JP4337596B2 - ガスバリア性積層体 - Google Patents
ガスバリア性積層体 Download PDFInfo
- Publication number
- JP4337596B2 JP4337596B2 JP2004090039A JP2004090039A JP4337596B2 JP 4337596 B2 JP4337596 B2 JP 4337596B2 JP 2004090039 A JP2004090039 A JP 2004090039A JP 2004090039 A JP2004090039 A JP 2004090039A JP 4337596 B2 JP4337596 B2 JP 4337596B2
- Authority
- JP
- Japan
- Prior art keywords
- gas barrier
- layer
- barrier laminate
- resin
- film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
ASTM−D3985に準処して、酸素透過率測定装置(モダンコントロール社製「OX−TRAN100」)を使用し、温度25℃、相対湿度80%の条件下で測定した。評価基準を以下に示す。
プラスチック基材/表面改質層/無機薄膜/塗工層/印刷層/接着剤層/他のプラスチックフィルムの積層体から成り、幅15mm、長さ100mmの短冊状フィルムであって、積層体の調製時(ラミネート時)に、長さ方向の1/2の部分(すなわち、幅15mm、長さ50mmの部分)に離型紙から成るスペーサーを介在させて接着剤層の不存在領域を形成して成る短冊状フィルムを試料フィルムとして使用した。そして、接着剤層の不存在領域側から、プラスチック基材/表面改質層/無機薄膜/塗工層/印刷層側(A側)と他のプラスチックフィルム側(B側)とから剥離するT型剥離試験を行った。すなわち、23℃50%RHの環境下、オートグラフ(JIS K 7127に準じる試験装置、島津製作所社製「DSS−100」)の固定掴み具と可動掴み具とに上記のA側とB側の夫々の端部を掴み、掴み具間距離60mmで取り付け、引っ張り速度300mm/minで可動掴み具を30mm移動させ、この間に歪み計に記録させた引張荷重の波状曲線から中心線の値を求め、試験片3本における平均値を求めた。評価基準を以下に示す。
印刷インキとしてグラビアインキを使用し、印刷機として富士機械工業社製「FE−185」を使用し、印刷速度100m/分で、黒、藍、赤、黄色、白の5色から成る印刷模様(網点)を塗工層に形成し、印刷模様の網点の濃度再現性を見て階調印刷性を評価した。なお、評価基準としてポリエチレンテレフタレート(PET)フィルムへの印刷模様を使用した。評価基準を以下に示す。
アクリル酸エチル40重量部、メタクリル酸メチル30重量部、メタクリル酸20重量部およびグリシジルメタクリレート10重量部から成る混合モノマーをエタノール中で溶液重合した。重合後水を添加しつつ加熱し、エタノールを除去した。アンモニア水でpH7.5に調節し、水性アクリル系樹脂塗料を得た。
テレフタル酸664重量部、イソフタル酸631重量部、1,4−ブタンジオール472重量部およびネオペンチルグリコール447重量部を原料とし、ポリエステルポリオールを得た。得られたポリエステルポリオールに、アジピン酸321重量部、ジメチロールプロピオン酸268重量部を添加し、ペンダントカルボキシル基含有ポリエステルポリオールAを得た。得られたポリエステルポリオールA1880重量部にヘキサメチレンジイソシアネート160重量部を添加し、水性ポリウレタン系樹脂水性塗料を得た。
ポリエチレンテレフタレート(PET、溶融粘度=0.65)を290℃の温度でTダイより押出し、冷却ドラムで急冷し、厚さ150μmの未延伸PETシートを得た。得られたPETシートを95℃で3.5倍縦方向に延伸した後、オキサゾリン基含有ポリマー(日本触媒社製「エポクロスWS−500」)60重量%、アンカーコート層用樹脂A(水性アクリル樹脂)20重量%、アンカーコート層用樹脂B(水性ポリウレタン樹脂)20重量%から成る混合樹脂の水溶液をインラインコーティング法により塗布し、110℃で3.5倍横方向に延伸し、230℃で熱処理し、上記混合樹脂から成る厚さ0.1μmのアンカーコート層を有する厚さ12.1μmの二軸延伸PETフィルムを得た。
再生ナイロン6を50重量%含有するナイロン6(三菱化学社製「ノバミッド 1020」、相対粘度=3.5)を230℃の温度でTダイより押出し、冷却ドラムで急冷し、厚さ144μmの未延伸ナイロンシートを得た。得られたナイロンシートを60℃で3倍縦方向に延伸した後、オキサゾリン基含有ポリマー(日本触媒社製「エポクロスWS−500」)60重量%、アンカーコート層用樹脂A(水性アクリル樹脂)20重量%、アンカーコート層用樹脂B(水性ポリウレタン樹脂)20重量%から成る混合樹脂の水溶液をインラインコーティング法により塗布し、90℃で3倍横方向に延伸し、205℃で熱処理し、フイルム厚16μmの2軸延伸ナイロンフイルムを得た。
酸化ケイ素蒸着PETフィルムの酸化ケイ素薄膜上に、塗工剤を塗工した後、100℃で60秒乾燥し、0.5μmの塗工層を形成した。塗工剤は、ガラス転移点57℃、分子量3000、酸価42mgKOH/gのポリエステル樹脂10重量部、ガラス転移点75℃、分子量8000、酸価20mgKOH/gのポリウレタン樹脂10重量部、シランカップリング剤としてγ−グリシドキシプロピルトリメトキシシラン1重量部、脂肪酸アミド系化合物としてステアリン酸アミド1重量部およびトルエン部39重量部、メチルエチルケトン(MEK)39重量部から成り、ポリイソシアネートとして日本ポリウレタン社製「コロネートL」を水酸基価当量の合計に対して1.2倍添加した。なお、以下の実施例および比較例において、ポリウレタン樹脂とポリエステル樹脂との合計は20重量部とした。得られた蒸着PETフィルムの酸素透過度は6fmol/m2/s/Paであった。
実施例1において、透明積層フィルムをエージング処理する代りに、オーブン中で150℃、30分の熱処理を行った以外は実施例1と同様の操作を行い、評価用フィルムを作成した。得られた評価用フィルムに対し、実施例1と同様の熱水処理後を施し、熱水処理前後の酸素透過度および密着強度を測定した。評価結果を表7に示す。
実施例1において、塗工剤を構成する樹脂の性質、配合量、添加剤を表3及び表4に示す様に変化させた以外は、実施例1と同様の操作を行って評価用フィルムを作成した。なお、実施例10にはシランカップリング剤、脂肪酸アミド系化合物およびポリイソシアネートを使用しなかった。得られた評価用フィルムに対し、実施例1と同様の熱水処理後を施し、熱水処理前後の酸素透過度および密着強度を測定した。評価結果を表7に示す。
酸化ケイ素蒸着ナイロンフィルムの酸化ケイ素薄膜上に、塗工剤を塗工した後、100℃で60秒乾燥し、0.5μmの塗工層を形成した。塗工剤は、ガラス転移点60℃、分子量8000、酸価23mgKOH/gのポリエステル樹脂10重量部、ガラス転移点82℃、分子量15000、酸価18mgKOH/gのポリウレタン樹脂10重量部、シランカップリング剤としてγ−グリシドキシプロピルトリメトキシシラン1重量部、脂肪酸アミド系化合物としてステアリン酸アミド1重量部およびトルエン部39重量部、メチルエチルケトン(MEK)39重量部から成り、ポリイソシアネートとして日本ポリウレタン社製「コロネートL」を水酸基価当量の合計に対して1.2倍添加した。得られた蒸着ナイロンフィルムの酸素透過度は9fmol/m2/s/Paであった。
実施例16において、塗工剤を構成する樹脂の性質、配合量、添加剤を表3及び表4に示す様に変化させた以外は、実施例16と同様の操作を行って評価用フィルムを作成した。得られた評価用フィルムに対し、実施例16と同様の熱水処理後を施し、熱水処理前後の酸素透過度および密着強度を測定した。評価結果を表7に示す。
酸化ケイ素蒸着PETフィルムの酸化ケイ素薄膜上に、塗工剤を塗工した後、100℃で60秒乾燥し、0.5μmの塗工層を形成した。塗工剤は、ガラス転移点60℃、分子量8000、酸価23mgKOH/gのポリエステル樹脂10重量部、ガラス転移点82℃、分子量15000、酸価18mgKOH/gのポリウレタン樹脂10重量部、シランカップリング剤としてγ−グリシドキシプロピルトリメトキシシラン1重量部、脂肪酸アミド系化合物としてステアリン酸アミド1重量部およびトルエン部39重量部、メチルエチルケトン(MEK)39重量部から成り、ポリイソシアネートとして日本ポリウレタン社製「コロネートL」を水酸基価当量の合計に対して1.2倍添加した。得られた蒸着PETフィルムの酸素透過度は9fmol/m2/s/Paであった。
実施例18において、塗工剤を構成する樹脂の性質、配合量、添加剤を表3及び表4に示す様に変化させた以外は、実施例18と同様の操作を行って評価用フィルムを作成した。得られた評価用フィルムに対し、実施例18と同様の熱水処理後を施し、熱水処理前後の酸素透過度および密着強度を測定した。評価結果を表7に示す。
実施例6において、酸化ケイ素蒸着PETフィルムの代りに酸化アルミニウム蒸着PETフィルムを使用した以外は、実施例6と同様の操作を行って評価用フィルムを作成した。得られた評価用フィルムに対し、実施例6と同様の熱水処理後を施し、熱水処理前後の酸素透過度および密着強度を測定した。評価結果を表7に示す。
実施例20において、塗工剤を構成する樹脂の性質、配合量、添加剤を表3及び表4に示す様に変化させた以外は、実施例20と同様の操作を行って評価用フィルムを作成した。得られた評価用フィルムに対し、実施例20と同様の熱水処理後を施し、熱水処理前後の酸素透過度および密着強度を測定した。評価結果を表1に示す。
実施例1において、塗工層を設けなかった以外は実施例1と同様の操作を行って評価用フィルムを作成した。得られた評価用フィルムに対し、実施例1と同様の熱水処理後を施し、熱水処理前後の酸素透過度および密着強度を測定した。評価結果を表8に示す。
実施例1において、塗工剤を構成する樹脂の性質、配合量、添加剤を表5及び表6に示す様に変化させた以外は、実施例1と同様の操作を行って評価用フィルムを作成した。得られた評価用フィルムに対し、実施例1と同様の熱水処理後を施し、熱水処理前後の酸素透過度および密着強度を測定した。評価結果を表8に示す。
実施例16において、塗工剤を構成する樹脂の性質、配合量、添加剤を表5及び表6に示す様に変化させた以外は、実施例16と同様の操作を行って評価用フィルムを作成した。得られた評価用フィルムに対し、実施例16と同様の熱水処理後を施し、熱水処理前後の酸素透過度および密着強度を測定した。評価結果を表8に示す
Claims (17)
- プラスチック基材(A)と、当該プラスチック基材(A)の少なくとも片面に形成された無機薄膜(B)と、当該無機薄膜(B)の表面に塗工剤を塗工して形成される塗工層(C)とから成るガスバリア性積層体であって、上記塗工剤が、分子量3000〜15000のポリエステル系樹脂(c1)と分子量8000〜30000のポリウレタン系樹脂(c2)とを重量比5/95〜95/5で含有し、ガスバリア性積層体の酸素透過度が25fmol/m2/s/Pa以下であることを特徴とするガスバリア性積層体。
- ポリエステル系樹脂(c1)及びポリウレタン系樹脂(c2)のガラス転移温度(Tg)がそれぞれ55〜100℃で、酸価がそれぞれ1〜100mgKOH/gである請求項1に記載のガスバリア性積層体。
- 塗工層(C)が、シランカップリング剤を0.1〜20重量%含有する請求項1又は2に記載のガスバリア性積層体。
- シランカップリング剤がエポキシ基含有シランカップリング剤および/またはアミノ基含有シランカップリング剤である請求項3に記載のガスバリア性積層体。
- 塗工剤が、ポリエステル系樹脂(c1)及びポリウレタン系樹脂(c2)の合計100重量部に対し、脂肪酸、脂肪酸エステル、脂肪酸アミド又はこれらの混合物を0.05〜20重量部含有する請求項1〜4の何れかに記載のガスバリア性積層体。
- 塗工剤が、ポリエステル系樹脂(c1)及びポリウレタン系樹脂(c2)の水酸基価当量の合計に対し、硬化剤として0.8〜1.5倍当量のポリイソシアネートを含有する請求項1〜5の何れかに記載のガスバリア性積層体。
- ポリイソシアネートが、1分子中に活性イソシアネート基を3個以上有する化合物を少なくとも1種含有する請求項6に記載のガスバリア性積層体。
- プラスチック基材(A)が、ポリエステル樹脂、ナイロン樹脂、ポリオレフィン樹脂、エチレン−ビニルアルコール共重合体樹脂または生分解性樹脂である請求項1に記載のガスバリア性積層体。
- 無機薄膜(B)が、酸化硅素、酸化アルミニウム、ダイアモンド状炭素またはこれらの混合物から成る物理蒸着膜または化学蒸着膜である請求項1〜8の何れかに記載のガスバリア性積層体。
- プラスチック基材(A)と無機薄膜(B)との間にアンカーコート層を有する請求項1〜9の何れかに記載のガスバリア性積層体。
- アンカーコート層が、ポリエステル系樹脂、ウレタン樹脂、アクリル系樹脂およびオキサゾリン基含有樹脂の群から選択される1種以上の樹脂にて形成される請求項10に記載のガスバリア性積層体。
- 塗工層(C)表面に印刷層を形成し、当該印刷層の表面にヒートシール層を積層した請求項1〜11の何れかに記載のガスバリア性積層体。
- 印刷層とヒートシール層との間に紙またはプラスチックフィルムを少なくとも1層以上積層した請求項12に記載のガスバリア性積層体。
- プラスチックフィルムがポリエステル系樹脂、ナイロン系樹脂、エチレン-酢酸ビニル共重合体樹脂またはこれらの混合物から成る請求項13記載のガスバリア性積層体。
- 請求項1〜14に記載のガスバリア性積層体に60℃以上の加熱処理を施した請求項1〜14の何れかに記載のガスバリア性積層体。
- 120℃で30分間の加圧熱水処理を行った場合、加圧熱水処理後の酸素透過度が25fmol/m2/s/Pa以下である請求項1〜15の何れかに記載のガスバリア性積層体。
- 120℃で30分間の加圧熱水処理を行った場合、無機薄膜層(B)と塗工層(C)との密着強度が100(g/15mm)以上であり、且つ塗工層(C)と印刷層との密着強度が100(g/15mm)以上である請求項12〜16記載のガスバリア性積層体。