JP4135940B2 - 異方性拡散媒体 - Google Patents
異方性拡散媒体 Download PDFInfo
- Publication number
- JP4135940B2 JP4135940B2 JP2004305232A JP2004305232A JP4135940B2 JP 4135940 B2 JP4135940 B2 JP 4135940B2 JP 2004305232 A JP2004305232 A JP 2004305232A JP 2004305232 A JP2004305232 A JP 2004305232A JP 4135940 B2 JP4135940 B2 JP 4135940B2
- Authority
- JP
- Japan
- Prior art keywords
- anisotropic diffusion
- diffusion medium
- light
- fluorine
- transmitted light
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明の異方性拡散媒体の一実施形態は、図1より説明できる。すなわち、フッ素含有の光硬化性化合物とフッ素不含の光硬化性化合物を含む組成物の硬化物からなるシート状の異方性拡散媒体1の内部には、微小な領域2が多数形成されている。これら微小領域2は、異方性拡散媒体1の法線S方向に配された点状光源から互いに平行な紫外線を照射して形成されており、これら微小領域は全て法線S方向と平行に形成されている。図1では微小領域2を円柱状に模式的に記載したが、その形状は円状、多角形状、不定形状など、特に限定されるものではない。
フッ素原子の割合が低いと、硬化した際に形成される領域が曖昧になり、異方性拡散が弱くなる。
厚さ75μm、76×26mmサイズのPETフィルム(東洋紡社製、商品名:A4300)の縁部全周に、ディスペンサーを使い硬化性樹脂で高さ0.2mmの隔壁を形成した。この中に下記の紫外線硬化樹脂組成物を滴下し、別のPETフィルムでカバーした。
・2−(パーフルオロオクチル)−エチルアクリレート 50重量部
(フッ素含有率61%、共栄社化学社製、商品名:ライトアクリレートFA−108)
・1,9−ノナンジオールジアクリレート 50重量部
(フッ素不含、共栄社化学社製、商品名:ライトアクリレート1.9ND−A)
・2−ヒドロキシ−2−メチル−1−フェニルプロパン−1−オン 4重量部
(チバ・スペシャルティ・ケミカルズ製、商品名:Darocure1173)
この両面をPETフィルムで挟まれた0.2mmの厚さの液膜に対して、UVスポット光源(浜松ホトニクス社製、商品名:L2859−01)の落射用照射ユニットから垂直に、照射強度30mW/cm2の紫外線を1分間照射して、図1に示すような棒状の微小な領域を多数有する実施例1の異方性拡散媒体を得た。
76×26mmサイズのスライドガラスの縁部全周に、ディスペンサーを使い硬化性樹脂で高さ0.2mmの隔壁を形成した。この中に下記の紫外線硬化樹脂組成物を滴下し、別のスライドガラスでカバーした。
・2−(パーフルオロオクチル)-エチルアクリレート 50重量部
(フッ素含有率61%、共栄社化学社製、商品名:ライトアクリレートFA−108)
・1,9−ノナンジオールジアクリレート 50重量部
(フッ素不含、共栄社化学社製、商品名:ライトアクリレート1.9ND−A)
・2−ヒドロキシ−2−メチル−1−フェニルプロパン−1−オン 4重量部
(チバ・スペシャルティ・ケミカルズ製、商品名:Darocure1173)
この両面をスライドガラスで挟まれた0.2mmの厚さの液膜に対して、UVスポット光源(浜松ホトニクス社製、商品名:L2859−01)の落射用照射ユニットから垂直に、照射強度30mW/cm2の紫外線を1分間照射した。その後両側のスライドガラスを外して、図1に示すような棒状の微小な領域を多数有する実施例2の異方性拡散媒体を得た。
76×26mmサイズのスライドガラスの縁部全周に、ディスペンサーを使い硬化性樹脂で高さ0.2mmの隔壁を形成した。この中に下記の紫外線硬化樹脂組成物を滴下し、別のスライドガラスでカバーした。
・2,2,2−トリフロロエチルメタクリレート 50重量部
(フッ素含有率33%、共栄社化学社製、商品名:ライトエステルM−3F)
・1,9−ノナンジオールジアクリレート 50重量部
(フッ素不含、共栄社化学社製、商品名:ライトアクリレート1.9ND−A)
・2−ヒドロキシ−2−メチル−1−フェニルプロパン−1−オン 4重量部
(チバ・スペシャルティ・ケミカルズ製、商品名:Darocure1173)
この両面をスライドガラスで挟まれた0.2mmの厚さの液膜に対して、UVスポット光源(浜松ホトニクス社製、商品名:L2859−01)の落射用照射ユニットから垂直に、照射強度30mW/cm2の紫外線を1分間照射した。その後両側のスライドガラスを外して、図1に示すような棒状の微小な領域を多数有する比較例3の異方性拡散媒体を得た。
実施例1と同じPETフィルムに挟まれた状態の紫外線硬化組成物に、PETフィルムの長辺と直交する方向に配置した発光長さ125mmの線状UV光源(日本UVマシーン社製、商品名:ハンディUV装置HUV−1000)から、実施例1と同じ照射強度の紫外線を垂直に照射して、図3に示すような屈折率の異なる板状の領域を有する比較例1の異方性拡散媒体を得た。
[比較例2]
76×26mmサイズのスライドガラスの縁部全周に、ディスペンサーを使い硬化性樹脂で高さ0.2mmの隔壁を形成した。この中に下記の紫外線硬化樹脂組成物を滴下し、別のスライドガラスでカバーした。
・3−メチル−n−ブチルアクリレート 50重量部
(フッ素不含、共栄社化学社製、商品名:ライトアクリレートIAA)
・1,9−ノナンジオールジアクリレート 50重量部
(フッ素不含、共栄社化学社製、商品名:ライトアクリレート1.9ND−A)
・2−ヒドロキシ−2−メチル−1−フェニルプロパン−1−オン 4重量部
(チバ・スペシャルティ・ケミカルズ製、商品名:Darocure1173)
この両面をスライドガラスで挟まれた0.2mmの厚さの液膜に対して、UVスポット光源(浜松ホトニクス社製、商品名:L2859−01)の落射用照射ユニットから垂直に、照射強度30mW/cm2の紫外線を1分間照射した。その後両側のスライドガラスを外して、図1に示すような棒状の微小な領域を多数有する比較例2の異方性拡散媒体を得た。
2 棒状硬化領域
3 受光部
I 入射光
T 透過光
P 入射方向
S 異方性拡散媒体表面の法線
Claims (4)
- 少なくともフッ素を含有する光硬化性化合物およびフッ素を含有しない光硬化性化合物を含む組成物の硬化物からなる樹脂層を有する異方性拡散媒体であって、
上記樹脂層の内部には、複数の棒状硬化領域の集合体が形成されており、
上記棒状硬化領域は、所定の方向Pに対して平行に延在し、
上記異方性拡散媒体の一方の側の任意の点において、任意の入射方向から光線を透過させたときに、上記光線の直線透過光量は入射方向の角度によって異なり、上記光線の直線透過光量及び出射方向をベクトル表示し、これらのベクトルの先端を結ぶと、上記所定の方向Pに対称軸を有する曲面が得られ、
上記フッ素を含有する光硬化性化合物中のフッ素原子が占める質量の割合が50%以上であることを特徴とする異方性拡散媒体。 - 前記所定の方向Pは、前記異方性拡散媒体表面に対する法線Sであることを特徴とする請求項1に記載の異方性拡散媒体。
- 透明基体上に請求項1または2に記載の異方性拡散媒体を積層した構成からなることを特徴とする異方性拡散媒体。
- 請求項1〜3のいずれかに記載の異方性拡散媒体の両側に透明基体を積層した構成からなることを特徴とする異方性拡散媒体。