JP5648848B2 - 抄紙用プレスフェルト - Google Patents
抄紙用プレスフェルト Download PDFInfo
- Publication number
- JP5648848B2 JP5648848B2 JP2011024366A JP2011024366A JP5648848B2 JP 5648848 B2 JP5648848 B2 JP 5648848B2 JP 2011024366 A JP2011024366 A JP 2011024366A JP 2011024366 A JP2011024366 A JP 2011024366A JP 5648848 B2 JP5648848 B2 JP 5648848B2
- Authority
- JP
- Japan
- Prior art keywords
- felt
- press
- papermaking
- fiber
- polyamide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は、図1に示すプレスパートで使用するプレスフェルトである。
図2および図3に例示した本発明の抄紙用プレスフェルトは、補強繊維基材5、該補強繊維基材の湿紙載置側(表側)に配置された表バット繊維層6、および該補強繊維基材のプレスロール側(裏側)に配置された裏バット繊維層7を備え、図2は高分子弾性体8が表バット繊維層6中に留まった状態を、図3は高分子弾性体8が表バット繊維層6から裏バット繊維層7まで達した状態を、それぞれ示す。そして、それぞれ表バット繊維層6と裏バット繊維層7の少なくとも一方には、溶融繊維が配置している状態を示す。
本実施例および比較例において使用したフェルトの基本構成は次のとおりである。
補強繊維基材(ポリアミドモノフィラメントの撚糸、平織):坪量750g/m2
バット層:17dtexのポリアミド6ステープルファイバーと溶融繊維とを、表1に記載した配合量で配合した混綿繊維を使用した。
溶融繊維:芯材料として高分子量ポリアミド6(25℃での絶対粘度85mPa・s、融点220℃)と鞘材料として共重合ポリアミド6/12(融点140℃)を使用し、芯部と鞘部の容積比率が1:1である芯鞘型複合繊維
補強繊維基材の湿紙載置側(表バット層):坪量500g/m2
補強繊維基材のプレスロール側(裏バット層):坪量250g/m2
補強繊維基材に裏バット繊維と表バット繊維とを積層し、ニードリングにより絡合一体化してフェルトを形成した後、高分子弾性体をフェルトの表側からスプレー塗布し、105℃で乾燥したのち、140℃の熱風を当て同時に熱プレスして熱処理した。
高分子弾性体は、表1に示す樹脂および条件で適用した。
搾水試験条件:加圧100KN/m、抄速1000m/分
プレス前湿紙含水率;70%
プレス前湿紙含水率=(プレス前湿紙重量−乾燥紙重量)÷プレス前湿紙重量×100
プレス後湿紙含水率=(プレス後湿紙重量−乾燥紙重量)÷プレス後湿紙重量×100
プレス後湿紙含水率が低いほど搾水性の良いフェルトである。製紙業界においては、プレス後湿紙含水率の差が1%であっても、プレス後の紙の乾燥工程における熱エネルギー量に多大な影響を及ぼすことが分かっている。
プレステスターにおいて、
プレス前厚み:T0
プレス下厚み:T1(100KN/m)
プレス後厚み:T2
プレス時圧縮率=(T0−T1)÷T0×100
プレス前後厚み保持率=T2÷T0×100
実施例1〜8においては、含有する高分子弾性体により湿紙の搾水性、フェルトの圧縮性と回復性及びその持続性が向上していることが分かる。
1a、4a … トップロール
1b、4b … ボトムロール
CR … センターロール
2、3 … ロール
5 … 補強繊維基材
5a … 経糸(MD糸)
5b … 緯糸(CMD糸)
6 … 表バット繊維層
7 … 裏バット繊維層
8 … 高分子弾性体含有層
10 … フェルト
41 … 試験片
42 … つかみ具
GR … ガイドロール
PR … プレスロール
SE0 … 厚みセンサー
SE1 … 厚みセンサー
SE2 … 厚みセンサー
Claims (2)
- 補強繊維基材と、該補強繊維基材の湿紙載置側に配置される表バット繊維層とプレスロール側に配置される裏バット繊維層とを備えた抄紙用プレスフェルトにおいて、前記表バット繊維層及び裏バット繊維層の少なくとも一方には、抄紙用プレスフェルトの重量に対して0.5〜30重量%の溶融繊維が含まれており、更に表バット繊維層には抄紙用プレスフェルトの重量に対して0.5〜20重量%の高分子弾性体が分散付着され、前記高分子弾性体は、前記高分子弾性体をフィルム状にした時のフィルム物性が、室温20℃、相対湿度65%の環境下で測定された100%モジュラス値が1〜100kg/cm2、100%伸長後残留歪が30%以下であることを特徴とする、抄紙用プレスフェルト。
- 前記溶融繊維が、絶対粘度が80mPa・s以上である高分子量ポリアミドからなる芯成分と、該芯成分よりも低融点のポリアミドからなる鞘成分、とから構成される芯鞘型複合繊維であることを特徴とする、請求項1に記載の抄紙用プレスフェルト。