JP5618276B2 - 高耐食性を有する高強度マグネシウム合金及びその製造方法 - Google Patents
高耐食性を有する高強度マグネシウム合金及びその製造方法 Download PDFInfo
- Publication number
- JP5618276B2 JP5618276B2 JP2012103120A JP2012103120A JP5618276B2 JP 5618276 B2 JP5618276 B2 JP 5618276B2 JP 2012103120 A JP2012103120 A JP 2012103120A JP 2012103120 A JP2012103120 A JP 2012103120A JP 5618276 B2 JP5618276 B2 JP 5618276B2
- Authority
- JP
- Japan
- Prior art keywords
- atomic
- magnesium alloy
- corrosion resistance
- strength
- close
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
これらの用途に使用するためにはマグネシウム合金に高強度と高靭性と高耐食性が要求される。高強度高靭性金属の製造のために従来から材料面及び製法面から種々検討されている。
(1)0.2≦a≦5.0
(2)0.2≦b≦5.0
(3)2a−3≦b
(4)0.05b≦c<0.75b
(5)0≦d≦b/2
前記長周期積層構造は、最密原子面に沿って溶質原子であるZnと希土類元素が積層方向に連続した二原子層の濃化した溶質原子濃化二原子層を含み、前記溶質原子濃化二原子層が積層方向に周期性を有するものであり、
前記最密原子面積層欠陥は、最密原子面に沿って溶質原子であるZnと希土類元素が積層方向に連続した二原子層の濃化した溶質原子濃化二原子層を含み、前記溶質原子濃化二原子層が積層方向に周期性を有さないものであることも可能である。
本発明者は、基本に立ち返り、2元マグネシウム合金から始めて合金の強度及び靭性を検討し、更にその検討を多元マグネシウム合金まで拡大した。その結果、強度、靭性及び耐食性を全て高いレベルで有するマグネシウム合金はMg−Zn−RE(希土類元素)−Al系であり、希土類元素がY、Gd、Dy、Ho、Er、Tb及びTmからなる群から選択される少なくとも1種の元素であるマグネシウム合金であり、更に従来技術とは異なり亜鉛の含有量が5.0原子%以下で希土類元素の含有量が5.0原子%以下という低含有量において従来にない高強度及び高靭性が得られることを見出した。
尚、本明細書でいう長周期積層構造とは、最密原子面に沿って溶質原子である亜鉛と希土類元素が積層方向に連続した二原子層の濃化した層(溶質原子濃化二原子層)を含み、その溶質原子濃化二原子層が長距離にわたって積層方向に周期性を有する場合をいう。また、最密原子面積層欠陥とは、最密原子面に沿って溶質原子である亜鉛と希土類元素が積層方向に連続した二原子層の濃化した層(溶質原子濃化二原子層)を含み、その溶質原子濃化二原子層が長距離にわたって積層方向に周期性を有さない場合をいう。
本発明の実施の形態1によるマグネシウム合金は、基本的にMg、Zn、希土類元素及びAlを含む4元以上の合金であり、希土類元素(RE)は、Y、Gd、Dy、Ho、Er、Tb及びTmからなる群から選択される1又は2以上の元素である。
(1)0.2≦a≦5.0
(2)0.2≦b≦5.0
(3)2a−3≦b
(4)0.05b≦c<0.75b
(6)0.1b≦c≦0.5b
本発明の実施の形態2によるマグネシウム合金は、基本的にMg、Zn、希土類元素、Al及びXを含む5元以上の合金である。希土類元素(RE)は、Y、Gd、Dy、Ho、Er、Tb及びTmからなる群から選択される1又は2以上の元素である。Xの元素は後記のとおりである。
(1)0.2≦a≦5.0
(2)0.2≦b≦5.0
(3)2a−3≦b
(4)0.05b≦c<0.75b
(5)0≦d≦b/2
(6)0.1b≦c≦0.5b
(7)0≦d≦b/3
本発明の実施の形態3によるマグネシウム合金の製造方法について説明する。
実施の形態1〜2のいずれかの組成からなるマグネシウム合金を溶解して鋳造し、マグネシウム合金鋳造物を作る。鋳造時の冷却速度は1000K/秒以下であり、より好ましくは100K/秒以下である。このマグネシウム合金鋳造物としては、インゴットから所定形状に切り出したものを用いる。
本発明の実施の形態4によるマグネシウム合金の製造方法について説明する。
実施の形態1〜2のいずれかの組成からなるマグネシウム合金を溶解して鋳造し、マグネシウム合金鋳造物を作る。鋳造時の冷却速度は1000K/秒以下であり、より好ましくは100K/秒以下である。このマグネシウム合金鋳造物としては、インゴットから所定形状に切り出したものを用いる。
本発明の実施の形態5によるマグネシウム合金の製造方法について説明する。
図1は、ビレットを押出成形するまでを示している。以下、急速凝固粉末の作製と固化成形について、詳しく説明する。
図2は、本発明の実施例によるマグネシウム合金の急速凝固薄片材のAl含有量と耐食性の関係を示す図である。図3は、図2の急速凝固薄片材を熱処理した急速凝固薄片熱処理材のAl含有量と耐食性の関係を示す図である。
340…スポット溶接機
400…押出プレス機
410…ヒータ
420…コンテナ
430…型(ダイ)
450…メイン・ステム
460…ダイ・バッカー
470…バック・ステム
Claims (2)
- Znをa原子%含有し、Dy、Ho、Er、Gd、Tb及びTmからなる群から選択される少なくとも1種類の元素を合計でb原子%含有し、Alをc原子%含有し、残部がMgから成り、aとbとcは下記式(1)〜(4)を満たすマグネシウム合金であり、
前記マグネシウム合金は、長周期積層構造又は最密原子面積層欠陥を含む相及びhcp構造マグネシウム相を有する結晶組織を具備し、
前記長周期積層構造は、最密原子面に沿って溶質原子であるZnと希土類元素が積層方向に連続した二原子層の濃化した溶質原子濃化二原子層を含み、前記溶質原子濃化二原子層が積層方向に周期性を有するものであり、
前記最密原子面積層欠陥は、最密原子面に沿って溶質原子であるZnと希土類元素が積層方向に連続した二原子層の濃化した溶質原子濃化二原子層を含み、前記溶質原子濃化二原子層が積層方向に周期性を有さないものであることを特徴とする高耐食性を有する高強度マグネシウム合金。
(1)0.2≦a≦5.0
(2)0.2≦b≦5.0
(3)2a−3≦b
(4)0.05b≦c<0.75b - 請求項1において、
前記長周期積層構造又は最密原子面積層欠陥を含む相がキンク変形していることを特徴とする高耐食性を有する高強度マグネシウム合金。