JP4210255B2 - エチレンオキシド製造用銀触媒およびエチレンオキシドの製造方法 - Google Patents
エチレンオキシド製造用銀触媒およびエチレンオキシドの製造方法 Download PDFInfo
- Publication number
- JP4210255B2 JP4210255B2 JP2004330981A JP2004330981A JP4210255B2 JP 4210255 B2 JP4210255 B2 JP 4210255B2 JP 2004330981 A JP2004330981 A JP 2004330981A JP 2004330981 A JP2004330981 A JP 2004330981A JP 4210255 B2 JP4210255 B2 JP 4210255B2
- Authority
- JP
- Japan
- Prior art keywords
- catalyst
- silver
- ethylene oxide
- carrier
- producing ethylene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
α−アルミナ粉体(一次粒子径1.5μm、二次粒子径45μm)900g、20%シリカゾル250g、20%アルミナゾル250g、酸化銀(和光純薬株式会社製特級)10g、ヒドロキシエチルセルロース50g、カルボキシメチルセルロース50g、コーンスターチ50gおよびアンズブリッド100gに水100gを加えて十分混練し、押し出し成型した後、ペレット状(直径10mm、高さ10mm)に切断した。これを乾燥後、1,500℃で2時間焼成して完成担体とした。
実施例1において、酸化銀の使用量を10gから30gに変更した以外は実施例1と同様にして完成担体、続いてエチレンオキシド製造用触媒(B)を得た。
実施例1において、酸化銀の使用量を10gから50gに変更した以外は実施例1と同様にして完成担体、続いてエチレンオキシド製造用触媒(C)を得た。
実施例1において、酸化銀10gの代わりに銀(和光純薬株式会社製粉末)20gを使用する以外は、実施例1と同様にして完成担体、続いてエチレンオキシド製造用触媒(D)を得た。
実施例1において、酸化銀10gの代わりに酢酸銀(和光純薬株式会社製一級)20gを使用する以外は、実施例1と同様にして完成担体、続いてエチレンオキシド製造用触媒(E)を得た。
実施例1において、酸化銀10gの代わりに塩化銀(和光純薬株式会社製特級)20gを使用する以外は、実施例1と同様にして完成担体、続いてエチレンオキシド製造用触媒(F)を得た。
実施例1において、酸化銀10gの代わりに硝酸銀(和光純薬株式会社製特級)20gを使用する以外は、実施例1と同様にして完成担体、続いてエチレンオキシド製造用触媒(G)を得た。
実施例1において、酸化銀10gの代わりに酸化銅(和光純薬株式会社製99.5%)20gを使用する以外は、実施例1と同様にして完成担体、続いてエチレンオキシド製造用触媒(H)を得た。
実施例1において、酸化銀10gの代わりに金コロイド(Au cont.20%)100gを使用する以外は、実施例1と同様にして完成担体、続いてエチレンオキシド製造用触媒(I)を得た。
実施例1において、酸化銀10gの代わりに酸化亜鉛(和光純薬株式会社製特級)20gを使用する以外は、実施例1と同様にして完成担体、続いてエチレンオキシド製造用触媒(J)を得た。
実施例1において、酸化銀10gの代わりに亜鉛粉末(和光純薬株式会社製特級)20gを使用する以外は、実施例1と同様にして完成担体、続いてエチレンオキシド製造用触媒(K)を得た。
実施例1において、酸化銀10gの代わりに塩化亜鉛(和光純薬株式会社製特級)20gを使用する以外は、実施例1と同様にして完成担体、続いてエチレンオキシド製造用触媒(L)を得た。
実施例1において、酸化銀10gの代わりに硝酸亜鉛(和光純薬株式会社製特級)20gを使用する以外は、実施例1と同様にして完成担体、続いてエチレンオキシド製造用触媒(M)を得た。
実施例1において、酸化銀10gの代わりに硫酸亜鉛(和光純薬株式会社製特級)20gを使用する以外は、実施例1と同様にして完成担体、続いてエチレンオキシド製造用触媒(N)を得た。
実施例1において、酸化銀を使用しなかった以外は実施例1と同様にして完成担体、続いてエチレンオキシド製造用触媒(O)を得た。
触媒(A)〜(O)を各々破砕し、600〜850メッシュにふるいわけ、その1.2gを内径3mm、管長600mmのステンレス鋼製の反応管に充填し、これに下記条件下にてエチレンの気相酸化を行った。エチレン転化率が10%のときの選択率および触媒層の反応温度を測定した。
反応圧力:20kg/cm2
原料エチレンガス:エチレン21%、酸素7.8%、二酸化炭素5.7%、エチレンジクロリド2ppm、残余(メタン、窒素、アルゴン、エタン)
結果を表1に示す。
Claims (7)
- 主成分としてのα−アルミナと、シリカと、周期律表第IbおよびIIb族の元素から選ばれた少なくとも1種の元素の金属または化合物とよりなる混合物を成形して得られる担体に少なくとも銀が担持されていることを特徴とするエチレンオキシド製造用触媒。
- シリカの含有量が完成担体に対して、0.01〜15重量%であり、かつ周期律表第IbおよびIIb族の元素から選ばれる少なくとも1種の元素の金属または化合物の含有量が金属換算で該担体に対して0.001〜15重量%である請求項1に記載の触媒。
- 周期律表第IbおよびIIb族の元素の金属または化合物が銅、銀、金および亜鉛の金属または化合物である請求項1または2に記載の触媒。
- 周期律表第IbおよびIIb族の元素の金属または化合物が酸化銀である請求項1〜3のいずれか一つに記載の触媒。
- 該触媒の表面積に対して0.01〜100μmol/m2のアルカリ金属を担持してなる請求項1〜4のいずれか一つに記載の触媒。
- 該担体は0.03〜10m2/gのBET比表面積、10〜70%の吸水率および0.1〜5μmの平均細孔径を有してなる請求項1〜5のいずれか一つに記載の触媒。
- 請求項1〜6のいずれか一つに記載の触媒の存在下にエチレンを分子状酸素含有ガスにより気相酸化することよりなるエチレンオキシドの製造方法。