JP4204745B2 - 熱現像画像記録材料 - Google Patents
熱現像画像記録材料 Download PDFInfo
- Publication number
- JP4204745B2 JP4204745B2 JP2000219943A JP2000219943A JP4204745B2 JP 4204745 B2 JP4204745 B2 JP 4204745B2 JP 2000219943 A JP2000219943 A JP 2000219943A JP 2000219943 A JP2000219943 A JP 2000219943A JP 4204745 B2 JP4204745 B2 JP 4204745B2
- Authority
- JP
- Japan
- Prior art keywords
- group
- silver
- layer
- mol
- dispersion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【発明の属する技術分野】
本発明は熱現像画像記録材料、特に熱現像感光材料に関するものである。
【0002】
【従来の技術】
近年、医療診断用フィルム分野や写真製版フィルム分野において環境保全、省スペースの観点から処理廃液の減量が強く望まれている。そこで、レーザー・イメージセッターまたはレーザー・イメージャーにより効率的に露光させることができ、高解像度および鮮鋭さを有する鮮明な黒色画像を形成することができる医療診断用フィルムおよび写真製版用フィルムとして熱現像感光材料に関する技術が必要とされている。これら熱現像感光材料によれば、溶液系の処理化学薬品を必要とせず、より簡単で環境を損なわない熱現像処理システムを顧客に対して供給することができる。
【0003】
一般の画像形成材料の分野でも同様の要求はあるが、特に医療診断用画像は微細な描写が要求されるため鮮鋭性、粒状性に優れる高画質が必要であるうえ、診断のし易さの観点から冷黒調の画像が好まれる特徴がある。現在、インクジェットプリンター、電子写真など顔料、染料を利用した各種ハードコピーシステムが一般画像形成システムとして流通しているが、医療用画像の出力システムとしては満足できるものがない。
【0004】
一方、有機銀塩を利用した熱画像形成システムが、例えば、米国特許3152904号明細書、同3457075号明細書およびD.クロスタボーア(Klosterboer)著「熱によって処理される銀システム(Thermally Processed Silver Systems)」(イメージング・プロセッシーズ・アンド・マテリアルズ(Imaging Processes and Materials)Neblette 第8版、J.スタージ(Sturge)、V.ウオールワース(Walworth)、A.シェップ(Shepp)編集、第9章、第279頁、1989年)に記載されている。特に、熱現像感光材料は、一般に、触媒活性量の光触媒(例えば、ハロゲン化銀)、還元剤、還元可能な銀塩(例えば、有機銀塩)、必要により銀の色調を制御する色調剤を、バインダーのマトリックス中に分散した感光性層を有している。熱現像感光材料は、画像露光後、高温(例えば80℃以上)に加熱し、還元可能な銀塩(酸化剤として機能する)と還元剤との間の酸化還元反応により、黒色の銀画像を形成する。酸化還元反応は、露光で発生したハロゲン化銀の潜像の触媒作用により促進される。そのため、黒色の銀画像は、露光領域に形成される。米国特許2910377号明細書、特公昭43-4924号公報をはじめとする多くの文献に開示されている。
【0005】
一般にハロゲン化銀写真感光材料は、支持体の上に上記の感光層を有するが、支持体と感光層の接着性が不十分であり、支持体の感光層面に下塗り層を設けて接着性を改良することが行われている。このような下塗りとしてはスチレン−ブタジエン共重合体やポリ塩化ビニリデンなどを含有する下塗りが行われ、特開昭56-95959号公報にもポリエステル類を含有する下塗り層を支持体の感光層面に設けて接着性を改良することが提案されている。また、特開平11-84574号公報には熱現像感光材料においてポリエステルを含有する下塗り層を支持体の感光層面に設けて接着性を改良することが提案されている。しかしながら、特開昭56-95959号公報に記載の特定の水性ポリエステルを含有する下塗り層では熱現像感光材料に適用しても支持体と下塗り層の間での接着性が十分ではなかったり、特開平11-84574号公報に開示の下塗り層でも支持体と下塗り層の間での接着性が十分ではなく、下塗り層の塗布において下塗り塗布液の剪断安定性が不足し、塗布スジが発生してしまったり、面状不良といった問題があった。
【0006】
【発明が解決しようとする課題】
本発明は上記した従来技術の問題点を解消することを解決すべき課題とした。即ち、本発明が解決しようとする課題は、支持体と下塗り層と画像形成層との接着性が良好な熱現像画像記録材料を提供することである。
本発明が解決しようとする別の課題は、支持体と画像形成層との密着が良好で、塗布面状が良好で、機械的な安定性が良好な下塗り層を提供することである。本発明が解決しようとするさらに別の課題は、面状、生産性の良い熱現像画像記録材料を得るために、面状が良好、具体的にはムラがなく、また塗布液の剪断安定性によるスジの発生のない下塗りを提供することにある。
【0007】
【課題を解決するための手段】
本発明者らは上記課題を解決するために鋭意検討した結果、熱現像画像記録材料の支持体の少なくとも一方の面に少なくとも1層のポリエステルを含有する下塗り層を設置し、該ポリエステルが、酸成分とアルコール成分からなるガラス転移温度が40℃〜100℃であるポリエステルであって、酸成分がテレフタル酸及び/またはイソフタル酸を合計40〜90mol%と一定の構造で表されるスルホニルオキシ基を有するイソフタル酸を60〜10mol%で構成され、アルコール成分がジエチレングリコールを40〜90mol%とシクロヘキサンジメタノールを60〜10mol%で構成される場合に、所望の効果を奏する優れた熱現像画像記録材料を提供しうることを見出し、本発明を完成するに至った。
【0008】
即ち、本発明によれば、支持体の少なくとも一方の面に少なくとも1層のポリエステルを含有する下塗り層を有し、この下塗り層上に画像形成層を有する熱現像画像記録材料において、該ポリエステルが酸成分とアルコール成分からなる、ガラス転移温度が40℃〜100℃であるポリエステルであって、酸成分がテレフタル酸及び/またはイソフタル酸を合計40〜90mol%と式1で表されるスルホニルオキシ基を有するイソフタル酸を60〜10mol%で構成され、アルコール成分がジエチレングリコールを40〜90mol%とシクロヘキサンジメタノールを60〜10mol%で構成されることを特徴とする熱現像画像記録材料が提供される。
式1 −(SO3)nM
(式中、nは1または2を表し、Mは水素原子、アルカリもしくはアルカリ土類金属または4級アンモニウム残基を表す。)
好ましくは、画像形成層は、感光性ハロゲン化銀、非感光性有機銀塩、銀イオンのための還元剤及びバインダーを含有する。
【0009】
【発明の実施の形態】
以下、本発明の実施方法及び実施態様を詳細に説明する。なお、本明細書において「〜」はその前後に記載される数値を下限値及び上限値として含む意味で使用される。
本発明の熱現像画像記録材料は、支持体の少なくとも一方の面に少なくとも1層のポリエステルを含有する下塗り層を有し、この下塗り層上に画像形成層を有する熱現像画像記録材料であり、前記ポリエステルが酸成分とアルコール成分からなる、ガラス転移温度(以下、Tgということもある)が40℃〜100℃であるポリエステルであって、酸成分がテレフタル酸及び/またはイソフタル酸を合計40〜90mol%と式1で表されるスルホニルオキシ基を有するイソフタル酸を60〜10mol%で構成され、アルコール成分がジエチレングリコールを40〜90mol%とシクロヘキサンジメタノールを60〜10mol%で構成される。
式1 −(SO3)nM
(式中、nは1または2を表し、Mは水素原子、アルカリもしくはアルカリ土類金属または4級アンモニウム残基を表す。)
【0010】
本発明で用いるポリエステルはTgが40〜100℃であり、好ましくは45℃〜98℃である。
本発明で用いるポリエステルは、多価アルコールと多塩基酸がエステル結合した構造を含むポリマーであるが、酸成分としては、テレフタル酸及び/またはイソフタル酸が合計40〜90mol%用いられ、式1で表されるスルホニルオキシ基を有するイソフタル酸が60〜10mol%用いられる。テレフタル酸及び/またはイソフタル酸は合計65〜90mol%用いられることが好ましく、その場合には式1で表されるスルホニルオキシ基を有するイソフタル酸は35〜10mol%用いられる。多価アルコール成分としてはジエチレングリコールを40〜90mol%とシクロヘキサンジメタノールを60〜10mol%が用いられ、ジエチレングリコールは40〜75mol%用いられることが好ましく、その場合にはシクロヘキサンジメタノールを60〜25mol%用いられる。
【0011】
本発明で用いるポリエステルは公知の任意の方法で製造することができる。たとえば、酸成分とアルコール成分を、周知の二段階製法、即ち、遊離カルボン酸から出発したエステル化および重縮合によるか、エステル交換及び重縮合にて行うことができる。式1のスルホニルオキシ基を有するイソフタル酸は、製造にあたってはMがアルカリもしくはアルカリ土類金属または4級アンモニウム残基にて使用する。
式1において、Mは水素原子、アルカリもしくはアルカリ土類金属または4級アンモニウム残基を表す。Mが表すアルカリ金属としてはLi、Na又はKなどが挙げられ、アルカリ土類金属としてはMg又はCaなどが挙げられる。Mが表す4級アンモニウム残基としては、テトラエチルアンモニウム、テトラブチルアンモニウム等が挙げられる。
【0012】
本発明で用いるポリエステルは下塗り層1層当たり、0.05〜5μm、より好ましくは0.1〜3μm程度になるように用いられることが好ましく、塗布液溶媒に溶解、分散して用いられる。塗布液溶媒としては、水、メタノール、イソプロピルアルコール、ブチルセロソルブ等が挙げられ、それぞれの混合溶媒も用いることもできる。
好ましくは水を溶媒として用いることが特に好ましい。
【0013】
本発明に用いることのできる支持体としては、透明支持体が好ましく、透明ポリエステル支持体(たとえば、ポリエチレンテレフタレート(PET)、ポリエチレンナフタレート)がより好ましい。透明ポリエステル支持体の中でも二軸延伸時にフィルム中に残存する内部歪みを緩和させ、熱現像処理中に発生する熱収縮歪みをなくすために、130〜185℃の温度範囲で熱処理を施したポリエステル、特にポリエチレンテレフタレートが好ましく用いられる。医療用の熱現像感光材料の場合、透明支持体は青色染料(例えば、特開平8-240877号公報実施例記載の染料-1)で着色されていてもよいし、無着色でもよい。また、支持体には帯電防止層として、特開昭56-143430号公報、同56-143431号公報、同58-62646号公報、同56-120519号公報、特開平11-84573号公報の段落番号0040〜0051、米国特許第5,575,957号明細書、特開平11-223898号公報の段落番号0078〜0084に記載の技術を適用することができる。
本発明の熱現像画像記録材料には、特開平11-84574号公報の水溶性ポリエステル、同10-186565号公報のスチレンブタジエン共重合体、特願平11-106881号明細書段落番号0063〜0080の塩化ビニリデン共重合体などの下塗り技術を併用して用いてもよい。
【0014】
本発明に用いることのできる有機銀塩は、光に対して比較的安定であるが、露光された光触媒(感光性ハロゲン化銀の潜像など)及び還元剤の存在下で、80℃或いはそれ以上に加熱された場合に銀画像を形成する銀塩である。有機銀塩は銀イオンを還元できる源を含む任意の有機物質であってよい。このような非感光性の有機銀塩については、特開平10-62899号公報の段落番号0048〜0049、欧州特許公開第0803764A1号公報の第18ページ第24行〜第19ページ第37行、欧州特許公開第0962812A1号公報に記載されている。有機酸の銀塩、特に(炭素数が10〜30、好ましくは15〜28の)長鎖脂肪族カルボン酸の銀塩が好ましい。有機銀塩の好ましい例としては、ベヘン酸銀、アラキジン酸銀、ステアリン酸銀、オレイン酸銀、ラウリン酸銀、カプロン酸銀、ミリスチン酸銀、パルミチン酸銀、これらの混合物などを含む。本発明においては、これら有機銀塩の中でも、ベヘン酸銀含有率75モル%以上の有機酸銀を用いることが好ましい。
【0015】
本発明に用いることができる有機銀塩の形状としては特に制限はなく、針状、棒状、平板状、りん片状でもよい。
本発明においてはりん片状の有機銀塩が好ましい。本明細書において、りん片状の有機銀塩とは、次のようにして定義する。有機酸銀塩を電子顕微鏡で観察し、有機酸銀塩粒子の形状を直方体と近似し、この直方体の辺を一番短い方からa、b、cとした(cはbと同じであってもよい。)とき、短い方の数値a、bで計算し、次のようにしてxを求める。
x=b/a
【0016】
このようにして200個程度の粒子についてxを求め、その平均値x(平均)としたとき、x(平均)≧1.5の関係を満たすものをりん片状とする。好ましくは30≧x(平均)≧1.5、より好ましくは20≧x(平均)≧2.0である。因みに針状とは1≦x(平均)<1.5である。
りん片状粒子において、aはbとcを辺とする面を主平面とした平板状粒子の厚さとみることができる。aの平均は0.01μm〜0.23μmが好ましく0.1μm〜0.20μmがより好ましい。c/bの平均は好ましくは1〜6、より好ましくは1.05〜4、さらに好ましくは1.1〜3、特に好ましくは1.1〜2である。
【0017】
有機銀塩の粒子サイズ分布は単分散であることが好ましい。単分散とは短軸、長軸それぞれの長さの標準偏差を短軸、長軸それぞれで割った値の100分率が好ましくは100%以下、より好ましくは80%以下、更に好ましくは50%以下である。有機銀塩の形状の測定方法としては有機銀塩分散物の透過型電子顕微鏡像より求めることができる。単分散性を測定する別の方法として、有機銀塩の体積加重平均直径の標準偏差を求める方法があり、体積加重平均直径で割った値の百分率(変動係数)が好ましくは100%以下、より好ましくは80%以下、更に好ましくは50%以下である。測定方法としては例えば液中に分散した有機銀塩にレーザー光を照射し、その散乱光のゆらぎの時間変化に対する自己相関関数を求めることにより得られた粒子サイズ(体積加重平均直径)から求めることができる。
【0018】
本発明に用いられる有機酸銀の製造及びその分散法は、公知の方法を適用することができる。例えば上記の特開平10-62899号公報、欧州特許公開第0803763A1号公報、欧州特許公開962812A1号公報を参考にすることができる。
なお、有機銀塩の分散時に、感光性銀塩を共存させると、カブリが上昇し、感度が著しく低下するため、分散時には感光性銀塩を実質的に含まないことがより好ましい。本発明は、分散される水分散液中での感光性銀塩量は、その液中の有機酸銀塩1molに対し0.1mol%以下であり、積極的な感光性銀塩の添加は行わないものである。
【0019】
本発明において有機銀塩水分散液と感光性銀塩水分散液を混合して感光材料を製造することが可能であるが、有機銀塩と感光性銀塩の混合比率は目的に応じて選べるが、有機銀塩に対する感光性銀塩の割合は1〜30モル%の範囲が好ましく、更に3〜20モル%、特に5〜15モル%の範囲が好ましい。混合する際に2種以上の有機銀塩水分散液と2種以上の感光性銀塩水分散液を混合することは、写真特性の調節のために好ましく用いられる方法である。
本発明で用いる有機銀塩は所望の量で使用できるが、銀量として0.1〜5g/m2が好ましく、さらに好ましくは1〜3g/m2である。
【0020】
本発明の熱現像画像記録材料には有機銀塩のための還元剤を含むことが好ましい。有機銀塩のための還元剤は、銀イオンを金属銀に還元する任意の物質(好ましくは有機物質)であってよい。このような還元剤は、特開平11-65021号公報の段落番号0043〜0045や、欧州特許公開第0803764A1号公報の第7ページ第34行〜第18ページ第12行に記載されている。
本発明において、還元剤としてはビスフェノール類還元剤が好ましく、下記一般式(I)で表される化合物がより好ましい。
【0021】
【化1】
【0022】
(一般式(I)において、R11およびR11'は各々独立に炭素数1〜20のアルキル基を表す。R12およびR12'は各々独立に水素原子またはベンゼン環に置換可能な置換基を表す。Lは−S−基または−CHR13−基を表す。R13は水素原子または炭素数1〜20のアルキル基を表す。X11およびX11'は各々独立に水素原子またはベンゼン環に置換可能な基を表す。)
【0023】
一般式(I)について詳細に説明する。
R11およびR11'は各々独立に置換または無置換の炭素数1〜20のアルキル基であり、アルキル基の置換基は特に限定されることはないが、好ましくは、アリール基、ヒドロキシ基、アルコキシ基、アリールオキシ基、アルキルチオ基、アリールチオ基、アシルアミノ基、スルホンアミド基、スルホニル基、ホスホリル基、アシル基、カルバモイル基、エステル基、ハロゲン原子等があげられる。
【0024】
R12およびR12'は各々独立に水素原子またはベンゼン環に置換可能な置換基であり、X11およびX11'も各々独立に水素原子またはベンゼン環に置換可能な基を表す。それぞれベンゼン環に置換可能な基としては、好ましくはアルキル基、アリール基、ハロゲン原子、アルコキシ基、アシルアミノ基があげられる。
R11またはR12とX11、R11'またはR12'とX11'は一緒になって環構造を形成してもよく、環構造としては置換基を有していてもよい炭化水素環などが挙げられる。
【0025】
Lは−S−基または−CHR13−基を表す。R13は水素原子または炭素数1〜20のアルキル基を表し、アルキル基は置換基を有していてもよい。R13の無置換のアルキル基の具体例はメチル基、エチル基、プロピル基、ブチル基、ヘプチル基、ウンデシル基、イソプロピル基、1−エチルペンチル基、2,4,4−トリメチルペンチル基などがあげられる。アルキル基の置換基の例はR11の置換基と同様で、ハロゲン原子、アルコキシ基、アルキルチオ基、アリールオキシ基、アリールチオ基、アシルアミノ基、スルホンアミド基、スルホニル基、ホスホリル基、オキシカルボニル基、カルバモイル基、スルファモイル基などがあげられる。
【0026】
R11およびR11'として好ましくは炭素数3〜15の2級または3級のアルキル基であり、具体的にはイソプロピル基、イソブチル基、t−ブチル基、t−アミル基、t−オクチル基、シクロヘキシル基、シクロペンチル基、1−メチルシクロヘキシル基、1−メチルシクロプロピル基などがあげられる。R11およびR11'としてより好ましくは炭素数4〜12の3級アルキル基で、その中でもt−ブチル基、t−アミル基、1−メチルシクロヘキシル基が更に好ましく、t−ブチル基が最も好ましい。
【0027】
R12およびR12'として好ましくは炭素数1〜20のアルキル基であり、具体的にはメチル基、エチル基、プロピル基、ブチル基、イソプロピル基、t−ブチル基、t−アミル基、シクロヘキシル基、1−メチルシクロヘキシル基、ベンジル基、メトキシメチル基、メトキシエチル基などがあげられる。より好ましくはメチル基、エチル基、プロピル基、イソプロピル基、t−ブチル基である。
X11およびX11'は、好ましくは水素原子、ハロゲン原子、アルキル基で、より好ましくは水素原子である。
【0028】
Lは好ましくは−CHR13−基である。
R13として好ましくは水素原子または炭素数1〜15のアルキル基であり、アルキル基としてはメチル基、エチル基、プロピル基、イソプロピル基、2,4,4−トリメチルペンチル基が好ましい。R13として特に好ましいのは水素原子、メチル基、エチル基またはプロピル基である。
【0029】
R13が水素原子である場合、R12およびR12'は好ましくは炭素数2〜5のアルキル基であり、エチル基、プロピル基がより好ましく、エチル基が最も好ましい。
R13は炭素数1〜8の1級または2級のアルキル基である場合、R12およびR12'はメチル基が好ましい。R13の炭素数1〜8の1級または2級のアルキル基としてはメチル基、エチル基、プロピル基、イソプロピル基がより好ましく、メチル基、エチル基、プロピル基が更に好ましい。
以下に本発明で用いる一般式(I)で表される化合物の具体例を示すが、これらに限定されるものではない。
【0030】
【化2】
【0031】
【化3】
【0032】
【化4】
【0033】
【化5】
【0034】
本発明において還元剤の添加量は0.01〜5.0g/m2であることが好ましく、0.1〜3.0g/m2であることがより好ましく、画像形成層を有する面の銀1モルに対しては5〜50モル%含まれることが好ましく、10〜40モル%で含まれることがさらに好ましい。還元剤は画像形成層に含有させることが好ましい。
【0035】
還元剤は溶液形態、乳化分散形態、固体微粒子分散物形態など、いかなる方法で塗布液に含有せしめ、感光材料に含有させてもよい。
よく知られている乳化分散法としては、ジブチルフタレート、トリクレジルフォスフェート、グリセリルトリアセテートあるいはジエチルフタレートなどのオイル、酢酸エチルやシクロヘキサノンなどの補助溶媒を用いて溶解し、機械的に乳化分散物を作製する方法が挙げられる。
【0036】
また、固体微粒子分散法としては、還元剤の粉末を水等の適当な溶媒中にボールミル、コロイドミル、振動ボールミル、サンドミル、ジェットミル、ローラーミルあるいは超音波によって分散し、固体分散物を作成する方法が挙げられる。尚、その際に保護コロイド(例えば、ポリビニルアルコール)、界面活性剤(例えばトリイソプロピルナフタレンスルホン酸ナトリウム(3つのイソプロピル基の置換位置が異なるものの混合物)などのアニオン性界面活性剤)を用いてもよい。水分散物には防腐剤(例えばベンゾイソチアゾリノンナトリウム塩)を含有させることができる。
本発明の熱現像感光材料では、現像促進剤として特願平11-73951号明細書に記載の式(A)で表されるフェノール誘導体が好ましく用いられる。
【0037】
本発明における還元剤が芳香族性の水酸基(−OH)を有する場合、特に前述のビスフェノール類の場合には、これらの基と水素結合を形成することが可能な基を有する非還元性の化合物を併用することが好ましい。水酸基またはアミノ基と水素結合を形成する基としては、ホスホリル基、スルホキシド基、スルホニル基、カルボニル基、アミド基、エステル基、ウレタン基、ウレイド基、3級アミノ基、含窒素芳香族基などが挙げられる。その中でも好ましいのはホスホリル基、スルホキシド基、アミド基(但し、>N−H基を持たず、>N−R(RはH以外の置換基)のようにブロックされている。)、ウレタン基(但し、>N−H基を持たず、>N−R(RはH以外の置換基)のようにブロックされている。)、ウレイド基(但し、>N−H基を持たず、>N−R(RはH以外の置換基)のようにブロックされている。)を有する化合物である。
本発明で、特に好ましい水素結合性の化合物は下記一般式(II)で表される化合物である。
【0038】
【化6】
【0039】
一般式(II)においてR21〜R23は各々独立にアルキル基、アリール基、アルコキシ基、アリールオキシ基、アミノ基またはヘテロ環基を表し、これらの基は無置換であっても置換基を有していてもよい。R21〜R23が置換基を有する場合の置換基としてはハロゲン原子、アルキル基、アリール基、アルコキシ基、アミノ基、アシル基、アシルアミノ基、アルキルチオ基、アリールチオ基、スルホンアミド基、アシルオキシ基、オキシカルボニル基、カルバモイル基、スルファモイル基、スルホニル基、ホスホリル基などが挙げられ、置換基として好ましいのはアルキル基またはアリール基であり、例えばメチル基、エチル基、イソプロピル基、t−ブチル基、t−オクチル基、フェニル基、4−アルコキシフェニル基、4−アシルオキシフェニル基などが挙げられる。
R21〜R23のアルキル基としては具体的にはメチル基、エチル基、ブチル基、オクチル基、ドデシル基、イソプロピル基、t−ブチル基、t−アミル基、t−オクチル基、シクロヘキシル基、1−メチルシクロヘキシル基、ベンジル基、フェネチル基、2−フェノキシプロピル基などが挙げられる。アリール基としてはフェニル基、クレジル基、キシリル基、ナフチル基、4−t−ブチルフェニル基、4−t−オクチルフェニル基、4−アニシジル基、3,5−ジクロロフェニル基などが挙げられる。アルコキシ基としてはメトキシ基、エトキシ基、ブトキシ基、オクチルオキシ基、2−エチルヘキシルオキシ基、3,5,5−トリメチルヘキシルオキシ基、ドデシルオキシ基、シクロヘキシルオキシ基、4−メチルシクロヘキシルオキシ基、ベンジルオキシ基等が挙げられる。アリールオキシ基としてはフェノキシ基、クレジルオキシ基、イソプロピルフェノキシ基、4−t−ブチルフェノキシ基、ナフトキシ基、ビフェニルオキシ基等が挙げられる。アミノ基としてはジメチルアミノ基、ジエチルアミノ基、ジブチルアミノ基、ジオクチルアミノ基、N−メチル−N−ヘキシルアミノ基、ジシクロヘキシルアミノ基、ジフェニルアミノ基、N−メチル−N−フェニルアミノ基等が挙げられる。
R21とR22、R22とR23またはR21とR22とR23は一緒になって、置換されていてもよい単環系または多環系炭化水素を表すことができる。
【0040】
R21〜R23はアルキル基、アリール基、アルコキシ基、アリールオキシ基が好ましい。本発明の効果の点ではR21〜R23のうち少なくとも一つ以上がアルキル基またはアリール基であることが好ましく、二つ以上がアルキル基またはアリール基であることがより好ましい。また、安価に入手する事ができるという点ではR21〜R23が同一の基である場合が好ましい。
以下に本発明で用いることができる一般式(II)の化合物の具体例を示すが、これらに限定されるものではない。
【0041】
【化7】
【0042】
【化8】
【0043】
【化9】
【0044】
【化10】
【0045】
本発明で用いる一般式(II)の化合物は、還元剤と同様に溶液形態、乳化分散形態、固体分散微粒子分散物形態で塗布液に含有せしめ、画像記録材料中で使用することができる。一般式(II)の化合物は、溶液状態でフェノール性水酸基、アミノ基を有する化合物と水素結合性の錯体を形成しており、還元剤と一般式(II)の化合物との組合せによっては錯体として結晶状態で単離することができる。このようにして単離した結晶粉体を固体分散微粒子分散物として使用することは安定した性能を得る上で特に好ましい。また、還元剤と一般式(II)の化合物を粉体で混合し、適当な分散剤を使って、サンドグラインダーミル等で分散時に錯形成させる方法も好ましく用いることができる。
本発明で用いる一般式(II)の化合物は還元剤に対して、1〜200モル%の範囲で使用することが好ましく、より好ましくは10〜150モル%の範囲で、さらに好ましくは30〜100モル%の範囲である。
【0046】
本発明の熱現像画像記録材料の画像形成層には、好ましくは感光性ハロゲン化銀が含まれる。
本発明に用いられる感光性ハロゲン化銀は、ハロゲン組成として特に制限はなく、塩化銀、塩臭化銀、臭化銀、ヨウ臭化銀、ヨウ塩臭化銀を用いることができる。粒子内におけるハロゲン組成の分布は均一であってもよく、ハロゲン組成がステップ状に変化したものでもよく、或いは連続的に変化したものでもよい。また、コア/シェル構造を有するハロゲン化銀粒子を好ましく用いることができる。構造として好ましいものは2〜5重構造であり、より好ましくは2〜4重構造のコア/シェル粒子を用いることができる。また塩化銀または塩臭化銀粒子の表面に臭化銀を局在させる技術も好ましく用いることができる。
【0047】
感光性ハロゲン化銀の形成方法は当業界ではよく知られており、例えば、リサーチディスクロージャー1978年6月の第17029号、および米国特許第3,700,458号明細書に記載されている方法を用いることができるが、具体的にはゼラチンあるいは他のポリマー溶液中に銀供給化合物及びハロゲン供給化合物を添加することにより感光性ハロゲン化銀を調製し、その後で有機銀塩と混合する方法を用いる。また、特開平11-119374号公報の段落番号0217〜0224に記載されている方法、特願平11-98708号明細書、同11-84182号明細書に記載の方法も好ましい。
感光性ハロゲン化銀の粒子サイズは、画像形成後の白濁を低く抑える目的のために小さいことが好ましく具体的には0.20μm以下、より好ましくは0.01μm〜0.15μm、更に好ましくは0.02μm〜0.12μmがよい。ここでいう粒子サイズとは、ハロゲン化銀粒子の投影面積(平板粒子の場合は主平面の投影面積)と同面積の円像に換算したときの直径をいう。
【0048】
ハロゲン化銀粒子の形状としては立方体、八面体、平板状粒子、球状粒子、棒状粒子、ジャガイモ状粒子等を挙げることができるが、本発明においては特に立方体状粒子が好ましい。ハロゲン化銀粒子のコーナーが丸まった粒子も好ましく用いることができる。感光性ハロゲン化銀粒子の外表面の面指数(ミラー指数)については特に制限はないが、分光増感色素が吸着した場合の分光増感効率が高い[100]面の占める割合が高いことが好ましい。その割合としては50%以上が好ましく、65%以上がより好ましく、80%以上が更に好ましい。ミラー指数[100]面の比率は増感色素の吸着における[111]面と[100]面との吸着依存性を利用したT.Tani;J.Imaging Sci.,29、165(1985年)に記載の方法により求めることができる。
【0049】
本発明においては、六シアノ金属錯体を粒子最表面に存在させたハロゲン化銀粒子が好ましい。六シアノ金属錯体としては、[Fe(CN)6]4-、[Fe(CN)6]3-、[Ru(CN)6]4-、[Os(CN)6]4-、[Co(CN)6]3-、[Rh(CN)6]3-、[Ir(CN)6]3-、[Cr(CN)6]3-、[Re(CN)6]3-などが挙げられる。本発明においては六シアノFe錯体が好ましい。
六シアノ金属錯体は、水溶液中でイオンの形で存在するので対陽イオンは重要ではないが、水と混和しやすく、ハロゲン化銀乳剤の沈澱操作に適合しているナトリウムイオン、カリウムイオン、ルビジウムイオン、セシウムイオンおよびリチウムイオン等のアルカリ金属イオン、アンモニウムイオン、アルキルアンモニウムイオン(例えばテトラメチルアンモニウムイオン、テトラエチルアンモニウムイオン、テトラプロピルアンモニウムイオン、テトラ(n-ブチル)アンモニウムイオン)を用いることが好ましい。
【0050】
六シアノ金属錯体は、水の他に水と混和しうる適当な有機溶媒(例えば、アルコール類、エーテル類、グリコール類、ケトン類、エステル類、アミド類等)との混合溶媒やゼラチンと混和して添加することができる。
六シアノ金属錯体の添加量は、銀1モル当たり1×10-5モル〜1×10-2モルが好ましく、より好ましくは1×10-4モル〜1×10-3モルである。
【0051】
六シアノ金属錯体をハロゲン化銀粒子最表面に存在させるには、六シアノ金属錯体を、粒子形成に使用する硝酸銀水溶液を添加終了した後、硫黄増感、セレン増感およびテルル増感のカルコゲン増感や金増感等の貴金属増感を行う化学増感工程の前までの仕込み工程終了前、水洗工程中、分散工程中、または化学増感工程前に直接添加する。ハロゲン化銀微粒子を成長させないためには、粒子形成後速やかに六シアノ金属錯体を添加することが好ましく、仕込み工程終了前に添加することが好ましい。
尚、六シアノ金属錯体の添加は、粒子形成をするために添加する硝酸銀の総量の96質量%を添加した後から開始してもよく、98質量%添加した後から開始するのがより好ましく、99質量%添加した後が特に好ましい。
【0052】
これら六シアノ金属錯体を粒子形成の完了する直前の硝酸銀水溶液を添加した後に添加すると、ハロゲン化銀粒子最表面に吸着することができ、そのほとんどが粒子表面の銀イオンと難溶性の塩を形成する。この六シアノ鉄(II)の銀塩は、AgIよりも難溶性の塩であるため、微粒子による再溶解を防ぐことができ、粒子サイズが小さいハロゲン化銀微粒子を製造することが可能となった。
本発明で用いる感光性ハロゲン化銀粒子は、周期律表(第1〜18族までを示す)の第8族〜第10族の金属または金属錯体を含有することができる。周期律表の第8族〜第10族の金属または金属錯体の中心金属として好ましくは、ロジウム、ルテニウム、イリジウムである。これら金属錯体は1種類でもよいし、同種金属及び異種金属の錯体を2種以上併用してもよい。好ましい含有率は銀1モルに対し1×10-9モル〜1×10-3モルの範囲が好ましい。これらの重金属や金属錯体及びそれらの添加法については特開平7-225449号公報、特開平11-65021号公報段落番号0018〜0024、特開平11-119374号公報段落番号0227〜0240に記載されている。
【0053】
さらに本発明に用いられるハロゲン化銀粒子に含有することのできる金属原子(例えば[Fe(CN)6]4-)、ハロゲン化銀乳剤の脱塩法や化学増感法については特開平11-84574号公報の段落番号0046〜0050、特開平11-65021号公報の段落番号0025〜0031、特開平11-119374号公報の段落番号0242〜0250に記載されている。
【0054】
本発明に用いる感光性ハロゲン化銀乳剤に含有されるゼラチンとしては、種々のゼラチンが使用することができる。感光性ハロゲン化銀乳剤の有機銀塩含有塗布液中での分散状態を良好に維持するために、分子量は、500〜60,000の低分子量ゼラチンを使用することが好ましい。これらの低分子量ゼラチンは粒子形成時あるいは脱塩処理後の分散時に使用してもよいが、脱塩処理後の分散時に使用することが好ましい。
【0055】
本発明に適用できる増感色素としてはハロゲン化銀粒子に吸着した際、所望の波長領域でハロゲン化銀粒子を分光増感できるもので、露光光源の分光特性に適した分光感度を有する増感色素を有利に選択することができる。増感色素及び添加法については、特開平11-65021号公報の段落番号0103〜0109、特開平10-186572号公報の一般式(II)で表される化合物、特開平11-119374号公報の一般式(I)で表される色素及び段落番号0106、米国特許第5,510,236号明細書、同第3,871,887号明細書の実施例5に記載の色素、特開平2-96131号公報、特開昭59-48753号公報に開示されている色素、欧州特許公開第0803764A1号公報の第19ページ第38行〜第20ページ第35行、特願2000-86865号明細書、特願2000-102560号明細書等に記載されている。これらの増感色素は単独で用いてもよく、2種以上組合せて用いてもよい。本発明において増感色素をハロゲン化銀乳剤中に添加する時期は、脱塩工程後、塗布までの時期が好ましく、より好ましくは脱塩後から化学熟成の開始前までの時期である。
本発明における増感色素の添加量は、感度やカブリの性能に合わせて所望の量にすることができるが、感光性層のハロゲン化銀1モル当たり10-6〜1モルが好ましく、さらに好ましくは10-4〜10-1モルである。
【0056】
本発明は分光増感効率を向上させるため、強色増感剤を用いることができる。本発明に用いる強色増感剤としては、欧州特許公開第587,338号公報、米国特許第3,877,943号明細書、同第4,873,184号明細書、特開平5-341432号公報、同11-109547号公報、同10-111543号公報等に記載の化合物が挙げられる。
【0057】
本発明における感光性ハロゲン化銀粒子は、硫黄増感法、セレン増感法もしくはテルル増感法にて化学増感されていることが好ましい。硫黄増感法、セレン増感法、テルル増感法に好ましく用いられる化合物としては公知の化合物、例えば、特開平7-128768号公報等に記載の化合物等を使用することができる。特に本発明においてはテルル増感が好ましく、特開平11-65021号公報の段落番号0030に記載の文献に記載の化合物、特開平5-313284号公報中の一般式(II),(III),(IV)で示される化合物がより好ましい。
【0058】
本発明においては、化学増感は粒子形成後で塗布前であればいかなる時期でも可能であり、脱塩後、(1)分光増感前、(2)分光増感と同時、(3)分光増感後、(4)塗布直前等があり得る。特に分光増感後に行われることが好ましい。
本発明で用いられる硫黄、セレンおよびテルル増感剤の使用量は、使用するハロゲン化銀粒子、化学熟成条件等によって変わるが、ハロゲン化銀1モル当たり10-8〜10-2モル、好ましくは10-7〜10-3モル程度を用いる。本発明における化学増感の条件としては特に制限はないが、pHとしては5〜8、pAgとしては6〜11、温度としては40〜95℃程度である。
本発明で用いるハロゲン化銀乳剤には、欧州特許公開第293,917号公報に示される方法により、チオスルホン酸化合物を添加してもよい。
【0059】
本発明に用いられる感光材料中の感光性ハロゲン化銀乳剤は、一種だけでもよいし、二種以上(例えば、平均粒子サイズの異なるもの、ハロゲン組成の異なるもの、晶癖の異なるもの、化学増感の条件の異なるもの)併用してもよい。感度の異なる感光性ハロゲン化銀を複数種用いることで階調を調節することができる。これらに関する技術としては特開昭57-119341号、同53-106125号、同47-3929号、同48-55730号、同46-5187号、同50-73627号、同57-150841号の公報などが挙げられる。感度差としてはそれぞれの乳剤で0.2logE以上の差を持たせることが好ましい。
【0060】
感光性ハロゲン化銀の添加量は、感光材料1m2当たりの塗布銀量で示して、0.03〜0.6g/m2であることが好ましく、0.05〜0.4g/m2であることがさらに好ましく、0.1〜0.4g/m2であることが最も好ましく、有機銀塩1モルに対しては、感光性ハロゲン化銀は0.01モル〜0.5モルが好ましく、0.02モル〜0.3モルがより好ましい。
別々に調製した感光性ハロゲン化銀と有機銀塩の混合方法及び混合条件については、それぞれ調製終了したハロゲン化銀粒子と有機銀塩を高速撹拌機やボールミル、サンドミル、コロイドミル、振動ミル、ホモジナイザー等で混合する方法や、あるいは有機銀塩の調製中のいずれかのタイミングで調製終了した感光性ハロゲン化銀を混合して有機銀塩を調製する方法等があるが、本発明の効果が十分に現れる限りにおいては特に制限はない。また、混合する際に2種以上の有機銀塩水分散液と2種以上の感光性銀塩水分散液を混合することは、写真特性の調節のために好ましい方法である。
【0061】
本発明で用いるハロゲン化銀の画像形成層塗布液中への好ましい添加時期は、塗布する180分前から直前、好ましくは60分前から10秒前であるが、混合方法及び混合条件については本発明の効果が十分に現れる限りにおいては特に制限はない。具体的な混合方法としては添加流量とコーターへの送液量から計算した平均滞留時間を所望の時間となるようにしたタンクでの混合する方法やN.Harnby、M.F.Edwards、A.W.Nienow著、高橋幸司訳“液体混合技術”(日刊工業新聞社刊、1989年)の第8章等に記載されているスタチックミキサーなどを使用する方法がある。
【0062】
本発明で用いる有機銀塩含有層のバインダーはいかなるポリマーであってもよく、好適なバインダーは透明又は半透明で、一般に無色であり、天然樹脂やポリマー及びコポリマー、合成樹脂やポリマー及びコポリマー、その他フィルムを形成する媒体、例えば、ゼラチン類、ゴム類、ポリ(ビニルアルコール)類、ヒドロキシエチルセルロース類、セルロースアセテート類、セルロースアセテートブチレート類、ポリ(ビニルピロリドン)類、カゼイン、デンプン、ポリ(アクリル酸)類、ポリ(メチルメタクリル酸)類、ポリ(塩化ビニル)類、ポリ(メタクリル酸)類、スチレン−無水マレイン酸共重合体類、スチレン−アクリロニトリル共重合体類、スチレン−ブタジエン共重合体類、ポリ(ビニルアセタール)類(例えば、ポリ(ビニルホルマール)及びポリ(ビニルブチラール))、ポリ(エステル)類、ポリ(ウレタン)類、フェノキシ樹脂、ポリ(塩化ビニリデン)類、ポリ(エポキシド)類、ポリ(カーボネート)類、ポリ(酢酸ビニル)類、ポリ(オレフィン)類、セルロースエステル類、ポリ(アミド)類がある。バインダーは水又は有機溶媒またはエマルションから被覆形成してもよい。
【0063】
本発明においては、有機銀塩含有層が溶媒の30質量%以上が水である塗布液を用いて塗布し、乾燥して形成される場合に、さらに有機銀塩含有層のバインダーが水系溶媒(水溶媒)に可溶または分散可能である場合に、特に25℃60%相対湿度での平衡含水率が2質量%以下のポリマーのラテックスからなる場合に向上する。最も好ましい形態は、イオン伝導度が2.5mS/cm以下になるように調製されたものであり、このような調製法としてポリマー合成後分離機能膜を用いて精製処理する方法が挙げられる。
【0064】
ここでいう前記ポリマーが可溶または分散可能である水系溶媒とは、水または水に70質量%以下の水混和性の有機溶媒を混合したものである。水混和性の有機溶媒としては、例えば、メチルアルコール、エチルアルコール、プロピルアルコール等のアルコール系、メチルセロソルブ、エチルセロソルブ、ブチルセロソルブ等のセロソルブ系、酢酸エチル、ジメチルホルミアミドなどを挙げることができる。
【0065】
なお、ポリマーが熱力学的に溶解しておらず、いわゆる分散状態で存在している系の場合にも、ここでは水系溶媒という言葉を使用する。
また「25℃60%相対湿度における平衡含水率」とは、25℃60%相対湿度の雰囲気下で調湿平衡にあるポリマーの質量W1と25℃で絶乾状態にあるポリマーの質量W0を用いて以下のように表すことができる。
25℃60%相対湿度における平衡含水率=[(W1-W0)/W0]×100(質量%)
含水率の定義と測定法については、例えば高分子工学講座14、高分子材料試験法(高分子学会編、地人書館)を参考にすることができる。
本発明で用いるバインダーポリマーの25℃60%相対湿度における平衡含水率は2質量%以下であることが好ましいが、より好ましくは0.01質量%〜1.5質量%、さらに好ましくは0.02質量%〜1質量%が望ましい。
【0066】
本発明においては水系溶媒に分散可能なポリマーが特に好ましい。分散状態の例としては、水不溶な疎水性ポリマーの微粒子が分散しているラテックスやポリマー分子が分子状態またはミセルを形成して分散しているものなどがあるが、いずれも好ましい。分散粒子の平均粒径は1〜50000nm、より好ましくは5〜1000nm程度の範囲が好ましい。分散粒子の粒径分布に関しては特に制限は無く、広い粒径分布を持つものでも単分散の粒径分布を持つものでもよい。
【0067】
本発明において水系溶媒に分散可能なポリマーの好ましい態様としては、アクリル系ポリマー、ポリ(エステル)類、ゴム類(例えばSBR樹脂)、ポリ(ウレタン)類、ポリ(塩化ビニル)類、ポリ(酢酸ビニル)類、ポリ(塩化ビニリデン)類、ポリ(オレフィン)類等の疎水性ポリマーを好ましく用いることができる。これらポリマーとしては直鎖のポリマーでも枝分かれしたポリマーでもまた架橋されたポリマーでもよいし、単一のモノマーが重合したいわゆるホモポリマーでもよいし、2種類以上のモノマーが重合したコポリマーでもよい。コポリマーの場合はランダムコポリマーでも、ブロックコポリマーでもよい。これらポリマーの分子量は数平均分子量で5000〜1000000、好ましくは10000〜200000がよい。分子量が小さすぎるものは乳剤層の力学強度が不十分であり、大きすぎるものは成膜性が悪く好ましくない。
【0068】
好ましいポリマーラテックスの具体例としては以下のものを挙げることができる。以下では原料モノマーを用いて表し、括弧内の数値は質量%、分子量は数平均分子量である。
P-1;-MMA(70)-EA(27)-MAA(3)-のラテックス(分子量37000)
P-2;-MMA(70)-2EHA(20)-St(5)-AA(5)-のラテックス(分子量40000)
P-3;-St(50)-Bu(47)-MAA(3)-のラテックス(分子量45000)
P-4;-St(68)-Bu(29)-AA(3)-のラテックス(分子量60000)
P-5;-St(71)-Bu(26)-AA(3)-のラテックス(分子量60000)
P-6;-St(70)-Bu(27)-IA(3)-のラテックス(分子量120000)
P-7;-St(75)-Bu(24)-AA(1)-のラテックス(分子量108000)
P-8;-St(60)-Bu(35)-DVB(3)-MAA(2)-のラテックス(分子量150000)
P-9;-St(70)-Bu(25)-DVB(2)-AA(3)-のラテックス(分子量280000)
P-10;-VC(50)-MMA(20)-EA(20)-AN(5)-AA(5)-のラテックス(分子量80000)
P-11;-VDC(85)-MMA(5)-EA(5)-MAA(5)-のラテックス(分子量67000)
P-12;-Et(90)-MAA(10)-のラテックス(分子量12000)
P-13;-St(70)-2EHA(27)-AA(3)のラテックス(分子量130000)
P-14;-MMA(63)-EA(35)-AA(2)のラテックス(分子量33000)
【0069】
上記構造の略号は以下のモノマーを表す。MMA;メチルメタクリレート,EA;エチルアクリレート、MAA;メタクリル酸,2EHA;2エチルヘキシルアクリレート,St;スチレン,Bu;ブタジエン,AA;アクリル酸,DVB;ジビニルベンゼン,VC;塩化ビニル,AN;アクリロニトリル,VDC;塩化ビニリデン,Et;エチレン,IA;イタコン酸。
【0070】
以上に記載したポリマーラテックスは市販もされていて、以下のようなポリマーが利用できる。アクリル系ポリマーの例としては、セビアンA-4635,46583,4601(以上ダイセル化学工業(株)製)、Nipol Lx811、814、821、820、857(以上日本ゼオン(株)製)など、ポリ(エステル)類の例としては、FINETEX ES650、611、675、850(以上大日本インキ化学(株)製)、WD-size、WMS(以上イーストマンケミカル製)など、ポリ(ウレタン)類の例としては、HYDRAN AP10、20、30、40(以上大日本インキ化学(株)製)など、ゴム類の例としては、LACSTAR 7310K、3307B、4700H、7132C(以上大日本インキ化学(株)製)、Nipol Lx416、410、438C、2507(以上日本ゼオン(株)製)など、ポリ(塩化ビニル)類の例としては、G351、G576(以上日本ゼオン(株)製)など、ポリ(塩化ビニリデン)類の例としては、L502、L513(以上旭化成工業(株)製)など、ポリ(オレフィン)類の例としては、ケミパールS120、SA100(以上三井石油化学(株)製)などを挙げることができる。
これらのポリマーラテックスは単独で用いてもよいし、必要に応じて2種以上ブレンドしてもよい。
【0071】
本発明に用いられるポリマーラテックスとしては、特に、スチレン-ブタジエン共重合体のラテックスが好ましい。スチレン-ブタジエン共重合体におけるスチレンのモノマー単位とブタジエンのモノマー単位との質量比は40:60〜95:5であることが好ましい。また、スチレンのモノマー単位とブタジエンのモノマー単位との共重合体に占める割合は60〜99質量%であることが好ましい。好ましい分子量の範囲は前記と同様である。
本発明に用いることが好ましいスチレン-ブタジエン共重合体のラテックスとしては、前記のP-3〜P-8、市販品であるLACSTAR-3307B、7132C、Nipol Lx416等が挙げられる。
【0072】
本発明に用いるラテックスとしては、ガラス転移温度(Tg)が10℃〜80℃の範囲にある場合が好ましく、より好ましくは20℃〜60℃の範囲である。Tgの異なるラテックスを2種以上ブレンドして使用する場合には、その質量平均Tgが上記の範囲にはいることが好ましい。
本発明の熱現像画像記録材料の有機銀塩含有層には必要に応じてゼラチン、ポリビニルアルコール、メチルセルロース、ヒドロキシプロピルセルロース、カルボキシメチルセルロースなどの親水性ポリマーを添加してもよい。これらの親水性ポリマーの添加量は有機銀塩含有層の全バインダーの30質量%以下、より好ましくは20質量%以下が好ましい。
【0073】
本発明の熱現像画像記録材料の有機銀塩含有層(即ち、画像形成層)は、ポリマーラテックスとを用いて形成されたものが好ましい。有機銀塩含有層のバインダーの量は、全バインダー/有機銀塩の質量比が1/10〜10/1、更には1/5〜4/1の範囲が好ましい。
また、このような有機銀塩含有層は、通常、感光性銀塩である感光性ハロゲン化銀が含有された感光性層(乳剤層)でもあり、このような場合の、全バインダー/ハロゲン化銀の質量比は400〜5、より好ましくは200〜10の範囲が好ましい。
画像形成層の全バインダー量は0.2〜30g/m2、より好ましくは1〜15g/m2の範囲が好ましい。画像形成層には架橋のための架橋剤、塗布性改良のための界面活性剤などを添加してもよい。
【0074】
本発明で用いる有機銀塩含有層塗布液の溶媒(ここでは簡単のため、溶媒と分散媒をあわせて溶媒と表す。)は、水を30質量%以上含む水系溶媒が好ましい。水以外の成分としてはメチルアルコール、エチルアルコール、イソプロピルアルコール、メチルセロソルブ、エチルセロソルブ、ジメチルホルムアミド、酢酸エチルなど任意の水混和性有機溶媒を用いてよい。塗布液の溶媒の水含有率は50質量%以上、より好ましくは70質量%以上が好ましい。好ましい溶媒組成の例を挙げると、水の他、水/メチルアルコール=90/10、水/メチルアルコール=70/30、水/メチルアルコール/ジメチルホルムアミド=80/15/5、水/メチルアルコール/エチルセロソルブ=85/10/5、水/メチルアルコール/イソプロピルアルコール=85/10/5などがある(数値は質量%)。
【0075】
本発明に用いることのできるカブリ防止剤、安定剤および安定剤前駆体としては特開平10-62899号公報の段落番号0070、欧州特許公開第0803764A1号公報の第20頁第57行〜第21頁第7行に記載の特許のものが挙げられる。また、本発明に好ましく用いられるカブリ防止剤は有機ハロゲン化物であり、これらについては、特開平11-65021号公報の段落番号0111〜0112に記載の特許に開示されているものが挙げられる。特に特願平11-87297号明細書の式(P)で表される有機ハロゲン化合物、特開平10-339934号公報の一般式(II)で表される有機ポリハロゲン化合物が好ましい。
【0076】
以下、本発明で好ましい有機ポリハロゲン化合物について具体的に説明する。本発明で好ましいポリハロゲン化合物は下記一般式(III)で表される化合物である。
一般式(III): Q−(Y)n−C(Z1)(Z2)X
一般式(III)において、Qは置換されていてもよいアルキル基、アリール基またはヘテロ環基を表し、Yは2価の連結基を表し、nは0または1を表し、Z1およびZ2はハロゲン原子を表し、Xは水素原子または電子吸引性基を表す。
一般式(III)において、Qは好ましくはハメットのσpが正の値をとる電子吸引性基で置換されたフェニル基を表す。具体的には、シアノ基、アルコキシカルボニル基、アリールオキシカルボニル基、カルバモイル基、スルファモイル基、アルキルスルホニル基、アリールスルホニル基、スルホキシド基、アシル基、ヘテロ環基、ハロゲン原子、ハロゲン化アルキル基、ホスホリル基等があげられる。σp値としては好ましくは0.2〜2.0の範囲で、より好ましくは0.4から1.0の範囲である。電子吸引性基として特に好ましいのは、カルバモイル基、アルコキシカルボニル基、アルキルスルホニル基、アルキルホスホリル基で、なかでもカルバモイル基が最も好ましい。
以下に本発明で用いる一般式(III)の化合物の具体例を示す。
【0077】
【化11】
【0078】
【化12】
【0079】
【化13】
【0080】
本発明において、カブリ防止剤を画像記録材料に含有せしめる方法としては、前記還元剤の含有方法に記載の方法が挙げられ、有機ポリハロゲン化合物についても固体微粒子分散物で添加することが好ましい。
その他のカブリ防止剤としては特開平11-65021号公報段落番号0113の水銀(II)塩、同号段落番号0114の安息香酸類、特願平11-87297号明細書の式(Z)で表されるサリチル酸誘導体、特願平11-23995号明細書の式(S)で表されるホルマリンスカベンジャー化合物、特開平11-352624号公報の請求項9に係るトリアジン化合物、特開平6-11791号公報の一般式(III)で表される化合物、4-ヒドロキシ-6-メチル-1,3,3a,7-テトラザインデン等が挙げられる。
【0081】
本発明の熱現像画像記録材料はカブリ防止を目的としてアゾリウム塩を含有しても良い。アゾリウム塩としては、特開昭59-193447号公報記載の一般式(XI)で表される化合物、特公昭55-12581号公報記載の化合物、特開昭60-153039号公報記載の一般式(II)で表される化合物が挙げられる。アゾリウム塩は感光材料のいかなる部位に添加しても良いが、添加層としては感光性層を有する面の層に添加することが好ましく、有機銀塩含有層に添加することがさらに好ましい。アゾリウム塩の添加時期としては塗布液調製のいかなる工程で行っても良く、有機銀塩含有層に添加する場合は有機銀塩調製時から塗布液調製時のいかなる工程でも良いが有機銀塩調製後から塗布直前が好ましい。アゾリウム塩の添加法としては粉末、溶液、微粒子分散物などいかなる方法で行っても良い。また、増感色素、還元剤、色調剤など他の添加物と混合した溶液として添加しても良い。本発明においてアゾリウム塩の添加量としてはいかなる量でも良いが、銀1モル当たり1×10-6モル〜2モルが好ましく、1×10-3モル〜0.5モルがさらに好ましい。
【0082】
本発明には現像を抑制あるいは促進させ現像を制御するため、分光増感効率を向上させるため、現像前後の保存性を向上させるためなどにメルカプト化合物、ジスルフィド化合物、チオン化合物を含有させることができ、特開平10-62899号公報の段落番号0067〜0069、特開平10-186572号公報の一般式(I)で表される化合物及びその具体例として段落番号0033〜0052、欧州特許公開第0803764A1号公報の第20ページ第36〜56行、特願平11-273670号明細書等に記載されている。中でもメルカプト置換複素芳香族化合物が好ましい。
【0083】
本発明の熱現像画像記録材料では色調剤の添加が好ましく、色調剤については、特開平10-62899号公報の段落番号0054〜0055、欧州特許公開第0803764A1号公報の第21ページ第23〜48行、特開2000−35631号公報に記載されており、特に、フタラジノン類(フタラジノン、フタラジノン誘導体もしくは金属塩;例えば4-(1-ナフチル)フタラジノン、6-クロロフタラジノン、5,7-ジメトキシフタラジノンおよび2,3-ジヒドロ-1,4-フタラジンジオン);フタラジノン類とフタル酸類(例えば、フタル酸、4-メチルフタル酸、4-ニトロフタル酸およびテトラクロロ無水フタル酸)との組合せ;フタラジン類(フタラジン、フタラジン誘導体もしくは金属塩;例えば4-(1-ナフチル)フタラジン、6-イソプロピルフタラジン、6-t-ブチルフラタジン、6-クロロフタラジン、5,7-ジメトキシフタラジンおよび2,3-ジヒドロフタラジン);フタラジン類とフタル酸類との組合せが好ましく、特にフタラジン類とフタル酸類の組合せが好ましい。
【0084】
本発明の熱現像画像記録材料における感光性層に用いることのできる可塑剤および潤滑剤については特開平11-65021号公報の段落番号0117、超硬調画像形成のための超硬調化剤やその添加方法や量については、同号段落番号0118、特開平11-223898号公報の段落番号0136〜0193、特願平11-87297号明細書の式(H)、式(1)〜(3)、式(A)、(B)の化合物、特願平11-91652号明細書記載の一般式(III)〜(V)の化合物(具体的化合物:化21〜化24)、硬調化促進剤については特開平11-65021号公報段落番号0102、特開平11-223898号公報段落番号0194〜0195に記載されている。
蟻酸や蟻酸塩を強いかぶらせ物質として用いるには、感光性ハロゲン化銀を含有する画像形成層を有する側に銀1モル当たり5ミリモル以下、さらには1ミリモル以下で含有することが好ましい。
【0085】
本発明の熱現像画像記録材料において超硬調化剤を用いる場合には五酸化二リンが水和してできる酸またはその塩を併用して用いることが好ましい。五酸化二リンが水和してできる酸またはその塩としては、メタリン酸(塩)、ピロリン酸(塩)、オルトリン酸(塩)、三リン酸(塩)、四リン酸(塩)、ヘキサメタリン酸(塩)などを挙げることができる。特に好ましく用いられる五酸化二リンが水和してできる酸またはその塩としては、オルトリン酸(塩)、ヘキサメタリン酸(塩)を挙げることができる。具体的な塩としてはオルトリン酸ナトリウム、オルトリン酸二水素ナトリウム、ヘキサメタリン酸ナトリウム、ヘキサメタリン酸アンモニウムなどがある。
五酸化二リンが水和してできる酸またはその塩の使用量(画像記録材料1m2あたりの塗布量)は感度やカブリなどの性能に合わせて所望の量でよいが、0.1〜500mg/m2が好ましく、0.5〜100mg/m2がより好ましい。
【0086】
本発明の熱現像画像記録材料は画像形成層の付着防止などの目的で表面保護層を設けることができる。表面保護層は単層でもよいし、複数層であってもよい。表面保護層については、特開平11-65021号公報の段落番号0119〜0120に記載されている。
表面保護層のバインダーとしてはゼラチンが好ましいが、ポリビニルアルコール(PVA)を用いることも好ましい。ゼラチンとしてはイナートゼラチン(例えば新田ゼラチン750)、フタル化ゼラチン(例えば新田ゼラチン801)など使用することができる。PVAとしては、完全けん化物のPVA−105、部分けん化物のPVA−205、PVA−335、変性ポリビニルアルコールのMP−203(以上、クラレ(株)製の商品名)などが挙げられる。保護層(1層当たり)のポリビニルアルコール塗布量(支持体1m2当たり)としては0.3〜4.0g/m2が好ましく、0.3〜2.0g/m2がより好ましい。
【0087】
特に寸法変化が問題となる印刷用途に本発明の熱現画像記録材料を用いる場合には、表面保護層やバック層にポリマーラテックスを用いることが好ましい。このようなポリマーラテックスについては「合成樹脂エマルジョン(奥田平、稲垣寛編集、高分子刊行会発行(1978))」、「合成ラテックスの応用(杉村孝明、片岡靖男、鈴木聡一、笠原啓司編集、高分子刊行会発行(1993))」、「合成ラテックスの化学(室井宗一著、高分子刊行会発行(1970))」などにも記載され、具体的にはメチルメタクリレート(33.5質量%)/エチルアクリレート(50質量%)/メタクリル酸(16.5質量%)コポリマーのラテックス、メチルメタクリレート(47.5質量%)/ブタジエン(47.5質量%)/イタコン酸(5質量%)コポリマーのラテックス、エチルアクリレート/メタクリル酸のコポリマーのラテックス、メチルメタクリレート(58.9質量%)/2−エチルヘキシルアクリレート(25.4質量%)/スチレン(8.6質量%)/2−ヒドロキシエチルメタクリレート(5.1質量%)/アクリル酸(2.0質量%)コポリマーのラテックス、メチルメタクリレート(64.0質量%)/スチレン(9.0質量%)/ブチルアクリレート(20.0質量%)/2−ヒドロキシエチルメタクリレート(5.0質量%)/アクリル酸(2.0質量%)コポリマーのラテックスなどが挙げられる。さらに、表面保護層用のバインダーとして、特願平11-6872号明細書のポリマーラテックスの組合せ、特願平11-143058号明細書の段落番号0021〜0025に記載の技術、特願平11-6872号明細書の段落番号0027〜0028に記載の技術、特開2000-19678号公報の段落番号0023〜0041に記載の技術を適用してもよい。表面保護層のポリマーラテックスの比率は全バインダーの10質量%〜90質量%が好ましく、特に20質量%〜80質量%が好ましい。
表面保護層(1層当たり)の全バインダー(水溶性ポリマー及びラテックスポリマーを含む)塗布量(支持体1m2当たり)としては0.3〜5.0g/m2が好ましく、0.3〜2.0g/m2がより好ましい。
【0088】
画像形成層塗布液の調製温度は30℃〜65℃がよく、さらに好ましい温度は35℃以上60℃未満、より好ましい温度は35℃〜55℃である。また、ポリマーラテックス添加直後の画像形成層塗布液の温度が30℃〜65℃で維持されることが好ましい。また、ポリマーラテックス添加前に還元剤と有機銀塩が混合されていることが好ましい。
【0089】
本発明における画像形成層は、支持体上に一またはそれ以上の層で構成される。一層で構成する場合は有機銀塩、感光性ハロゲン化銀、還元剤およびバインダーよりなり、必要により色調剤、被覆助剤および他の補助剤などの所望による追加の材料を含む。二層以上で構成する場合は、第1画像形成層(通常は支持体に隣接した層)中に有機銀塩および感光性ハロゲン化銀を含み、第2画像形成層または両層中にいくつかの他の成分を含まなければならない。多色感光性熱現像写真材料の構成は、各色についてこれらの二層の組合せを含んでよく、また、米国特許第4,708,928号明細書に記載されているように単一層内に全ての成分を含んでいてもよい。多染料多色感光性熱現像写真材料の場合、各乳剤層は、一般に、米国特許第4,460,681号明細書に記載されているように、各感光性層の間に官能性もしくは非官能性のバリアー層を使用することにより、互いに区別されて保持される。
【0090】
感光性層には色調改良、レーザー露光時の干渉縞発生防止、イラジエーション防止の観点から各種染料や顔料(例えばC.I.Pigment Blue 60、C.I.Pigment Blue 64、C.I.Pigment Blue 15:6)を用いることができる。これらについては国際公開WO98/36322号公報、特開平10-268465号公報、同11-338098号公報等に詳細に記載されている。
本発明の熱現像画像記録材料においては、アンチハレーション層を感光性層に対して光源から遠い側に設けることができる。
熱現像画像記録材料は一般に、感光性層に加えて非感光性層を有する。非感光性層は、その配置から(1)感光性層の上(支持体よりも遠い側)に設けられる保護層、(2)複数の感光性層の間や感光性層と保護層の間に設けられる中間層、(3)感光性層と支持体との間に設けられる下塗り層、(4)感光性層の反対側に設けられるバック層に分類できる。フィルター層は、(1)または(2)の層として感光材料に設けられる。アンチハレーション層は、(3)または(4)の層として感光材料に設けられる。
【0091】
アンチハレーション層については特開平11-65021号公報の段落番号0123〜0124、特開平11-223898号公報、同9-230531号公報、同10-36695号公報、同10-104779号公報、同11-231457号公報、同11-352625号公報、同11-352626号公報等に記載されている。
アンチハレーション層には、露光波長に吸収を有するアンチハレーション染料を含有する。露光波長が赤外域にある場合には赤外線吸収染料を用いればよく、その場合には可視域に吸収を有しない染料が好ましい。
可視域に吸収を有する染料を用いてハレーション防止を行う場合には、画像形成後には染料の色が実質的に残らないようにすることが好ましく、熱現像の熱により消色する手段を用いることが好ましく、特に非感光性層に熱消色染料と塩基プレカーサーとを添加してアンチハレーション層として機能させることが好ましい。これらの技術については特開平11-231457号公報等に記載されている。
【0092】
消色染料の添加量は、染料の用途により決定する。一般には、目的とする波長で測定したときの光学濃度(吸光度)が0.1を越える量で使用する。光学濃度は、0.2〜2であることが好ましい。このような光学濃度を得るための染料の使用量は、一般に0.001〜1g/m2程度である。
なお、このように染料を消色すると、熱現像後の光学濃度を0.1以下に低下させることができる。二種類以上の消色染料を、熱消色型記録材料や熱現像感光材料において併用してもよい。同様に、二種類以上の塩基プレカーサーを併用してもよい。
このような消色染料と塩基プレカーサーを用いる熱消色においては、特開平11-352626号公報に記載のような塩基プレカーサーと混合すると融点を3℃(deg)以上降下させる物質(例えば、ジフェニルスルホン、4-クロロフェニル(フェニル)スルホン)を併用することが熱消色性等の点で好ましい。
【0093】
本発明においては、銀色調、画像の経時変化を改良する目的で300〜450nmに吸収極大を有する着色剤を添加することができる。このような着色剤は、特開昭62-210458号公報、同63-104046号公報、同63-103235号公報、同63-208846号公報、同63-306436号公報、同63-314535号公報、特開平01-61745号公報、特願平11-276751号明細書などに記載されている。
このような着色剤は、通常、0.1mg/m2〜1g/m2の範囲で添加され、添加する層としては感光性層の反対側に設けられるバック層が好ましい。
【0094】
本発明の熱現像画像記録材料は、支持体の一方の側に少なくとも1層のハロゲン化銀乳剤を含む感光性層を有し、他方の側にバック層を有する、いわゆる片面感光材料であることが好ましい。
本発明において、搬送性改良のためにマット剤を添加することが好ましく、マット剤については、特開平11-65021号公報の段落番号0126〜0127に記載されている。マット剤は画像記録材料1m2当たりの塗布量で示した場合、好ましくは1〜400mg/m2、より好ましくは5〜300mg/m2である。
また、乳剤面のマット度は星屑故障が生じなければいかようでも良いが、ベック平滑度が30秒〜2000秒が好ましく、特に40秒〜1500秒が好ましい。ベック平滑度は、日本工業規格(JIS)P8119「紙および板紙のベック試験器による平滑度試験方法」およびTAPPI標準法T479により容易に求めることができる。
【0095】
本発明においてバック層のマット度としてはベック平滑度が1200秒〜10秒が好ましく、800秒〜20秒が好ましく、さらに好ましくは500秒〜40秒である。
本発明において、マット剤は画像記録材料の最外表面層もしくは最外表面層として機能する層、あるいは外表面に近い層に含有されるのが好ましく、またいわゆる保護層として作用する層に含有されることが好ましい。
本発明に適用することのできるバック層については特開平11-65021号公報の段落番号0128〜0130に記載されている。
【0096】
本発明の熱現像感光材料は、熱現像処理前の膜面pHが6.0以下であることが好ましく、さらに好ましくは5.5以下である。その下限には特に制限はないが、3程度である。膜面pHの調節はフタル酸誘導体などの有機酸や硫酸などの不揮発性の酸、アンモニアなどの揮発性の塩基を用いることが、膜面pHを低減させるという観点から好ましい。特にアンモニアは揮発しやすく、塗布する工程や熱現像される前に除去できることから低膜面pHを達成する上で好ましい。なお、膜面pHの測定方法は、特願平11-87297号明細書の段落番号0123に記載されている。
【0097】
本発明における感光性層、保護層、バック層など各層には硬膜剤を用いても良い。硬膜剤の例としてはT.H.James著“THE THEORY OF THE PHOTOGRAPHIC PROCESS FOURTH EDITION”(Macmillan Publishing Co., Inc.刊、1977年刊)77頁から87頁に記載の各方法があり、クロムみょうばん、2,4-ジクロロ-6-ヒドロキシ-s-トリアジンナトリウム塩、N,N-エチレンビス(ビニルスルホンアセトアミド)、N,N-プロピレンビス(ビニルスルホンアセトアミド)の他、同書78頁など記載の多価金属イオン、米国特許4,281,060号明細書、特開平6-208193号公報などのポリイソシアネート類、米国特許4,791,042号明細書などのエポキシ化合物類、特開昭62-89048号公報などのビニルスルホン系化合物類が好ましく用いられる。
【0098】
硬膜剤は溶液として添加され、この溶液の保護層塗布液中への添加時期は、塗布する180分前から直前、好ましくは60分前から10秒前であるが、混合方法及び混合条件については本発明の効果が十分に現れる限りにおいては特に制限はない。具体的な混合方法としては添加流量とコーターへの送液量から計算した平均滞留時間を所望の時間となるようにしたタンクでの混合する方法やN.Harnby、M.F.Edwards、A.W.Nienow著、高橋幸司訳“液体混合技術”(日刊工業新聞社刊、1989年)の第8章等に記載されているスタチックミキサーなどを使用する方法がある。
【0099】
本発明に適用できる界面活性剤については特開平11-65021号公報の段落番号0132、溶剤については同号公報の段落番号0133、支持体については同号公報の段落番号0134、帯電防止又は導電層については同号公報の段落番号0135、カラー画像を得る方法については同号公報の段落番号0136に、滑り剤については特開平11-84573号公報の段落番号0061〜0064や特願平11-106881号明細書の段落番号0049〜0062記載されている。
本発明の熱現像画像記録材料は、モノシート型(受像材料のような他のシートを使用せずに、熱現像画像記録材料上に画像を形成できる型)であることが好ましい。
【0100】
本発明の熱現像画像記録材料には、さらに、酸化防止剤、安定化剤、可塑剤、紫外線吸収剤あるいは被覆助剤を添加してもよい。各種の添加剤は、感光性層あるいは非感光性層のいずれかに添加する。それらについて国際公開WO98/36322号公報、欧州特許公開EP803764A1号公報、特開平10-186567号公報、同10-18568号公報等を参考にすることができる。
本発明の熱現像画像記録材料はいかなる方法で塗布されても良い。具体的には、エクストルージョンコーティング、スライドコーティング、カーテンコーティング、浸漬コーティング、ナイフコーティング、フローコーティング、または米国特許第2,681,294号明細書に記載の種類のホッパーを用いる押出コーティングを 含む種々のコーティング操作が用いられ、Stephen F. Kistler、Petert M. Schweizer著“LIQUID FILM COATING”(CHAPMAN & HALL社刊、1997年)399頁から536頁記載のエクストルージョンコーティング、またはスライドコーティング好ましく用いられ、特に好ましくはスライドコーティングが用いられる。スライドコーティングに使用されるスライドコーターの形状の例は同書427頁のFigure 11b.1にある。また、所望により同書399頁から536頁記載の方法、米国特許第2,761,791号明細書および英国特許第837,095号明細書に記載の方法により2層またはそれ以上の層を同時に被覆することができる。
【0101】
本発明における有機銀塩含有層塗布液は、いわゆるチキソトロピー流体であることが好ましい。チキソトロピー性とは剪断速度の増加に伴い、粘度が低下する性質を言う。粘度測定にはいかなる装置を使用してもよいが、レオメトリックスファーイースト株式会社製RFSフルードスペクトロメーターが好ましく用いられ、25℃で測定される。ここで、本発明における有機銀塩含有層塗布液は剪断速度0.1S-1における粘度は400mPa・s〜100,000mPa・sが好ましく、さらに好ましくは500mPa・s〜20,000mPa・sである。また、剪断速度1000S-1においては1mPa・s〜200mPa・sが好ましく、さらに好ましくは5mPa・s〜80mPa・sである。
【0102】
チキソトロピー性を発現する系は各種知られており高分子刊行会編「講座・レオロジー」、室井、森野共著「高分子ラテックス」(高分子刊行会発行)などに記載されている。流体がチキソトロピー性を発現させるには固体微粒子を多く含有することが必要である。また、チキソトロピー性を強くするには増粘線形高分子を含有させること、含有する固体微粒子の異方形でアスペクト比を大きくすること、アルカリ増粘、界面活性剤の使用などが有効である。
本発明の熱現像画像記録材料に用いることのできる技術としては、欧州特許公開EP803764A1号公報、欧州特許公開EP883022A1号公報、国際公開WO98/36322号公報、特開昭56-62648号公報、同58-62644号公報、特開平9-281637号公報、同9-297367号公報、同9-304869号公報、同9-311405号公報、同9-329865号公報、同10-10669号公報、同10-62899号公報、同10-69023号公報、同10-186568号公報、同10-90823号公報、同10-171063号公報、同10-186565号公報、同10-186567号公報、同10-186569号〜同10-186572号公報、同10-197974号公報、同10-197982号公報、同10-197983号公報、同10-197985号〜同10-197987号公報、同10-207001号公報、同10-207004号公報、同10-221807号公報、同10-282601号公報、同10-288823号公報、同10-288824号公報、同10-307365号公報、同10-312038号公報、同10-339934号公報、同11-7100号公報、同11-15105号公報、同11-24200号公報、同11-24201号公報、同11-30832号公報、同11-84574号公報、同11-65021号公報、同11-109547号公報、同11-125880号公報、同11-129629号公報、同11-133536号〜同11-133539号公報、同11-133542号公報、同11-133543号公報、同11-223898号公報、同11-352627号公報も挙げられる。
【0103】
本発明の熱現像画像記録材料はいかなる方法で現像されても良いが、通常イメージワイズに露光した熱現像画像記録材料を昇温して現像される。好ましい現像温度としては80〜250℃であり、さらに好ましくは100〜140℃である。現像時間としては1〜180秒が好ましく、10〜90秒がさらに好ましく、10〜40秒が特に好ましい。
熱現像の方式としてはプレートヒータ方式が好ましい。プレートヒータ方式による熱現像方式とは特開平11-133572号公報に記載の方法が好ましく、潜像を形成した熱現像画像記録材料を熱現像部にて加熱手段に接触させることにより可視像を得る熱現像装置であって、前記加熱手段がプレートヒータからなり、かつ前記プレートヒータの一方の面に沿って複数個の押えローラが対向配設され、前記押えローラと前記プレートヒータとの間に前記熱現像感光材料を通過させて熱現像を行うことを特徴とする熱現像装置である。プレートヒーターを2〜6段に分けて先端部については1〜10℃程度温度を下げることが好ましい。このような方法は特開昭54-30032号公報にも記載されており、熱現像画像記録材料に含有している水分や有機溶媒を系外に除外させることができ、また、急激に熱現像画像記録材料が加熱されることでの熱現像画像記録材料の支持体形状の変化を押えることもできる。
【0104】
本発明の感光材料はいかなる方法で露光されても良いが、露光光源としてレーザー光が好ましい。本発明によるレーザー光としては、ガスレーザー(Ar+、He-Ne)、YAGレーザー、色素レーザー、半導体レーザーなどが好ましい。また、半導体レーザーと第2高調波発生素子などを用いることもできる。好ましくは赤〜赤外発光のガス若しくは半導体レーザーである。
露光部及び熱現像部を備えた医療用のレーザーイメージャーとしては富士メディカルドライレーザーイメージャーFM−DP Lを挙げることができる。FM−DP Lに関しては、Fuji Medical Review No.8,page 39〜55に記載されており、それらの技術は本発明の熱現像感光材料のレーザーイメージャーとして適用することは言うまでもない。また、DICOM規格に適応したネットワークシステムとして富士メディカルシステムが提案した「AD network」の中でのレーザーイメージャー用の熱現像感光材料としても適用することができる。
【0105】
本発明の熱現像画像記録材料は、銀画像による黒白画像を形成し、医療診断用の熱現像感光材料、工業写真用熱現像感光材料、印刷用熱現像感光材料、COM用の熱現像感光材料として使用されることが好ましい。
以下の実施例により本発明をさらに具体的に説明するが、本発明は実施例によって限定されることはない。
【0106】
【実施例】
実施例1
(PET支持体の作成)
テレフタル酸とエチレングリコールを用い、常法に従い固有粘度IV=0.66(フェノール/テトラクロルエタン=6/4(質量比)中25℃で測定)のPETを得た。これをペレット化した後130℃で4時間乾燥し、300℃で溶融後T型ダイから押し出して急冷し、熱固定後の膜厚が175μmになるような厚みの未延伸フィルムを作成した。これを、周速の異なるロ−ルを用い3.3倍に縦延伸、ついでテンターで4.5倍に横延伸を実施した。この時の温度はそれぞれ、110℃、130℃であった。この後、240℃で20秒間熱固定後これと同じ温度で横方向に4%緩和した。この後テンターのチャック部をスリットした後、両端にナール加工を行い、4kg/cm2で巻き取り、厚み175μmのロールを得た。
【0107】
(表面コロナ処理)
ピラー社製ソリッドステートコロナ処理機6KVAモデルを用い、支持体の両面を室温下において20m/分で処理した。この時の電流、電圧の読み取り値から、支持体には0.375kV・A・分/m2の処理がなされていることがわかった。この時の処理周波数は9.6kHz、電極と誘電体ロールのギャップクリアランスは1.6mmであった。
【0108】
(下塗り支持体の作成)
(1)下塗層塗布液の作成
(下塗塗布液Aの調製)
ポリエステル水分散物(種類と添加量は表1参照)にPMMA微粒子(綜研化学社製MP-1000、平均粒子径0.4μ)0.9g、ポリエチレングリコールモノフェニルエーテル(平均エチレンオキシド数=8.5)10質量%溶液4gを添加して、これに蒸留水を加えて1000mlとして、下塗塗布液Aとした。
【0109】
【表1】
【0110】
成分の略号:
TPA:テレフタル酸
IPA:イソフタル酸
IPS:スルホイソフタル酸ナトリウム塩
EG:エチレングリコール
DEG:ジエチレングリコール
CHDM:シクロヘキサンジメタノール
NPG:ネオペンチルグリコール
【0111】
比較例
1.ペスレジンA−515GB(高松油脂(株)製変性水性ポリエステル)
Tg=60℃、固形分濃度=30%、添加量=240g
2.ファインテックスES-675(大日本インキ化学(株)製水性ポリエステル)
Tg=35℃、固形分濃度=37%、添加量=194.6g
3.バイロン200(東洋紡(株)製水性ポリエステル)
(TPA/IPA//EG/NPG=50/50//50/50(mol%))、
Tg=67℃、固形分濃度=40%になるようにトルエン/MEK(=4/1質量比)に溶解、添加量=180g
A.特開昭56-95959(アグファ)記載のコポリエステルNo.13
(TPA/IPA/IPS//EG=50/40/10//100(mol%))B.特公昭62-21380(東洋紡)記載のポリエステル樹脂A−2
(TPA/IPS//DEG=93/7//100(mol%))
【0112】
(バック面第1層塗布液処方)
ブタジエン−スチレン共重合体ラテックス:131g
(固形分40質量%、ブタジエン/スチレン質量比=32/68)
2,4-ジクロロ-6-ヒドロキシ-S-トリアジンナトリウム塩8質量%水溶液:5gポリスチレン粒子(平均粒子径2μ)20質量%水分散物:0.5g
蒸留水:863.5ml
【0113】
(バック面第2層塗布液処方)
SnO2/Sb2O3(9/1質量比、平均粒子径0.04μ、17質量%分散物):62gゼラチン(10%水溶液):66g
信越化学社製 メトローズTC-5(2%水溶液):6g
プロキセル(ICI社製)0.5ml
蒸留水:865.5ml
【0114】
(下塗り支持体の作成)
上記厚さ175μmの2軸延伸ポリエチレンテレフタレート支持体の両面それぞれに、上記コロナ放電処理を施した後、片面(感光性層面)に上記下塗り塗布液処方Aをワイヤーバーでウエット塗布量が6.6ml/m2(片面当たり)になるように塗布して180℃で5分間乾燥し、ついでこの裏面(バック面)に上記バック面第1層塗布液処方をワイヤーバーでウエット塗布量が5.7ml/m2になるように塗布して180℃で5分間乾燥し、更に裏面(バック面)に上記第2層塗布液処方をワイヤーバーでウエット塗布量が7.7ml/m2になるように塗布して180℃で6分間乾燥して下塗り支持体を作成した。
【0115】
(バック面塗布液の調製)
(塩基プレカーサーの固体微粒子分散液(a)の調製)
塩基プレカーサー化合物11を64g、ジフェニルスルホンを28gおよび花王(株)製界面活性剤デモールN 10gを蒸留水220mlと混合し、混合液をサンドミル(1/4 Gallonサンドグラインダーミル、アイメックス(株)製)を用いてビーズ分散し、平均粒子径0.2μmの塩基プレカーサー化合物の固体微粒子分散液(a)を得た。
【0116】
(染料固体微粒子分散液の調製)
シアニン染料化合物13を9.6gおよびp−ドデシルベンゼンスルホン酸ナトリウム5.8gを蒸留水305mlと混合し、混合液をサンドミル(1/4 Gallonサンドグラインダーミル、アイメックス(株)製)を用いてビーズ分散して平均粒子径0.2μmの染料固体微粒子分散液を得た。
【0117】
(ハレーション防止層塗布液の調製)
ゼラチン17g、ポリアクリルアミド9.6g、上記塩基プレカーサーの固体微粒子分散液(a)70g、上記染料固体微粒子分散液56g、ポリメチルメタクリレート微粒子(平均粒子サイズ6.5μm)1.5g、ベンゾイソチアゾリノン0.03g、ポリエチレンスルホン酸ナトリウム2.2g、青色染料化合物14を0.2g、黄色染料化合物15を3.9g、水を844ml混合し、ハレーション防止層塗布液を調製した。
【0118】
【化14】
【0119】
【化15】
【0120】
(バック面保護層塗布液の調製)
容器を40℃に保温し、ゼラチン50g、ポリスチレンスルホン酸ナトリウム0.2g、N,N-エチレンビス(ビニルスルホンアセトアミド)2.4g、t-オクチルフェノキシエトキシエタンスルホン酸ナトリウム1g、ベンゾイソチアゾリノン30mg、N-パーフルオロオクチルスルホニル-N-プロピルアラニンカリウム塩37mg、ポリエチレングリコールモノ(N-パーフルオロオクチルスルホニル-N-プロピル-2-アミノエチル)エーテル[エチレンオキサイド平均重合度15]0.15g、C8F17SO3K 32mg、C8F17SO2N(C3H7)(CH2CH2O)4(CH2)4-SO3Na 64mg、アクリル酸/エチルアクリレート共重合体(共重合質量比5/95)8.8g、エアロゾールOT(アメリカンサイアナミド社製)0.6g、流動パラフィン乳化物を流動パラフィンとして1.8g、水を950ml混合してバック面保護層塗布液とした。
【0121】
《ハロゲン化銀乳剤1の調製》
蒸留水1421mlに1質量%臭化カリウム溶液3.1mlを加え、さらに0.5mol/Lの硫酸を3.5ml、フタル化ゼラチン31.7gを添加した液をステンレス製反応壺中で攪拌しながら、34℃に液温を保ち、硝酸銀22.22gに蒸留水を加え95.4mlに希釈した溶液Aと臭化カリウム15.9gを蒸留水にて容量97.4mlに希釈した溶液Bを一定流量で45秒間かけて全量添加した。その後、3.5質量%の過酸化水素水溶液を10ml添加し、さらにベンツイミダゾールの10質量%水溶液を10.8ml添加した。さらに、硝酸銀51.86gに蒸留水を加えて317.5mlに希釈した溶液Cと臭化カリウム45.8gを蒸留水にて容量400mlに希釈した溶液Dを、溶液Cは一定流量で20分間かけて全量添加し、溶液DはpAgを8.1に維持しながらコントロールドダブルジェット法で添加した。銀1モル当たり1×10-4モルになるよう六塩化イリジウム(III)酸カリウム塩を溶液Cおよび溶液Dを添加しはじめてから10分後に全量添加した。また、溶液Cの添加終了の5秒後に六シアン化鉄(II)カリウム水溶液を銀1モル当たり3×10-4モル全量添加した。0.5mol/Lの硫酸を用いてpHを3.8に調整し、攪拌を止め、沈降/脱塩/水洗工程をおこなった。1mol/Lの水酸化ナトリウムを用いてpH5.9に調整し、pAg8.0のハロゲン化銀分散物を作成した。
【0122】
上記ハロゲン化銀分散物を攪拌しながら38℃に維持して、0.34質量%の1,2-ベンゾイソチアゾリン-3-オンのメタノール溶液を5ml加え、40分後に分光増感色素Aのメタノール溶液を銀1モル当たり1×10-3モル加え、1分後に47℃に昇温した。昇温の20分後にベンゼンチオスルホン酸ナトリウムをメタノール溶液で銀1モルに対して7.6×10-5モル加え、さらに5分後にテルル増感剤Bをメタノール溶液で銀1モル当たり1.9×10-4モル加えて91分間熟成した。N,N'-ジヒドロキシ-N"-ジエチルメラミンの0.8質量%メタノール溶液1.3mlを加え、さらに4分後に、5-メチル-2-メルカプトベンヅイミダゾールをメタノール溶液で銀1モル当たり3.7×10-3モル及び1-フェニル-2-ヘプチル-5-メルカプト-1,3,4-トリアゾールをメタノール溶液で銀1モルに対して4.9×10-3モル添加して、ハロゲン化銀乳剤1を作成した。
【0123】
調製できたハロゲン化銀乳剤中の粒子は、平均球相当径0.046μm、球相当径の変動係数20%の純臭化銀粒子であった。粒子サイズ等は、電子顕微鏡を用い1000個の粒子の平均から求めた。この粒子の[100]面比率は、クベルカムンク法を用いて80%と求められた。
【0124】
《ハロゲン化銀乳剤2の調製》
ハロゲン化銀乳剤1の調製において、粒子形成時の液温34℃を49℃に変更し、溶液Cの添加時間を30分にして、六シアノ鉄(II)カリウムを除去した以外は同様にして、ハロゲン化銀乳剤2の調製を行った。ハロゲン化銀乳剤1と同様に沈殿/脱塩/水洗/分散を行った。更に分光増感色素Aの添加量を銀1モル当たり7.5×10-4モル、テルル増感剤Bの添加量を銀1モル当たり1.1×10-4モル、1-フェニル-2-ヘプチル-5-メルカプト-1,3,4-トリアゾールを銀1モルに対して3.3×10-3モルに変えた以外は乳剤1と同様にして分光増感、化学増感及び5-メチル-2-メルカプトベンヅイミダゾール、1-フェニル-2-ヘプチル-5-メルカプト-1,3,4-トリアゾールの添加を行い、ハロゲン化銀乳剤2を得た。ハロゲン化銀乳剤2の乳剤粒子は、平均球相当径0.080μm、球相当径の変動係数20%の純臭化銀立方体粒子であった。
【0125】
《ハロゲン化銀乳剤3の調製》
ハロゲン化銀乳剤1の調製において、粒子形成時の液温34℃を27℃に変更する以外は同様にして、ハロゲン化銀乳剤3の調製を行った。また、ハロゲン化銀乳剤1と同様に沈殿/脱塩/水洗/分散を行った。分光増感色素Aを固体分散物(ゼラチン水溶液)で添加量を銀1モル当たり6×10-3モル、テルル増感剤Bの添加量を銀1モル当たり5.2×10-4モルに変えた以外は乳剤1と同様にして、ハロゲン化銀乳剤3を得た。ハロゲン化銀乳剤3の乳剤粒子は、平均球相当径0.038μm、球相当径の変動係数20%の純臭化銀立方体粒子であった。
【0126】
《塗布液用混合乳剤Aの調製》
ハロゲン化銀乳剤1を70質量%、ハロゲン化銀乳剤2を15質量%、ハロゲン化銀乳剤3を15質量%溶解し、ベンゾチアゾリウムヨーダイドを1質量%水溶液にて銀1モル当たり7×10-3モル添加した。
【0127】
《脂肪酸銀分散物の調製》
ヘンケル社製ベヘン酸(製品名Edenor C22-85R)87.6kg、蒸留水423リットル、5mol/LのNaOH水溶液49.2リットル、tert-ブタノール120リットルを混合し、75℃にて1時間攪拌し反応させ、ベヘン酸ナトリウム溶液を得た。別に、硝酸銀40.4kgの水溶液206.2リットル(pH4.0)を用意し、10℃にて保温した。635リットルの蒸留水と30リットルのtert−ブタノールを入れた反応容器を30℃に保温し、撹拌しながら先のベヘン酸ナトリウム溶液の全量と硝酸銀水溶液の全量を流量一定でそれぞれ62分10秒と60分かけて添加した。このとき、硝酸銀水溶液添加開始後7分20秒間は硝酸銀水溶液のみが添加されるようにし、そのあとベヘン酸ナトリウム溶液を添加開始し、硝酸銀水溶液の添加終了後9分30秒間はベヘン酸ナトリウム溶液のみが添加されるようにした。このとき、反応容器内の温度は30℃とし、液温度が一定になるように外温コントロールした。また、ベヘン酸ナトリウム溶液の添加系の配管は、スチームトレースにより保温し、添加ノズル先端の出口の液温度が75℃になるようにスチーム開度を調製した。また、硝酸銀水溶液の添加系の配管は、2重管の外側に冷水を循環させることにより保温した。ベヘン酸ナトリウム溶液の添加位置と硝酸銀水溶液の添加位置は撹拌軸を中心として対称的な配置とし、また反応液に接触しないような高さに調整した。
【0128】
ベヘン酸ナトリウム溶液を添加終了後、そのままの温度で20分間撹拌放置し、25℃に降温した。その後、吸引濾過で固形分を濾別し、固形分を濾過水の伝導度が30μS/cmになるまで水洗した。こうして脂肪酸銀塩を得た。得られた固形分は、乾燥させないでウエットケーキとして保管した。
得られたベヘン酸銀粒子の形態を電子顕微鏡撮影により評価したところ、平均値でa=0.14μm、b=0.4μm、c=0.6μm、平均アスペクト比5.2、平均球相当径0.52μm、球相当径の変動係数15%のりん片状結晶であった(a,b,cは本文の規定)。
【0129】
乾燥固形分100g相当のウエットケーキに対し、ポリビニルアルコール(商品名:PVA-217)7.4gおよび水を添加し、全体量を385gとしてからホモミキサーにて予備分散した。
次に予備分散済みの原液を分散機(商品名:マイクロフルイダイザーM−110S−EH、マイクロフルイデックス・インターナショナル・コーポレーション製、G10Zインタラクションチャンバー使用)の圧力を1750kg/cm2に調節して、三回処理し、ベヘン酸銀分散物を得た。冷却操作は蛇管式熱交換器をインタラクションチャンバーの前後に各々装着し、冷媒の温度を調節することで18℃の分散温度に設定した。
【0130】
《還元剤の25質量%分散物の調製》
1,1-ビス(2-ヒドロキシ-3,5-ジメチルフェニル)-3,5,5-トリメチルヘキサン10kgと変性ポリビニルアルコール(クラレ(株)製、ポバールMP203)の20質量%水溶液10kgに、水16kgを添加して、良く混合してスラリーとした。このスラリーをダイアフラムポンプで送液し、平均直径0.5mmのジルコニアビーズを充填した横型サンドミル(UVM−2:アイメックス(株)製)にて3時間30分間分散したのち、ベンゾイソチアゾリノンナトリウム塩0.2gと水を加えて還元剤の濃度が25質量%になるように調整し、還元剤分散物を得た。こうして得た還元剤分散物に含まれる還元剤粒子はメジアン径0.42μm、最大粒子径2.0μm以下であった。得られた還元剤分散物は孔径10.0μmのポリプロピレン製フィルターにて濾過を行い、ゴミ等の異物を除去して収納した。
【0131】
《還元剤錯体の25質量%分散物の調製》
2,2-メチレンビス-(4-エチル-6-tert-ブチルフェノール)とトリフェニルホスフィンオキシドの1:1錯体10kgと変性ポリビニルアルコール(クラレ(株)製、ポバールMP203)の20質量%水溶液10kgに、水16kgを添加して、良く混合してスラリーとした。このスラリーをダイアフラムポンプで送液し、平均直径0.5mmのジルコニアビーズを充填した横型サンドミル(UVM−2:アイメックス(株)製)にて3時間30分間分散したのち、ベンゾイソチアゾリノンナトリウム塩0.2gと水を加えて還元剤の濃度が25質量%になるように調整し、還元剤錯体分散物を得た。こうして得た還元剤錯体分散物に含まれる還元剤錯体粒子はメジアン径0.46μm、最大粒子径2.0μm以下であった。得られた還元剤錯体分散物は孔径10.0μmのポリプロピレン製フィルターにて濾過を行い、ゴミ等の異物を除去して収納した。
【0132】
《メルカプト化合物の10質量%分散物の調製》
1-フェニル-2-ヘプチル-5-メルカプト-1,3,4-トリアゾールを5kgと変性ポリビニルアルコール(クラレ(株)製ポバールMP203)の20質量%水溶液5kgに、水8.3kgを添加して、良く混合してスラリーとした。このスラリーをダイアフラムポンプで送液し、平均直径0.5mmのジルコニアビーズを充填した横型サンドミル(UVM−2:アイメックス(株)製)にて6時間分散したのち、水を加えてメルカプト化合物の濃度が10質量%になるように調整し、メルカプト分散物を得た。こうして得たメルカプト化合物分散物に含まれるメルカプト化合物粒子はメジアン径0.40μm、最大粒子径2.0μm以下であった。得られたメルカプト化合物分散物は孔径10.0μmのポリプロピレン製フィルターにて濾過を行い、ゴミ等の異物を除去して収納した。また、使用直前に再度孔径10μmのポリプロピレン製フィルターにてろ過した。
【0133】
《有機ポリハロゲン化合物の20質量%分散物−1の調製》
トリブロモメチルナフチルスルホン5kgと変性ポリビニルアルコール(クラレ(株)製ポバールMP203)の20質量%水溶液2.5kgと、トリイソプロピルナフタレンスルホン酸ナトリウムの20質量%水溶液213gと、水10kgを添加して、良く混合してスラリーとした。このスラリーをダイアフラムポンプで送液し、平均直径0.5mmのジルコニアビーズを充填した横型サンドミル(UVM−2:アイメックス(株)製)にて5時間分散したのち、ベンゾイソチアゾリノンナトリウム塩0.2gと水を加えて有機ポリハロゲン化合物の濃度が20質量%になるように調整し、有機ポリハロゲン化合物分散物を得た。こうして得たポリハロゲン化合物分散物に含まれる有機ポリハロゲン化合物粒子はメジアン径0.36μm、最大粒子径2.0μm以下であった。得られた有機ポリハロゲン化合物分散物は孔径3.0μmのポリプロピレン製フィルターにて濾過を行い、ゴミ等の異物を除去して収納した。
【0134】
《有機ポリハロゲン化合物の25質量%分散物−2の調製》
有機ポリハロゲン化合物の20質量%分散物−1と同様に、但し、トリブロモメチルナフチルスルホン5kgの代わりにトリブロモメチル(4-(2,4,6-トリメチルフェニルスルホニル)フェニル)スルホン5kgを用い、分散し、この有機ポリハロゲン化合物が25質量%となるように希釈し、濾過を行った。こうして得た有機ポリハロゲン化合物分散物に含まれる有機ポリハロゲン化合物粒子はメジアン径0.38μm、最大粒子径2.0μm以下であった。得られた有機ポリハロゲン化合物分散物は孔径3.0μmのポリプロピレン製フィルターにて濾過を行い、ゴミ等の異物を除去して収納した。
【0135】
《有機ポリハロゲン化合物の26質量%分散物−3の調製》
有機ポリハロゲン化合物の20質量%分散物−1と同様に、但し、トリブロモメチルナフチルスルホン5kgの代わりにトリブロモメチルフェニルスルホン5kgを用い、20質量%MP203水溶液を5kgとし、分散し、この有機ポリハロゲン化合物が26質量%となるように希釈し、濾過を行った。こうして得た有機ポリハロゲン化合物分散物に含まれる有機ポリハロゲン化合物粒子はメジアン径0.41μm、最大粒子径2.0μm以下であった。得られた有機ポリハロゲン化合物分散物は孔径3.0μmのポリプロピレン製フィルターにて濾過を行い、ゴミ等の異物を除去して収納した。また、収納後、使用までは10℃以下で保管した。
【0136】
《有機ポリハロゲン化合物の25質量%分散物−4の調製》
有機ポリハロゲン化合物の20質量%分散物−1と同様に、但し、トリブロモメチルナフチルスルホン5kgの代わりにトリブロモメチル−3−ペンタノイルアミノフェニルスルホン5kgを用い、分散し、この有機ポリハロゲン化合物が25質量%となるように希釈し、濾過を行った。こうして得た有機ポリハロゲン化合物分散物に含まれる有機ポリハロゲン化合物粒子はメジアン径0.41μm、最大粒子径2.0μm以下であった。得られた有機ポリハロゲン化合物分散物は孔径3.0μmのポリプロピレン製フィルターにて濾過を行い、ゴミ等の異物を除去して収納した。
【0137】
《フタラジン化合物の5質量%溶液の調製》
8kgのクラレ(株)製変性ポリビニルアルコールMP203を水174.57Kgに溶解し、次いでトリイソプロピルナフタレンスルホン酸ナトリウムの20質量%水溶液3.15Kgと6-イソプロピルフタラジンの70質量%水溶液14.28Kgを添加し、6-イソプロピルフタラジンの5質量%液を調製した。
【0138】
《顔料の20質量%分散物の調製》
C.I.Pigment Blue 60を64gと花王(株)製デモールNを6.4gに水250gを添加し良く混合してスラリーとした。平均直径0.5mmのジルコニアビーズ800gを用意してスラリーと一緒にベッセルに入れ、分散機(1/4Gサンドグラインダーミル:アイメックス(株)製)にて25時間分散し顔料分散物を得た。こうして得た顔料分散物に含まれる顔料粒子は平均粒径0.21μmであった。
【0139】
《SBRラテックス40質量%の調製》
限外濾過(UF)精製したSBRラテックスは以下のように得た。
下記のSBRラテックスを蒸留水で10倍に希釈したものをUF-精製用モジュールFS03-FC-FUY03A1(ダイセン・メンブレン・システム(株))を用いてイオン伝導度が1.5mS/cmになるまで希釈精製し、三洋化成(株)製サンデット-BLを0.22質量%になるよう添加した。更にNaOHとNH4OHを用いてNa+イオン:NH4 +イオン=1:2.3(モル比)になるように添加し、pH8.4に調整した。この時のラテックス濃度は40質量%であった。
(SBRラテックス:-St(71)-Bu(26)-AA(3)-のラテックス)
平均粒径0.1μm、濃度45質量%、25℃60%相対湿度における平衡含水率0.6質量%、イオン伝導度4.2mS/cm(イオン伝導度の測定は東亜電波工業(株)製伝導度計CM-30S使用し、ラテックス原液(40質量%)を25℃にて測定)、pH8.2。
【0140】
《乳剤層(感光性層)塗布液の調製》
上記で得た顔料の20質量%分散物を1.1g、脂肪酸銀分散物103g、ポリビニルアルコールPVA-205(クラレ(株)製)の20質量%水溶液5g、還元剤の25質量%分散物25g、有機ポリハロゲン化合物分散物-1,-2,-3を5:1:3(質量比)で総量16.3g、メルカプト化合物の10質量%分散物6.2g、限外濾過(UF)精製し、pH調整したSBRラテックス(Tg:24℃)40質量%を106g、フタラジン化合物の5質量%溶液18mlを添加し、塗布直前にハロゲン化銀混合乳剤Aの10gと良く混合した乳剤層塗布液をそのままコーティングダイへ70ml/m2となるように送液し、塗布した。
上記乳剤層塗布液の粘度は東京計器のB型粘度計で測定して、40℃(No.1ローター、60rpm)で85[mPa・s]であった。
レオメトリックスファーイースト株式会社製RFSフルードスペクトロメーターを使用した25℃での塗布液の粘度は剪断速度が0.1、1、10、100、1000[1/秒]においてそれぞれ1500、220、70、40、20[mPa・s]であった。
【0141】
《乳剤面中間層塗布液の調製》
ポリビニルアルコールPVA-205(クラレ(株)製)の10質量%水溶液772g、顔料の20質量%分散物5.3g、メチルメタクリレート/スチレン/ブチルアクリレート/ヒドロキシエチルメタクリレート/アクリル酸共重合体(共重合質量比64/9/20/5/2)ラテックス27.5質量%液226gにエアロゾールOT(アメリカンサイアナミド社製)の5質量%水溶液を2ml、フタル酸二アンモニウム塩の20質量%水溶液を10.5ml、総量880gになるように水を加え、pHが7.5になるようにNaOHで調整して中間層塗布液とし、10ml/m2になるようにコーティングダイへ送液した。
塗布液の粘度はB型粘度計40℃(No.1ローター、60rpm)で21[mPa・s]であった。
【0142】
《乳剤面保護層第1層塗布液の調製》
イナートゼラチン64gを水に溶解し、メチルメタクリレート/スチレン/ブチルアクリレート/ヒドロキシエチルメタクリレート/アクリル酸共重合体(共重合質量比64/9/20/5/2)ラテックス27.5質量%液80g、フタル酸の10質量%メタノール溶液を23ml、4-メチルフタル酸の10質量%水溶液23ml、0.5mol/Lの硫酸を28ml、エアロゾールOT(アメリカンサイアナミド社製)の5質量%水溶液を5ml、フェノキシエタノール0.5g、ベンゾイソチアゾリノン0.1gを加え、総量750gになるように水を加えて塗布液とし、4質量%のクロムみょうばん26mlを塗布直前にスタチックミキサーで混合したものを18.6ml/m2になるようにコーティングダイへ送液した。
塗布液の粘度はB型粘度計40℃(No.1ローター、60rpm)で17[mPa・s]であった。
【0143】
《乳剤面保護層第2層塗布液の調製》
イナートゼラチン80gを水に溶解し、メチルメタクリレート/スチレン/ブチルアクリレート/ヒドロキシエチルメタクリレート/アクリル酸共重合体(共重合質量比64/9/20/5/2)ラテックス27.5質量%液102g、N-パーフルオロオクチルスルフォニル-N-プロピルアラニンカリウム塩の5質量%溶液を3.2ml、ポリエチレングリコールモノ(N-パーフルオロオクチルスルホニル-N-プロピル-2-アミノエチル)エーテル[エチレンオキシド平均重合度=15]の2質量%水溶液を32ml、エアロゾールOT(アメリカンサイアナミド社製)の5質量%溶液を23ml、ポリメチルメタクリレート微粒子(平均粒径0.7μm)4g、ポリメチルメタクリレート微粒子(平均粒径6.4μm)21g、4-メチルフタル酸1.6g、フタル酸4.8g、0.5mol/Lの硫酸44ml、ベンゾイソチアゾリノン10mgに総量650gとなるよう水を添加して、4質量%のクロムみょうばんと0.67質量%のフタル酸を含有する水溶液445mlを塗布直前にスタチックミキサーで混合したものを表面保護層塗布液とし、8.3ml/m2になるようにコーティングダイへ送液した。
塗布液の粘度はB型粘度計40℃(No.1ローター,60rpm)で9[mPa・s]であった。
【0144】
《熱現像感光材料−1の作成》
上記下塗り支持体のバック面側に、ハレーション防止層塗布液を固体微粒子染料の固形分塗布量が0.04g/m2となるように、またバック面保護層塗布液をゼラチン塗布量が1.7g/m2となるように同時重層塗布し、乾燥し、バック層を作成した。
バック面と反対の面に下塗り面から乳剤層(ハロゲン化銀の塗布銀量0.14g/m2)、中間層、保護層第1層、保護層第2層の順番でスライドビード塗布方式にて同時重層塗布し、熱現像感光材料の試料を作成した。塗布乾燥条件は以下のとおりである。
塗布はスピード160m/分で行い、コーティングダイ先端と支持体との間隙を0.10〜0.30mmとし、減圧室の圧力を大気圧に対して196〜882Pa低く設定した。支持体は塗布前にイオン風にて除電した。
引き続くチリングゾーンにて、乾球温度10〜20℃の風にて塗布液を冷却した後、無接触型搬送して、つるまき式無接触型乾燥装置にて、乾球温度23〜45℃、湿球温度15〜21℃の乾燥風で乾燥させた。
乾燥後、25℃、湿度40〜60%相対湿度で調湿した後、膜面を70〜90℃になるように加熱した。加熱後、膜面を25℃まで冷却した。
作製された熱現像感光材料のマット度はベック平滑度で感光性層面側が550秒、バック面が130秒であった。また、感光層面側の膜面のpHを測定したところ6.0であった。
【0145】
(接着性の評価)
試料の感光層が塗設されている面の表面にカミソリを用いて4mm間隔で縦横それぞれ6本ずつの傷をつけて、25マスのマス目を作った。ただし傷は支持体の表面に到達する深さでつけた。この上に25mmのマイラーテープを貼り付けて十分に圧着した。圧着後5分してから、マイラーテープを180度の剥離角で急激に引っ張って試料から剥離した。これを処理前の接着性とする。このとき感光層から剥離したマス目の数を数え、以下のように分類した。
○:剥離が0マス
△:剥離が5マス未満
×:剥離が5マス以上
また、120℃の熱現像ドラムに25秒間押し付けて熱現像した試料についても同様の評価を実施した。
これを処理後の接着性とする。
【0146】
(面状の評価)
目視にて塗布面状の検査を行い、塗布ムラが良好でスジの発生していないものを〇、塗布ムラ、スジが発生しているものを△、塗布ムラが著しく悪化していてスジが多数発生しているものを×とした。
【0147】
(機械的安定性評価)
熊谷理機工業社製マーロン安定度試験機を用い、25℃、20kg、1200rpm、10分の条件で剪断力を加えた。その後、凝固物を400メッシュの金網で濾過し、乾燥質量を測定し、次式より凝固率を求めた。
【0148】
【式1】
【0149】
評価として、上式で求められた凝固率が0.1%以上を×、0.1%未満を○とした。以上の評価結果を、表2に示した。
【0150】
【表2】
【0151】
実施例2
《熱現像感光材料−2の作成》
熱現像感光材料−1に対して、乳剤層塗布液を以下の様に変更し同様にして熱現像感光材料−2を作製し、同様に評価したところ同様の効果が確認された。
《乳剤層(感光性層)塗布液の調製》
上記で得た顔料の20質量%水分散物を1.1g、脂肪酸銀分散物103g、ポリビニルアルコールPVA-205(クラレ(株)製)の20質量%水溶液5g、上記還元剤錯体の25質量%分散物26g、有機ポリハロゲン化合物分散物-3,-4を1:3(質量比)で総量8.2g、メルカプト化合物10%分散物6.2g、限外濾過(UF)精製しpH調整したSBRラテックス(Tg:24℃)40質量%を106g、フタラジン化合物の5質量%溶液18mlを添加し、塗布直前にハロゲン化銀混合乳剤Aを10gを良く混合した乳剤層塗布液をそのままコーティングダイへ70ml/m2となるように送液し、塗布した。
【0152】
【発明の効果】
本発明により、支持体及び乳剤との密着が良好で、面状が良好で、機械的な安定性が良好な下塗り層を有する熱現像画像記録材料を提供することが可能になった。
Claims (3)
- 支持体の少なくとも一方の面に少なくとも1層のポリエステルを含有する下塗り層を有し、この下塗り層上に画像形成層を有する熱現像画像記録材料において、該ポリエステルが酸成分とアルコール成分からなる、ガラス転移温度が40℃〜100℃であるポリエステルであって、酸成分がテレフタル酸及び/またはイソフタル酸を合計40〜90mol%と式1で表されるスルホニルオキシ基を有するイソフタル酸を60〜10mol%で構成され、アルコール成分がジエチレングリコールを40〜90mol%とシクロヘキサンジメタノールを60〜10mol%で構成されることを特徴とする熱現像画像記録材料。
式1 −(SO3)nM
(式中、nは1または2を表し、Mは水素原子、アルカリもしくはアルカリ土類金属または4級アンモニウム残基を表す。) - 前記nが1であることを特徴とする請求項1に記載の熱現像画像記録材料。
- 画像形成層が、感光性ハロゲン化銀、非感光性有機銀塩、銀イオンのための還元剤及びバインダーを含有することを特徴とする請求項1または2に記載の熱現像画像記録材料。