JP5446247B2 - アミン誘導体及びその用途 - Google Patents
アミン誘導体及びその用途 Download PDFInfo
- Publication number
- JP5446247B2 JP5446247B2 JP2008328496A JP2008328496A JP5446247B2 JP 5446247 B2 JP5446247 B2 JP 5446247B2 JP 2008328496 A JP2008328496 A JP 2008328496A JP 2008328496 A JP2008328496 A JP 2008328496A JP 5446247 B2 JP5446247 B2 JP 5446247B2
- Authority
- JP
- Japan
- Prior art keywords
- group
- carbon atoms
- substituted
- carbazole
- phenyl
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は、カルバゾール基並びにベンゾフルオレン基が置換した新規なアミン誘導体、並びにその誘導体を利用した有機エレクトロルミネッセンス（ＥＬ）素子に関するものである。本発明における新規なベンゾフルオレン誘導体は、感光材料、有機光導電材料として使用でき、具体的には、平面光源や表示に使用される有機ＥＬ素子若しくは電子写真感光体等の正孔輸送材料、正孔注入材料及び発光材料として有用である。
有機ＥＬ素子は、次世代の薄型平面ディスプレイとして現在盛んに研究されており、一部では携帯電話のサブディスプレイ等への実用化も始まっている。一般に有機ＥＬ素子は、陽極と陰極との間に、正孔輸送材料、発光材料及び電子輸送材料を積層させた構造であるが、現在では上述した低消費電力化、さらには長寿命化を達成させるため、正孔注入材料を陽極と正孔輸送材料との間に、電子注入材料を陰極と電子輸送材料との間に挿入した構造が主流となっている。
正孔輸送材料としては、例えば、４，４’−ビス［Ｎ−（１−ナフチル）−Ｎ−フェニルアミノ］ビフェニル（α−ＮＰＤ）、Ｎ，Ｎ，Ｎ’，Ｎ’−テトラ（（１，１’−ビフェニル）−４−イル）ベンジジン（ＴＢＤＢ）等のジアミン構造を有するトリアリールアミン誘導体が報告されているが、近年では、さらに有機ＥＬ素子の高効率化と長寿命化のための新しい材料開発が求められている。
例えば、高効率化と長寿命化を達成する目的で、正孔輸送材料として、カルバゾール基のモノ置換誘導体（例えば、特許文献１〜４参照）、カルバゾール基のジ置換誘導体（例えば、特許文献５〜６参照）、フルオレニル基が置換したカルバゾール基のモノ置換誘導体（例えば、特許文献７参照）がそれぞれ報告されている。
また、特許文献７には、以下に示す化合物（６０）のような化合物は例示されているが、正孔輸送材料としての具体的な例示はなく、また、明細書中には、本発明のベンゾフルオレニル基を有するカルバゾール誘導体を示す記載はない。
本発明の目的は、従来材料以上に高い効率と高い耐久性を有するカルバゾール系正孔輸送材料を提供することにある。さらに詳しくは、有機ＥＬ素子等の正孔注入材料、正孔輸送材料及び発光材料に適したカルバゾール基が置換した新規アミン誘導体を提供することにある。
本発明者らは鋭意検討した結果、一般式（１）で表される特定のアミン誘導体が、効率及び長寿命化の面で、従来報告されているカルバゾール誘導体よりも非常に優れていることを見出し、本発明を完成させるに至った。即ち本発明は、一般式（１）で表されるカルバゾール基が置換したアミン誘導体及びその用途に関するものである。
（式中、Ｒ１〜Ｒ５はそれぞれ同一または異なっていても良く、水素原子、炭素数１〜１８の直鎖、分岐若しくは環状のアルキル基、炭素数１〜１８の直鎖、分岐若しくは環状のアルコキシ基、炭素数６〜４０の置換若しくは無置換のアリール基、または炭素数５〜４０の置換若しくは無置換のヘテロアリール基を表す。尚、Ｒ１とＲ２は互いに結合して環を形成しても良い。Ａｒ１，Ａｒ２はそれぞれ同一または異なっていても良く、炭素数６〜４０の置換若しくは無置換のアリール基、または炭素数５〜４０の置換若しくは無置換のヘテロアリール基を表す。）
以下、本発明を詳細に説明する。
以下、本発明を詳細に説明する。
本発明の一般式（１）で表されるベンゾフルオレン基を有するアミン誘導体は新規化合物であり、一般式（１）において、Ａｒ１及びＡｒ２は各々独立して炭素数６〜４０の置換若しくは無置換のアリール基、または炭素数５〜４０の置換若しくは無置換のヘテロアリール基を示す。
炭素数６〜４０の置換若しくは無置換のアリール基としては、具体的には、フェニル基、１−ナフチル基、２−ナフチル基、２−アントリル基、９−アントリル基、２−フルオレニル基、フェナントリル基、ピレニル基、クリセニル基、ペリレニル基、ピセニル基、４−メチルフェニル基、３−メチルフェニル基、２−メチルフェニル基、４−エチルフェニル基、３−エチルフェニル基、２−エチルフェニル基、４−ｎ−プロピルフェニル基、４−イソプロピルフェニル基、２−イソプロピルフェニル基、４−ｎ−ブチルフェニル基、４−イソブチルフェニル基、４−ｓｅｃ−ブチルフェニル基、２−ｓｅｃ−ブチルフェニル基、４−ｔｅｒｔ−ブチルフェニル基、３−ｔｅｒｔ−ブチルフェニル基、２−ｔｅｒｔ−ブチルフェニル基、４−ｎ−ペンチルフェニル基、４−イソペンチルフェニル基、２−ネオペンチルフェニル基、４−ｔｅｒｔ−ペンチルフェニル基、４−ｎ−ヘキシルフェニル基、４−（２’−エチルブチル）フェニル基、４−ｎ−ヘプチルフェニル基、４−ｎ−オクチルフェニル基、４−（２’−エチルヘキシル）フェニル基、４−ｔｅｒｔ−オクチルフェニル基、４−ｎ−デシルフェニル基、４−ｎ−ドデシルフェニル基、４−ｎ−テトラデシルフェニル基、４−シクロペンチルフェニル基、４−シクロヘキシルフェニル基、４−（４’−メチルシクロヘキシル）フェニル基、４−（４’−ｔｅｒｔ−ブチルシクロヘキシル）フェニル基、３−シクロヘキシルフェニル基、２−シクロヘキシルフェニル基、４−エチル−１−ナフチル基、６−ｎ−ブチル−２−ナフチル基、２，４−ジメチルフェニル基、２，５−ジメチルフェニル基、３，４−ジメチルフェニル基、３，５−ジメチルフェニル基、２，６−ジメチルフェニル基、２，４−ジエチルフェニル基、２，３，５−トリメチルフェニル基、２，３，６−トリメチルフェニル基、３，４，５−トリメチルフェニル基、２，６−ジエチルフェニル基、２，５−ジイソプロピルフェニル基、２，６−ジイソブチルフェニル基、２，４−ジ−ｔｅｒｔ−ブチルフェニル基、２，５−ジ−ｔｅｒｔ−ブチルフェニル基、４，６−ジ−ｔｅｒｔ−ブチル−２−メチルフェニル基、５−ｔｅｒｔ−ブチル−２−メチルフェニル基、４−ｔｅｒｔ−ブチル−２，６−ジメチルフェニル基、９−メチル−２−フルオレニル基、９−エチル−２−フルオレニル基、９−ｎ−ヘキシル−２−フルオレニル基、９，９−ジメチル−２−フルオレニル基、９，９−ジエチル−２−フルオレニル基、９，９−ジ−ｎ−プロピル−２−フルオレニル基、４−メトキシフェニル基、３−メトキシフェニル基、２−メトキシフェニル基、４−エトキシフェニル基、３−エトキシフェニル基、２−エトキシフェニル基、４−ｎ−プロポキシフェニル基、３−ｎ−プロポキシフェニル基、４−イソプロポキシフェニル基、２−イソプロポキシフェニル基、４−ｎ−ブトキシフェニル基、４−イソブトキシフェニル基、２−ｓｅｃ−ブトキシフェニル基、４−ｎ−ペンチルオキシフェニル基、４−イソペンチルオキシフェニル基、２−イソペンチルオキシフェニル基、４−ネオペンチルオキシフェニル基、２−ネオペンチルオキシフェニル基、４−ｎ−ヘキシルオキシフェニル基、２−（２’−エチルブチル）オキシフェニル基、４−ｎ−オクチルオキシフェニル基、４−ｎ−デシルオキシフェニル基、４−ｎ−ドデシルオキシフェニル基、４−ｎ−テトラデシルオキシフェニル基、４−シクロヘキシルオキシフェニル基、２−シクロヘキシルオキシフェニル基、２−メトキシ−１−ナフチル基、４−メトキシ−１−ナフチル基、４−ｎ−ブトキシ−１−ナフチル基、５−エトキシ−１−ナフチル基、６−メトキシ−２−ナフチル基、６−エトキシ−２−ナフチル基、６−ｎ−ブトキシ−２−ナフチル基、６−ｎ−ヘキシルオキシ−２−ナフチル基、７−メトキシ−２−ナフチル基、７−ｎ−ブトキシ−２−ナフチル基、２−メチル−４−メトキシフェニル基、２−メチル−５−メトキシフェニル基、３−メチル−４−メトキシフェニル基、３−メチル−５−メトキシフェニル基、３−エチル−５−メトキシフェニル基、２−メトキシ−４−メチルフェニル基、３−メトキシ−４−メチルフェニル基、２，４−ジメトキシフェニル基、２，５−ジメトキシフェニル基、２，６−ジメトキシフェニル基、３，４−ジメトキシフェニル基、３，５−ジメトキシフェニル基、３，５−ジエトキシフェニル基、３，５−ジ−ｎ−ブトキシフェニル基、２−メトキシ−４−エトキシフェニル基、２−メトキシ−６−エトキシフェニル基、３，４，５−トリメトキシフェニル基、４−ビフェニリル基、３−ビフェニリル基、２−ビフェニリル基、４−（４’−メチルフェニル）フェニル基、４−（３’−メチルフェニル）フェニル基、４−（４’−メトキシフェニル）フェニル基、４−（４’−ｎ−ブトキシフェニル）フェニル基、２−（２’−メトキシフェニル）フェニル基、４−（４’−クロロフェニル）フェニル基、３−メチル−４−フェニルフェニル基、３−メトキシ−４−フェニルフェニル基、ターフェニル基、３，５−ジフェニルフェニル基、１０−フェニルアントリル基、１０−（３，５−ジフェニルフェニル）−９−アントリル基、９−フェニル−２−フルオレニル基、４−フルオロフェニル基、３−フルオロフェニル基、２−フルオロフェニル基、４−クロロフェニル基、３−クロロフェニル基、２−クロロフェニル基、４−ブロモフェニル基、２−ブロモフェニル基、４−クロロ−１−ナフチル基、４−クロロ−２−ナフチル基、６−ブロモ−２−ナフチル基、２，３−ジフルオロフェニル基、２，４−ジフルオロフェニル基、２，５−ジフルオロフェニル基、２，６−ジフルオロフェニル基、３，４−ジフルオロフェニル基、３，５−ジフルオロフェニル基、２，３−ジクロロフェニル基、２，４−ジクロロフェニル基、２，５−ジクロロフェニル基、３，４−ジクロロフェニル基、３，５−ジクロロフェニル基、２，５−ジブロモフェニル基、２，４，６−トリクロロフェニル基、２，４−ジクロロ−１−ナフチル基、１，６−ジクロロ−２−ナフチル基、２−フルオロ−４−メチルフェニル基、２−フルオロ−５−メチルフェニル基、３−フルオロ−２−メチルフェニル基、３−フルオロ−４−メチルフェニル基、２−メチル−４−フルオロフェニル基、２−メチル−５−フルオロフェニル基、３−メチル−４−フルオロフェニル基、２−クロロ−４−メチルフェニル基、２−クロロ−５−メチルフェニル基、２−クロロ−６−メチルフェニル基、２−メチル−３−クロロフェニル基、２−メチル−４−クロロフェニル基、３−クロロ−４−メチルフェニル基、３−メチル−４−クロロフェニル基、２−クロロ−４，６−ジメチルフェニル基、２−メトキシ−４−フルオロフェニル基、２−フルオロ−４−メトキシフェニル基、２−フルオロ−４−エトキシフェニル基、２−フルオロ−６−メトキシフェニル基、３−フルオロ−４−エトキシフェニル基、３−クロロ−４−メトキシフェニル基、２−メトキシ−５−クロロフェニル基、３−メトキシ−６−クロロフェニル基、５−クロロ−２，４−ジメトキシフェニル基などを挙げることができるが、これらに限定されるものではない。
また、炭素数５〜４０の置換若しくは無置換のヘテロアリール基としては、酸素原子、窒素原子及び硫黄原子から選ばれる少なくとも一つのヘテロ原子を含有する芳香環基であり、例えば、４−キノリル基、４−ピリジル基、３−ピリジル基、２−ピリジル基、３−フリル基、２−フリル基、３−チエニル基、２−チエニル基、２−オキサゾリル基、２−チアゾリル基、２−ベンゾオキサゾリル基、２−ベンゾチアゾリル基、２−ベンゾイミダゾリル基等の複素環基を挙げることができるが、これらに限定されるものではない。
さらに、これらアリール基若しくはヘテロアリール基については、芳香環基が結合して縮合環を形成しても良い。
上記一般式（１）で表されるアミン誘導体中のＲ１〜Ｒ５は、各々独立して、水素原子、炭素数１〜１８の直鎖、分岐若しくは環状のアルキル基、炭素数１〜１８の直鎖、分岐若しくは環状のアルコキシ基、または置換若しくは無置換のフェニル基を表す。尚、Ｒ１とＲ２は互いに結合して環を形成しても良い。
炭素数１〜１８の直鎖、分岐若しくは環状のアルキル基としては、具体的には、メチル基、エチル基、プロピル基、イソプロピル基、ブチル基、ｓｅｃ−ブチル基、ｔｅｒｔ−ブチル基、ペンチル基、ヘキシル基、ヘプチル基、オクチル基、ステアリル基、トリクロロメチル基、トリフルオロメチル基、シクロプロピル基、シクロヘキシル基、１，３−シクロヘキサジエニル基、２−シクロペンテン−１−イル基等を挙げることができる。
炭素数１〜１８の直鎖、分岐若しくは環状のアルコキシ基としては、具体的には、メトキシ基、エトキシ基、プロポキシ基、イソプロポキシ基、ｎ−ブトキシ基、ｓｅｃ−ブトキシ基、ｔｅｒｔ−ブトキシ基、ペンチルオキシ基、ヘキシルオキシ基、ステアリルオキシ基、トリフルオロメトキシ基等を挙げることができる。
また、炭素数６〜４０の置換若しくは無置換のアリール基、または炭素数５〜４０の置換若しくは無置換のヘテロアリール基としては、前述したＡｒ１及びＡｒ２と同じ置換基を挙げることができる。さらに、これらアリール基若しくはヘテロアリール基については、芳香環基が結合して縮合環を形成しても良い。
以下に好ましい化合物を例示するが、これらの化合物に限定されるものではない。
本発明の一般式（１）で表されるアミン誘導体は、例えば、公知の方法によって合成することができる（例えば、非特許文献１参照）。
Ｔｅｔｒａｈｅｄｒｏｎ Ｌｅｔｔｅｒｓ（テトラヘドロンレターズ），１９９８年，第３９巻，２３６７頁（アミノ化反応） より詳細な合成方法としては、例えば、下式に示すような公知の方法で合成することができる。即ち、カルバゾール誘導体とハロゲン化アリールとのアミノ化反応によって、Ｎ−アリール置換カルバゾール誘導体を得、続いて、このカルバゾール誘導体を、ベンゾフルオレン基及びアリール基を有する２級アミンとアミノ化反応させる方法が例示される。尚、Ｎ−アリール置換カルバゾール誘導体と２級アミンとをアミノ化反応させる際に、Ｎ−アリール置換カルバゾール誘導体の骨格中に適当な反応部位がない場合、別途、ハロゲン化等の手法を用いて、Ｎ−アリール置換カルバゾール誘導体中にハロゲン原子等の適当な反応部位を導入しても良い。合成したアミン誘導体は、クロマトグラフィー、再結晶及び昇華精製等の精製操作を行うことによって、純度９９．９％以上で得ることができる。
本発明のアミン誘導体は、有機ＥＬ素子の正孔注入材料、正孔輸送材料または発光層のホスト材料として利用可能であるが、特に正孔輸送材料として使用した際に、従来の材料以上に駆動電圧の改善と高い電力効率が期待できる。さらに、本発明のアミン誘導体は、量産化技術が先行している蛍光発光素子のみならず、将来技術として注目されている燐光発光素子に対しても有用となることが期待される。また、本発明のアミン誘導体は、カルバゾール基を部分構造に持ちながらも、ベンゾフルオレニル基の１１位に結合した置換基により、材料自身の結晶化が抑制されることから、有機ＥＬ素子の耐久性向上も期待できる。
従って、有機ＥＬ素子若しくは電子写真感光体等の正孔注入材料、正孔輸送材料または発光材料としてのみならず、光電変換素子、太陽電池、イメージセンサー等の有機光導電材料への分野にも応用可能である。
本発明による一般式（１）で表されるアミン誘導体は、従来の材料以上に低電圧駆動と高い電力効率を示し、さらに高いガラス転移温度を有するため、有機ＥＬ素子の耐久性向上、寿命の改善が期待できる。そのため、有機ＥＬ素子若しくは電子写真感光体等の正孔注入材料、正孔輸送材料または発光材料として利用できる。
以下、本発明を実施例に基づき、さらに詳細に説明するが、本発明はこれら実施例に何ら限定されるものではない。
なお、本実施例で用いた分析機器及び測定方法を以下に列記する。
［元素分析］
元素分析計：パーキンエルマー全自動元素分析装置 ２４００ＩＩ
酸素フラスコ燃焼−ＩＣ測定法：東ソー製 イオンクロマトグラフ ＩＣ−２００１
［質量分析］
質量分析装置：日立製作所製 Ｍ−８０Ｂ
測定方法：ＦＤ−ＭＳ分析
［ガラス転移温度測定］
測定装置：マックサイエンス製 ＤＳＣ−３１００
測定方法：標準試料＝Ａｌ２Ｏ３ ５．０ｍｇ、昇温速度＝１０℃／分（窒素雰囲気）
［ＨＰＬＣ分析］
測定装置：東ソー製 マルチステーションＬＣ−８０２０
測定方法：カラム Ｉｎｅｒｔｓｉｌ ＯＤＳ−３Ｖ（４．６ｍｍΦ×２５０ｍｍ）
検出器 ＵＶ検出（波長 ２５４ｎｍ）
溶離液 メタノール／テトラヒドロフラン＝９／１（ｖ／ｖ比）
［有機ＥＬ素子の駆動電圧及び発光輝度測定］
測定装置：ＴＯＰＣＯＮ製 輝度計ＬＵＭＩＮＡＮＣＥ ＭＥＴＥＲ（ＢＭ−９）
合成例１ Ｎ−（４−ビフェニリル）カルバゾールの合成
元素分析計：パーキンエルマー全自動元素分析装置 ２４００ＩＩ
酸素フラスコ燃焼−ＩＣ測定法：東ソー製 イオンクロマトグラフ ＩＣ−２００１
［質量分析］
質量分析装置：日立製作所製 Ｍ−８０Ｂ
測定方法：ＦＤ−ＭＳ分析
［ガラス転移温度測定］
測定装置：マックサイエンス製 ＤＳＣ−３１００
測定方法：標準試料＝Ａｌ２Ｏ３ ５．０ｍｇ、昇温速度＝１０℃／分（窒素雰囲気）
［ＨＰＬＣ分析］
測定装置：東ソー製 マルチステーションＬＣ−８０２０
測定方法：カラム Ｉｎｅｒｔｓｉｌ ＯＤＳ−３Ｖ（４．６ｍｍΦ×２５０ｍｍ）
検出器 ＵＶ検出（波長 ２５４ｎｍ）
溶離液 メタノール／テトラヒドロフラン＝９／１（ｖ／ｖ比）
［有機ＥＬ素子の駆動電圧及び発光輝度測定］
測定装置：ＴＯＰＣＯＮ製 輝度計ＬＵＭＩＮＡＮＣＥ ＭＥＴＥＲ（ＢＭ−９）
合成例１ Ｎ−（４−ビフェニリル）カルバゾールの合成
窒素雰囲気下、攪拌装置を備えた１Ｌフラスコ中に、カルバゾール［関東化学品］ ４０．１ｇ（０．２５ｍｏｌ）、４−ブロモビフェニル［キシダ化学品］ ２８．０ｇ（０．１２ｍｏｌ）、炭酸カリウム［和光純薬品］ ３３．２ｇ（０．２４ｍｏｌ）、パラジウム（０）ビス（ジベンジリデンアセトン）［アルドリッチ品］ １．１ｇ（１．２ｍｍｏｌ）、トリ−ｔ−ブチルホスフィン［アルドリッチ品］ １．５ｇ（７．２ｍｍｏｌ）、ｏ−キシレン［キシダ化学品］ ７００．０ｇを加え、１３０℃で１６時間攪拌した。反応終了後、蒸留水 ５０ｍＬを添加し、室温にて０．５時間攪拌して静置した後、水層を分離した。さらに、飽和塩化ナトリウム水溶液で洗浄分液した後、減圧濃縮に付してｏ−キシレン溶媒を留去した。さらに、得られた残渣をシリカゲルカラムクロマトグラフィーに付し、淡黄色固体２０．３ｇを得た（収率 ５３％、純度 ９７．０％）。質量分析の結果より、得られた白色固体は目的のＮ−（４−ビフェニリル）カルバゾールであることを確認した。
質量分析（ＦＤＭＳ）：３１９（Ｍ＋）
合成例２ ３−ブロモ−Ｎ−（４−ビフェニリル）カルバゾールの合成
合成例２ ３−ブロモ−Ｎ−（４−ビフェニリル）カルバゾールの合成
窒素雰囲気下、攪拌装置を備えた１Ｌフラスコ中に、合成例１で合成したＮ−（４−ビフェニリル）カルバゾール １５．０ｇ（４７．０ｍｍｏｌ）、ジクロロメタン［和光純薬品］ ５００．０ｇを仕込んだ溶液中に、Ｎ−ブロモコハク酸イミド［東京化成品］ ７．９ｇ（４５ｍｍｏｌ）をジクロロメタン ３００．０ｇに溶解させた液を室温で３時間かけて滴下し、さらに室温で２時間熟成させた。反応終了後、蒸留水 ２００ｍＬを添加し、室温にて０．５時間攪拌して静置した後、水層を分離した。さらに、飽和塩化ナトリウム水溶液で洗浄分液した後、減圧濃縮に付してジクロロメタン溶媒を留去した。さらに、得られた残渣をシリカゲルカラムクロマログラフィーに付し、淡黄色固体１５．１ｇを得た（収率 ４５％、純度 ９６．５％）。質量分析の結果より、得られた白色固体は目的の３−ブロモ−Ｎ−（４−ビフェニリル）カルバゾールであることを確認した。
質量分析（ＦＤＭＳ）：３９８（Ｍ＋）
合成例３ Ｎ−フェニル−９−アミノ−１１，１１−ジメチル−１１Ｈ−ベンゾ［ａ］フルオレンの合成
合成例３ Ｎ−フェニル−９−アミノ−１１，１１−ジメチル−１１Ｈ−ベンゾ［ａ］フルオレンの合成
窒素雰囲気下、攪拌装置を備えた３００ｍＬフラスコ中に、９−クロロ−１１，１１−ジメチル−１１Ｈ−ベンゾ［ａ］フルオレン［国際公開２００７／１１９８００号パンフレットの方法に従って合成］ ２７．９ｇ（０．１０ｍｏｌ）、アニリン［和光純薬品］ ４６．５ｇ（０．５０ｍｏｌ）、ナトリウム−ｔ−ブトキシド［キシダ化学品］ １４．４ｇ（０．１５ｍｏｌ）、酢酸パラジウム［キシダ化学品］ ２２５ｍｇ（１．０ｍｍｏｌ）、トリ−ｔ−ブチルホスフィン［アルドリッチ品］ ０．８ｇ（４．０ｍｍｏｌ）、ｏ−キシレン［キシダ化学品］ １００．０ｇを加え、１３０℃で３時間攪拌した。反応終了後、蒸留水 ３０ｍＬを添加し、室温にて０．５時間攪拌して静置した後、水層を分離した。さらに、飽和塩化ナトリウム水溶液で洗浄分液した後、減圧濃縮に付してｏ−キシレン溶媒を留去した。さらに、得られた残渣をシリカゲルカラムクロマログラフィーに付し、白色固体２７．５ｇを得た（収率 ８２％、純度 ９９．８％）。質量分析及び元素分析の結果より、得られた白色固体は目的のＮ−フェニル−９−アミノ−１１，１１−ジメチル−１１Ｈ−ベンゾ［ａ］フルオレンであることを確認した。
質量分析（ＦＤＭＳ）：３３５（Ｍ＋）
元素分析（計算値）：Ｃ＝８９．５， Ｈ＝６．３， Ｎ＝４．２
元素分析（実測値）：Ｃ＝８９．３， Ｈ＝６．４， Ｎ＝４．３
実施例１ 化合物Ａ３の合成
元素分析（計算値）：Ｃ＝８９．５， Ｈ＝６．３， Ｎ＝４．２
元素分析（実測値）：Ｃ＝８９．３， Ｈ＝６．４， Ｎ＝４．３
実施例１ 化合物Ａ３の合成
窒素雰囲気下、攪拌装置を備えた３００ｍＬフラスコ中に、合成例２で合成した３−ブロモ−Ｎ−（４−ビフェニリル）カルバゾール ７．０ｇ（１７．８ｍｍｏｌ）、合成例３で合成したＮ−フェニル−９−アミノ−１１，１１−ジメチル−１１Ｈ−ベンゾ［ａ］フルオレン ６．５ｇ（２０．０ｍｍｏｌ）、ナトリウム−ｔ−ブトキシド［キシダ化学品］ ２．４ｇ（２５．０ｍｍｏｌ）、酢酸パラジウム［キシダ化学品］ １９ｍｇ（０．０９ｍｍｏｌ）、トリ−ｔ−ブチルホスフィン［アルドリッチ品］ ６２ｍｇ（０．３１ｍｍｏｌ）、ｏ−キシレン［キシダ化学品］ １５０．０ｇを加え、１３０℃で６時間攪拌した。反応終了後、蒸留水 ８０ｍＬを添加し、室温にて０．５時間攪拌して静置した後、水層を分離した。さらに、飽和塩化ナトリウム水溶液で洗浄分液した後、減圧濃縮に付してｏ−キシレン溶媒を留去した。さらに、得られた残渣をシリカゲルカラムクロマログラフィーに付し、白色固体６．０ｇを得た（収率 ５０％、純度 ９９．７％）。質量分析及び元素分析の結果より、得られた白色固体は目的の化合物Ａ３であることを確認した。
質量分析（ＦＤＭＳ）：６５２（Ｍ＋）
元素分析（計算値）：Ｃ＝９０．２， Ｈ＝５．６， Ｎ＝４．２
元素分析（実測値）：Ｃ＝９０．２， Ｈ＝５．８， Ｎ＝４．０
ガラス転移温度：１３９℃
実施例２ 有機ＥＬ素子の作製
厚さ１３０ｎｍのＩＴＯ透明電極を有するガラス基板をアセトン、イソプロピルアルコールで順次超音波洗浄し、次いでイソプロピルアルコールで煮沸洗浄した後、乾燥した。さらに、本基板をＵＶ／オゾン処理したものを透明導電性支持基板として使用した。本ＩＴＯ透明電極上に、銅フタロシアニンを真空蒸着法により２５ｎｍの膜厚で成膜し、正孔注入層を形成した。次に、実施例１で合成した化合物Ａ３を真空蒸着法により４５ｎｍの膜厚で成膜し、正孔輸送層を形成した。次に、アルミニウムトリスキノリノール錯体を真空蒸着法により６０ｎｍの膜厚で成膜し、発光層兼電子輸送層を形成した。次に、陰極としてＬｉＦを０．５ｎｍ、Ａｌを１００ｎｍ成膜して金属電極を形成した。さらに、窒素雰囲気下、保護用ガラス基板を重ね、ＵＶ硬化樹脂で封止した。このようにして得られた素子に、ＩＴＯ電極を正極、ＬｉＦ−Ａｌ電極を負極にして、２０ｍＡ／ｃｍ２の定電流密度条件下で駆動させた際の輝度、駆動電圧、電流効率及び電力効率を測定した。結果を表１に示す。
元素分析（計算値）：Ｃ＝９０．２， Ｈ＝５．６， Ｎ＝４．２
元素分析（実測値）：Ｃ＝９０．２， Ｈ＝５．８， Ｎ＝４．０
ガラス転移温度：１３９℃
実施例２ 有機ＥＬ素子の作製
厚さ１３０ｎｍのＩＴＯ透明電極を有するガラス基板をアセトン、イソプロピルアルコールで順次超音波洗浄し、次いでイソプロピルアルコールで煮沸洗浄した後、乾燥した。さらに、本基板をＵＶ／オゾン処理したものを透明導電性支持基板として使用した。本ＩＴＯ透明電極上に、銅フタロシアニンを真空蒸着法により２５ｎｍの膜厚で成膜し、正孔注入層を形成した。次に、実施例１で合成した化合物Ａ３を真空蒸着法により４５ｎｍの膜厚で成膜し、正孔輸送層を形成した。次に、アルミニウムトリスキノリノール錯体を真空蒸着法により６０ｎｍの膜厚で成膜し、発光層兼電子輸送層を形成した。次に、陰極としてＬｉＦを０．５ｎｍ、Ａｌを１００ｎｍ成膜して金属電極を形成した。さらに、窒素雰囲気下、保護用ガラス基板を重ね、ＵＶ硬化樹脂で封止した。このようにして得られた素子に、ＩＴＯ電極を正極、ＬｉＦ−Ａｌ電極を負極にして、２０ｍＡ／ｃｍ２の定電流密度条件下で駆動させた際の輝度、駆動電圧、電流効率及び電力効率を測定した。結果を表１に示す。
比較例１〜３ 有機ＥＬ素子の作製
正孔輸送層として、実施例１で合成した化合物Ａ３の代わりに、以下に示した比較化合物１〜３（それぞれ、特許文献５に記載の化合物（７）、特許文献１に記載の化合物Ａ６及びＡ３９）を用いた以外は、実施例２に準じて同様に有機ＥＬ素子を作製した。２０ｍＡ／ｃｍ２の定電流密度条件下で駆動させた際の輝度、駆動電圧、電流効率及び電力効率を測定した結果を、併せて表１に示す。
正孔輸送層として、実施例１で合成した化合物Ａ３の代わりに、以下に示した比較化合物１〜３（それぞれ、特許文献５に記載の化合物（７）、特許文献１に記載の化合物Ａ６及びＡ３９）を用いた以外は、実施例２に準じて同様に有機ＥＬ素子を作製した。２０ｍＡ／ｃｍ２の定電流密度条件下で駆動させた際の輝度、駆動電圧、電流効率及び電力効率を測定した結果を、併せて表１に示す。
Claims (2)
- 一般式（１）で表されるアミン誘導体。
- 請求項１に記載のアミン誘導体を、発光層、正孔輸送層または正孔注入層のいずれかに用いることを特徴とする有機エレクトロルミネッセンス素子。