JP5652962B2 - カーペット用基布 - Google Patents
カーペット用基布 Download PDFInfo
- Publication number
- JP5652962B2 JP5652962B2 JP2011218611A JP2011218611A JP5652962B2 JP 5652962 B2 JP5652962 B2 JP 5652962B2 JP 2011218611 A JP2011218611 A JP 2011218611A JP 2011218611 A JP2011218611 A JP 2011218611A JP 5652962 B2 JP5652962 B2 JP 5652962B2
- Authority
- JP
- Japan
- Prior art keywords
- carpet
- base fabric
- phase change
- change material
- fabric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
基布・・・目付100g/m2ポリプロピレンテープヤーン織布(14×13)に目付80g/m2ポリエステル不織布をニードリングにより積層一体化
相転移材料を封入したマイクロカプセル・・・プレサーモ(大和化学工業株式会社製)融点25℃と融点31℃の二種類
吸湿剤・・・ポリエーテルポリオール型ウレタン樹脂
浸透剤・・・「ペレックスOT−P」(花王株式会社製)
Qmax・・・カトーテック株式会社製THERMO LABO II TYPEを用い、純銅板の初期温度36℃、接触圧0.98kPaで測定した。基布温度28℃で、Qmaxが0.105j/cm2・secより大きいものを合格とした。但し基布は、予め3.92MPa、温度60℃で2分間プレスを行い、基布表面を整え、測定環境に2時間以上放置してから測定を行った。
官能評価・・・相転移材料を封入したマイクロカプセルを固着していない基布を基準に冷たいと感じるかどうかを一対比較法で評価し、被験者数を10人とし、80%以上の人が冷たいと感じたものを合格で「○」とし、それ以外を不合格で「×」とした。(気温20℃湿度65%の標準室内にて評価)
水1重量部に相転移材料を封入したマイクロカプセル分散液(パラフィン封入、融点25℃、固形分40%)を60重量部分散させておいてから、浸透剤を0.5重量部、バインダー樹脂を10重量部及び吸湿剤を30重量部分散した水溶液をスプレーにて基布の不織布側から250g/m2塗布し、120℃、10分間乾燥処理して、基布の不織布に相転移材料を封入したマイクロカプセルを100g/m2及び吸湿剤を50g/m2固着したカーペット用基布を得た。涼感性能測定試験でQmaxは0.112j/cm2・secで、官能評価においては9人の人が冷たいと感じていた。
実施例1において、水1重量部に相転移材料を封入したマイクロカプセル分散液(パラフィン封入、融点25℃、固形分40%)を60重量部と相転移材料を封入したマイクロカプセル分散液(パラフィン封入、融点31℃、固形分40%)を30重量部分散させておいてから、浸透剤を0.5重量部、バインダー樹脂を10重量部及び吸湿剤を30重量部分散した水溶液を用いた以外は実施例1と同様にしてカーペット用基布を得た。相転移材料を封入したマイクロカプセルの固着量は150g/m2、吸湿剤の固着量は50g/m2であった。Qmaxは0.12j/cm2・secで、官能評価においては9人の人が冷たいと感じていた。
実施例2において、目付100g/m2ポリプロピレンテープヤーン織布(14×13)に、ロールコーターを用いてエチレン−酢酸ビニル共重合体(EVA)等の樹脂を50g/m2塗布した後、目付80g/m2ポリエステル不織布を張り合わせて、120℃で10分乾燥し、積層一体化した基布を用いた以外は実施例2と同様にしてカーペット用基布を得た。相転移材料を封入したマイクロカプセルの固着量は150g/m2、吸湿剤の固着量は50g/m2であった。Qmaxは0.118j/cm2・secで、官能評価においては9人の人が冷たいと感じていた。
実施例2において、目付100g/m2の綿の織布(14×13)を用いた以外は実施例2と同様にしてカーペット用基布を得た。相転移材料を封入したマイクロカプセルの固着量は150g/m2、吸湿剤の固着量は50g/m2であった。Qmaxは0.118j/cm2・secで、官能評価においては9人の人が冷たいと感じていた。
実施例4において、目付80g/m2ポリプロピレン不織布を用いた以外は実施例4と同様にしてカーペット用基布を得た。相転移材料を封入したマイクロカプセルの固着量は150g/m2、吸湿剤の固着量は50g/m2であった。Qmaxは0.118j/cm2・secで、官能評価においては9人の人が冷たいと感じていた。
実施例2において、目付30g/m2ポリエステル不織布を用い、水1重量部に相転移材料を封入したマイクロカプセル分散液(パラフィン封入、融点25℃、固形分40%)を24重量部と相転移材料を封入したマイクロカプセル分散液(パラフィン封入、融点31℃、固形分40%)を12重量部分散させておいてから、浸透剤を0.5重量部、バインダー樹脂を10重量部及び吸湿剤を12重量部分散した水溶液を用いた以外は実施例2と同様にしてカーペット用基布を得た。相転移材料を封入したマイクロカプセルの固着量は60g/m2、吸湿剤の固着量は20g/m2であった。Qmaxは0.11j/cm2・secで、官能評価においては8人の人が冷たいと感じていた。
実施例2において、目付120g/m2ポリエステル不織布を用い、水1重量部に相転移材料を封入したマイクロカプセル分散液(パラフィン封入、融点25℃、固形分40%)を120重量部と相転移材料を封入したマイクロカプセル分散液(パラフィン封入、融点31℃、固形分40%)を60重量部分散させておいてから、浸透剤を0.5重量部、バインダー樹脂を10重量部及び吸湿剤を60重量部分散した水溶液を用いた以外は実施例2と同様にしてカーペット用基布を得た。相転移材料を封入したマイクロカプセルの固着量は300g/m2、吸湿剤の固着量は100g/m2であった。Qmaxは0.125j/cm2・secで、官能評価においては10人の人が冷たいと感じていた。
実施例2において、水1重量部に相転移材料を封入したマイクロカプセル分散液(パラフィン封入、融点25℃、固形分40%)を12重量部と相転移材料を封入したマイクロカプセル分散液(パラフィン封入、融点31℃、固形分40%)を24重量部分散させておいてから、浸透剤を0.5重量部、バインダー樹脂を10重量部及び吸湿剤を18重量部分散した水溶液を用いた以外は実施例2と同様にしてカーペット用基布を得た。相転移材料を封入したマイクロカプセルの固着量は60g/m2、吸湿剤の固着量は30g/m2であった。Qmaxは0.108j/cm2・secで、比較例1との官能評価においては8人の人が冷たいと感じていた。
目付100g/m2ポリプロピレンテープヤーン織布(14×13)を用意した(不織布は積層されていない)。相転移材料を封入したマイクロカプセル及び吸湿剤を固着させなかった。Qmaxは0.08j/cm2・secであった。なお、比較例1を官能評価の基準とした。
実施例1において、不織布を積層していない目付100g/m2の綿の織布(14×13)を用いて、水1重量部に相転移材料を封入したマイクロカプセル分散液(パラフィン封入、融点25℃、固形分40%)を6重量部分散させておいてから、浸透剤を0.5重量部、バインダー樹脂を10重量部及び吸湿剤を3重量部分散した水溶液を用いた以外は実施例1と同様にして基布を得た。相転移材料を封入したマイクロカプセルの固着量は10g/m2、吸湿剤の固着量は5g/m2であった。Qmaxは0.085j/cm2・secで、官能評価においては3人の人が冷たいと感じていた。
実施例1において、相転移材料を封入したマイクロカプセル及び吸湿剤を固着させる前の基布を用意した。Qmaxは0.075j/cm2・secで、官能評価において誰も冷たいと感じなかった。
実施例1において、水1重量部に吸湿剤を分散させなかった以外は、実施例1と同様にして基布を得た。相転移材料を封入したマイクロカプセルの固着量は100g/m2であった。Qmaxは0.1j/cm2・secで、官能評価においては6人の人が冷たいと感じていた。
実施例1において、水1重量部に相転移材料を封入したマイクロカプセルを分散させなかった以外は、実施例1と同様にして基布を得た。吸湿剤の固着量は50g/m2であった。Qmaxは0.095j/cm2・secで、官能評価においては5人の人が冷たいと感じていた。
2・・・相転移材料を封入したマイクロカプセル
3・・・吸湿剤
4・・・不織布
5・・・織基布
5−1・・・経糸
5−2・・・横糸
Claims (7)
- 不織布と、織基布とが積層一体化された基布において、
相転移材料を封入したマイクロカプセルが少なくとも60〜500g/m 2 、
及び吸湿剤が少なくとも50〜250g/m 2 が
バインダー樹脂によって該不織布に固着していることに特徴のあるカーペット用基布。 - 前記不織布と前記織基布とがニードリングにより絡ませられ積層一体化されている請求項1に記載のカーペット用基布。
- 前記不織布の目付量が10〜200g/m2である請求項1または2に記載のカーペット用基布。
- 前記相転移材料の融点が20〜35℃である請求項1〜3のいずれか1項に記載のカーペット用基布。
- 前記吸湿剤は、ポリエーテルポリオール型ウレタン樹脂、尿素、エチレン尿素、チオ尿素、スクワラン、シルクプロテイン、キシリトール、エリスリトール、コラーゲンのうち少なくとも1種を含有する吸湿剤である請求項1〜4のいずれか1項に記載のカーペット用基布。
- 前記マイクロカプセルには、相転移材料の融点が20〜35℃の範囲のうちの二種類以上の融点を持つ相転移材料が封入された請求項1〜5のいずれか1項に記載のカーペット用基布。
- 請求項1〜6のいずれか1項に記載のカーペット用基布にパイルを植設したカーペット表皮層を用いたことに特徴のある涼感カーペット。