)とを反応させてなる、ガラス転移温度が−60〜−10℃である(メタ)アクリロイル基を有するウレタン樹脂(C)、及びエポキシ樹脂(D)を含有することを特徴とする活性エネルギー線硬化性接着剤。
- ポリイソシアネート成分(B)が、(メタ)アクリロイル基及び水酸基を有する化合物(b1)とポリイソシアネート化合物(b2)との反応により生成する成分であって、アロファネート結合を有する成分である、請求項1記載の活性エネルギー線硬化性接着剤。
- ポリイソシアネート化合物(b2)が、ジイソシアネート化合物(b2−1)であり、ポリイソシアネート成分(B)が、(メタ)アクリロイル基及び水酸基を有する化合物(b1)とポリイソシアネート化合物(b2−1)との反応により生成するウレタン結合に、前記ジイソシアネート化合物(b2−1)由来のイソシアネート基がさらに反応してなる、アロファネート結合を有する成分である、請求項2記載の活性エネルギー線硬化性接着剤。
- ポリイソシアネート成分(B)が、下記一般式(I)及び/又は下記一般式(II)にて示される部分構造を含有する成分である、請求項3記載の活性エネルギー線硬化性接着剤。
一般式(I)、(II)において、
R1はジイソシアネート化合物(b2−1)からイソシアネート基を除いた残基を表し、
R2は(メタ)アクリロイル基及び水酸基を有する化合物(b1)から水酸基を除いた残基を表す。) - (メタ)アクリロイル基を有するウレタン樹脂(C)の数平均分子量が5000〜150000であることを特徴とする、請求項1〜4いずれか記載の活性エネルギー線硬化性接着剤。
- (メタ)アクリロイル基を有するウレタン樹脂(C)の(メタ)アクリロイル基当量が500〜40000であることを特徴とする、請求項1〜5いずれか記載の活性エネルギー線硬化性接着剤。
- エポキシ樹脂(D)の数平均分子量が500〜5000であることを特徴とする請求項1〜6いずれか記載の活性エネルギー線硬化性接着剤。
- (メタ)アクリロイル基を有するウレタン樹脂(C)100重量部に対して、エポキシ樹脂(D)を5〜40重量部含有することを特徴とする請求項1〜7いずれか記載の活性エネルギー線硬化性接着剤。
- 請求項1〜8いずれか記載の活性エネルギー線硬化性接着剤から形成された活性エネルギー線硬化接着剤層を介して、少なくとも2つ以上のシート状部材が積層されてなる太陽電池用裏面保護シート。
- シート状部材の1つが、金属箔であるか、あるいは、プラスチックフィルムの少なくとも一方の面に金属酸化物もしくは非金属無機酸化物が蒸着されてなる蒸着層付きプラスチックフィルムであることを特徴とする請求項9記載の太陽電池用裏面保護シート。
- 活性エネルギー線硬化接着剤層のガラス転移温度が、−20〜30℃であることを特徴とする請求項9または10記載の太陽電池用裏面保護シート。