JP5505574B1 - 熱間プレス用鋼板、その製造方法、及び熱間プレス鋼板部材 - Google Patents

熱間プレス用鋼板、その製造方法、及び熱間プレス鋼板部材 Download PDF

Info

Publication number
JP5505574B1
JP5505574B1 JP2013552765A JP2013552765A JP5505574B1 JP 5505574 B1 JP5505574 B1 JP 5505574B1 JP 2013552765 A JP2013552765 A JP 2013552765A JP 2013552765 A JP2013552765 A JP 2013552765A JP 5505574 B1 JP5505574 B1 JP 5505574B1
Authority
JP
Japan
Prior art keywords
steel sheet
hot
content
less
chemical composition
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
JP2013552765A
Other languages
English (en)
Japanese (ja)
Other versions
JPWO2014027682A1 (ja
Inventor
朱理 玉城
和夫 匹田
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nippon Steel Corp
Original Assignee
Nippon Steel and Sumitomo Metal Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nippon Steel and Sumitomo Metal Corp filed Critical Nippon Steel and Sumitomo Metal Corp
Priority to JP2013552765A priority Critical patent/JP5505574B1/ja
Application granted granted Critical
Publication of JP5505574B1 publication Critical patent/JP5505574B1/ja
Publication of JPWO2014027682A1 publication Critical patent/JPWO2014027682A1/ja
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Links

Classifications

    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0247—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment
    • C21D8/0263—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment following hot rolling
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B15/00—Layered products comprising a layer of metal
    • B32B15/01—Layered products comprising a layer of metal all layers being exclusively metallic
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
    • C21D1/18—Hardening; Quenching with or without subsequent tempering
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
    • C21D1/62—Quenching devices
    • C21D1/673—Quenching devices for die quenching
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D6/00—Heat treatment of ferrous alloys
    • C21D6/001—Heat treatment of ferrous alloys containing Ni
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D6/00—Heat treatment of ferrous alloys
    • C21D6/002—Heat treatment of ferrous alloys containing Cr
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D6/00—Heat treatment of ferrous alloys
    • C21D6/004—Heat treatment of ferrous alloys containing Cr and Ni
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D6/00—Heat treatment of ferrous alloys
    • C21D6/005—Heat treatment of ferrous alloys containing Mn
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D6/00—Heat treatment of ferrous alloys
    • C21D6/008—Heat treatment of ferrous alloys containing Si
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D7/00—Modifying the physical properties of iron or steel by deformation
    • C21D7/13—Modifying the physical properties of iron or steel by deformation by hot working
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0205—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips of ferrous alloys
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0221—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the working steps
    • C21D8/0226—Hot rolling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0221—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the working steps
    • C21D8/0236—Cold rolling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0247—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
    • C21D9/46—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for sheet metals
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/001—Ferrous alloys, e.g. steel alloys containing N
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/002—Ferrous alloys, e.g. steel alloys containing In, Mg, or other elements not provided for in one single group C22C38/001 - C22C38/60
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/005—Ferrous alloys, e.g. steel alloys containing rare earths, i.e. Sc, Y, Lanthanides
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/02—Ferrous alloys, e.g. steel alloys containing silicon
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/04—Ferrous alloys, e.g. steel alloys containing manganese
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/06—Ferrous alloys, e.g. steel alloys containing aluminium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/08—Ferrous alloys, e.g. steel alloys containing nickel
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/12—Ferrous alloys, e.g. steel alloys containing tungsten, tantalum, molybdenum, vanadium, or niobium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/14—Ferrous alloys, e.g. steel alloys containing titanium or zirconium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/16—Ferrous alloys, e.g. steel alloys containing copper
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/22—Ferrous alloys, e.g. steel alloys containing chromium with molybdenum or tungsten
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/24—Ferrous alloys, e.g. steel alloys containing chromium with vanadium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/26—Ferrous alloys, e.g. steel alloys containing chromium with niobium or tantalum
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/28—Ferrous alloys, e.g. steel alloys containing chromium with titanium or zirconium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/32—Ferrous alloys, e.g. steel alloys containing chromium with boron
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/38—Ferrous alloys, e.g. steel alloys containing chromium with more than 1.5% by weight of manganese
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
    • C22C38/50—Ferrous alloys, e.g. steel alloys containing chromium with nickel with titanium or zirconium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
    • C22C38/54—Ferrous alloys, e.g. steel alloys containing chromium with nickel with boron
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
    • C22C38/58—Ferrous alloys, e.g. steel alloys containing chromium with nickel with more than 1.5% by weight of manganese
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C23C2/022—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by heating
    • C23C2/0224—Two or more thermal pretreatments
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C23C2/024—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by cleaning or etching
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/04—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the coating material
    • C23C2/06—Zinc or cadmium or alloys based thereon
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/002—Bainite
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/005—Ferrite
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/008—Martensite

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Materials Engineering (AREA)
  • Mechanical Engineering (AREA)
  • Metallurgy (AREA)
  • Organic Chemistry (AREA)
  • Thermal Sciences (AREA)
  • Physics & Mathematics (AREA)
  • Crystallography & Structural Chemistry (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Heat Treatment Of Sheet Steel (AREA)
  • Heat Treatment Of Articles (AREA)
  • Coating With Molten Metal (AREA)
JP2013552765A 2012-08-15 2013-08-15 熱間プレス用鋼板、その製造方法、及び熱間プレス鋼板部材 Active JP5505574B1 (ja)

Priority Applications (1)

Application Number Priority Date Filing Date Title
JP2013552765A JP5505574B1 (ja) 2012-08-15 2013-08-15 熱間プレス用鋼板、その製造方法、及び熱間プレス鋼板部材

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
JP2012180186 2012-08-15
JP2012180186 2012-08-15
JP2013552765A JP5505574B1 (ja) 2012-08-15 2013-08-15 熱間プレス用鋼板、その製造方法、及び熱間プレス鋼板部材
PCT/JP2013/071971 WO2014027682A1 (ja) 2012-08-15 2013-08-15 熱間プレス用鋼板、その製造方法、及び熱間プレス鋼板部材

Publications (2)

Publication Number Publication Date
JP5505574B1 true JP5505574B1 (ja) 2014-05-28
JPWO2014027682A1 JPWO2014027682A1 (ja) 2016-07-28

Family

ID=50101304

Family Applications (1)

Application Number Title Priority Date Filing Date
JP2013552765A Active JP5505574B1 (ja) 2012-08-15 2013-08-15 熱間プレス用鋼板、その製造方法、及び熱間プレス鋼板部材

Country Status (12)

Country Link
US (1) US10570470B2 (Direct)
EP (1) EP2886674B1 (Direct)
JP (1) JP5505574B1 (Direct)
KR (1) KR101674331B1 (Direct)
CN (2) CN104583437A (Direct)
CA (1) CA2880946C (Direct)
IN (1) IN2015DN00705A (Direct)
MX (1) MX2015001772A (Direct)
RU (1) RU2599934C2 (Direct)
TW (1) TWI481729B (Direct)
WO (1) WO2014027682A1 (Direct)
ZA (1) ZA201501490B (Direct)

Families Citing this family (28)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR101417260B1 (ko) * 2012-04-10 2014-07-08 주식회사 포스코 재질 균일성이 우수한 고탄소 열연강판 및 이의 제조방법
JP2015196890A (ja) * 2014-04-02 2015-11-09 本田技研工業株式会社 ホットスタンプ成形体
JP6075517B1 (ja) * 2015-04-01 2017-02-08 Ｊｆｅスチール株式会社 熱延鋼板およびその製造方法
WO2017006144A1 (en) 2015-07-09 2017-01-12 Arcelormittal Steel for press hardening and press hardened part manufactured from such steel
CN105316601B (zh) * 2015-10-28 2017-03-22 安徽省三方新材料科技有限公司 一种顽石破碎机用衬板及其制备方法
KR20170075046A (ko) 2015-12-22 2017-07-03 주식회사 포스코 내식성이 우수한 열간 프레스 성형품 및 그 제조방법
CN107127238B (zh) * 2016-02-26 2019-12-27 宝山钢铁股份有限公司 一种锌系镀覆钢板或钢带的热冲压成型方法
KR101819345B1 (ko) 2016-07-07 2018-01-17 주식회사 포스코 균열전파 저항성 및 연성이 우수한 열간성형 부재 및 이의 제조방법
KR101963936B1 (ko) 2016-11-08 2019-07-31 한국과학기술원 전자파 신호 송수신 안테나 및 em-터널이 내장된 구조를 갖는 인쇄회로기판 및 그 제작 방법
WO2018220430A1 (en) 2017-06-02 2018-12-06 Arcelormittal Steel sheet for manufacturing press hardened parts, press hardened part having a combination of high strength and crash ductility, and manufacturing methods thereof
KR101977474B1 (ko) * 2017-08-09 2019-05-10 주식회사 포스코 표면 품질, 강도 및 연성이 우수한 도금강판
CA3076581A1 (en) * 2017-10-24 2019-05-02 Arcelormittal A method for the manufacture of a coated steel sheet
ES2982286T3 (es) 2017-10-24 2024-10-15 Arcelormittal Un procedimiento para la fabricación de una lámina de acero galvano-recocido
CN107604266A (zh) * 2017-10-31 2018-01-19 桂林加宏汽车修理有限公司 一种高韧性钢合金
UA125102C2 (uk) 2017-11-17 2022-01-05 Арселорміттал Спосіб виготовлення сталевого листа з цинковим покриттям, стійкого до рідинно-металічного окрихчування
CN109365606A (zh) * 2018-11-30 2019-02-22 宝山钢铁股份有限公司 一种耐腐蚀性优良的锌系镀层钢板或钢带的成形方法
US11795520B2 (en) 2019-02-22 2023-10-24 Jfe Steel Corporation Hot-pressed member, method for manufacturing the same, and method for manufacturing steel sheet for hot-pressed member
EP4065736A1 (en) * 2019-11-27 2022-10-05 Tata Steel IJmuiden B.V. Method of hot press forming a steel article and steel article
JP7648620B2 (ja) * 2019-12-20 2025-03-18 ポスコホールディングス インコーポレーティッド 熱間成形用鋼材、熱間成形部材及びこれらの製造方法
CN111676417A (zh) * 2020-05-07 2020-09-18 天津英利模具制造有限公司 一种轻量化汽车用高强钢板及其热冲压成型工艺
WO2021230150A1 (ja) * 2020-05-13 2021-11-18 日本製鉄株式会社 ホットスタンプ用鋼板およびホットスタンプ成形体
WO2021230149A1 (ja) * 2020-05-13 2021-11-18 日本製鉄株式会社 ホットスタンプ成形体
JP7553837B2 (ja) * 2020-10-16 2024-09-19 日本製鉄株式会社 ホットスタンプ用鋼板及びその製造方法、並びに、ホットスタンプ部材及びその製造方法
WO2022195024A1 (en) * 2021-03-17 2022-09-22 Tata Steel Ijmuiden B.V. Steel strip, sheet or blank and method for producing a hot-formed part or a heat-treated pre-formed part
EP4379084A4 (en) * 2021-07-30 2025-11-19 Hyundai Steel Co STEEL SHEET FOR HOT PRESSING AND ALUMINUM-COATED FLAN MADE USING SAID SHEET
JP7512987B2 (ja) * 2021-09-22 2024-07-09 Ｊｆｅスチール株式会社 熱間プレス用鋼板、その製造方法、熱間プレス部材およびその製造方法
WO2023079344A1 (en) * 2021-11-05 2023-05-11 Arcelormittal Method for producing a steel sheet having excellent processability before hot forming, steel sheet, process to manufacture a hot stamped part and hot stamped part
TWI876779B (zh) * 2023-12-18 2025-03-11 中國鋼鐵股份有限公司 高平坦度及超高強度鋼材及其製造方法

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2005126733A (ja) * 2003-10-21 2005-05-19 Nippon Steel Corp 高温加工性にすぐれた熱間プレス用鋼板及び自動車用部材
JP2006070346A (ja) * 2004-09-06 2006-03-16 Nippon Steel Corp 耐水素脆化特性に優れたホットプレス用鋼板、自動車用部材及びその製造方法
JP2006212663A (ja) * 2005-02-02 2006-08-17 Nippon Steel Corp 成形性に優れたホットプレス高強度鋼製部材の製造方法
JP2007211276A (ja) * 2006-02-08 2007-08-23 Sumitomo Metal Ind Ltd 熱間プレス用めっき鋼板およびその製造方法ならびに熱間プレス成形部材の製造方法
JP2010174301A (ja) * 2009-01-28 2010-08-12 Jfe Steel Corp ダイクエンチ用鋼板

Family Cites Families (32)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2001226741A (ja) 2000-02-15 2001-08-21 Kawasaki Steel Corp 伸びフランジ加工性に優れた高強度冷延鋼板およびその製造方法
JP3389562B2 (ja) 2000-07-28 2003-03-24 アイシン高丘株式会社 車輌用衝突補強材の製造方法
JP3879459B2 (ja) 2001-08-31 2007-02-14 Ｊｆｅスチール株式会社 高焼入れ性高炭素熱延鋼板の製造方法
JP3468239B2 (ja) * 2001-10-01 2003-11-17 住友金属工業株式会社 機械構造用鋼及びその製造方法
CN100591789C (zh) 2002-12-24 2010-02-24 新日本制铁株式会社 焊接热影响区的耐软化性优良且扩孔弯边性好的高强度钢板及其制造方法
JP4160840B2 (ja) * 2003-02-19 2008-10-08 新日本製鐵株式会社 形状凍結性に優れた高加工性高強度熱延鋼板とその製造方法
JP4292986B2 (ja) * 2003-04-16 2009-07-08 Ｊｆｅスチール株式会社 高張力冷延鋼板およびその製造方法
JP3885763B2 (ja) 2003-04-25 2007-02-28 住友金属工業株式会社 焼入用溶融亜鉛系めっき鋼板とその製造方法及び用途
KR101062087B1 (ko) * 2003-12-19 2011-09-02 엑손모빌 업스트림 리서치 캄파니 초고강도 라인파이프용 강판 및 우수한 저온 인성을 갖는 초고강도 라인파이프, 및 그 제조 방법
RU2277594C1 (ru) * 2005-03-30 2006-06-10 Открытое акционерное общество "Северсталь" Способ производства холоднокатаных листов для глубокой вытяжки
EP2671960B1 (en) 2005-03-31 2017-11-01 Kabushiki Kaisha Kobe Seiko Sho High strength cold-rolled steel sheet and automobile components of steel having excellent properties in coating film adhesion, workability, and hydrogen embrittlement resistivity
CN101218362B (zh) 2005-07-07 2010-05-12 住友金属工业株式会社 无方向性电磁钢板及其制造方法
EP1832667A1 (fr) * 2006-03-07 2007-09-12 ARCELOR France Procédé de fabrication de tôles d'acier à très hautes caractéristiques de résistance, de ductilité et de tenacité, et tôles ainsi produites
JP5008173B2 (ja) * 2006-05-17 2012-08-22 日産自動車株式会社 抵抗溶接用高張力鋼板及びその接合方法
CN101821419B (zh) * 2007-10-25 2015-03-18 杰富意钢铁株式会社 加工性优良的高强度热镀锌钢板及其制造方法
JP5167487B2 (ja) 2008-02-19 2013-03-21 Ｊｆｅスチール株式会社 延性に優れる高強度鋼板およびその製造方法
JP5418047B2 (ja) * 2008-09-10 2014-02-19 Ｊｆｅスチール株式会社 高強度鋼板およびその製造方法
JP5347392B2 (ja) 2008-09-12 2013-11-20 Ｊｆｅスチール株式会社 延性に優れたホットプレス部材、そのホットプレス部材用鋼板、およびそのホットプレス部材の製造方法
JP4811528B2 (ja) * 2009-07-28 2011-11-09 Ｊｆｅスチール株式会社 高強度冷延鋼板およびその製造方法
JP5786317B2 (ja) * 2010-01-22 2015-09-30 Ｊｆｅスチール株式会社 材質安定性と加工性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
KR101447791B1 (ko) 2010-01-26 2014-10-06 신닛테츠스미킨 카부시키카이샤 고강도 냉연 강판 및 그 제조 방법
BR112012021348A2 (pt) 2010-02-26 2016-08-23 Nippon Steel & Sumitomo Metal Corp "material de aço tratado por calor, método para produzir o mesmo, e material de base de aço para o mesmo."
EP2374910A1 (de) 2010-04-01 2011-10-12 ThyssenKrupp Steel Europe AG Stahl, Stahlflachprodukt, Stahlbauteil und Verfahren zur Herstellung eines Stahlbauteils
JP5440371B2 (ja) 2010-05-12 2014-03-12 新日鐵住金株式会社 熱処理用鋼板およびその製造方法
CN102409235A (zh) * 2010-09-21 2012-04-11 鞍钢股份有限公司 高强度冷轧相变诱导塑性钢板及其制备方法
CA2814630C (en) * 2010-10-22 2016-04-26 Nippon Steel & Sumitomo Metal Corporation Method for manufacturing hot stamped body and hot stamped body
US10023925B2 (en) 2011-05-13 2018-07-17 Nippon Steel & Sumitomo Metal Corporation Hot stamped article, method of producing hot stamped article, energy absorbing member, and method of producing energy absorbing member
MX357148B (es) 2012-01-13 2018-06-28 Nippon Steel & Sumitomo Metal Corp Lamina de acero laminada en frio y metodo para la produccion de la misma.
PL2803747T3 (pl) 2012-01-13 2019-09-30 Nippon Steel & Sumitomo Metal Corporation Blacha stalowa cienka walcowana na zimno i sposób wytwarzania blachy stalowej cienkiej walcowanej na zimno
CA2863218C (en) 2012-01-13 2017-07-18 Nippon Steel & Sumitomo Metal Corporation Hot stamped steel and method for producing the same
TWI484050B (zh) 2012-08-06 2015-05-11 Nippon Steel & Sumitomo Metal Corp 冷軋鋼板、及其製造方法、以及熱壓印成形體
RU2603762C2 (ru) 2012-08-07 2016-11-27 Ниппон Стил Энд Сумитомо Метал Корпорейшн Гальванизированный стальной лист для формовки в горячем состоянии

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2005126733A (ja) * 2003-10-21 2005-05-19 Nippon Steel Corp 高温加工性にすぐれた熱間プレス用鋼板及び自動車用部材
JP2006070346A (ja) * 2004-09-06 2006-03-16 Nippon Steel Corp 耐水素脆化特性に優れたホットプレス用鋼板、自動車用部材及びその製造方法
JP2006212663A (ja) * 2005-02-02 2006-08-17 Nippon Steel Corp 成形性に優れたホットプレス高強度鋼製部材の製造方法
JP2007211276A (ja) * 2006-02-08 2007-08-23 Sumitomo Metal Ind Ltd 熱間プレス用めっき鋼板およびその製造方法ならびに熱間プレス成形部材の製造方法
JP2010174301A (ja) * 2009-01-28 2010-08-12 Jfe Steel Corp ダイクエンチ用鋼板

Also Published As

Publication number Publication date
TWI481729B (zh) 2015-04-21
MX2015001772A (es) 2015-05-08
RU2599934C2 (ru) 2016-10-20
CA2880946A1 (en) 2014-02-20
IN2015DN00705A (Direct) 2015-06-26
TW201410878A (zh) 2014-03-16
EP2886674B1 (en) 2020-09-30
US20150284819A1 (en) 2015-10-08
WO2014027682A1 (ja) 2014-02-20
KR20150029742A (ko) 2015-03-18
CN104583437A (zh) 2015-04-29
JPWO2014027682A1 (ja) 2016-07-28
CN109023051A (zh) 2018-12-18
ZA201501490B (en) 2016-01-27
RU2015108067A (ru) 2016-10-10
US10570470B2 (en) 2020-02-25
KR101674331B1 (ko) 2016-11-08
EP2886674A1 (en) 2015-06-24
EP2886674A4 (en) 2016-11-30
CA2880946C (en) 2018-06-12

Similar Documents

Publication Publication Date Title
JP5505574B1 (ja) 熱間プレス用鋼板、その製造方法、及び熱間プレス鋼板部材
KR102143834B1 (ko) 강판, 도금 강판 및, 그들의 제조 방법
US10711333B2 (en) High-strength steel sheet and method for manufacturing same
CN102712977B (zh) 加工性和耐冲击特性优良的高强度热镀锌钢板及其制造方法
CN109963958B (zh) 高强度钢板及其制造方法
JP5983896B2 (ja) 高強度鋼板およびその製造方法、ならびに高強度亜鉛めっき鋼板の製造方法
US20170306435A1 (en) High-strength steel sheet, high-strength hot-dip galvanized steel sheet, high-strength hot-dip aluminum-coated steel sheet, and high-strength electrogalvanized steel sheet, and methods for manufacturing same
JP6202096B2 (ja) 熱処理鋼材及びその製造方法
CN109937265B (zh) 高强度钢板及其制造方法
JP7095818B2 (ja) 被覆鋼部材、被覆鋼板およびそれらの製造方法
US20190276907A1 (en) Steel sheet, coated steel sheet, and methods for manufacturing same
JP6750771B1 (ja) 溶融亜鉛めっき鋼板およびその製造方法
JP6601253B2 (ja) 高強度鋼板
CN114585766A (zh) 高强度钢板及其制造方法
JP5835624B2 (ja) 熱間プレス用鋼板および表面処理鋼板とそれらの製造方法
JP6683292B2 (ja) 鋼板及び鋼板の製造方法
CN114585761A (zh) 高强度钢板及其制造方法
JP6683291B2 (ja) 鋼板及び鋼板の製造方法
JP2018003114A (ja) 高強度鋼板およびその製造方法
JP2018003115A (ja) 高強度鋼板およびその製造方法

Legal Events

Date Code Title Description
TRDD Decision of grant or rejection written
A01 Written decision to grant a patent or to grant a registration (utility model)

Free format text: JAPANESE INTERMEDIATE CODE: A01

Effective date: 20140218

A61 First payment of annual fees (during grant procedure)

Free format text: JAPANESE INTERMEDIATE CODE: A61

Effective date: 20140303

R151 Written notification of patent or utility model registration

Ref document number: 5505574

Country of ref document: JP

Free format text: JAPANESE INTERMEDIATE CODE: R151

S533 Written request for registration of change of name

Free format text: JAPANESE INTERMEDIATE CODE: R313533

R350 Written notification of registration of transfer

Free format text: JAPANESE INTERMEDIATE CODE: R350